CN104910529A - Composite plastic pipe - Google Patents
Composite plastic pipe Download PDFInfo
- Publication number
- CN104910529A CN104910529A CN201510333943.0A CN201510333943A CN104910529A CN 104910529 A CN104910529 A CN 104910529A CN 201510333943 A CN201510333943 A CN 201510333943A CN 104910529 A CN104910529 A CN 104910529A
- Authority
- CN
- China
- Prior art keywords
- parts
- resin
- plastic pipe
- composite plastic
- polystyrene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a composite plastic pipe which is composed of the following raw materials: 40-45 parts of polypropylene, 30-35 parts of tetrafluoroethylene, 25-30 parts of polyvinyl fluoride, 20-25 parts of polystyrene, 40-50 parts of polyester resin, 60-70 parts of polystyrene, 40-50 parts of phenolic resin, 35-40 parts of rosin resin, 45-50 parts of rosin modified maleic acid resin, 30-35 parts of polyamide resin, 30-35 parts of petroleum resin, 15-20 parts of alkyd resin, 8-10 parts of barium stearate, 8-10 parts of calcium stearate, 15-20 parts of methyl oleate, 15-25 parts of dioctyl adipate, 10-15 parts of diisobutyl phthalate and 10-15 parts of diethyl phthalate. The composite plastic pipe has hot properties and applicability of engineering plastics, and also has the advantage of high strength, thereby having great market prospects.
Description
Technical field
The present invention relates to a kind of technical field of plastics tubing, particularly relate to a kind of composite plastic pipe.
Background technology
Most main components of plastic pipe are polyvinyl chloride, add other one-tenth in addition and assign to strengthen its thermotolerance, toughness, ductility etc.Plastic pipe is a kind of tubing of maturation, is mainly used in water supply and sewage work.Its surface hardness of existing plastic pipe and tensile strength poor, work-ing life is short, is not suitable with severe environment and uses, and for not staiing, oily dirt free do not have good effect yet.
Summary of the invention
The object of the invention is to overcome the upper existing shortcoming stating prior art, provide a kind of composite plastic pipe, this composite plastic pipe not only has thermal characteristics and the suitability of engineering plastics, and have more the remarkable performance of very intensity, market is huge.
The technical solution adopted for the present invention to solve the technical problems is: a kind of composite plastic pipe, be made up of the feed composition of following number: 40-45 part polypropylene, 30-35 part tetrafluoroethylene, 25-30 part fluorinated ethylene propylene, 20-25 part polystyrene, 40-50 part vibrin, 60-70 part gathers the third ethene, 40-50 part resol, 35-40 part Gum Rosin, the Abietyl modified maleic acid resin of 45-50 part, 30-35 part polyamide resin, 30-35 part petroleum resin, 15-20 part Synolac, 8-10 part barium stearate, 8-10 part calcium stearate, 15-20 part Witconol 2301, 15-25 part Octyl adipate, 10-15 part diisobutyl phthalate, 10-15 part diethyl phthalate.
Further, the number of each feed composition is: 40 parts of polypropylene, 30 parts of tetrafluoroethylene, 25 parts of fluorinated ethylene propylenes, 20 parts of polystyrene, 40 parts of vibrin, 60 parts of poly-third ethene, 40 parts of resol, 35 parts of Gum Rosins, 45 parts of Abietyl modified maleic acid resins, 30 parts of polyamide resins, 30 parts of petroleum resin, 15 parts of Synolac, 8 parts of barium stearates, 8 parts of calcium stearates, 15 parts of Witconol 2301s, 15 parts of Octyl adipates, 10 parts of diisobutyl phthalates, 10 parts of diethyl phthalates.
Or the number of each feed composition is: 45 parts of polypropylene, 35 parts of tetrafluoroethylene, 30 parts of fluorinated ethylene propylenes, 25 parts of polystyrene, 50 parts of vibrin, 70 parts of poly-third ethene, 50 parts of resol, 40 parts of Gum Rosins, 50 parts of Abietyl modified maleic acid resins, 35 parts of polyamide resins, 35 parts of petroleum resin, 20 parts of Synolac, 10 parts of barium stearates, 10 parts of calcium stearates, 20 parts of Witconol 2301s, 25 parts of Octyl adipates, 15 parts of diisobutyl phthalates, 15 parts of diethyl phthalates.
