CN104947465B - A kind of wear-resisting printing coating for textile fabrics of rapid-curing cutback - Google Patents
A kind of wear-resisting printing coating for textile fabrics of rapid-curing cutback Download PDFInfo
- Publication number
- CN104947465B CN104947465B CN201510454448.5A CN201510454448A CN104947465B CN 104947465 B CN104947465 B CN 104947465B CN 201510454448 A CN201510454448 A CN 201510454448A CN 104947465 B CN104947465 B CN 104947465B
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- coating
- rapid
- wear
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of wear-resisting printing coating for textile fabrics of rapid-curing cutback, the coating of the present invention have employed the acrylic resin being conducive to improving coating dry rate prepared by special process, also added N-[2-(2-methyl-4-oxopentyl) and alkyd resin simultaneously, further increase the dry rate of coating.
Description
Technical field
The present invention relates to a kind of wear-resisting printing coating for textile fabrics of rapid-curing cutback.
Background of invention
Being coated with by color containing dyestuff or pigment and directly print to white or be infected with on the fabric of ground colour, on dyestuff or pigment, dye is solid
In place of stamp, thus obtain the printing method of various floral designs, be direct printing technique.Coating direct printing is at fibre
In dimension, the principle of coloring is different from general dyestuff, and its nationality binding agent is by insoluble granules of pigments set on the textile.Coating prints
Flower process environmental protection, it is not necessary to washing, the restriction to fabric is little, and technique is simple, and colorant match is convenient, and coloured light is prone to adjust and control, and prints
Pattern profile clear, well arranged, be rich in third dimension.Its printing quality directly shows very clear on printing machine, technique
Process is relatively brief, and printing quality is easily controlled, and is a kind of highly developed and most widely used technique.
Along with the rise of clothing personalized customization cybertimes and e-commerce field are provided and delivered requirement timely, personalized fixed
The rapid batch of uniform dress produces and the requirement of packaging delivery is more and more higher.This just requires printing coating energy within the extremely short time
Enough rapid draing is firm, to avoid occurring that adhesion is stained when packaging.But current pigment printing its drying time, print after
Rub resistance in short time, resistance to washing by rubbing with the hands property, heat-resisting stability are poor, have impact on the development of clothing personalized customization.
Summary of the invention
For solving the problems referred to above of printing coating, present invention employs following technical scheme:
A kind of wear-resisting printing coating for textile fabrics of rapid-curing cutback, is made up of the raw material of following mass fraction:
N-[2-(2-methyl-4-oxopentyl) 10 parts
Alkyd resin 15 parts
Acrylic resin 20 parts
Levelling agent 1 part
Thickening agent 2 parts
Fatty alcohol-polyoxyethylene ether 0.5 part
Diluent 1.5 parts
Pigment 50 parts
SiO 2 powder 10 parts
Bentonite 3 parts
Alumina powder 10 parts
Lignin sulfonic acid 3 parts
Etherification starch 4 parts
Distilled water 40 parts；
The preparation of printing coating comprises the steps:
A) in terms of parts by weight, following component is weighed: 10 parts of N-[2-(2-methyl-4-oxopentyl)s, 15 parts of alkyd resin, 20 parts of acrylic acid
Resin, 40 parts of distilled water, 1 part of levelling agent, 2 parts of thickening agents, 0.5 part of fatty alcohol-polyoxyethylene ether, 1.5 parts of diluent etc., add
In agitator, with the speed of 350 turns/min, it is sufficiently stirred for disperseing 30 minutes, treats each component mix homogeneously, prepare mixed liquor；
B) in terms of parts by weight, weigh 50 parts of pigment, 10 parts of silicon dioxide powders, 3 parts of bentonite, 10 parts of alumina powders, mix
Closing uniformly, then feed the mixture in the mixed liquor that step 1) prepares, add the lignin sulfonic acid of 3 weight portions, 4 parts of etherificates are formed sediment
Powder, blender stirs 1 hour with the speed of 400 turns/min, more ground machine is fully ground, and is filtrated to get coating composition；
Described acrylic resin is adopted and is prepared with the following method:
In terms of parts by weight, take 20 parts of ethanol, 20 parts of propanol, 15 parts of isopropyl acetates, after mix homogeneously, add reactor
In, with the ramp of about 5-10 DEG C/min to 80 DEG C, it is incubated 30min, is then sequentially added into 20 parts of ethyl acrylate, 10 parts of first
Base acrylic acid, 15 parts of 2-(Acryloyloxy)ethanols, 2 parts of diacetone acrylamides, 1 part of azo dicyclohexyl formonitrile HCN, stirring mixing is all
Even, isothermal reaction 5 hours, it is cooled to 30 DEG C, drips 1.5ml strong aqua ammonia, be stirred for 30min, obtain acrylic resin.
