CN104966462B - On Orgnic Luminous Materials anti-counterfeiting mark and preparation method thereof - Google Patents
On Orgnic Luminous Materials anti-counterfeiting mark and preparation method thereof Download PDFInfo
- Publication number
- CN104966462B CN104966462B CN201510394562.3A CN201510394562A CN104966462B CN 104966462 B CN104966462 B CN 104966462B CN 201510394562 A CN201510394562 A CN 201510394562A CN 104966462 B CN104966462 B CN 104966462B
- Authority
- CN
- China
- Prior art keywords
- layer
- materials
- luminous materials
- orgnic luminous
- pet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention belongs to anti-counterfeiting mark technical field, and in particular to a kind of On Orgnic Luminous Materials anti-counterfeiting mark and preparation method thereof.On Orgnic Luminous Materials anti-counterfeiting mark is that digital code information layer, On Orgnic Luminous Materials layer, PET anti-fake materials layer, holographic information layer and printing figure message layer, aluminium coated, adhesive layer and silicone oil ply of paper are sequentially connected from top to bottom, holographic information layer and printing figure message layer are located at same aspect and are set up in parallel, and PET anti-fake materials layer is made up of pet layer and contour forging imaging layer.The present invention solves the problems, such as the proportioning of On Orgnic Luminous Materials, solve the problem of optics recognition system is corresponded with the spectrum that On Orgnic Luminous Materials are sent, solve On Orgnic Luminous Materials and lose problem in process of production, enhance the anti-counterfeiting power of anti-counterfeiting mark.
Description
Technical field
The invention belongs to anti-counterfeiting mark technical field, and in particular to a kind of On Orgnic Luminous Materials anti-counterfeiting mark and its system
Preparation Method.
Background technology
Using exciting, fluorescent ink is false proof to have had one-hundred-year history, particularly infrared excitation ink and burst of ultraviolel ink to exist
False proof industry is also widely used, and these anti-counterfeiting technologies are mainly entered by the glow color after ultraviolet or infrared radiation
Row is false proof, this to seem simple and easy to apply with the technology that sense organ is told truth from falsehood but actually and unreliable, because human eye is to color
Differentiate actually very fuzzy, criminal is easy for producing the imitation that color is similar and human eye can not be distinguished.
The content of the invention
It is an object of the invention to provide a kind of On Orgnic Luminous Materials anti-counterfeiting mark, peculiar spectrum can be sent, is had
Multiple anti-fake function, with very high false proof exclusivity, greatly strengthen anti-counterfeiting power；Invention also provides organic photic
The preparation method of luminescent material anti-counterfeiting mark, it is scientific and reasonable, simple and easy to apply.
On Orgnic Luminous Materials anti-counterfeiting mark of the present invention is digital code information layer, On Orgnic Luminous Materials layer, PET
Anti-fake material layer, holographic information layer and printing figure message layer, aluminium coated, adhesive layer and silicone oil ply of paper are sequentially connected from top to bottom, holography letter
Breath layer and printing figure message layer are located at same aspect and are set up in parallel, and PET anti-fake materials layer is made up of pet layer and contour forging imaging layer.
Described PET anti-fake materials layer, holographic information layer are sequentially connected from top to bottom with aluminium coated, PET anti-fake materials layer,
Printing figure message layer is sequentially connected from top to bottom with aluminium coated.
On Orgnic Luminous Materials in described On Orgnic Luminous Materials layer can not light in a free state,
The invisible spectrum of different wave length can be just sent under only coordinating with aluminium coated.
The spectrum that described On Orgnic Luminous Materials are sent is distinguished with light knowledge read apparatus, and is not shared the same light
Spectrum is one-to-one with optics recognition system.
Described On Orgnic Luminous Materials layer and the pet layer on PET anti-fake materials layer are inseparable.
Described On Orgnic Luminous Materials layer both can be disposable or permanent.
The preparation method of On Orgnic Luminous Materials anti-counterfeiting mark of the present invention, step is as follows：
(1) it is molded：On PET anti-fake materials, stamping machine embossed holographic information and printing figure message information are utilized；
(2) aluminium coated：Aluminized using vacuum aluminizing method；
(3) gluing：Gluing is carried out using glue spreader and compound with silicone oil paper；
(4) coating layer：Using coating machine PET anti-fake materials PET faces applied coating solution；
(5) digital code information is printed on coating layer using endowed machine；
(6) it is die cut：Single mark is die-cut to using automatic die cutter.
The thickness of PET anti-fake materials described in step (1) is 16-50 μm.
Aluminium coated sheet resistance value described in step (2) is 0.8-1.2.
Glue-spread is 13-25 Ke/㎡ in gluing described in step (3).
Coating fluid described in step (4) is made up of the raw material of following percentage by weight：
On Orgnic Luminous Materials 2-3%
Resin 15-30%
Organic solvent 70-85%.
Described resin is thermoplastic resin, and organic solvent is one kind in alcohols, ketone, benzene class or esters.
110-150 mesh metal rollers are used in coating described in step (4), oven temperature is 75-95 DEG C, and speed is
60-80 ms/min.
The present invention compared with prior art, has the advantages that：
1st, the proportioning of On Orgnic Luminous Materials is solved the problems, such as.
2nd, the problem of spectrum that optics recognition system and On Orgnic Luminous Materials are sent is corresponded is solved.
3rd, On Orgnic Luminous Materials are solved and loses problem in process of production, it is ensured that organic light inside anti-counterfeiting mark
Electroluminescent material keeps constant.
4th, the anti-counterfeiting power of anti-counterfeiting mark is enhanced.