In sum, composite plastic pipe of the present invention not only has thermal characteristics and the suitability of engineering plastics, and have more the remarkable performance of very intensity, market is huge.
Embodiment
Embodiment 1
A kind of composite plastic pipe described by the present embodiment 1, is made up of the feed composition of following number: 40 parts of polypropylene, 30 parts of tetrafluoroethylene, 25 parts of fluorinated ethylene propylenes, 20 parts of polystyrene, 40 parts of vibrin, 60 parts of poly-third ethene, 40 parts of resol, 35 parts of Gum Rosins, 45 parts of Abietyl modified maleic acid resins, 30 parts of polyamide resins, 30 parts of petroleum resin, 15 parts of Synolac, 8 parts of barium stearates, 8 parts of calcium stearates, 15 parts of Witconol 2301s, 15 parts of Octyl adipates, 10 parts of diisobutyl phthalates, 10 parts of diethyl phthalates.
Embodiment 2
A kind of composite plastic pipe described by the present embodiment 2, is made up of the feed composition of following number: 45 parts of polypropylene, 35 parts of tetrafluoroethylene, 30 parts of fluorinated ethylene propylenes, 25 parts of polystyrene, 50 parts of vibrin, 70 parts of poly-third ethene, 50 parts of resol, 40 parts of Gum Rosins, 50 parts of Abietyl modified maleic acid resins, 35 parts of polyamide resins, 35 parts of petroleum resin, 20 parts of Synolac, 10 parts of barium stearates, 10 parts of calcium stearates, 20 parts of Witconol 2301s, 25 parts of Octyl adipates, 15 parts of diisobutyl phthalates, 15 parts of diethyl phthalates.
The above is only preferred embodiment of the present invention, not does any pro forma restriction to technical scheme of the present invention.Every above embodiment is done according to technical spirit of the present invention any simple modification, equivalent variations and modification, all still belong in the scope of technical scheme of the present invention.
Claims (3)
1. a composite plastic pipe, it is characterized in that, be made up of the feed composition of following number: 40-45 part polypropylene, 30-35 part tetrafluoroethylene, 25-30 part fluorinated ethylene propylene, 20-25 part polystyrene, 40-50 part vibrin, 60-70 part gathers the third ethene, 40-50 part resol, 35-40 part Gum Rosin, the Abietyl modified maleic acid resin of 45-50 part, 30-35 part polyamide resin, 30-35 part petroleum resin, 15-20 part Synolac, 8-10 part barium stearate, 8-10 part calcium stearate, 15-20 part Witconol 2301, 15-25 part Octyl adipate, 10-15 part diisobutyl phthalate, 10-15 part diethyl phthalate.
2. a kind of composite plastic pipe according to claim 1, it is characterized in that, the number of each feed composition is: 40 parts of polypropylene, 30 parts of tetrafluoroethylene, 25 parts of fluorinated ethylene propylenes, 20 parts of polystyrene, 40 parts of vibrin, 60 parts of poly-third ethene, 40 parts of resol, 35 parts of Gum Rosins, 45 parts of Abietyl modified maleic acid resins, 30 parts of polyamide resins, 30 parts of petroleum resin, 15 parts of Synolac, 8 parts of barium stearates, 8 parts of calcium stearates, 15 parts of Witconol 2301s, 15 parts of Octyl adipates, 10 parts of diisobutyl phthalates, 10 parts of diethyl phthalates.
3. a kind of composite plastic pipe according to claim 1, it is characterized in that, the number of each feed composition is: 45 parts of polypropylene, 35 parts of tetrafluoroethylene, 30 parts of fluorinated ethylene propylenes, 25 parts of polystyrene, 50 parts of vibrin, 70 parts of poly-third ethene, 50 parts of resol, 40 parts of Gum Rosins, 50 parts of Abietyl modified maleic acid resins, 35 parts of polyamide resins, 35 parts of petroleum resin, 20 parts of Synolac, 10 parts of barium stearates, 10 parts of calcium stearates, 20 parts of Witconol 2301s, 25 parts of Octyl adipates, 15 parts of diisobutyl phthalates, 15 parts of diethyl phthalates.