CN1049869A - The quick-acting gaseous combined cementation process of carbon and other elements - Google Patents
The quick-acting gaseous combined cementation process of carbon and other elements Download PDFInfo
- Publication number
- CN1049869A CN1049869A CN 89106936 CN89106936A CN1049869A CN 1049869 A CN1049869 A CN 1049869A CN 89106936 CN89106936 CN 89106936 CN 89106936 A CN89106936 A CN 89106936A CN 1049869 A CN1049869 A CN 1049869A
- Authority
- CN
- China
- Prior art keywords
- stove
- carbon
- carbonitriding
- elements
- altogether
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention belongs to the metal heat treatmet field, what relate to is the quick-acting gaseous combined cementation process of steel part carbon and other elements, is particularly suitable for carbonitriding and adopts.The existing processes cycle is long.This technology is earlier the workpiece surface oxidation to be generated layer of even, the thickness oxide film (Fe less than 1 μ
3O
4), restore to the first pig iron, ooze altogether with ordinary method then.Because just the pig iron has intensive absorption and katalysis, oozes significantly altogether and is quickened.The present invention can obtain high infiltration rate, again equipment, penetration enhancer, steel grade is not had special pearl requirement, and technology is simple, pollution-free.With the carbonitriding is example, and the present invention can shorten process cycle 56%.
Description
The invention belongs to the metal heat treatmet field, what relate to is the quick-acting gaseous combined cementation process of steel part carbon and other elements.The composite cementation of so-called here carbon and other elements is meant that workpiece surface infiltrates carbon and another or more than one element simultaneously, as carbonitriding, carbon, nitrogen and boron ooze altogether, carbon nitrogen sulphur common seeping etc., therefore also can be described as the binary or the multiple permeation of carbon and other elements.
Steel part is after gaseous carbon nitrogen worker is oozed, and its fatigue strength, wear resistance, solidity to corrosion, temper resistance all are better than gas cementation.The gas carbonitriding treatment temp is low, the workpiece deformation tendency is little, crystal grain is difficult for growing up, and prolong the work-ing life of stove and instrument, and energy direct quenching, and operation is simple.This technology now has been widely used in each industrial sector, handles multiple parts such as gear, axle class, fastening piece, obtains good result.In order further to improve the comprehensive mechanical performance of infiltration layer, to satisfy the performance requriements of part under various working conditions, some enterprises and research institution also test and have adopted carbon and other elements to ooze altogether in recent years, what particularly the ternary of carbon, nitrogen and other elements or ternary were above oozes altogether, as carbon, nitrogen and boron ooze altogether, carbon nitrogen sulphur common seeping or the like, also obtained good effect.On the other hand, the same with other thermo-chemical treatments, long, energy consumption height of treatment process cycle is a big shortcoming of this class composite cementation of comprising carbonitriding.Quicken the composite cementation process of carbon and other elements, particularly quicken the carbonitriding process, this is thermal treatment worker's an effort target always.Though people once proposed many schemes by fair means or foul, be difficult to effectively because of the restriction that is subjected to equipment, material and other factors eventually and employing widely, and infiltration rate improves not remarkable." quick gas carburizing process with activating catalysis and infiltration for steel pieces " (Chinese patent literature CN87100497) of applicant invention, make the steel piece surface initial oxidation restore the pig iron just, use the ordinary method gas cementation subsequently, shortened process cycle greatly, and must not change existing equipment, have distinct economic.But because composite cementations such as carbonitridings, its process mechanism, structure of vanadinizing layer all are different from single carburizing, the acting gaseous combined cementation production technique of therefore also necessary further development research steel part activating catalysis and infiltration carbon and other elements, particularly carbon and nitrogen.
The object of the present invention is to provide a kind of carbon and other elements, the quick-acting gaseous combined cementation process of carbon and nitrogen particularly requires not only to shorten process cycle, the requirement of quality product conformance with standard, and is applicable to that common gases oozes stove altogether, do not need special penetration enhancer and exotic materials, no industrial pollution.
