CN104910575A - 一种用于饮水机壳体的注塑料 - Google Patents
一种用于饮水机壳体的注塑料 Download PDFInfo
- Publication number
- CN104910575A CN104910575A CN201510315883.XA CN201510315883A CN104910575A CN 104910575 A CN104910575 A CN 104910575A CN 201510315883 A CN201510315883 A CN 201510315883A CN 104910575 A CN104910575 A CN 104910575A
- Authority
- CN
- China
- Prior art keywords
- injection molding
- molding material
- water dispenser
- parts
- casing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种用于饮水机壳体的注塑料，解决了现有的饮水机壳体注塑料容易挥发有毒物质的技术问题，本发明一种用于饮水机壳体的注塑料，包括以下组分且各组分的重量份为：ABS：40～65份，聚氯乙烯：20～30份，碳酸钙：10～20份，钛白粉：8～15份，有机溶剂：10～20份，抗氧剂：1～5份，阻燃剂：3～6份。
Description
技术领域
本发明涉及一种用于饮水机壳体的注塑料。
技术背景
目前，饮水机壳体注塑料中，含有甲醛、氯乙烯、苯乙烯、丙烯腈等有毒原料，它们都会从成品中慢慢的挥发出来，另外在注塑料中还有许多挥发性的增塑剂、防老剂等添加剂，对饮用水造成污染。
发明内容
本发明解决的技术问题提供了一种用于饮水机壳体的注塑料，解决现有的饮水机壳体注塑料容易挥发有毒物质的技术问题。
为解决上述技术问题，本发明采用如下技术方案：一种用于饮水机壳体的注塑料，包括以下组分且各组分的重量份为：
作为优选的技术方案，各组分的重量份为：
作为优选的技术方案，各组分的重量份为：
进一步的优选方案，所述有机溶剂为二甲基甲酰胺。
进一步的优选方案，所述抗氧剂为2,6-二叔丁基对甲酚。。
进一步的优选方案，所述阻燃剂由三甲硅基甲基膦酸二甲酯和二羟烷基次磷酸盐以1：2的质量比组成。
本发明的有益效果为：本发明采用环保配方制成，ABS和聚氯乙烯配比具有良好的热稳定性和机械性能，本发明不含挥发性的有毒物质，不会使饮水机壳体挥发出难闻的气味，确保饮用水不会受到有毒挥发物质的污染。
具体实施方式
本发明一种用于饮水机壳体的注塑料，包括以下组分且各组分的重量份为：
实施例1：各组分的重量份为：
实施例2：各组分的重量份为：
上述的有机溶剂为二甲基甲酰胺，抗氧剂为2,6-二叔丁基对甲酚，阻燃剂由三甲硅基甲基膦酸二甲酯和二羟烷基次磷酸盐以1：2的质量比组成。
Claims (6)
1.一种用于饮水机壳体的注塑料，其特征在于：包括以下组分且各组分的重量份为：
2.根据权利要求1所述的一种用于饮水机壳体的注塑料，其特征在于：各组分的重量份为：
3.根据权利要求1所述的一种用于饮水机壳体的注塑料，其特征在于：各组分的重量份为：
4.根据权利要求1至3任意一项所述的一种用于饮水机壳体的注塑料，其特征在于：所述有机溶剂为二甲基甲酰胺。
5.根据权利要求1至3任意一项所述的一种用于饮水机壳体的注塑料，其特征在于：所述抗氧剂为2,6-二叔丁基对甲酚。
6.根据权利要求1至3任意一项所述的一种用于饮水机壳体的注塑料，其特征在于：所述阻燃剂由三甲硅基甲基膦酸二甲酯和二羟烷基次磷酸盐以1：2的质量比组成。