CN104938186A - 一种用于陡坡加固修复的生态绿植构件及制备方法 - Google Patents
一种用于陡坡加固修复的生态绿植构件及制备方法 Download PDFInfo
- Publication number
- CN104938186A CN104938186A CN201510358311.XA CN201510358311A CN104938186A CN 104938186 A CN104938186 A CN 104938186A CN 201510358311 A CN201510358311 A CN 201510358311A CN 104938186 A CN104938186 A CN 104938186A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- ecological green
- obtains
- repair
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种用于陡坡加固修复的生态绿植构件及制备方法,制备方法为:(1)将去除金属和木材的建筑工程废弃物,通过筛选、切割、磨细、水冲洗得到粒径为0.5-4μm的颗粒,干燥;(2)将快硬硫铝酸盐水泥,粉煤灰,腐殖土,步骤(1)获得的颗粒,炭黑,混合搅拌均匀得到A;再将动物骨胶粉,减水剂,聚乙烯醇,纤维素醚,聚丙烯纤维,碳酸氢钠混合均匀得到B;(3)将B和A混合均匀,加入水,倒入构件模具中,反应,制成用于陡坡加固修复的生态绿植构件。本发明制备的绿植构件绿色环保,适合植物生长。具有保水性、保肥性,又有透水性、透气性,可以给植物提供最大的生长空间及生长所需要的营养基。
Description
技术领域
本发明属于陡坡山体坡面植被生态保护和道路交通工程安全领域,特别是涉及一种用于陡坡加固修复的生态绿植构件及制备方法。
背景技术
保护生态环境,促进社会经济的健康、持续发展,已成为世界各国的共识和共同面临的任务。近年,伴随西部大开发步伐的加快,出现了越来越多的山体开挖,并产生严重的生态破坏,合理、有效的植被护坡工程技术的研究与应用是再造我国良好生态环境,建设绿色通道,保证交通要道畅通的迫切需要。
喀斯特是碳酸盐类岩石分布地区特有的地貌现象,目前单一的边坡的植被护坡方法有铺草皮护坡、植生带护坡、液压喷播植草护坡、三维植被网护坡、香根草篱护坡等,同时传统的客土喷播工艺也不能从根本解决喀斯特的山体土质结构、土壤密实度、硬度、整体性的问题,造成边坡越高、越陡,这种累积压力便越大,处理的护坡所承受的侧向压力也越大,并伴随降雨出现,大量水土流失,植被破坏、便越容易破损、坍滑,危害巨大。
发明目的
本发明的目的是克服现有技术的不足,提供一种用于陡坡加固修复的生态绿植构件。
本发明的第二个目的是提供一种用于陡坡加固修复的生态绿植构件的制备方法。
本发明的技术方案概述如下:
一种用于陡坡加固修复的生态绿植构件的制备方法,包括如下步骤:
(1)将去除金属和木材的建筑工程废弃物,通过筛选、切割、磨细、水冲洗得到粒径为0.5-4μm的颗粒,干燥;
(2)按重量,将快硬硫铝酸盐水泥5-30份,粉煤灰5-15份,腐殖土15-60份,步骤(1)获得的颗粒5-10份,炭黑1-4份,混合搅拌均匀得到A;再将动物骨胶粉1-4份,减水剂5-8份,聚乙烯醇0.5-2份,纤维素醚0.5-2份,聚丙烯纤维0.05-1份,碳酸氢钠0.5-10份混合均匀得到B;
