CN103072393A - Preparation method for laser hot stamping foil of metal coin and prepared product - Google Patents

Abstract

The invention relates to the technology of laser holography anti-counterfeiting hot stamping, in particular to a preparation method for laser hot stamping foil of a metal coin and prepared laser hot stamping foil by using the method, and provides a preparation method for laser hot stamping foil of a metal coin and prepared laser hot stamping foil by using the method, which can adapt to gold stamping on the surface of the metal coin, enrich patterns on the surface of the metal coin, has an anti-counterfeiting function and is suitable for printing after stamping. The preparation method comprises the steps that a metallic nickel plate is manufactured, and a release layer, an imaging layer, a mold pressing layer, an aluminum coated layer and an adhesive layer are coated on a basement membrane strip, so that the metal coin has a brand-new effect, the operation process is simple and rapid, reproducibility of texts is good, large-scale production and durability are realized, the cost is reduced, the adhesion of the laser hot stamping foil is high, after being fastened on the surface of a metal product, the hot stamping foil does not easily fall off and has a smooth surface, through changing the formula of the adhesive layer and coating the adhesive layer for multiple times, a multi-layer bonding layer is formed, so that texts are firmly adhered on the surface of the metal, and wear resistance and weather fastness are realized.

Description

Be used for the laser electrochemical aluminum stamping systems preparation method of metal coins and the product of making

Technical field

The present invention relates to antiforge laser holographic thermoprint technology, particularly a kind of for the laser electrochemical aluminum stamping systems preparation method of metal coins and the laser electrochemical aluminum stamping systems made from the method thereof.

Background technology

Gold stamping is under uniform temperature and pressure anodized aluminium to be commonly called as gold stamping paper tinsel thermoprint to the technical process on stock surface.In recent years along with the raising of living standards of the people, the development of national economy, people more and more pay attention to outward appearance and the delicately packed degree of various product, figure line by gold stamping paper tinsel thermoprint presents strong metallic luster, color glow, will never fade, its bright degree has substantially exceeded ink printing, make product have high-grade sensation and give Beautiful treat, improved the artistry of product, so gold stamping all trades and professions that are widely used in, gilding technology is also improved rapidly, the laser anti-counterfeiting sign is widely used at industry-by-industry and field as the crystallization of new and high technology at present, the laser anti-counterfeiting anodized aluminium is applied in paper in false proof industry more, gold stamping form processing on the cloth, not only stock is partially soft, and thickness is less, be convenient to the enforcement of gold stamping operation, but also be in the starting stage at thermoprint laser holographic mark on the metal coins both application of laser holography in the metal coins manufacturing, metal coins is high because of hardness, thickness is large, there is great difference with common in the industry stock, therefore, at tobacco bale, medicine wait utilization in the packing more widely laser hologram locating thermoprint technology be applied to not yet maturely the manufacturing technology field of gold and silver coin, producing perfect laser hologram locating thermoprint pattern on metal coins also has many problems to need to be resolved hurrily at present, need to be according to the characteristics of metal coins, customize gold stamping paper tinsel and realize that metal coins is gold stamping, the preparation method of existing gold stamping paper tinsel and gold stamping paper tinsel product are applied to exist on the metal coins many larger defectives, for example gold stamping paper tinsel raw material use in test slightly has improper will causing to peel off weak effect, can not very clean peeling off, and the aluminium coated tack is poor, be full of cracks, printing ink adheres to the problems such as bad, how to design and be suitable for the gold stamping paper tinsel of thermoprint on metal coins, how to adopt the trans-printing mode that graph text information is made into laser holographic thermoprinted paper tinsel, and then adopt the thermoprint of laser holographic locating thermoprint technology to metal coins, and operation requirements is simple, environmental protection and can steady implementation be industry engineers and technicians problems in the urgent need to address.

Summary of the invention

The purpose of this invention is to provide and a kind ofly can adapt at the metal coins surface gilding, enrich the metal coins picture on surface, the laser electrochemical aluminum stamping systems preparation method who is used for metal coins of printing performance and the laser electrochemical aluminum stamping systems made from the method thereof after possessing simultaneously the surface and scalding.