The composite cementation of carbon and other elements is that the decomposition by chemical carburizer obtains activity and oozes atom altogether, and active atomic is absorbed afterwards to the workpiece internal divergence by steel piece surface.Catalyzer can improve the decomposition rate of penetration enhancer, and itself composition, quantity and chemical property remain unchanged before and after reaction.Iron is one of modal catalyzer.Be adsorbed on oozing atom altogether and the lattice of iron can further be invaded and dissolving of workpiece surface, by workpiece surface is absorbed.Absorption can be divided into physical adsorption and chemisorption two classes.In the thermo-chemical treatment of steel, mainly be chemisorption.Absorption is the extremely important ring of heterogeneous reaction.Having only by absorption just to make chemical reaction velocity obtain accelerating; Also have only by absorption, catalyzer is had an effect; Also make active atomic further become possibility to the workpiece internal divergence just because of absorption.General workpiece all will remove dirt settlings such as degreasing and iron rust before oozing altogether, this accomplishes than being easier to.In fact, even the oil removing that carefully eliminates rust obtains the workpiece surface of " cleaning ", also still there is one deck passive film to some extent.The existence of passive film will hinder the decomposition of penetration enhancer, and the absorption of active atomic, absorption make and ooze altogether and can't quicken.Simultaneous test shows that after the sample of same stove same position oozed altogether, the surface was the sample of active state, and it is that the sample of " cleaning " state is high by about 50% that its depth of penetration is wanted specific surface.If take technological measure, make workpiece surface become the first pig iron of active state, the first pig iron is the active catalyst that penetration enhancer decomposes, and Chemical Composition and the weave construction owing to workpiece surface changes simultaneously, chemisorption and physical adsorption are all greatly strengthened, and can play one's part to the full.By first pig iron intensive absorption and catalysis, increased workpiece surface active atomic concentration effectively, accelerated active absorption of oozing atom altogether, make workpiece surface obtain higher infiltration concentration of element, and very steep concentration gradient, and then make diffusion obtain quickening.The decomposition of composite cementation like this, absorption, three processes of diffusion have all obtained acceleration, and whole infiltrate journey altogether just can be finished within a short period of time.
Purpose of the present invention realizes according to above-mentioned principle.Processing method of the present invention is to allow the workpiece surface oxidation generate layer of even, the thickness oxide film (Fe less than 1 μ earlier
3O
4), restore and be the first pig iron, carry out the acting gaseous combined cementation of carbon such as carbonitriding and other elements then according to a conventional method.
Implement the present invention, preferably allow workpiece oxidation, reduction and several stages such as ooze altogether and all once finish oozing in the stove altogether.Therefore for gas carbonitriding, production technique of the present invention preferably includes following steps:
1, workpiece is packed into and is oozed stove altogether.
2, making stove interior is oxidizing atmosphere, and in the process that temperature rises gradually, workpiece surface generates layer of even oxide film (Fe
3O
4).
Making stove interior is oxidizing atmosphere, the visual type of furnace, workpiece what, situation such as workpiece surface Residual oil, close the hole immediately after taking workpiece to go into stove, feed the method for the carburizing agent of low discharge or the organic agent of carbonitriding (as trolamine etc.), the air of bringing into during by shove charge is realized, also can not feed any penetration enhancer under situation about having.When big and workpiece surface Residual oil is a lot of when batch, need close the hole, even also will open bell.The oxide film that generates is the grey blue translucent, because thickness is less than 1 μ, thereby workpiece size precision and smooth finish is had no effect.
3, make and changed to reducing atmosphere by oxidizing atmosphere in the stove, the oxide film of workpiece surface is by the first pig iron of reduction such as the hydrogen in the furnace gas.
Changed to reducing atmosphere by oxidizing atmosphere in the stove, a kind of method of taking is to strengthen the penetration enhancer flow gradually.The increasing of flow does not have obvious black smoke with venting hole and is advisable.
4, make furnace atmosphere reach common carbonitriding atmosphere, ooze by force.
Because first pig iron intensive sorption, workpiece surface is difficult for producing " accumulations " phenomenon of penetration enhancer atom, thereby can adopt routine to ooze big penetration enhancer consumption altogether to ooze by force.The time of oozing the stage is by force mainly depended on the requirement of depth of penetration and surface structure, generally accounts for the 1/3-1/2 of technological process.
5, spread according to a conventional method and come out of the stove.
Because NH
3Has extremely strong reductibility, under lower temperature, just can make iron oxide reduction, feed too early ammonia (routine is oozed method) and can't make workpiece obtain the nascent iron surface of active state, after the therefore logical ammonia time was reduced to just the pig iron with ferric oxide, stove was good to Wen Shiwei.Thus, for carbonitriding optimum implementation of the present invention be: according to circumstances adopt 0-30 to drip oxidizing atmosphere in the kerosene control stove, after generating oxide film, strengthening the kerosene amount of dripping makes oxide film be reduced into the pig iron just, stove feeds kerosene to Wen Houtong ammonia and the big amount of dripping, and reduces the penetration enhancer flow after oozing by force and spreads.
Common gas carbonitriding technology, workpiece go into will feed behind the stove big flow penetration enhancer (big flow ammonia or supply with carburizing agent and ammonia simultaneously, but based on ammonia also has only to add carburizing agent), with quick eliminating furnace air, prevent workpiece oxidation and decarburization.Think if not like this, then can cause adverse consequencess such as the slow and diffusion layer organization defective of common infiltration rate degree.The present invention has changed this traditional concept, adopted initial oxidation, restored, after the method for oozing altogether.As long as control is proper, process cycle is shortened significantly than common carbonitriding, conservation of power and penetration enhancer improve plant factor and reduce equipment attrition, reduce production costs, and up-to-standard rate reaches 100% simultaneously, and can realize that carbides-free oozes altogether.Compare with existing method, advantage of the present invention just is to guarantee to obtain high infiltration rate and qualified quality product, again equipment, penetration enhancer, steel grade is not had particular requirement, and technological process is simple, pollution-free, " newly-increased material consumption cost " is zero, thereby can obtain distinct economic.With the carbonitriding is example, behind employing the present invention, compares with common process, and process cycle shortens 56%, and kerosene saves 55%, and ammonia saves 50%.