(3)将B和A混合均匀,加入B和A总重量15%-30%的水,倒入构件模具中,反应,制成用于陡坡加固修复的生态绿植构件。
步骤(2)优选为:按重量,将快硬硫铝酸盐水泥8份,粉煤灰8份,腐殖土20份,步骤(1)获得的颗粒10份,炭黑2份,混合搅拌均匀得到A;再将动物骨胶粉1.5份,减水剂7份,聚乙烯醇1份,纤维素醚1份,聚丙烯纤维0.08份,碳酸氢钠5份混合均匀得到B。
所述减水剂优选为固含量为20%的聚羧酸减水剂。
上述方法制备的用于陡坡加固修复的生态绿植构件。
本发明的用于陡坡加固修复的生态绿植构件绿色环保,适合植物生长。配合山体的实际情况加固并结合改进的客土喷播工艺,具有保水性、保肥性,又有透水性、透气性,可以给植物提供最大的生长空间及生长所需要的营养基。能有效的使高陡裸露岩石坡面的生态恢复,使生态固废绿色构件和山体紧密结合成一体,利用生态固废绿色构件的特殊结构,充分给植物提供生长的空间和营养物质,并能有效的防止水土流失,以达到最大利用植被加固和绿化山体的目的。对于保护生态环境,恢复道路沿线及其它工程建设造成破坏的山体坡面植被,消除道路交通工程隐患,确保建设工程质量,减轻或避免边坡水毁事故的发生,对提高经济和社会效益均具有十分积极的意义。
附图说明
图1为本发明的方法制备的各种形态的生态绿植构件。
具体实施方式
下面的实施例是为了使本领域的技术人员能够更好地理解本发明,但并不对本发明作任何限制。
本发明各实施例快硬硫铝酸盐水泥以R.SAC 42.5为例,其它与此水泥性质相似的水泥也可以用于本发明,属于本发明的保护范围。
各实施例采用的粉煤灰采用二级。实验证明,用与其性质相似的粉煤灰也可用于本发明。
各实施例采用的聚乙烯醇的型号为1788。实验证明,用与其性质相似的聚乙烯醇也可用于本发明。
各实施例采用的纤维素醚40000。实验证明,用与其性质相似的纤维素醚也可用于本发明。
各实施例采用的聚丙烯纤维的长度为4-6mm。实验证明,用与其性质相似的聚丙烯纤维也可用于本发明。
各实施例采用的减水剂为固含量为20%的聚羧酸减水剂。实验证明,用与其性质相似的减水剂也可用于本发明。
下面结合具体实施例对本发明作进一步的说明。
实施例1
一种用于陡坡加固修复的生态绿植构件的制备方法,包括如下步骤:
(1)将去除金属和木材的建筑工程废弃物,通过筛选、切割、磨细、水冲洗得到粒径为0.5μm的颗粒,干燥;
(2)按重量,将快硬硫铝酸盐水泥5份,粉煤灰5份,腐殖土15份,步骤(1)获得的颗粒5份,炭黑1份,混合搅拌均匀得到A;再将动物骨胶粉1份,减水剂5份,聚乙烯醇0.5份,纤维素醚0.5份,聚丙烯纤维0.05份,碳酸氢钠0.5份混合均匀得到B;
(3)将B和A混合均匀,加入B和A总重量15%的水,倒入构件模具中,反应,制成用于陡坡加固修复的生态绿植构件。
实施例2
一种用于陡坡加固修复的生态绿植构件的制备方法,包括如下步骤:
(1)将去除金属和木材的建筑工程废弃物,通过筛选、切割、磨细、水冲洗得到粒径为2μm的颗粒,干燥;
(2)按重量,将快硬硫铝酸盐水泥8份,粉煤灰8份,腐殖土20份,步骤(1)获得的颗粒10份,炭黑2份,混合搅拌均匀得到A;再将动物骨胶粉1.5份,减水剂7份,聚乙烯醇1份,纤维素醚1份,聚丙烯纤维0.08份,碳酸氢钠5份混合均匀得到B。
(3)将B和A混合均匀,加入B和A总重量20%的水,倒入构件模具中,反应,制成用于陡坡加固修复的生态绿植构件。