The objective of the invention is to finish by the following technical programs:

A kind of laser electrochemical aluminum stamping systems preparation method for metal coins of the present invention, wherein: may further comprise the steps:

Step 1), make the metallic nickel version: picture and text are engraved on laser by litho machine and produce the laser hologram version on the sensitization offset plate, adopt again the electroforming mode that the laser hologram version is made metallic nickel version for mold pressing;

Step 2) be coated with release layer at basement membrane film band: according to release layer composition component preparation melamine releasing layer coating be: by mass parts: melamine mould release solvent is alcohol 40-50 mass parts, butanone 30-35 mass parts, auxiliary agent 0.007-0.008 mass parts, melamine 70-85 quality, after first described alcohol, butanone mixing, homogenizer being stirred, add melmac and described auxiliary agent, stirred 20 minutes with homogenizer, make releasing layer coating and upper coating machine and be coated on the basement membrane film band and consist of release layer;

Step 3) is coated with imaging layer at described release layer: be mixed with the picture coating according to the imaging layer composition component: count butanone 30 mass parts, the mixing of butyl ester 10 mass parts and dissolving pigment by mass parts, add thermoplastic resin 30 mass parts, on the described release layer that has been coated with, evenly be coated with one deck imaging layer with coating machine, be coated with the coating layer thickness of described imaging layer in coating dry measure 0.9 g/m 2-1.2g/m 2, through the drying chamber oven dry, its bake out temperature is at 140 ℃-160 ℃;

Step 4), by the moulding press that described metallic nickel version is housed the holographic false proof pattern mold pressing on the described metallic nickel version is transferred to and to be formed embossed plies on the imaging layer, molding pressure 2 kg-3kg, molding temperature are at 200 ℃-240 ℃, mold pressing speed 20m/min;

Step 5), there is the described basement membrane film band of holographic pattern to carry out vacuum aluminum-coated formation aluminium coated by vacuum aluminum-plating machine mold pressing, described aluminum layer thickness is take the electric-resistivity method detection as 2.0 Ω, because the aluminium coated on the vacuum aluminized film is very thin, aluminum layer thickness is measured can not detect its thickness with the thickness measuring instrument of routine, and detection method is electric-resistivity method;

Step 6), on described aluminium coated, evenly be coated with adhesive with coating machine and consist of the gluing layer, be coated with adhesive twice, be double-deck gluing layer structure, the described adhesive material of twice coating is respectively thermoplastics type's adhesive of two kinds, and wherein the first thermoplastics type adhesive is the elastic body toughening agent and improves the thermoplastic resin of solidfied material fragility; The second thermoplastics type adhesive is raising adhesive force, increases adaptive resin, 130 ℃-140 ℃ of coating temperatures, and speed 60 m/min obtain laser electrochemical aluminum stamping systems finished product after cutting.

The laser electrochemical aluminum stamping systems preparation method of metal coins of the present invention, wherein: thermoplastics type's adhesive that the described adhesive material of twice coating is respectively two kinds of components in step 6), wherein thermoplastics type's adhesive of coating is the elastic body toughening agent and improves the thermoplastic polyurethane of solidfied material fragility for the first time, coated heat plastotype adhesive is to improve adhesive force for the second time, increase adaptive acrylic acid, be coated with adhesive with coating machine, the adhesive coating layer thickness is expressed as by its coating dry measure: 0.7-0.9 g/m2,120 ℃-130 ℃ of coating temperatures, speed 60 m/min obtain the gluing layer of suitable side cut.

Utilize the product of making for the method for laser electrochemical aluminum stamping systems on the metal coins of the present invention, it is the laser electrochemical aluminum stamping systems, wherein: be provided with five-layer structure at described basement membrane film band, be followed successively by from inside to outside by described basement membrane film band one side surface: release layer, imaging layer, embossed plies, aluminium coated, gluing layer, wherein said gluing layer are two gluing layer structure.

Utilize the product laser electrochemical aluminum stamping systems of making for the method for laser electrochemical aluminum stamping systems on the metal coins of the present invention, wherein: described gluing layer is two gluing layer structure, and described pair of gluing layer structure is respectively elasticity gluing toughening layer and gluing adhesive force enhancement Layer.

The laser electrochemical aluminum stamping systems preparation method of metal coins of the present invention, wherein: the described release layer that is coated with at described basement membrane film band in step 2 is the celluosic resin releasing layer coating: count toluene 50-70 mass parts, butanone 25-35 mass parts, celluosic resin 10-20 mass parts by mass parts; After first described toluene, butanone mixing homogenizer being stirred, add described celluosic resin and stirred 20 minutes with homogenizer, make releasing layer coating and upper coating machine and be coated on the described basement membrane film band and consist of release layer.

