CN104947422A - Novel oiling agent for polyamide fibers - Google Patents
Novel oiling agent for polyamide fibers Download PDFInfo
- Publication number
- CN104947422A CN104947422A CN201510410341.0A CN201510410341A CN104947422A CN 104947422 A CN104947422 A CN 104947422A CN 201510410341 A CN201510410341 A CN 201510410341A CN 104947422 A CN104947422 A CN 104947422A
- Authority
- CN
- China
- Prior art keywords
- parts
- polyamide fibers
- oiling agent
- triethanolamine
- novel oiling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a novel oiling agent for polyamide fibers. The novel oiling agent for the polyamide fibers comprises, by weight, 10-20 parts of butyl palmitate, 3-8 parts of polyoxyethylene ether, 0.1-0.3 part of triethanolamine, 0.2-0.6 part of alkyl sodium sulfonate, 4-6 parts of oleic acid, 3-6 parts of dihexyl adipate, 10-20 parts of triethanolamine oleate, 2-5 parts of dimethyl phthalate, 4-8 parts of emulsifier OP-10 and 40-60 parts of deionized water. Compared with the prior art, the novel oiling agent for the polyamide fibers has the following advantages that the novel oiling agent for the polyamide fibers is suitable for lubricating arrangement of the polyamide fibers, tar formation can be reduced in spinning, stretching and deforming of the polyamide fibers, and good lubricating performance is achieved; the oiled polyamide fibers have higher storage stability.
Description
Technical field
The invention belongs to technical field of textile auxiliary agent, more specifically relate to a kind of Novel polyamide fiber finish.
Background technology
Nylon fibre has the advantages such as brute force, ABRASION RESISTANCE be good, occupies first of all fibres.Its ABRASION RESISTANCE is 10 times of cotton fiber, is 10 times of dry state viscose, is 140 times of hygrometric state fiber.Therefore, its durability is splendid.
Summary of the invention
The object of the invention is to the deficiency overcoming prior art existence, a kind of Novel polyamide fiber finish is provided.
For achieving the above object, this invention takes following technical scheme:
A kind of Novel polyamide fiber finish, with parts by weight, composed of the following components:
Butyl palmitate: 10 ~ 20, polyoxyethylene ether: 3 ~ 8, triethanolamine: 0.1 ~ 0.3,
Sodium alkyl sulfonate: 0.2 ~ 0.6, oleic acid: 4 ~ 6, adipic acid two ester: 3 ~ 6,
Emulphor FM: 10 ~ 20, repefral: 2 ~ 5,
Emulsifier op-10: 4 ~ 8, deionized water: 40 ~ 60.
In technique scheme, the preparation technology of described Novel polyamide fiber finish is: by proportioning, each component is mixed, after being uniformly dispersed finished product.
Compared with prior art, the present invention has following beneficial effect:
1, the present invention is suitable for the lubricating finish of nylon fibre, can make nylon fibre in spinning, stretching and distortion, reduce the formation of tar, have good greasy property.
2, the nylon fibre oiled through the present invention has very high storage stability.
Detailed description of the invention
Embodiment 1
A kind of Novel polyamide fiber finish, with parts by weight, composed of the following components:
Butyl palmitate: 10, polyoxyethylene ether: 3, triethanolamine: 0.1,
Sodium alkyl sulfonate: 0.2, oleic acid: 4, adipic acid two ester: 3,
Emulphor FM: 10, repefral: 2,
Emulsifier op-10: 4, deionized water: 40.
Embodiment 2
A kind of Novel polyamide fiber finish, with parts by weight, composed of the following components:
Butyl palmitate: 20, polyoxyethylene ether: 8, triethanolamine: 0.3,
Sodium alkyl sulfonate: 0.6, oleic acid: 6, adipic acid two ester: 6,
Emulphor FM: 20, repefral: 5,
Emulsifier op-10: 8, deionized water: 60.
Embodiment 3
A kind of Novel polyamide fiber finish, with parts by weight, composed of the following components:
Butyl palmitate: 16, polyoxyethylene ether: 5, triethanolamine: 0.2,
Sodium alkyl sulfonate: 0.4, oleic acid: 5, adipic acid two ester: 5,
Emulphor FM: 16, repefral: 4,
Emulsifier op-10: 6, deionized water: 50.
In above-described embodiment, the preparation technology of described Novel polyamide fiber finish is: by proportioning, each component is mixed, after being uniformly dispersed finished product.
Claims (4)
1. a Novel polyamide fiber finish, is characterized in that, with parts by weight, composed of the following components:
Butyl palmitate: 10 ~ 20, polyoxyethylene ether: 3 ~ 8, triethanolamine: 0.1 ~ 0.3,
Sodium alkyl sulfonate: 0.2 ~ 0.6, oleic acid: 4 ~ 6, adipic acid two ester: 3 ~ 6,
Emulphor FM: 10 ~ 20, repefral: 2 ~ 5,
Emulsifier op-10: 4 ~ 8, deionized water: 40 ~ 60.
2. a kind of Novel polyamide fiber finish according to claim 1, is characterized in that, with parts by weight, composed of the following components:
Butyl palmitate: 10, polyoxyethylene ether: 3, triethanolamine: 0.1,
Sodium alkyl sulfonate: 0.2, oleic acid: 4, adipic acid two ester: 3,
Emulphor FM: 10, repefral: 2,
Emulsifier op-10: 4, deionized water: 40.
3. a kind of Novel polyamide fiber finish according to claim 1, is characterized in that, with parts by weight, composed of the following components:
Butyl palmitate: 20, polyoxyethylene ether: 8, triethanolamine: 0.3,
Sodium alkyl sulfonate: 0.6, oleic acid: 6, adipic acid two ester: 6,
Emulphor FM: 20, repefral: 5,
Emulsifier op-10: 8, deionized water: 60.
4. a kind of Novel polyamide fiber finish according to claim 1, is characterized in that, with parts by weight, composed of the following components:
Butyl palmitate: 16, polyoxyethylene ether: 5, triethanolamine: 0.2,
Sodium alkyl sulfonate: 0.4, oleic acid: 5, adipic acid two ester: 5,
Emulphor FM: 16, repefral: 4,
Emulsifier op-10: 6, deionized water: 50.