Embodiment
The present invention is described further with reference to embodiments.
Embodiment 1
2,000,000 pieces of customer order
(1) it is molded：On 16 μm of PET anti-fake materials, stamping machine embossed holographic information and printing figure message information are utilized.
(2) aluminium coated：Aluminized using vacuum aluminizing method, aluminium coated sheet resistance value is 0.8.
(3) gluing：Gluing is carried out using glue spreader and compound with silicone oil paper, and glue-spread is 13 Ke/㎡.
(4) coating layer：Using coating machine PET anti-fake materials PET faces applied coating solution, using 110 mesh metal rollers,
Oven temperature is set to 75 DEG C, 60 ms/min of speed.Coating fluid is made up of the raw material of following percentage by weight：
On Orgnic Luminous Materials CD-152 2%
Rosin 15%
Ethanol 83%.
CD-152 is the production of INKSURE Technologies companies.
(5) digital code information is printed on coating layer using endowed machine.
(6) it is die cut：Single mark is die-cut to using automatic die cutter.
Embodiment 2
1,500,000 pieces of customer order
(1) it is molded：On PET anti-fake materials, stamping machine embossed holographic information and printing figure message information are utilized.PET prevents
The thickness of pseudo- material is 20 μm.
(2) aluminium coated：Aluminized using vacuum aluminizing method, aluminium coated sheet resistance value is 1.0.
(3) gluing：Gluing is carried out using glue spreader and compound with silicone oil paper, and glue-spread is 20 Ke/㎡.
(4) coating layer：Using coating machine in the PET faces applied coating solution of PET anti-fake materials, 130 mesh gold is used during coating
Belong to roller, oven temperature is set to 85 DEG C, 70 ms/min of speed.Coating fluid is made up of the raw material of following percentage by weight：
On Orgnic Luminous Materials CD-157 2.5%
C9 Petropols 17.5%
Ethyl acetate 80%.
CD-157 is the production of INKSURE Technologies companies.
(5) digital code information is printed on coating layer using endowed machine.
(6) it is die cut：Single mark is die-cut to using automatic die cutter.
Embodiment 3
3,000,000 pieces of customer order
(1) it is molded：On PET anti-fake materials, stamping machine embossed holographic information and printing figure message information are utilized.PET prevents
The thickness of pseudo- material is 50 μm.
(2) aluminium coated：Aluminized using vacuum aluminizing method, aluminium coated sheet resistance value is 1.2.
(3) gluing：Gluing is carried out using glue spreader and compound with silicone oil paper, and glue-spread is 25 Ke/㎡.
(4) coating layer：Using coating machine in the PET faces applied coating solution of PET anti-fake materials, 150 mesh gold is used during coating
Belong to roller, oven temperature is set to 95 DEG C, 80 ms/min of speed.Coating fluid is made up of the raw material of following percentage by weight：
On Orgnic Luminous Materials CD-238 3%
C5 Petropols 25%
Toluene 72%.
CD-238 is the production of INKSURE Technologies companies.
(5) digital code information is printed on coating layer using endowed machine.
(6) it is die cut：Single mark is die-cut to using automatic die cutter.
Claims (6)
1. a kind of On Orgnic Luminous Materials anti-counterfeiting mark, it is characterised in that digital code information layer, On Orgnic Luminous Materials layer,
PET anti-fake materials layer, holographic information layer and printing figure message layer, aluminium coated, adhesive layer and silicone oil ply of paper phase successively from top to bottom
Even, holographic information layer and printing figure message layer are located at same aspect and are set up in parallel, and PET anti-fake materials layer is by pet layer and holographic mould
Press imaging layer composition；
On Orgnic Luminous Materials in described On Orgnic Luminous Materials layer can not light in a free state, only
The invisible spectrum of different wave length can be just sent under coordinating with aluminium coated；
The preparation method of described On Orgnic Luminous Materials anti-counterfeiting mark, step is as follows：
（1）Molding：On PET anti-fake materials, stamping machine embossed holographic information and printing figure message information are utilized；
（2）Aluminium coated：Aluminized using vacuum aluminizing method；
（3）Gluing：Gluing is carried out using glue spreader and compound with silicone oil paper；
（4）Coating layer：Using coating machine PET anti-fake materials PET faces applied coating solution；
（5）Digital code information is printed on coating layer using endowed machine；
（6）Cross cutting：Single mark is die-cut to using automatic die cutter；
Step（4）Described in coating fluid be made up of the raw material of following percentage by weight：
On Orgnic Luminous Materials 2-3%
Resin 15-25%
Organic solvent 72-83%.
2. On Orgnic Luminous Materials anti-counterfeiting mark according to claim 1, it is characterised in that described organic photic hair
The spectrum that luminescent material is sent is distinguished with light knowledge read apparatus, and different spectrum and optics recognition system are one a pair
Answer.
3. On Orgnic Luminous Materials anti-counterfeiting mark according to claim 1, it is characterised in that step（1）Described in
The thickness of PET anti-fake materials is 16-50 μm.
4. On Orgnic Luminous Materials anti-counterfeiting mark according to claim 1, it is characterised in that step（2）Described in plating
Aluminium lamination sheet resistance value is 0.8-1.2.
5. On Orgnic Luminous Materials anti-counterfeiting mark according to claim 1, it is characterised in that step（3）Described in painting
Glue-spread is 13-25 Ke/㎡ in glue.
6. On Orgnic Luminous Materials anti-counterfeiting mark according to claim 1, it is characterised in that step（4）Described in painting
110-150 mesh metal rollers are used in cloth, oven temperature is 75-95 DEG C, and speed is 60-80 ms/min.