CN104910531A - High-foaming-ratio microporous ethylene-propylene-diene monomer rubber material and preparation method of material - Google Patents
High-foaming-ratio microporous ethylene-propylene-diene monomer rubber material and preparation method of material Download PDFInfo
- Publication number
- CN104910531A CN104910531A CN201510344384.3A CN201510344384A CN104910531A CN 104910531 A CN104910531 A CN 104910531A CN 201510344384 A CN201510344384 A CN 201510344384A CN 104910531 A CN104910531 A CN 104910531A
- Authority
- CN
- China
- Prior art keywords
- diene monomer
- rubber
- foaming
- ethylene propylene
- propylene diene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a high-foaming-ratio microporous ethylene-propylene-diene monomer rubber material and a preparation method of the material. The preparation method of the material comprises the following steps: optimizing the formula of the microporous ethylene-propylene-diene monomer rubber material, then simultaneously vulcanizing, cross-linking and foaming the material in a blending extrusion manner to prepare the high-foaming-ratio microporous ethylene-propylene-diene monomer rubber material. The method is simple, is easy to implement, low in cost and excellent in using effect.
Description
Technical field
The present invention relates to materials science field, micropore ethylene propylene diene monomer (EPDM) material of especially a kind of high foamability and preparation method thereof.
Background technology
Ethylene propylene diene rubber foaming materials is widely used in automobile, electrical equipment, daily product, the industry such as furniture and packaging.Developing in recent years along with automobile industry, ethylene propylene diene rubber foaming materials is also more and more extensive in the application of automobile industry, such as in weather strip for automobile etc.But the deficiency that conventional formulation and technique are prepared etc., ethylene propylene diene rubber foaming materials abscess is larger, mechanical property is lower, and these defects of ethylene propylene diene rubber foaming materials become the serious obstruction of ethylene propylene diene rubber foaming materials on the developing application road of frontier.
Summary of the invention
The object of the invention is: micropore ethylene propylene diene monomer (EPDM) material providing a kind of high foamability and preparation method thereof, its expansion ratio is high, and mechanical property is better, to overcome the deficiencies in the prior art.
The present invention is achieved in that the micropore ethylene propylene diene monomer (EPDM) material of high foamability, calculate according to the mass fraction, comprise terpolymer EP rubber 90-110 part, carbon black 35-45 part, rubber reinforcing filler E1 15-25 part, paraffin oil 12-17 part, whipping agent 5-7 part, sulphur 2-5 part, calcium oxide 10-15 part, predispersed accelerator 2-3 part.
Described predispersed accelerator by etc. the MBT-80 of mass parts, ETU-80, CBS-80, ZDBC-80 and DPTT-70 form.
The preparation method of the micropore ethylene propylene diene monomer (EPDM) material of high foamability, by terpolymer EP rubber 90-110 part, carbon black 35-45 part, rubber reinforcing filler E1 15-25 part, paraffin oil 12-17 part, whipping agent 5-7 part, sulphur 2-5 part, after calcium oxide 10-15 part and predispersed accelerator 2-3 part mix, sends in Rubber Extruder, the delivery temperature of screw rod is at 165-180 DEG C, through Rubber Extruder shearing and mixing after, material melting, compound, foaming, finally extrude, cool, and pelletizing, obtain finished product.
Owing to have employed above technical scheme, the present invention carries out preferably the formula of micropore ethylene propylene diene monomer (EPDM) material, by mode material cures is the crosslinked and foaming simultaneously of blending extrusion, improves obtained high foamability, microvesicle hole ethylene propylene diene monomer (EPDM) material.The inventive method is simple, and easy to implement, with low cost, result of use is good.
Embodiment
Embodiments of the invention 1: the micropore ethylene propylene diene monomer (EPDM) material of high foamability, calculate according to the mass fraction, comprise terpolymer EP rubber 100 parts, carbon black 40 parts, rubber reinforcing filler E1 20 parts, paraffin oil 15 parts, whipping agent 6 parts, 3 parts, sulphur, 12 parts, calcium oxide (CaO-80), predispersed accelerator 2.5 parts; Described predispersed accelerator by etc. the MBT-80 of mass parts, ETU-80, CBS-80, ZDBC-80 and DPTT-70 form.
The preparation method of the micropore ethylene propylene diene monomer (EPDM) material of high foamability, by above-mentioned mass fraction, by terpolymer EP rubber, carbon black, rubber reinforcing filler E1, paraffin oil, whipping agent, sulphur, after calcium oxide and predispersed accelerator mix, send in Rubber Extruder, the delivery temperature of screw rod is 165 DEG C, through Rubber Extruder shearing and mixing after, material melting, compound, foaming, finally extrude, cool, and pelletizing, obtain finished product.