The laser electrochemical aluminum stamping systems preparation method of metal coins of the present invention, wherein: when the laser electrochemical aluminum stamping systems is finished gold stamping rear separation, the separation point position is that described release layer separates with described imaging layer, and described release layer tears off thermoprint thing metal coins with described basement membrane film band.

The present invention adopts melmac or celluosic resin as mould release, melmac or celluosic resin are to be stained with to apply on described basement membrane film band to break away from described imaging layer along with described basement membrane film band separation, can not be stained with and apply on described imaging layer, there is not attachment above the described imaging layer behind the thermoprint holographic pattern, so can finish again printing-ink, realize the purpose of printing after the holographic pattern thermoprint; Described imaging layer of the present invention is a kind of resin of Wear-resistant, high-temperature resistant.Auxiliary agent of the present invention is epoxy resin promoter, and mainly as the thermoset epoxy curing agent, Main Function promotes epoxy resin cure speed and effect, improves solidification rate.

The present invention has following remarkable advantage: the present invention is intended to by gold stamping so that the gold stamping paper tinsel of laser hologram has had new application to metal coins, and then can be by laser electrochemical aluminum stamping systems locating thermoprint technology so that metal coins be color from the enterprising circumstances in which people get things ready for a trip of microcosmic and the stack of brightness, provide a kind of can metal coins implement with the laser antifalse effect, contain again the exquisite pattern stack of laser hologram, and be the laser electrochemical aluminum stamping systems preparation method of high-quality thermoprint, the laser electrochemical aluminum stamping systems that adopts method of the present invention to produce can make metal coins have brand-new effect, the operating procedure simple and fast, the repeatability of picture and text is good, but large-scale industrial production, reduce widely manufacturing cost, laser electrochemical aluminum stamping systems strong adhesion of the present invention, durable wear.Because the pattern decoration layer is to be fastened on the metallic article surface by adhesive, surface smoothing, so pattern decoration layer difficult drop-off, and adhesive layer is by changing its prescription and passing through the adhesive layer that repeatedly coating forms multilayer, and then reach better and be combined with the metal surface, thereby make the pattern decoration layer be attached to more securely the metal surface, make pattern decoration have wear-resisting, weatherability.

Description of drawings:

Fig. 1: the laser electrochemical aluminum stamping systems that the present invention is used on the metal coins is made flow chart;

Fig. 2: of the present invention for the laser electrochemical aluminum stamping systems structural representation on the metal coins;

The specific embodiment:

The present invention will be described in detail below in conjunction with specific embodiment:

Embodiment 1:

That the laser electrochemical aluminum stamping systems that the present invention is used on the metal coins is made flow chart as shown in Figure 1.In Fig. 1, the present invention is used for the laser electrochemical aluminum stamping systems preparation method of metal coins, may further comprise the steps:

Step 1), make the metallic nickel version: picture and text are engraved on laser by litho machine and produce the laser hologram version on the sensitization offset plate, adopt again the electroforming mode that the laser hologram version is made metallic nickel version for mold pressing;

Step 2) as shown in Figure 2, be coated with release layer 2 at basement membrane film band 1: prepare the melmac releasing layer coating according to the release layer composition component: count by mass parts, its raw material solvent of melamine mould release is alcohol 40 mass parts, butanone 30 mass parts, auxiliary agent 0.007 mass parts, melmac 70 mass parts, first with described alcohol 40 mass parts, butanone 30 mass parts are mixed, after homogenizer stirs, add described melmac 70 mass parts and described auxiliary agent 0.007 mass parts, stirred 20 minutes with homogenizer, make releasing layer coating and upper coating machine and be coated on formation release layer 2 on the described basement membrane film band 1; Basement membrane film band 1 of the present invention is the PET film, adopt the mylar of the thick biaxial tension of 12 μ m-25 μ m, Main Function is to support each coating that depends in the above, be convenient to add the continuous thermoprint in man-hour, it has the performances such as stretch-proof, anti-TRANSIENT HIGH TEMPERATURE, and the PET film of described basement membrane film band 1 must be separated from metal coins by described release layer 2 after thermoprint is finished;

