CN104939432A - Olive cellulose colloid shoe pad and preparation method thereof - Google Patents
Olive cellulose colloid shoe pad and preparation method thereof Download PDFInfo
- Publication number
- CN104939432A CN104939432A CN201510242003.0A CN201510242003A CN104939432A CN 104939432 A CN104939432 A CN 104939432A CN 201510242003 A CN201510242003 A CN 201510242003A CN 104939432 A CN104939432 A CN 104939432A
- Authority
- CN
- China
- Prior art keywords
- temperature
- olive cellulose
- preparation
- pad
- extract
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an olive cellulose colloid shoe pad and a preparation method thereof. The colloid shoe pad is composed of water, olive cellulose, methylcellulose, ginkgol biloba extract, pseudo-ginseng extract and honeysuckle extract, the preparation method comprises the steps of placing 20-24 parts of olive cellulose and 8-10 parts of methylcellulose into 200-250 parts of water at the temperature of 90-100 DEG C, maintaining the temperature, stirring for 30-40 minutes repetitively in a mixer so that complete dissolution can be achieved, and obtaining liquid which is uniformly mixed; stopping the stirring for the solution, waiting the temperature to drop to 50-60 DEG C, adding in 0.7-0.9 part of ginkgol biloba extract, 0.7-0.9 part of pseudo-ginseng extract and 0.7-0.9 part of honeysuckle extract, stirring for 30-40 minutes repetitively at the temperature so that the intensive mixing can be achieved, and obtaining slurry which is uniformly mixed; delivering the slurry at the temperature of 50-60 DEG C into a plywood press through a screw pump, and producing the colloid shoe pad. According to the olive cellulose colloid shoe pad and the preparation method thereof, the olive cellulose which has the natural healthcare function is added in, therefore the colloid shoe pad has a good health care effect.
Description
Technical field
Colloid shoe-pad that the present invention relates to a kind of field of health care products and preparation method thereof, particularly relates to a kind of olive cellulose colloid shoe-pad with health care and preparation method thereof.
Background technology
In current health products trade, product with health role often needs, in specific environment, to use specific device fabrication, makes the man power and material of the production at substantial of product.And existing health products have unicity in its function, and on using, also there is the phenomenon of various inconvenience.
Because the defect that above-mentioned existing health products and production thereof exist, the present inventor is based on being engaged in the practical experience and professional knowledge that this type of product design manufacture enriches for many years, and coordinate the utilization of scientific principle, actively in addition research and innovation, to founding a kind of olive inoglia shoe-pad with health care newly and preparation method thereof, general existing health products and preparation method thereof can be improved, make it have more practicality.Through constantly research, design, and through repeatedly studying sample and after improving, finally creating the present invention had practical value.
Summary of the invention
Main purpose of the present invention is, overcomes the defect of prior art, and provides a kind of olive cellulose colloid shoe-pad with health care newly and preparation method thereof.
The object of the invention to solve the technical problems realizes by the following technical solutions.According to a kind of olive cellulose colloid shoe-pad that the present invention proposes, raw material calculates by weight, and it is composed of the following components: water 200-250 part, olive cellulose 20-24 part, methylcellulose 8-10 part, ginkgo biloba extract 0.7-0.9 part, Notogineng Extract 0.7-0.9 part and Honegsukle flower P.E 0.7-0.9 part.
The object of the invention to solve the technical problems also realizes by the following technical solutions.The preparation method of a kind of olive cellulose colloid shoe-pad proposed according to the present invention, raw material calculates by weight, and it contains following steps:
1) olive cellulose 20-24 part, methylcellulose 8-10 part are placed in the water that 200-250 part temperature is 90-100 DEG C, keep this temperature, repeatedly stir 30-40 minute in the mixing container, make it fully dissolve, form mixed uniformly liquid;
2) stirring to above-mentioned solution is stopped, when its temperature is reduced to 50 DEG C-60 DEG C, add ginkgo biloba extract 0.7-0.9 part, Notogineng Extract 0.7-0.9 part and Honegsukle flower P.E 0.7-0.9 part, repeatedly stir 30-40 minute at this temperature, make it fully mix, form mixed uniformly slurry;
3) be that the slurry of 50 DEG C-60 DEG C is transported in offset plate machine by screw pump by said temperature, make colloid shoe-pad.
The present invention compared with prior art has obvious advantage and beneficial effect.By technique scheme, a kind of olive cellulose of the present invention colloid shoe-pad and preparation method thereof can reach suitable technological progress and practicality, and the extensive value had in industry, it at least has following advantages: have the features such as technique is simple, with low cost, good in economic efficiency, and owing to adding the olive cellulose with natural health function, a kind of olive cellulose of the present invention colloid shoe-pad have promote that children's's brain intelligence increases, promote children's upgrowth and development, prevention cardiovascular and cerebrovascular disease, diabetes, the function such as antiviral and ultraviolet-resistent property.
