CN104909702A - Composite slag block and manufacturing method thereof - Google Patents
Composite slag block and manufacturing method thereof Download PDFInfo
- Publication number
- CN104909702A CN104909702A CN201410091073.6A CN201410091073A CN104909702A CN 104909702 A CN104909702 A CN 104909702A CN 201410091073 A CN201410091073 A CN 201410091073A CN 104909702 A CN104909702 A CN 104909702A
- Authority
- CN
- China
- Prior art keywords
- powder
- complex ore
- ore clinker
- mass ratio
- complex
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a composite slag block and its manufacturing method. The manufacturing method comprises the following steps: mixing 70-75 wt% of any one ingredient of water granulated slag, mineral powder and basalt, 5-15wt% of any one ingredient of dolomite, silica and fluorite powder and 15-20 wt% of any one ingredient of lignin humic calcium, sodium silicate and molasses meal, grinding the mixture to a powder, adding water, uniformly mixing, pressing with a die to form a block and airing to obtain the composite slag block. According to the invention, species and sources of the raw materials can be broadened, contents of elements in the raw materials that influence product quality are effectively controlled, and product quality is more excellent. The composite slag block provided by the invention is designed to a prismatic shape, is not easy to roll, and has large area of thrust surface, strong resistance capability and the like. Each component content is uniformly distributed in the polygon.
Description
Technical field
The present invention relates to a kind of complex ore clinker and preparation method thereof.
Background technology
The raw materials for production of rock wool, slag wool are more single, and rely on the shaping slag that blast fumance line gets off, this slag is non-environment-friendly type product, and output is fewer and feweri, are badly in need of increasing raw material types and meet this environmental protection industry demand.
Summary of the invention
For the problems referred to above, the object of the present invention is to provide a kind of complex ore clinker and preparation method thereof, expand raw material types and source, effectively control the constituent content affecting quality product in starting material, make quality product more excellent.
For achieving the above object, a kind of complex ore clinker of the present invention, this complex ore clinker comprises following several component and respective mass percent: major ingredient 70-75%, modified powder 5-15%, binding agent 15-20%.
Preferably, described major ingredient is any one in grain slag, ore powder, basalt.
Preferably, described modified powder is any one in rhombspar, silica, Fluorspar Powder.
Preferably, described binding agent be wooden detritus acid calcium, sodium silicate, molasses powder any one.
Preferably, described complex ore clinker is that the pyramid block of tetragon to be integrated with bottom split and to form by two top planes, and the length of side of Mosaic face is between 40--80mm.
Preferably, the fineness of described major ingredient is 10-200 order.
For achieving the above object, the making method of a kind of complex ore clinker of the present invention, be any one in the grain slag of 70-75%, ore powder, basalt by mass ratio, mass ratio is any one in the rhombspar of 5-15%, silica, Fluorspar Powder, mass ratio is the wooden detritus acid calcium of 15-20%, sodium silicate, molasses powder any one mix pulverize after to add water Homogeneous phase mixing, and be press-forming into block by mould, until become dry.
Beneficial effect of the present invention is:
The present invention can expand raw material types and source, effectively controls the constituent content affecting quality product in starting material, makes quality product more excellent.Its profile design is prismatic, and have not easily rolling, stressed area is large, the advantages such as anti-shot ability is strong, each component content is uniformly distributed in multiple edge body.In addition, the ultimate compression strength >=1MPa of complex ore clinker; Density 2.0-2.5g/cm3 is close with shaping slag data.
Accompanying drawing explanation
Fig. 1 is the structural plan figure of complex ore clinker described in the embodiment of the present invention;
Fig. 2 is the structural perspective of complex ore clinker described in the embodiment of the present invention.
Embodiment
Below in conjunction with Figure of description, the present invention will be further described.
For achieving the above object, the making method of a kind of complex ore clinker of the present invention, be any one in the grain slag of 70-75%, ore powder, basalt by mass ratio, mass ratio is any one in the rhombspar of 5-15%, silica, Fluorspar Powder, mass ratio is the wooden detritus acid calcium of 15-20%, sodium silicate, molasses powder any one mix pulverize after to add water Homogeneous phase mixing, and be press-forming into complex ore clinker by mould, until become dry.Wherein, the fineness of described major ingredient is 10-200 order.
As depicted in figs. 1 and 2, described complex ore clinker is that the pyramid block of tetragon to be integrated with bottom split and to form by two top planes, and the length of side of Mosaic face is between 40--80mm.
Embodiment 1:
Be the grain slag of 72.3% by mass ratio, mass ratio is the silica of 8.6%, mass ratio be 19.1% sodium silicate mix pulverize after to add water Homogeneous phase mixing, and be press-forming into complex ore clinker by mould, until become dry.
Embodiment 2:
Be the ore powder of 70.8% by mass ratio, mass ratio is the silica of 10.3%, mass ratio be 18.9% wooden detritus acid calcium mix pulverize after to add water Homogeneous phase mixing, and be press-forming into complex ore clinker by mould, until become dry.
Embodiment 3:
Be the basalt of 71.0% by mass ratio, mass ratio is the Fluorspar Powder of 9.3%, mass ratio be 19.8% molasses powder mix pulverize after to add water Homogeneous phase mixing, and be press-forming into complex ore clinker by mould, until become dry.
Above; be only preferred embodiment of the present invention, but protection scope of the present invention is not limited thereto, is anyly familiar with those skilled in the art in the technical scope that the present invention discloses; the change that can expect easily or replacement, all should be encompassed within protection scope of the present invention.Therefore, the protection domain that protection scope of the present invention should define with claim is as the criterion.
Claims (7)
1. a complex ore clinker, is characterized in that, this complex ore clinker comprises following several component and respective mass percent: major ingredient 70-75%, modified powder 5-15%, binding agent 15-20%.
2. complex ore clinker according to claim 1, is characterized in that, described major ingredient is any one in grain slag, ore powder, basalt.
3. complex ore clinker according to claim 1, is characterized in that, described modified powder is any one in rhombspar, silica, Fluorspar Powder.
4. complex ore clinker according to claim 1, is characterized in that, described binding agent be wooden detritus acid calcium, sodium silicate, molasses powder any one.
5. complex ore clinker according to claim 1, is characterized in that, described complex ore clinker is that the pyramid block of tetragon to be integrated with bottom split and to form by two top planes, and the length of side of Mosaic face is between 40--80mm.
6. complex ore clinker according to claim 1, is characterized in that, the fineness of described major ingredient is 10-200 order.
7. the making method of a complex ore clinker, it is characterized in that, be any one in the grain slag of 70-75%, ore powder, basalt by mass ratio, mass ratio is any one in the rhombspar of 5-15%, silica, Fluorspar Powder, mass ratio is the wooden detritus acid calcium of 15-20%, sodium silicate, molasses powder any one mix pulverize after to add water Homogeneous phase mixing, and be press-forming into block by mould, until become dry.