Step 3) is at described release layer 2 coating imaging layers 3: be mixed with the picture coating according to the imaging layer composition component: count butanone 30 mass parts, butyl ester 10 mass parts mixed dissolution pigment by mass parts and stir 5 minutes to fully evenly, stirred 30 minutes after adding again thermoplastic resin 30 mass parts, on the release layer 2 that has been coated with, evenly be coated with one deck imaging layer 3 with coating machine, the coating layer thickness of coating imaging layer 3 is coating dry measure 0.9g/m2, through the drying chamber oven dry, its bake out temperature is at 140 ℃; Imaging layer Main Function of the present invention has two: the one, and Show Color; The 2nd, the protection thermoprint is not oxidized at the aluminium coated picture and text on metal coins surface.The color of electrochemical aluminum foil has golden yellow, orange, grey, red, blue, green etc. multiple.Coating requirement to imaging layer is fine and smooth in any granule, in order to avoid go out trachoma, the coating uniformity;

Step 4), mold pressing: the moulding press by described metallic nickel version is housed is transferred to the holographic false proof pattern mold pressing on the described metallic nickel version and is formed embossed plies 4 on the described imaging layer 3, and molding pressure 2kg, molding temperature be at 200 ℃, mold pressing speed 20m/min;

Step 5), aluminize: have the described basement membrane film band 1 of holographic pattern to carry out vacuum aluminum-coated formation aluminium coated 5 by vacuum aluminum-plating machine mold pressing, aluminum layer thickness is 2.0 ohm; The color of described imaging layer 3 is endowed gloss after seeing through aluminium coated 5, and color has significant change, becomes silver color etc. for golden, grey after aluminizing such as yellow after plating is bored;

Step 6), gluing: on described aluminium coated 5, evenly be coated with adhesive with coating machine and consist of gluing layer 6, be coated with adhesive twice, be double-deck gluing layer structure, the adhesive material of twice coating is respectively thermoplastics type's adhesive of two kinds of components, and wherein the first thermoplastics type adhesive is that elastic body toughening agent and the thermoplastic resin of raising solidfied material fragility are polyurethane; The second thermoplastics type adhesive is to improve adhesive force, the adaptive resin acrylic acid of increase, 130 ℃ of coating temperatures, and speed 60 m/min obtain laser electrochemical aluminum stamping systems finished product after cutting.Release layer 2 Main Functions of the present invention be transferred making imaging layer 3, embossed plies 4, aluminium coated 5, gluing layer 6 can hightail basement membrane film band 1 after the thermoprint be bonded in by the surface of thermoprint thing metal coins on, release layer 2 should have the performance that well comes off, grow dim otherwise the picture and text that can make thermoprint are smudgy, reveal the mansion, affect the product matter of thermoprint.

Embodiment 2:

The present embodiment can also have following difference, all the other are all identical with embodiment 1, its something in common does not repeat to repeat, in step 2 of the present invention) in, following difference can also be arranged: 2) at described basement membrane film band 1 coating release layer 2: prepare the melmac releasing layer coating according to the release layer composition component: count by mass parts: its raw material solvent of melamine mould release is alcohol 45 mass parts, butanone 35 mass parts, auxiliary agent 0.008 mass parts, melmac 80 mass parts stir, and releasing layer coating was made in mixing in 20 minutes and upper coating machine is coated on formation release layer 2 on the basement membrane film band 1, and described auxiliary agent is curing agent;

Mold pressing in step 4): the moulding press by described metallic nickel version is housed is transferred to imaging layer 3 with the holographic false proof pattern mold pressing on the described metallic nickel version and is formed embossed plies 4, and molding pressure 2 kg/m 2, molding temperature are at 240 ℃, mold pressing speed 20m/min;

Respectively thermoplastics type's adhesive of two kinds of components at twice coating gluing agent material described in the step the 6 of the present invention, wherein thermoplastics type's adhesive of coating is the elastic body toughening agent and improves the thermoplastic polyurethane of solidfied material fragility for the first time, coated heat plastotype adhesive is raising adhesive force, increases adaptive acrylic acid for the second time, be coated with adhesive with coating machine, the adhesive coating layer thickness is expressed as by its coating dry measure: 0.8 g/m2,130 ℃ of coating temperatures, speed 60 m/min obtain the gluing layer of suitable side cut.Two glue-lines are the combination of two groups of different formulations, mainly are that to play follow-up printing performance good, do not fall aluminium, scratch resistance, produce and metal conjugation effect more firmly.

