CN104946205B - 抑尘剂及其制备方法 - Google Patents
抑尘剂及其制备方法 Download PDFInfo
- Publication number
- CN104946205B CN104946205B CN201510319326.5A CN201510319326A CN104946205B CN 104946205 B CN104946205 B CN 104946205B CN 201510319326 A CN201510319326 A CN 201510319326A CN 104946205 B CN104946205 B CN 104946205B
- Authority
- CN
- China
- Prior art keywords
- dust
- dust suppressant
- suppressant
- coal
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种抑尘剂及其制备方法。该抑尘剂包括如下重量份的原料：聚阴离子纤维素0.05‑0.15份、曲拉通X‑1000.01‑0.09份、功能助剂0.03‑0.07份、水100份。该抑尘剂将聚阴离子纤维素与曲拉通X‑100进行配合使用，在短时间内即可对扬尘产生优良的凝并抑尘效果，适用于动态煤流的抑尘。同时，该抑尘剂是通过渗透润湿使扬尘凝并形成大颗粒，快速沉降以实现抑尘，而非现有技术的抑尘剂利用结壳性在煤流表面形成固化层来实现抑尘，避免了抑尘剂对煤炭的装卸、转载以及在皮带上运输的影响。此外，本发明所述抑尘剂还具有易降解、环保无污染、成本低等优点。
Description
技术领域
本发明涉及环境污染治理技术领域，特别是涉及一种抑尘剂及其制备方法。
背景技术
煤炭在开采、运输过程中产生大量煤粉扬尘，造成资源浪费和环境污染。粉尘的产生方式有动态煤流扬尘和静态扬尘两种。动态煤流扬尘产生的因素包括在装卸、转载时煤炭由于受自由落体的空气挤压作用而产生的扬尘，以及煤炭在皮带上输送时由于皮带牵引气流的作用而产生的扬尘。而静态扬尘则是存煤在来流风的风力作用下形成的。
目前开发出来的抑尘剂主要针对静态扬尘，由于静态扬尘抑尘剂大都具有结壳性，如果将其用于动态煤流扬尘会产生结壳，影响煤炭的装卸、转载以及在皮带上的运输，而且由于煤炭装卸、转载以及在皮带上运输的时间相对较短，因此还要求抑尘剂能够快速的起到抑尘效果。
基于此，开发出一种能够适用于动态煤流扬尘的抑尘剂是非常必要的。
发明内容
基于此，有必要提供一种抑尘剂。
一种抑尘剂，包括如下重量份的原料：
在其中一个实施例中，包括如下重量份的原料：
在其中一个实施例中，所述聚阴离子纤维素为高粘度型聚阴离子纤维素。
在其中一个实施例中，所述曲拉通X-100的纯度为化学纯，pH为5.0-7.0，密度为1.06-1.07g/mL。
在其中一个实施例中，所述功能助剂为聚环氧乙烷。
在其中一个实施例中，所述聚环氧乙烷的分子量为500万-700万。优选为分子量600万。
本发明还提供所述的抑尘剂的制备方法，包括如下步骤：
于所述聚阴离子纤维素中依次加入曲拉通X-100和功能助剂，再加入水，搅拌溶解，即得所述抑尘剂。
本发明的原理及优点如下：
本发明所述抑尘剂适用于对动态煤流进行抑尘，其原理如下：
由于输煤皮带具有一定的速度，动态的煤流受到皮带牵引气流的影响，皮带表层粒径小的煤粒会在牵引气流的影响下产生扬尘，煤流在皮带上运输的时间相对较短，抑尘剂必须能够在短时间内快速渗透至煤层表面10mm厚度的煤样并增大其粒径才能够对动态煤流进行抑尘。
根据这一原理，本发明所述抑尘剂选择将聚阴离子纤维素与曲拉通X-100进行配合使用，其中，聚阴离子纤维素的粘度大，凝并效果好，配合曲拉通X-100则能够显著降低水的表面张力、提高抑尘剂对煤样的润湿性及渗透性，以此在短时间内即可对扬尘产生优良的凝并抑尘效果，显著地抑制动态煤流扬尘。
同时，本发明抑尘剂是通过渗透润湿使动态扬尘凝并形成大颗粒，快速沉降以实现抑尘，而非现有技术的抑尘剂利用结壳性在煤流表面形成固化层来抑制扬尘，由此避免了对煤炭的装卸、转载以及在皮带上的运输的影响。
此外，本发明所述抑尘剂还具有易降解、环保无污染、成本低等优点。