Detailed description of the invention
For further setting forth the present invention for preferred embodiment below the technological means reaching predetermined goal of the invention and take, a kind of olive cellulose colloid shoe-pad proposed according to the present invention and preparation method thereof its detailed description of the invention is described in detail as follows.
Embodiment 1
A kind of olive cellulose colloid shoe-pad, it is made up of water 200ml, olive cellulose 20g, methylcellulose 8g, ginkgo biloba extract 0.7g, Notogineng Extract 0.7g and Honegsukle flower P.E 0.7g.The preparation of this colloid shoe-pad, containing following steps:
1) olive cellulose 20g, methylcellulose 8g are placed in the water that 200ml temperature is 90 DEG C, keep this temperature, repeatedly stir 30 minutes in the mixing container, make it fully dissolve, form mixed uniformly liquid;
2) stirring to above-mentioned solution is stopped, when its temperature is reduced to 50 DEG C, add ginkgo biloba extract 0.7g, Notogineng Extract 0.7g and Honegsukle flower P.E 0.7g, repeatedly stir 30 minutes at this temperature, make it fully mix, form mixed uniformly slurry;
3) be that the slurry of 50 DEG C is transported in offset plate machine by screw pump by said temperature, make colloid shoe-pad.
Embodiment 2
A kind of olive cellulose colloid shoe-pad, it is made up of water 225ml, olive cellulose 22g, methylcellulose 9g, ginkgo biloba extract 0.8g, Notogineng Extract 0.8g and Honegsukle flower P.E 0.8g.The preparation method of this colloid shoe-pad, it contains following steps:
1) olive cellulose 22g, methylcellulose 9g are placed in the water that 225g temperature is 95 DEG C, keep this temperature, repeatedly stir 35 minutes in the mixing container, make it fully dissolve, form mixed uniformly liquid;
2) stirring to above-mentioned solution is stopped, when its temperature is reduced to 55 DEG C, add ginkgo biloba extract 0.8g, Notogineng Extract 0.8g and Honegsukle flower P.E 0.8g, repeatedly stir 35 minutes at this temperature, make it fully mix, form mixed uniformly slurry;
3) be that the slurry of 55 DEG C is transported in offset plate machine by screw pump by said temperature, make colloid shoe-pad.
Embodiment 3
A kind of olive cellulose colloid shoe-pad, it is made up of water 250ml, olive cellulose 24g, methylcellulose 10g, ginkgo biloba extract 0.9g, Notogineng Extract 0.9g and Honegsukle flower P.E 0.9g.The preparation method of this colloid shoe-pad, containing following steps:
1) olive cellulose 24g, methylcellulose 10g are placed in the water that 250ml temperature is 100 DEG C, keep this temperature, repeatedly stir 40 minutes in the mixing container, make it fully dissolve, form mixed uniformly liquid;
2) stirring to above-mentioned solution is stopped, when its temperature is reduced to 60 DEG C, add ginkgo biloba extract 0.9g, Notogineng Extract 0.9g and Honegsukle flower P.E 0.9g, repeatedly stir 40 minutes at this temperature, make it fully mix, form mixed uniformly slurry;
3) be that the slurry of 60 DEG C is transported in offset plate machine by screw pump by said temperature, make colloid shoe-pad.
The above, it is only preferred embodiment of the present invention, not any pro forma restriction is done to the present invention, although the present invention discloses as above with preferred embodiment, but and be not used to limit the present invention, any those skilled in the art, do not departing within the scope of technical solution of the present invention, make a little change when the technology contents of above-mentioned announcement can be utilized or be modified to the Equivalent embodiments of equivalent variations, in every case be the content not departing from technical solution of the present invention, according to technical spirit of the present invention to any simple modification made for any of the above embodiments, equivalent variations and modification, all still belong in the scope of technical solution of the present invention.
Claims (2)
1. an olive cellulose colloid shoe-pad, raw material calculates by weight, it is characterized in that, it is composed of the following components:
Water 200-250 part;
Olive cellulose 20-24 part;
Methylcellulose 8-10 part;
Ginkgo biloba extract 0.7-0.9 part;
Notogineng Extract 0.7-0.9 part;
And
Honegsukle flower P.E 0.7-0.9 part.
2. a preparation method for olive cellulose colloid shoe-pad, raw material calculates by weight, it is characterized in that, it contains following steps:
1) olive cellulose 20-24 part, methylcellulose 8-10 part are placed in the water that 200-250 part temperature is 90-100 DEG C, keep this temperature, repeatedly stir 30-40 minute in the mixing container, make it fully dissolve, form mixed uniformly liquid;
2) stirring to above-mentioned solution is stopped, when its temperature is reduced to 50 DEG C-60 DEG C, add ginkgo biloba extract 0.7-0.9 part, Notogineng Extract 0.7-0.9 part and Honegsukle flower P.E 0.7-0.9 part, repeatedly stir 30-40 minute at this temperature, make it fully mix, form mixed uniformly slurry;
3) be that the slurry of 50 DEG C-60 DEG C is transported in offset plate machine by screw pump by said temperature, make colloid shoe-pad.