Embodiment 3:

The present embodiment can also have following difference, all the other are all identical with embodiment 1, its something in common does not repeat to repeat, in step 2 of the present invention) in, following difference can also be arranged: step 2) at described basement membrane film band 1 coating release layer 2: described release layer 2 is melamine release layers, prepare the melmac releasing layer coating according to the release layer composition component: count by mass parts: solvent alcohol 50 mass parts, butanone 32 mass parts, auxiliary agent 0.008 mass parts, melmac 82 mass parts stir to mix with homogenizer and stirred 20 minutes, respectively thermoplastics type's adhesive of two kinds of components at twice coating gluing agent material described in the step 6) of the present invention, wherein thermoplastics type's adhesive of coating is polyurethane for the first time, coated heat plastotype adhesive is acrylic acid for the second time, be coated with adhesive with coating machine, the adhesive coating layer thickness is expressed as by its coating dry measure: 0.7 g/m2,120 ℃ of coating temperatures, speed 60 m/min.

Embodiment 4

The present embodiment can also have following difference, all the other are all identical with embodiment 1, its something in common does not repeat to repeat, in step 2) in be the celluosic resin release layer at the described release layer 2 of basement membrane film band 1 coating, according to release layer composition component preparation celluosic resin releasing layer coating: count toluene 50 mass parts, butanone 25 mass parts, celluosic resin 10 mass parts by mass parts; After first toluene 50 mass parts, butanone 25 mass parts mixing homogenizer being stirred, add celluosic resin 10 mass parts and stirred 20 minutes with homogenizer; Respectively thermoplastics type's adhesive of two kinds of components at twice coating gluing agent material described in the step the 6 of the present invention, wherein thermoplastics type's adhesive of coating is polyurethane for the first time, coated heat plastotype adhesive is acrylic acid for the second time, be coated with adhesive with coating machine, the adhesive coating layer thickness is expressed as by its coating dry measure: 0.9 g/m2,140 ℃ of coating temperatures, speed 60 m/min.

Embodiment 5: the present embodiment can also have following difference, all the other are all identical with embodiment 4, its something in common does not repeat to repeat, described release layer 2 in 1 coating of basement membrane film band in step the 2 is celluosic resin release layers, prepares the celluosic resin releasing layer coating according to the release layer composition component: count by mass parts: toluene 70 mass parts, butanone 35 mass parts, celluosic resin 20 mass parts; After first toluene 70 mass parts, butanone 35 mass parts mixing homogenizer being stirred, add described celluosic resin 20 mass parts and stirred 20 minutes with homogenizer, make releasing layer coating and upper coating machine and be coated on formation release layer 2 on the basement membrane film band.

Embodiment 6

The present embodiment can also have following difference, all the other are all identical with embodiment 4, its something in common does not repeat to repeat, described release layer 2 in 1 coating of basement membrane film band in step 2 is celluosic resin release layers, prepare the celluosic resin releasing layer coating according to the release layer composition component: count toluene 60 mass parts, butanone 30 mass parts, celluosic resin 15 mass parts by mass parts; After first toluene 60 mass parts, butanone 30 mass parts mixing homogenizer being stirred, add celluosic resin 15 mass parts and stirred 20 minutes with homogenizer, make releasing layer coating and upper coating machine and be coated on formation release layer 2 on the described basement membrane film band.

The product of making for the method for laser electrochemical aluminum stamping systems on the metal coins of the present invention, it is laser electrochemical aluminum stamping systems 8, be provided with five-layer structure at basement membrane film band 1, be followed successively by from inside to outside by basement membrane one side surface: release layer 2, imaging layer 3, embossed plies 4, aluminium coated 5, gluing layer 6, wherein said gluing layer 6 are two gluing layer structure; Further specifying the described gluing layer 6 of laser electrochemical aluminum stamping systems of the present invention for two gluing layer structure, is two gluing layer structure of different layers structure, and different gluing layer structure are respectively elasticity gluing toughening layer 6-1 and gluing adhesive force enhancement Layer 6-2; Except having good adhesive force, also consider to guarantee its side cut performance when making pattern decoration have wear-resisting, weatherable layer.

