CN104927605A - Water-based alkyd carpentry paint and preparation method thereof - Google Patents
Water-based alkyd carpentry paint and preparation method thereof Download PDFInfo
- Publication number
- CN104927605A CN104927605A CN201510286300.5A CN201510286300A CN104927605A CN 104927605 A CN104927605 A CN 104927605A CN 201510286300 A CN201510286300 A CN 201510286300A CN 104927605 A CN104927605 A CN 104927605A
- Authority
- CN
- China
- Prior art keywords
- water
- agent
- parts
- dispersion
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention particularly relates to water-based carpentry paint and a preparation method thereof. The carpentry paint comprises the following components in parts by weight: 40-60 parts of a water-based acrylic modified alkyd emulsion STW310, 5-20 parts of water, 0-10 parts of ammonia water, 0-2 parts of a dispersing agent D-128, 1-10 parts of talcum powder, 1-10 parts of silica powder, 1-10 parts of extinction powder, 5-20 parts of Bas, 0-1 part of an antifoaming agent tegoFoamex 1488, 0-1 part of a flatting agent EFKA3034, 0-1 part of a wetting agent BYK187, 0-5 parts of a thickening agent RM-12W and 0-5 parts of a preservative HTK-30. The preparation method comprises the following steps: putting the water-based acrylic modified alkyd emulsion STW310, the water, the ammonia water and the dispersing agent in a predetermined weight ratio into a dispersing jar, and dispersing the components at the speed of 600 revolutions for 5minutes 5rpm to form a uniform solution; adding the talcum powder, the silica powder and the extinction powder in a predetermined weight ratio, then adding the Bas, the antifoaming agent, the flatting agent, the wetting agent, the thickening agent and the preservative in a predetermined weight ratio, dispersing the components at the speed of 600 revolutions for 5minutes to form a uniform solution, and filtering, packaging and warehousing the uniform solution.
Description
Technical field
The invention belongs to paint field, be specifically related to a kind of water alcohol acid wood lacquer and preparation method thereof.
Background technology
Continuous worsening along with environment, environmental protection become government consider Economic development time most important factor, wherein coating industry is the important factor causing environmental pollution, therefore at coating industry, how to study application coating that is nontoxic, environmental protection and become coating worker problem in the urgent need to address, in recent years, the restriction of government to organic volatile VOC is more and more stricter, due to the organism VOC that can volatilize a large amount of when traditional solvent-borne coating uses, bring serious pollution to environment.Therefore water-borne coatings must become after the developing direction of coating, although a lot of performance of water-borne coatings does not also reach the performance of solvent based coating, but water-borne coatings is using water as primary solvent, water does not fire, safe, nontoxic, renewable, and low price, through the effort of vast coatings enterprises and coating worker, the product of water-borne coatings and application are ripe gradually, are accepted gradually by consumers in general.
Wherein water alcohol acid wood lacquer is the important directions of water-borne coatings research, and it is high that Synolac has fullness ratio, the advantage that kindliness is good, performance is various, but the weathering resistance of Synolac is undesirable, easy xanthochromia, and hardness is low, therefore the coating existing defects made of single-component water-based Synolac.
Summary of the invention
The object of this invention is to provide a kind of water alcohol acid wood lacquer.The present invention uses acrylic acid modified alkyd resin, but because vinylformic acid has the crisp feature of good weatherability paint film, has both had the weathering resistance of acrylic resin, and had again high fullness ratio, the high-flexibility of Synolac through the Synolac of modification; Invention also uses oil number low, the silicon powder that transparency is high, make product of the present invention have high-clarity and high rigidity.
A kind of aqueous woodware paint, each component of the weight proportion of described wood lacquer is:
Water-based acrylic acid modified alcoholic acid emulsion 40-60;
Water 5-20;
Ammoniacal liquor 0-10;
Dispersion agent D-128 0-2;
Talcum powder 1-10;
Silicon powder 1-10;
Flatting silica 1-10;
Bas 5-20；
Defoamer tegoFoamex1488 0-1;
Flow agent EFKA3034 0-1;
Wetting agent BYK187 0-1;
Thickening material RM-12W 0-5;
Sanitas HTK-30 0-5.