Performance is as follows after tested for this obtained routine high-impact scrape resistant matrix material:
Proportion: 0.84g/cm
3
Expansion ratio 1.19
Hardness: 63
Tensile strength: 4.10Mpa
Break-draw strains: 400%
Embodiments of the invention 2: the micropore ethylene propylene diene monomer (EPDM) material of high foamability, material composition is identical with embodiment 1.
The preparation method of the micropore ethylene propylene diene monomer (EPDM) material of high foamability, by above-mentioned mass fraction, by terpolymer EP rubber, carbon black, rubber reinforcing filler E1, paraffin oil, whipping agent, sulphur, after calcium oxide and predispersed accelerator mix, send in Rubber Extruder, the delivery temperature of screw rod is 170 DEG C, through Rubber Extruder shearing and mixing after, material melting, compound, foaming, finally extrude, cool, and pelletizing, obtain finished product.
Performance is as follows after tested for this obtained routine high-impact scrape resistant matrix material:
Proportion: 0.86g/cm
3
Expansion ratio 1.16
Hardness: 62
Tensile strength: 5.71Mpa
Break-draw strains: 420%
Embodiments of the invention 3: the micropore ethylene propylene diene monomer (EPDM) material of high foamability, material composition is identical with embodiment 1.
The preparation method of the micropore ethylene propylene diene monomer (EPDM) material of high foamability, by above-mentioned mass fraction, by terpolymer EP rubber, carbon black, rubber reinforcing filler E1, paraffin oil, whipping agent, sulphur, after calcium oxide and predispersed accelerator mix, send in Rubber Extruder, the delivery temperature of screw rod is 175 DEG C, through Rubber Extruder shearing and mixing after, material melting, compound, foaming, finally extrude, cool, and pelletizing, obtain finished product.
Performance is as follows after tested for this obtained routine high-impact scrape resistant matrix material:
Proportion: 0.78g/cm
3
Expansion ratio 1.28
Hardness: 61
Tensile strength: 5.86Mpa
Break-draw strains: 430%
Embodiments of the invention 4: the micropore ethylene propylene diene monomer (EPDM) material of high foamability, material composition is identical with embodiment 1.
The preparation method of the micropore ethylene propylene diene monomer (EPDM) material of high foamability, by above-mentioned mass fraction, by terpolymer EP rubber, carbon black, rubber reinforcing filler E1, paraffin oil, whipping agent, sulphur, after calcium oxide and predispersed accelerator mix, send in Rubber Extruder, the delivery temperature of screw rod is 180 DEG C, through Rubber Extruder shearing and mixing after, material melting, compound, foaming, finally extrude, cool, and pelletizing, obtain finished product.
Performance is as follows after tested for this obtained routine high-impact scrape resistant matrix material:
Proportion: 0.88g/cm
3
Expansion ratio 1.14
Hardness: 57
Tensile strength: 4.56Mpa
Break-draw strains: 400%
Of the present inventionly be not limited to the embodiment described in embodiment, those skilled in the art's technical scheme according to the present invention draws and other embodiment belongs to technological innovation scope of the present invention equally.Obvious those skilled in the art can carry out various change and modification to the present invention and not depart from the spirit and scope of the present invention.Like this, if these amendments of the present invention and modification belong within the scope of the claims in the present invention and equivalent technologies thereof, then the present invention is also intended to comprise these change and modification.
Claims (3)
1. the micropore ethylene propylene diene monomer (EPDM) material of a high foamability, it is characterized in that: calculate according to the mass fraction, comprise terpolymer EP rubber 90-110 part, carbon black 35-45 part, rubber reinforcing filler E1 15-25 part, paraffin oil 12-17 part, whipping agent 5-7 part, sulphur 2-5 part, calcium oxide 10-15 part and predispersed accelerator 2-3 part.
2. the micropore ethylene propylene diene monomer (EPDM) material of high foamability according to claim 1, is characterized in that: described predispersed accelerator by etc. the MBT-80 of mass parts, ETU-80, CBS-80, ZDBC-80 and DPTT-70 form.
3. the preparation method of the micropore ethylene propylene diene monomer (EPDM) material of a high foamability as claimed in claim 1, it is characterized in that: by terpolymer EP rubber 90-110 part, carbon black 35-45 part, rubber reinforcing filler E1 15-25 part, paraffin oil 12-17 part, whipping agent 5-7 part, sulphur 2-5 part, after calcium oxide 10-15 part and predispersed accelerator 2-3 part mix, send in Rubber Extruder, the delivery temperature of screw rod is at 165-180 DEG C, through Rubber Extruder shearing and mixing after, material melting, compound, foaming, finally extrude, cooling, and pelletizing, obtain finished product.