Described levelling agent is organosilicon levelling agent.
Beneficial effect:
1) containing water-dispersible acrylic's resin in the coating of the present invention, it has good adhesive force, rate of drying
Hurry up, as one of the film-forming components of coating, it is possible to significantly improve the dry rate of coating serous coat.
2) coating of the present invention also uses beneficially improve N-[2-(2-methyl-4-oxopentyl) and the alkyd resin of dry rate, its
Work in coordination with acrylic resin, further increase the dry rate of ink slurry.
3) rate of drying of present invention water paint faster, can significantly reduce what water paint rate of drying brought slowly
The pattern adhesion that produces in printing and packaging process, the quality problems such as being stained, reduce production cost, there is actual application value pole.
4) rub resistance in the short time and resistance to wash fastness by rubbing with the hands after the coating of the present invention has good printing.
5) present invention does not contains the harmful substances such as formaldehyde, heavy metal and organotin, environmental protection, health.
Detailed description of the invention
Below in conjunction with embodiment, the present invention will be further described, but the scope of protection of present invention is not limited to reality
Execute the scope that example is expressed.
Embodiment 1
The preparation of acrylic resin:
In terms of parts by weight, take 20 parts of ethanol, 20 parts of propanol, 15 parts of isopropyl acetates, after mix homogeneously, add reactor
In, with the ramp of about 5-10 DEG C/min to 80 DEG C, it is incubated 30min, is then sequentially added into 20 parts of ethyl acrylate, 10 parts of first
Base acrylic acid, 15 parts of 2-(Acryloyloxy)ethanols, 2 parts of diacetone acrylamides, 1 part of azo dicyclohexyl formonitrile HCN, stirring mixing is all
Even, isothermal reaction 5 hours, it is cooled to 30 DEG C, drips 1.5ml strong aqua ammonia, be stirred for 30min, obtain acrylic resin.
The preparation of coating:
Following component is weighed: 10 parts of N-[2-(2-methyl-4-oxopentyl)s, 15 parts of alkyd resin, 20 parts of acrylic acid trees in terms of parts by weight
Fat, 40 parts of distilled water, 1 part of levelling agent, 2 parts of thickening agents, 0.5 part of fatty alcohol-polyoxyethylene ether, 1.5 parts of diluent etc., addition is stirred
Mix in device, with the speed of 350 turns/min, be sufficiently stirred for disperseing 30 minutes, treat each component mix homogeneously, prepare mixed liquor；
Weighing 50 parts of pigment, 10 parts of silicon dioxide powders, 3 parts of bentonite, 10 parts of alumina powders in terms of parts by weight, mixing is all
Even, then feed the mixture in the mixed liquor that step 1) prepares, add the lignin sulfonic acid of 3 weight portions, 4 parts of etherification starch,
Blender stirs 1 hour with the speed of 400 turns/min, more ground machine is fully ground, and is filtrated to get coating composition.
Comparative example 1
Following component is weighed: 25 parts of N-[2-(2-methyl-4-oxopentyl)s in terms of parts by weight, 20 parts of alkyd resin, 40 parts of distilled water, 1
Part levelling agent, 1 part of thickening agent, 0.5 part of fatty alcohol-polyoxyethylene ether, 1.3 parts of diluent, add in agitator, with 350 turns/min
Speed, be sufficiently stirred for disperseing 30 minutes, treat each component mix homogeneously, prepare mixed liquor；
Weighing 50 parts of pigment, 10 parts of silicon dioxide powders, 3 parts of bentonite, 10 parts of alumina powders in terms of parts by weight, mixing is all
Even, then feed the mixture in aforementioned prepared mixed liquor, add the lignin sulfonic acid of 3 weight portions, blender with 400 turns/
The speed of min stirs 1 hour, more ground machine is fully ground, and is filtrated to get coating composition.