Wherein, each component of the weight proportion of described wood lacquer is:
Water-based acrylic acid modified alcoholic acid emulsion 45-55;
Water 5-15;
Ammoniacal liquor 2-6;
Dispersion agent D-128 1.0;
Talcum powder 3-8;
Silicon powder 3-8;
Flatting silica 3-8;
Bas 10-15；
Defoamer tegoFoamex1488 0.5;
Flow agent EFKA3034 0.5;
Wetting agent BYK187 1.0;
Thickening material RM-12W 2;
Sanitas HTK-30 3.
Another technical problem that the present invention solves there is provided a kind of preparation method of aqueous woodware paint, it is characterized in that, comprises the steps:
A. the water-based acrylic acid modified alcoholic acid emulsion of predetermined weight proportioning, water, ammoniacal liquor, dispersion agent are put into dispersion cylinder;
B. at 600 turns of dispersion 5min, homogeneous solution is formed to the material of step a;
C. talcum powder, silicon powder, the flatting silica of predetermined weight proportioning is added in solution in stepb;
D. at 1200 turns of dispersion 10 ~ 15min, homogeneous solution is formed to the solution of step c;
E. in the solution of steps d, add Bas, flow agent, froth breaking, wetting agent, thickening material, the sanitas of predetermined weight proportioning;
F. at 600 turns of dispersion 5min, homogeneous solution is formed to the material of step a;
G. the solution of f step is filtered and packaged, put in storage.
Compared with prior art, the present invention has following beneficial effect:
1., because formula uses water-based acrylic acid modified alcoholic acid emulsion, it combines the high fullness ratio of acrylic acid weathering resistance and alkyd, therefore the paint film weatherability of product of the present invention is good, fullness ratio is high;
2. the invention to employ oil number low, the silicon powder that transparency is high, makes product of the present invention have high-clarity and high rigidity.
3. the sanitas HTK-30 anticorrosive mildewproof performance of the present invention's use is good, and the water that therefore the present invention uses is tap water, reduces the cost of product.
Embodiment
Below in conjunction with embodiment, the present invention is described further:
Example 1 is equipped with 100Kg waterborne UV coating wood lacquer of the present invention, formulated by the component of following weight proportion:
By water-based acrylic acid modified alcoholic acid emulsion 52Kg, water 11Kg, ammoniacal liquor 3Kg, dispersion agent 1Kg, put into dispersion cylinder; 600 turns of dispersion 5min form homogeneous solution; talcum powder 7Kg, silicon powder 5Kg, flatting silica 3Kg; 1200 turns of dispersion 10 ~ 15min form homogeneous solution, then add flow agent 0.5Kg, defoamer 0.5Kg, Bas11 Kg, wetting agent 1Kg, thickening material 2Kg, sanitas 3Kg; 600 turns of dispersion 5min form homogeneous solution, filter and package, put in storage.
Stability in storage: place 30 days for 50 DEG C, product is without precipitation, without layering, prove that product shelf life is greater than 12 months, normal temperature places 12 months, without going mouldy, pencil hardness 2H(GB6739-96), sticking power 0 grade (hundred lattice methods), tack-free 1h(25 DEG C), resistance to MEK wiping 100 paint films are intact, ultraviolet accelerated weathering test case 168h, △ E<2.0.
Example 2 is equipped with 100Kg waterborne UV coating wood lacquer of the present invention, formulated by the component of following weight proportion:
By water-based acrylic acid modified alcoholic acid emulsion 47Kg, 14 water Kg, ammoniacal liquor 4Kg, dispersion agent 1Kg, put into dispersion cylinder; 600 turns of dispersion 5min form homogeneous solution; talcum powder 6Kg, silicon powder 6Kg, flatting silica 3Kg; 1200 turns of dispersion 10 ~ 15min form homogeneous solution, then add flow agent 0.5Kg, defoamer 0.5Kg, Bas12 Kg, wetting agent 1Kg, thickening material 2Kg, sanitas 3Kg; 600 turns of dispersion 5min form homogeneous solution, filter and package, put in storage.
Stability in storage: place 30 days for 50 DEG C, product is without precipitation, without layering, prove that product shelf life is greater than 12 months, normal temperature places 12 months, without going mouldy, pencil hardness 2H(GB6739-96), sticking power 0 grade (hundred lattice methods), tack-free 1h(25 DEG C), resistance to MEK wiping 100 paint films are intact, ultraviolet accelerated weathering test case 168h, △ E<2.0.