When the present invention finished gold stamping rear separation at the laser electrochemical aluminum stamping systems, the separation point position was that described release layer 2 separates with described imaging layer 3, and described release layer 2 tears off thermoprint thing metal coins with described basement membrane film band 1.

The present invention has the described basement membrane film band 1 of holographic pattern to carry out the described aluminium coated 5 of vacuum aluminum-coated formation by vacuum aluminum-plating machine mold pressing, described aluminum layer thickness is take resistance measurement as 2.0 Ω, aluminum layer thickness is measured because the aluminium coated on the vacuum aluminized film is very thin, therefore can not detect its thickness with the thickness measuring instrument of routine, detection method commonly used is electric-resistivity method, to utilize Ohm's law to come the thickness of aluminium coated is measured, according to Ohm's law R=ρ * L/S, the resistance value of unit are metallized film is less, the thickness of its aluminium coated is thicker, otherwise then thinner, the thickness that electric-resistivity method detects aluminium coated represents with sheet resistance, unit is Ω, and the larger explanation aluminum layer thickness of numerical value is thinner, and standard GB/T/T 15717-1995 " vacuum metal thickness of coating test methods electrical resistance method " has been carried out detailed regulation to this method.

The described release layer 2 of prior art usually is to adopt water wax or OP wax, metal coins surface at the release layer after separating can not be printed again, because the dyne value of water wax is low, water wax separates with basement membrane film band 1, water wax is retained on the imaging layer 3, can not realize the surface printing-ink again after the metal coins thermoprint holographic pattern owing to there being wax to exist, the present invention adopts melmac or celluosic resin as mould release, its key is that melmac or celluosic resin are along with basement membrane film band 1 breaks away from embossed plies 4, on imaging layer 3, there is not residual attachment, so can finish again printing-ink, realize the purpose of printing after the holographic pattern thermoprint.

What described imaging layer resin of the present invention adopted is high temperature resistant, wear-resisting resin, makes pattern decoration have wear-resisting, weatherability, has protective effect.

The present invention is in the process of coating gluing layer, prior art is at papery or cloth surface with the electrochemical aluminum foil thermoprint, sticking glutinous object is soft material with respect to metal coins, usually the thickness of coating adhesive is thicker, it is generally acknowledged that gluing is The more the better, what adhere to is more firm, on the contrary at metal coins coating adhesive, because metal coins is the smooth surface that casts out, the adhesive of coating is slightly more, the gluing layer is slightly thicker because glue is soft scraping with regard to producing fearness, softening, caducous problem, analyze by experiment the inventor and think that paper material has certain permeability after paper material applies adhesive, adhesive has sticking stickiness more and strengthens, sticking glutinous firmly situation, and the metal coins smooth surface, and there is not permeability, the slightly more stickiness of will gluing of coating adhesive descends, easily scratch, though can not cohere securely on the metal coins surface, therefore, the adhesive that is coated on the metal coins surface is to get over Bao Yuehao with respect to the adhesive coating layer thickness that is coated on papery thermoprint thing surface, described like this adhesive is strengthened greatly in the firm degree of metal coins surface attachment, and it also is very important selecting suitable and metal that the resin of good compatibility is arranged.Be coated with adhesive with coating machine, gel coating thickness is expressed as by its coating dry measure: 0.7-0.9 g/m2, and side cut property is dried at 140 ℃ of-160 ℃ of drying chambers through bake out temperature like this, and the firmness of adhesive adhesiving metal thing meets design requirement.

In addition for the adaptability problem of ink printing after release layer 2 and the thermoprint, celluosic resin then is the situation that is fit to the thinner ink lay of printing for the printing-ink of metal coins as release layer, and melmac is more suitable for ink lay than the printing of heat-bodied oil China ink as release layer for the metal coins ink printing.