Embodiment: use the RJJ-60-9T pit gas carburizing furnace to carry out the quick carbonitriding of gas.Penetration enhancer is kerosene and ammonia, and per 100 kerosene are 3.8 milliliters.Workpiece is an automobile gear, and material is 20CrMnTi.Depth of penetration requires to reach 0.6-0.8mm, and surface hardness requires to reach IIRC58-64.Adopt routine to ooze temperature altogether, be specially 360 ℃.Technological process is as follows:
1, the preparatory stage:, leave the 5-10 millimeter between each workpiece at interval with the workpiece behind the surface degreasing pack into charging basket or anchor clamps.
2, oxidation, reduction, exhaust phase: after furnace temperature is raised to 860 ℃, charging basket that workpiece is housed or anchor clamps are put into stove, close the hole air is entered again.The flow that drips (look batch and adjust, as follows) with per minute 4-20 splashes into kerosene.When workpiece surface reaches required degree of oxidation, the kerosene amount of dripping is increased to per minute 80-150 gradually drips, furnace air is discharged gradually, furnace gas is changed to reducing atmosphere by oxidizing atmosphere, and the oxide film of workpiece surface is reduced into the active catalyst pig iron just.
3, ooze by force, diffusion and cooling come out of the stove: when furnace temperature is raised to 860 ℃,, and kerosene is increased to 150 of per minutes with the logical ammonia of low discharge.Through after 1.5 hours, ammonia is adjusted into 3 liters of per minutes again, kerosene is adjusted to 120 of per minutes.Again through 1 hour, sampling records depth of penetration and has reached more than the 0.6mm, and be adjusted to 60 of per minutes to kerosene this moment, allows stove be cooled to 830 ℃ and stop for ammonia.Stop the ammonia oil quenching of coming out of the stove after 15 minutes.Carry out strictness by " automobile carbonitriding gear metallographic examination standard " and check, every metallographic structure rank of product, surface hardness, centre hardness stove stove are qualified, and infiltration layer black tissue never occurs.Oozing time ratio " two sections carbonitridings " technology altogether significantly shortens: 3 hours depth of penetration of technology carbonitriding of the present invention can reach to begin to calculate when 0.77mm(finishes by common exhaust and ooze the time altogether), and " two sections carbonitridings " technology must be oozed 4 hours depth of penetration altogether and just can be reached 0.6mm.What also must illustrate is that " two sections carbonitridings " technology is compared with general carbonitriding technology, and its time of oozing has altogether shortened about 40% (seeing " metal heat treatmet " 1988.12, the Cui Xiang of Hebei Polytechnical College etc.: two sections carbonitriding technologies and application).According to consulting reference materials, " two sections carbonitriding technologies " is domestic disclosed the fastest infiltration rate gas carbonitriding technology.
Claims (4)
1, the quick-acting gaseous combined cementation process of carbon and other elements is characterized in that allowing earlier the workpiece surface oxidation generate layer of even, the thickness oxide film (Fe less than 1 μ
3O
4), restore and be the first pig iron, carry out the acting gaseous combined cementation of carbon such as carbonitriding and other elements then according to a conventional method.
2, the quick-acting gaseous combined cementation process of carbon as claimed in claim 1 and other elements, several stages such as it is characterized in that oxidation, the reduction of workpiece and ooze are altogether all once finished oozing in the stove altogether.
3, the quick-acting gaseous combined cementation process of carbon as claimed in claim 2 and other elements is characterized in that may further comprise the steps for carbonitriding:
A, workpiece are packed into and are oozed stove altogether,
B, allow and be oxidizing atmosphere in the stove, in the process that temperature rises gradually, workpiece surface generates the layer of even oxide film,
C, make and changed to reducing atmosphere by oxidizing atmosphere in the stove, the oxide film of workpiece surface is reduced into the pig iron just by the hydrogen in the furnace gas etc.,
D, make furnace atmosphere reach common carbonitriding atmosphere, ooze by force,
E, spread according to a conventional method and come out of the stove.
4, the acting gaseous combined cementation process of carbon as claimed in claim 3 and other elements, it is characterized in that: for carbonitriding, according to circumstances adopt 0-30 to drip oxidizing atmosphere in the kerosene control stove, after generating oxide film, strengthening the kerosene amount of dripping makes oxide film be reduced into the pig iron just, stove feeds kerosene to Wen Houtong ammonia and the big amount of dripping, and reduces the penetration enhancer flow after oozing by force and spreads.