进一步地，本发明所述功能性助剂聚环氧乙烷既是一种粘度较高的水溶性树脂又是一种非离子表面活性剂，将其与本发明所述聚阴离子纤维素和曲拉通X-100进行配合使用，既能增强抑尘剂的凝并效果，又对抑尘剂的润湿性、渗透性起到进一步促进作用，提高本发明抑尘剂对动态煤流的抑尘效果。
具体实施方式
本发明所述聚阴离子纤维素购自任丘市鹏宇化工销售有限公司，为高粘度型聚阴离子纤维素；
所述曲拉通X-100购自广东光华科技股份有限公司，化学纯，pH为5.0-7.0，密度为1.06-1.07g/mL；
所述聚环氧乙烷购自美国陶氏化学公司，分子量为600万。
以下结合具体实施例对本发明的抑尘剂及其制备方法作进一步详细的说明。
实施例1
本实施例一种抑尘剂，包括如下重量份的原料：
上述抑尘剂的制备方法，包括如下步骤：
按重量份数取聚阴离子纤维素0.1份、曲拉通X-1000.03份、聚环氧乙烷0.05份、水100份，在装有机械搅拌器的容器中依次加入聚阴离子纤维素、曲拉通X-100、功能性助剂聚环氧乙烷、水，充分搅拌，溶解得所述抑尘剂成品。
实施例2
本实施例一种抑尘剂，包括如下重量份的原料：
上述抑尘剂的制备方法，包括如下步骤：
按重量份数取聚阴离子纤维素0.05份、曲拉通X-1000.01份、聚环氧乙烷0.03份、水100份，在装有机械搅拌器的容器中依次加入聚阴离子纤维素、曲拉通X-100、功能性助剂聚环氧乙烷、水充分搅拌，溶解得所述抑尘剂成品。
实施例3
本实施例一种抑尘剂，包括如下重量份的原料：
上述抑尘剂的制备方法，包括如下步骤：
按重量份数取聚阴离子纤维素0.15份、曲拉通X-1000.09份、聚环氧乙烷0.07份、水100份，在装有机械搅拌器的容器中依次加入聚阴离子纤维素、曲拉通X-100、功能性助剂聚环氧乙烷、水充分搅拌，溶解得所述抑尘剂成品。
对比例
本对比例一种抑尘剂，其原料组成和制备方法同实施例1，区别在于：将所述曲拉通X-100替换为十二烷基硫酸钠。
实施例和对比例所述抑尘剂的性能测试结果如下(表1)：
表1
| 项目 | 实施例1 | 对比例 |
| 外观 | 无色透明液体，无刺激性气味 | 略微有点浑浊，无刺激性气味 |
| 粘度/mPa.s | 10.5-11.5 | 10.3-11.2 |
| 表面张力/mN/m | 40.5-41.5 | 52-53 |
| 密度/g/cm | 0.97-0.99 | 0.97-0.99 |
| pH | 6.5-7.0 | 6.8-7.3 |
用动态煤流模拟实验台架对实施例1和对比例所述抑尘剂进行抑尘效果实验。煤样用量为1kg，皮带速度3m/s，用CCZ-1000直读式粉尘仪分别测量喷撒水、实施例1所述抑尘剂以及对比例所述抑尘剂之后的动态煤样的粉尘浓度，结果见表2。
表2
从表2可以看出，喷撒实施例1所述抑尘剂后产生的粉尘浓度最低，本发明所述抑尘剂对动态煤流扬尘的抑尘效果显著。
以上所述实施例的各技术特征可以进行任意的组合，为使描述简洁，未对上述实施例中的各个技术特征所有可能的组合都进行描述，然而，只要这些技术特征的组合不存在矛盾，都应当认为是本说明书记载的范围。
以上所述实施例仅表达了本发明的几种实施方式，其描述较为具体和详细，但并不能因此而理解为对发明专利范围的限制。应当指出的是，对于本领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干变形和改进，这些都属于本发明的保护范围。因此，本发明专利的保护范围应以所附权利要求为准。
Claims (6)
1.一种抑尘剂，其特征在于，由如下重量份的原料组成：
2.根据权利要求1所述的抑尘剂，其特征在于，由如下重量份的原料组成：
3.根据权利要求1或2所述的抑尘剂，其特征在于，所述聚阴离子纤维素为高粘度型聚阴离子纤维素。
4.根据权利要求1或2所述的抑尘剂，其特征在于，所述曲拉通X-100的纯度为化学纯，pH为5.0-7.0，密度为1.06-1.07g/mL。
5.根据权利要求1所述的抑尘剂，其特征在于，所述聚环氧乙烷的分子量为500万-700万。
6.权利要求1-5任一项所述的抑尘剂的制备方法，其特征在于，包括如下步骤：于所述聚阴离子纤维素中依次加入所述曲拉通X-100和功能助剂，再加入所述水，搅拌溶解，即得所述抑尘剂。