Claims (6)

1. laser electrochemical aluminum stamping systems preparation method who is used for metal coins is characterized in that: may further comprise the steps:

Step 1), make the metallic nickel version: picture and text are engraved on laser by litho machine and produce the laser hologram version on the sensitization offset plate, adopt again the electroforming mode that the laser hologram version is made metallic nickel version for mold pressing;

Step 2) at basement membrane film band (1) coating release layer (2): according to release layer composition component preparation melamine releasing layer coating be: by mass parts: melamine mould release solvent is alcohol 40-50 mass parts, butanone 30-35 mass parts, auxiliary agent 0.007-0.008 mass parts, melamine 70-85 quality, after first alcohol, butanone mixing, homogenizer being stirred, add melmac, stirred 20 minutes with homogenizer, make releasing layer coating and upper coating machine and be coated on and consist of release layer (2) on the basement membrane film band;

Step 3) is coated with imaging layer (3) at release layer (2): be mixed with the picture coating according to the imaging layer composition component: count butanone 30 mass parts, the mixing of butyl ester 10 mass parts and dissolving pigment by mass parts, add thermoplastic resin 30 mass parts, upward evenly be coated with one deck imaging layer (3) with coating machine at the release layer that has been coated with (2), Coating thickness is 0.7 g/m 2-0.9g/m 2, through the drying chamber oven dry, its bake out temperature is at 140 ℃-160 ℃;

Step 4), by the moulding press that described metallic nickel version is housed the holographic false proof pattern mold pressing on the described metallic nickel version is transferred to and to be formed embossed plies (4) on the imaging layer, molding pressure 2 kg/m 2-3kg/m2, molding temperature is at 200 ℃-240 ℃, mold pressing speed 20m/min;

Step 5), have the film band of holographic pattern to carry out vacuum aluminum-coated formation aluminium coated (5) by vacuum aluminum-plating machine mold pressing, aluminium coated (5) thickness is 2.0 Ω;

Step 6), evenly be coated with adhesive with coating machine and consist of gluing layer (6) aluminium coated (5) is upper, be coated with adhesive twice, be double-deck gluing layer structure, the adhesive material of twice coating is respectively thermoplastics type's adhesive of two kinds of components, and wherein the first thermoplastics type adhesive component is the elastic body toughening agent and improves the thermoplastic resin of solidfied material fragility; The second thermoplastics type adhesive component is raising adhesive force, increases adaptive resin, 120 ℃-140 ℃ of coating temperatures, and speed 60 m/min obtain laser electrochemical aluminum stamping systems finished product after cutting.

2. the laser electrochemical aluminum stamping systems preparation method of metal coins according to claim 1, it is characterized in that: be respectively thermoplastics type's adhesive of two kinds of components at twice coating gluing agent material described in the step the 6, wherein thermoplastics type's adhesive component of coating is the elastic body toughening agent and improves the thermoplastic polyurethane of solidfied material fragility for the first time, coated heat plastotype adhesive component is to improve adhesive force for the second time, increase adaptive acrylic acid, be coated with adhesive with coating machine, the adhesive coating layer thickness is expressed as by its coating dry measure: 0.7-0.9 g/m2,120 ℃-130 ℃ of coating temperatures, speed 60 m/min obtain the gluing layer (6) of suitable side cut.

3. utilize the product of making for the method for laser electrochemical aluminum stamping systems on the metal coins claimed in claim 1, it is the laser electrochemical aluminum stamping systems, it is characterized in that: be coated with five layers at basement membrane film band (1), be followed successively by from inside to outside by basement membrane one side surface: release layer (2), imaging layer (3), embossed plies (4), aluminium coated (5), gluing layer (6), wherein said gluing layer are two gluing layer structure.

4. laser electrochemical aluminum stamping systems according to claim 3 is characterized in that: wherein said gluing layer is two gluing layer structure, and two gluing layers (6) structure is respectively elasticity gluing toughening layer (6-1) and gluing adhesive force enhancement Layer (6-2).

5. the laser electrochemical aluminum stamping systems preparation method of metal coins according to claim 1, it is characterized in that: the described release layer (2) in basement membrane film band (1) coating in step the 2 is the celluosic resin releasing layer coating: count toluene 50-70 mass parts, butanone 25-35 mass parts, celluosic resin 10-20 mass parts by mass parts; After first toluene, butanone mixing homogenizer being stirred, add celluosic resin and stirred 20 minutes with homogenizer, make releasing layer coating and upper coating machine and be coated on and consist of release layer (2) on the basement membrane film band.

6. the laser electrochemical aluminum stamping systems preparation method of metal coins according to claim 1, it is characterized in that: when the laser electrochemical aluminum stamping systems is finished gold stamping rear separation, the separation point position is that described release layer (2) separates with described imaging layer (3), and described release layer (2) tears off thermoprint thing metal coins with described basement membrane film band (1).