Example 3 is equipped with 100Kg waterborne UV coating wood lacquer of the present invention, formulated by the component of following weight proportion:
By water-based acrylic acid modified alcoholic acid emulsion 48Kg, water 12Kg, ammoniacal liquor 5Kg, dispersion agent 1Kg, put into dispersion cylinder; 600 turns of dispersion 5min form homogeneous solution; talcum powder 5Kg, silicon powder 3Kg, flatting silica 6Kg; 1200 turns of dispersion 10 ~ 15min form homogeneous solution, then add flow agent 0.5Kg, defoamer 0.5Kg, Bas13 Kg, wetting agent 1Kg, thickening material 2Kg, sanitas 3Kg; 600 turns of dispersion 5min form homogeneous solution, filter and package, put in storage.
Stability in storage: place 30 days for 50 DEG C, product is without precipitation, without layering, prove that product shelf life is greater than 12 months, normal temperature places 12 months, without going mouldy, pencil hardness 2H(GB6739-96), sticking power 0 grade (hundred lattice methods), tack-free 1h(25 DEG C), resistance to MEK wiping 100 paint films are intact, ultraviolet accelerated weathering test case 168h, △ E<2.0.
Example 4 is equipped with 100Kg waterborne UV coating wood lacquer of the present invention, formulated by the component of following weight proportion:
By water-based acrylic acid modified alcoholic acid emulsion 50Kg, water 7Kg, ammoniacal liquor 6Kg, dispersion agent 1Kg, put into dispersion cylinder; 600 turns of dispersion 5min form homogeneous solution; talcum powder 4Kg, silicon powder 4Kg, flatting silica 7Kg; 1200 turns of dispersion 10 ~ 15min form homogeneous solution, then add flow agent 0.5Kg, defoamer 0.5Kg, Bas14 Kg, wetting agent 1Kg, thickening material 2Kg, sanitas 3Kg; 600 turns of dispersion 5min form homogeneous solution, filter and package, put in storage.
Stability in storage: place 30 days for 50 DEG C, product is without precipitation, without layering, prove that product shelf life is greater than 12 months, normal temperature places 12 months, without going mouldy, pencil hardness 2H(GB6739-96), sticking power 0 grade (hundred lattice methods), tack-free 1h(25 DEG C), resistance to MEK wiping 100 paint films are intact, ultraviolet accelerated weathering test case 168h, △ E<2.0.
The foregoing is only one embodiment of the invention, do not limit the present invention, the technical scheme that the mode that all employings are equal to replacement or equivalent transformation obtains, all drop in protection scope of the present invention.
Claims (3)
1. an aqueous woodware paint, is characterized in that, each component of the weight proportion of described wood lacquer is:
Water-based acrylic acid modified alcoholic acid emulsion 40-60;
Water 5-20;
Ammoniacal liquor 0-10;
Dispersion agent D-128 0-2;
Talcum powder 1-10;
Silicon powder 1-10;
Flatting silica 1-10;
Bas 5-20；
Defoamer tegoFoamex1488 0-1;
Flow agent EFKA3034 0-1;
Wetting agent BYK187 0-1;
Thickening material RM-12W 0-5;
Sanitas HTK-30 0-5.
2. a kind of cement based penetration crystallization type water proofing paint according to claims 1, is characterized in that, each component of the weight proportion of described wood lacquer is:
Water-based acrylic acid modified alcoholic acid emulsion 45-55;
Water 5-15;
Ammoniacal liquor 2-6;
Dispersion agent D-128 1.0;
Talcum powder 3-8;
Silicon powder 3-8;
Flatting silica 3-8;
Bas 10-15；
Defoamer tegoFoamex1488 0.5;
Flow agent EFKA3034 0.5;
Wetting agent BYK187 1.0;
Thickening material RM-12W 2;
Sanitas HTK-30 3.
3. a kind of cement based penetration crystallization type water proofing paint according to claims 1, is characterized in that, it is characterized in that, comprise the steps:
A. the water-based acrylic acid modified alcoholic acid emulsion of predetermined weight proportioning, water, ammoniacal liquor, dispersion agent are put into dispersion cylinder;
B. at 600 turns of dispersion 5min, homogeneous solution is formed to the material of step a;
C. talcum powder, silicon powder, the flatting silica of predetermined weight proportioning is added in solution in stepb;
D. at 1200 turns of dispersion 10 ~ 15min, homogeneous solution is formed to the solution of step c;
E. in the solution of steps d, add Bas, flow agent, froth breaking, wetting agent, thickening material, the sanitas of predetermined weight proportioning;
F. at 600 turns of dispersion 5min, homogeneous solution is formed to the material of step a;
G. the solution of f step is filtered and packaged, put in storage.