CN104946829B - 一种1800立方米高炉提高烧结矿利用率的布料方法 - Google Patents
一种1800立方米高炉提高烧结矿利用率的布料方法 Download PDFInfo
- Publication number
- CN104946829B CN104946829B CN201510391285.0A CN201510391285A CN104946829B CN 104946829 B CN104946829 B CN 104946829B CN 201510391285 A CN201510391285 A CN 201510391285A CN 104946829 B CN104946829 B CN 104946829B
- Authority
- CN
- China
- Prior art keywords
- cloth
- sintering
- encloses
- tons
- swivel chute
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及高炉领域。一种1800立方米高炉提高烧结矿利用率的布料方法，按照顺序准备3.68吨球团、9.66吨粒径为3‑5毫米烧结、10.58吨球团、8.28吨粒径为3‑5毫米烧结、4.14吨球团、9.66吨粒径大于5毫米烧结并按照顺序排入高炉炉顶料罐，布料旋转溜槽在45.5°上旋转布料3圈，布料旋转溜槽在42.5°上旋转布料3圈，布料旋转溜槽在39°上旋转布料3圈，布料旋转溜槽在35.5°上旋转布料3圈，布料旋转溜槽在29°上旋转布料2圈。
Description
技术领域
本发明涉及高炉领域，具体是一种1800立方米高炉提高烧结矿利用率的布料方法。
背景技术
按照冶金理论，一般烧结矿中小于5mm的粉末进入高炉以后，由于其粒级太小，所以在高炉的上部固体块矿集中的地方，它会向大粒级烧结矿与烧结矿之间形成的孔隙中渗透，最终导致高炉料柱（在高炉内由于炉料的排列而形成的柱状炉料叫做料柱）透气性严重变差，会使得从高炉下部上升的煤气流受到很大的阻力，严重影响高炉的顺行，也就严重影响高炉的技术经济指标。
传统的做法是将小于5mm的粉末当成烧结的废弃物（冶金专业名称叫返矿）来处理。它与大块烧结通过筛子筛分出来后通过汽车再次运往烧结厂再次参与烧结过程，大大降低了烧结矿的成品率以及增加了烧结的成本。
发明内容
本发明所要解决的技术问题是：在高炉内如何使用小粒级烧结，从而降低了烧结成本。
本发明所采用的技术方案是：一种1800立方米高炉提高烧结矿利用率的布料方法，按照顺序准备3.68吨球团（球团是一种常见的炼铁原料，与烧结按照一定的比例配合使用）、9.66吨粒径为3-5毫米烧结、10.58吨球团、8.28吨粒径为3-5毫米烧结、4.14吨球团、9.66吨粒径大于5毫米烧结并按照顺序排入高炉炉顶料罐，布料旋转溜槽在45.5°上旋转布料3圈，布料旋转溜槽在42.5°上旋转布料3圈，布料旋转溜槽在39°上旋转布料3圈，布料旋转溜槽在35.5°上旋转布料3圈，布料旋转溜槽在29°上旋转布料2圈。
本发明的有益效果是：本发明创造性地利用高炉内横向截面对高炉气流要求的不同，通过对烧结筛网的改造，将含有3~5mm小粒级的烧结布在对气流要求不太高的地方，而将大于5mm的烧结布在高炉内对气流要求较高的地方，从而对返矿中大于3mm的烧结矿进行了再利用，使得烧结返矿运输成本和烧结返矿的二次烧结成本得以降低。
具体实施方式
由于高炉内横向界面上对气流的要求是不一样的，所以可以将小粒级的烧结放在对气流要求不高的地方，减少小粒级烧结入炉后对高炉炉况的影响，以此来提高烧结矿的利用率，而对于高炉内对气流要求较高的地方则仍然使用大于5mm的烧结。
太钢1800m³高炉使用的炼铁原料结构为“60%烧结+40%球团”，常用的一批炼铁原料的质量大小为46吨，烧结矿的质量为27.6吨，球团的质量应为18.4吨。1800高炉烧结矿的1#筛和2#筛都以及改为3mm筛。
按照“球团+烧结+球团+烧结+球团+烧结”的方式排出相应的原料。即排料系统按照“3.68吨球团、9.66吨粒径为3-5毫米烧结、10.58吨球团、8.28吨粒径为3-5毫米烧结、4.14吨球团、9.66吨粒径大于5毫米烧结”的量和顺序进行排料。
在排出烧结的程序上保证第一段烧结9.66吨和第二段烧结8.28吨粒径为3-5毫米烧结。严禁粒径为3-5毫米烧结排在料段最后一段烧结位置，即9.66吨烧结处。
将上述排好的原料排入高炉炉顶料罐。由于排料系统排出料是按照一定的顺序排出的，所以，原料进入炉顶料罐也是按照该顺序进行的。
将料罐中的料按照给定的角度和圈数排出进入高炉，利用烧结将球团进行分割，形成稳定的炉顶料面。太钢1800m³高炉布料使用的布料矩阵是3（45.5°）3（42.5°）3（39°）3（35.5°）2（29°）,其中，3（45.5°）是指布料旋转溜槽在45.5°上旋转布料3圈； 3（42.5°）是指布料旋转溜槽在42.5°上旋转布料3圈；3（39°）是指布料旋转溜槽在39°上旋转布料3圈；3（35.5°）是指布料旋转溜槽在35.5°上旋转布料3圈；2（29°）是指布料旋转溜槽在29°上旋转布料2圈。这样，在高炉横截面上包含有小粒级烧结的烧结矿便放置在了高炉内对透气性要求不高的边缘地带。
本项目的实施大大增加了小粒级（粒径为3-4毫米）烧结的入炉量，减少了返矿量以及返矿运输成本和二次烧结的成本，为铁厂和公司创造了效益。
通过将一部分小粒级（粒径为3-4毫米）烧结布在边缘，起到了对边缘气流的抑制作用，从而达到了热负荷（煤气流中的热量传递给高炉水系统热量的多少）的稳定。
Claims (1)
1.一种1800立方米高炉提高烧结矿利用率的布料方法，其特征在于：按照顺序准备3.68吨球团、9.66吨粒径为3-5毫米烧结、10.58吨球团、8.28吨粒径为3-5毫米烧结、4.14吨球团、9.66吨粒径大于5毫米烧结并按照顺序排入高炉炉顶料罐，布料旋转溜槽在45.5°上旋转布料3圈，布料旋转溜槽在42.5°上旋转布料3圈，布料旋转溜槽在39°上旋转布料3圈，布料旋转溜槽在35.5°上旋转布料3圈，布料旋转溜槽在29°上旋转布料2圈。