CN104927434A - Water-tolerant paint for glass - Google Patents

Abstract

A water-tolerant paint for glass is made from, by weight, 2 to 4 parts of methyl methacrylate, 8 to 14 parts of butyl stearate, 6 to 9 parts of hydroxyethyl cellulose, 4 to 7 parts of 1, 2-propanediol, 3 to 6 parts of nano-colloid, 4 to 8 parts of modified dry oil, 3 to 6 parts of mica powder, 2 to 7 parts of oleic alcohol, 1 to 6 parts of water-soluble resin, 5 to 8 parts of phthalate anhydride, 3 to 7 parts of dye, 4 to 6 parts of 4-phenylsulfamic acid, 2 to 5 parts of amino resin, 3 to 7 parts of fluxing agent, 15 to 18 parts of red ink, 2 to 5 parts of AEL date red, 3 to 4 parts of bismuth oxychloride, and 3 to 5 parts of petroleum. The water-tolerant paint for glass is good in water tolerance and acid resistance, good in adhesion and higher in safety, and a coating of the water-tolerant paint for glass is uniform.

Description

A kind of water tolerance glass paint

Technical field

The present invention relates to a kind of water tolerance glass paint.

Background technology

Glistening glass furniture can add much beauty to for household, and the glass furniture of brief fashion can promote indoor air makings, and simultaneously under the effect of light, glass can also reflect the ring of light of various romance.Glass paint aims at sprayed glass design, glass paint with common paint to plant compare there is extremely strong sticking power, glass paints the features such as water-fast, acid-and base-resisting, salt.Glass paint according to different needs, can be made into transparent, translucent, opaque, flash of light, radium-shine, illusion-colour, various multi color pattern, glass paint be widely used in the industries such as family property, decoration, bathroom facilities, stove and accessory.But the glass paint poor water resistance on market, and time of drying is long, and weather resistance is not good, and complex manufacturing technology, can not meet the need of market.

Summary of the invention

For the deficiencies in the prior art, the problem to be solved in the present invention is, provide a kind of water tolerance glass to paint, have good water tolerance and acid resistance, adhesivity is good, and paint film is even, and safety performance is higher.

For solving prior art problem, technical scheme provided by the invention is, a kind of water tolerance glass paint, and it is made up of the raw material of following parts by weight:

Methyl methacrylate 2-4 part, butyl stearate 8-14 part, Natvosol 6-9 part, 1,2-propylene glycol 4-7 part, nanometer colloid 3-6 part, modified drying oil 4-8 part, mica powder 3-6 part, oleyl alcohol 2-7 part, water soluble resin 1-6 part, phthalate anhydride 5-8 part, color dye 3-7 part, 4-anilinesulfonic acid 4-6 part, aminoresin 2-5 part, fusing assistant 3-7 part, red black 15-18 part, the purplish red 2-5 part of AEL, Basic Bismuth Chloride 3-4 part, oil 3-5 part.

The invention has the beneficial effects as follows: water tolerance glass paint of the present invention, have good water tolerance and acid resistance, adhesivity is good, and paint film is even, and safety performance is higher.

Embodiment

embodiment 1

A water tolerance glass paint, it is made up of the raw material of following parts by weight:

Methyl methacrylate 2 parts, butyl stearate 8 parts, Natvosol 6 parts, 1,2-propylene glycol 4 parts, nanometer colloid 3 parts, modified drying oil 4 parts, mica powder 3 parts, oleyl alcohol 2 parts, water soluble resin 1 part, phthalate anhydride 5 parts, color dye 3 parts, 4-anilinesulfonic acid 4 parts, 2 parts, aminoresin, fusing assistant 3 parts, red black 15 parts, purplish red 2 parts of AEL, Basic Bismuth Chloride 3 parts, 3 parts, oil.

embodiment 2

A water tolerance glass paint, it is made up of the raw material of following parts by weight:

Methyl methacrylate 4 parts, butyl stearate 14 parts, Natvosol 9 parts, 1,2-propylene glycol 7 parts, nanometer colloid 6 parts, modified drying oil 8 parts, mica powder 3-6 part, oleyl alcohol 2-7 part, water soluble resin 1-6 part, phthalate anhydride 5-8 part, color dye 7 parts, 4-anilinesulfonic acid 6 parts, 5 parts, aminoresin, fusing assistant 7 parts, red black 18 parts, purplish red 5 parts of AEL, Basic Bismuth Chloride 4 parts, 5 parts, oil.

Claims (1)

1. a water tolerance glass paint, is characterized in that: it is made up of the raw material of following parts by weight:

Methyl methacrylate 2-4 part, butyl stearate 8-14 part, Natvosol 6-9 part, 1,2-propylene glycol 4-7 part, nanometer colloid 3-6 part, modified drying oil 4-8 part, mica powder 3-6 part, oleyl alcohol 2-7 part, water soluble resin 1-6 part, phthalate anhydride 5-8 part, color dye 3-7 part, 4-anilinesulfonic acid 4-6 part, aminoresin 2-5 part, fusing assistant 3-7 part, red black 15-18 part, the purplish red 2-5 part of AEL, Basic Bismuth Chloride 3-4 part, oil 3-5 part.