Comparative example 2
Following component is weighed: 25 parts of alkyd resin in terms of parts by weight, the acrylic resins that 20 parts of embodiments 1 prepare, 40
Part distilled water, 1 part of levelling agent, 1 part of thickening agent, 0.5 part of fatty alcohol-polyoxyethylene ether, 1.3 parts of diluent, add in agitator,
With the speed of 350 turns/min, it is sufficiently stirred for disperseing 30 minutes, treats each component mix homogeneously, prepare mixed liquor.
Weighing 50 parts of pigment, 10 parts of silicon dioxide powders, 3 parts of bentonite, 10 parts of alumina powders in terms of parts by weight, mixing is all
Even, then feed the mixture in aforementioned prepared mixed liquor, add the lignin sulfonic acid of 3 weight portions, blender with 400 turns/
The speed of min stirs 1 hour, more ground machine is fully ground, and is filtrated to get coating composition.
Above-mentioned each coating is dried speed, tack evaluation, and result is as follows:
Drying property evaluation method: print each coating to place 1 hour after leaflet, then stick covering paper tape and execute
Pressure, opens paper tape, measures the coating transfer amount on paper tape, and evaluation is divided into 3 grades:
Good: to transfer on paper tape almost without coating；General: only local has a small amount of coating to transfer on paper tape；
Difference: have many places and substantial amounts of coating to transfer on paper tape.
Claims (2)
1. the wear-resisting printing coating for textile fabrics of rapid-curing cutback, it is characterised in that be made up of the raw material of following parts by weight:
N-[2-(2-methyl-4-oxopentyl) 10 parts
Alkyd resin 15 parts
Acrylic resin 20 parts
Levelling agent 1 part
Thickening agent 2 parts
Fatty alcohol-polyoxyethylene ether 0.5 part
Diluent 1.5 parts
Pigment 50 parts
SiO 2 powder 10 parts
Bentonite 3 parts
Alumina powder 10 parts
Lignin sulfonic acid 3 parts
Etherification starch 4 parts
Distilled water 40 parts；
The preparation of printing coating comprises the steps:
A) in terms of parts by weight, following component is weighed: 10 parts of N-[2-(2-methyl-4-oxopentyl)s, 15 parts of alkyd resin, 20 parts of acrylic acid trees
Fat, 40 parts of distilled water, 1 part of levelling agent, 2 parts of thickening agents, 0.5 part of fatty alcohol-polyoxyethylene ether, 1.5 parts of diluent, add stirring
In device, with the speed of 350 turns/min, it is sufficiently stirred for disperseing 30 minutes, treats each component mix homogeneously, prepare mixed liquor；
B) in terms of parts by weight, weigh 50 parts of pigment, 10 parts of SiO 2 powders, 3 parts of bentonite, 10 parts of alumina powders, mixing
Uniformly, then feeding the mixture in the mixed liquor that step a) prepares, add the lignin sulfonic acid of 3 parts by weight, 4 parts of etherificates are formed sediment
Powder, blender stirs 1 hour with the speed of 400 turns/min, more ground machine is fully ground, and is filtrated to get coating composition；
Described acrylic resin is adopted and is prepared with the following method:
In terms of parts by weight, take 20 parts of ethanol, 20 parts of propanol, 15 parts of isopropyl acetates, add after mix homogeneously in reactor, with
The ramp of 5-10 DEG C/min, to 80 DEG C, is incubated 30min, is then sequentially added into 20 parts of ethyl acrylate, 10 parts of metering systems
Acid, 15 parts of 2-(Acryloyloxy)ethanols, 2 parts of diacetone acrylamides, 1 part of azo dicyclohexyl formonitrile HCN, be uniformly mixed, constant temperature
React 5 hours, be cooled to 30 DEG C, drip 1.5ml strong aqua ammonia, be stirred for 30min, obtain acrylic resin.
The wear-resisting printing coating for textile fabrics of rapid-curing cutback the most according to claim 1, it is characterised in that: described levelling agent is organic
Silicon levelling agent.