实施例3
一种用于陡坡加固修复的生态绿植构件的制备方法,包括如下步骤:
(1)将去除金属和木材的建筑工程废弃物,通过筛选、切割、磨细、水冲洗得到粒径为4μm的颗粒,干燥;
(2)按重量,将快硬硫铝酸盐水泥15份,粉煤灰12份,腐殖土25份,步骤(1)获得的颗粒8份,炭黑3份,混合搅拌均匀得到A;再将动物骨胶粉3份,减水剂8份,聚乙烯醇2份,纤维素醚2份,聚丙烯纤维1份,碳酸氢钠10份混合均匀得到B。
(3)将B和A混合均匀,加入B和A总重量30%的水,倒入构件模具中,反应,制成用于陡坡加固修复的生态绿植构件。
实施例4
一种用于陡坡加固修复的生态绿植构件的制备方法,包括如下步骤:
(1)将去除金属和木材的建筑工程废弃物,通过筛选、切割、磨细、水冲洗得到粒径为0.5μm的颗粒,干燥;
(2)按重量,将快硬硫铝酸盐水泥20份,粉煤灰8份,腐殖土40份,步骤(1)获得的颗粒8份,炭黑3份,混合搅拌均匀得到A;再将动物骨胶粉2份,减水剂8份,聚乙烯醇1.5份,纤维素醚1份,聚丙烯纤维1份,碳酸氢钠5份混合均匀得到B。
(3)将B和A混合均匀,加入B和A总重量20%的水,倒入构件模具中,反应,制成用于陡坡加固修复的生态绿植构件。
实施例5
一种用于陡坡加固修复的生态绿植构件的制备方法,包括如下步骤:
(1)将去除金属和木材的建筑工程废弃物,通过筛选、切割、磨细、水冲洗得到粒径为0.5μm的颗粒,干燥;
(2)按重量,将快硬硫铝酸盐水泥30份,粉煤灰15份,腐殖土60份,步骤(1)获得的颗粒10份,炭黑4份,混合搅拌均匀得到A;再将动物骨胶粉4份,减水剂8份,聚乙烯醇2份,纤维素醚2份,聚丙烯纤维1份,碳酸氢钠9份混合均匀得到B。
(3)将B和A混合均匀,加入B和A总重量20%的水,倒入构件模具中,反应,制成用于陡坡加固修复的生态绿植构件。
各实施例制备的用于陡坡加固修复的生态绿植构件性能见表1
表1
用高羊茅种子、紫花苜蓿种子、多花木兰种子、刺槐种子、黑麦草种子依次撒在实施例1-实施例5制备的用于陡坡加固修复的生态绿植构件上,在气温20±5℃的条件下,于第3天、第6天浇水,第7天观察,均有大量幼苗长出。
Claims (4)
1.一种用于陡坡加固修复的生态绿植构件的制备方法,其特征是包括如下步骤:
(1)将去除金属和木材的建筑工程废弃物,通过筛选、切割、磨细、水冲洗得到粒径为0.5-4μm的颗粒,干燥;
(2)按重量,将快硬硫铝酸盐水泥5-30份,粉煤灰5-15份,腐殖土15-60份,步骤(1)获得的颗粒5-10份,炭黑1-4份,混合搅拌均匀得到A;再将动物骨胶粉1-4份,减水剂5-8份,聚乙烯醇0.5-2份,纤维素醚0.5-2份,聚丙烯纤维0.05-1份,碳酸氢钠0.5-10份混合均匀得到B;
(3)将B和A混合均匀,加入B和A总重量15%-30%的水,倒入构件模具中,反应,制成用于陡坡加固修复的生态绿植构件。
2.根据权利要求1所述的方法,其特征是所述步骤(2)为:按重量,将快硬硫铝酸盐水泥8份,粉煤灰8份,腐殖土20份,步骤(1)获得的颗粒10份,炭黑2份,混合搅拌均匀得到A;再将动物骨胶粉1.5份,减水剂7份,聚乙烯醇1份,纤维素醚1份,聚丙烯纤维0.08份,碳酸氢钠5份混合均匀得到B。
3.根据权利要求1或2所述的方法,其特征是所述减水剂为固含量为20%的聚羧酸减水剂。
4.权利要求1、2或3的方法制备的用于陡坡加固修复的生态绿植构件。