CN104909618A - Manufacturing method of regenerated brick capable of purifying water - Google Patents
Manufacturing method of regenerated brick capable of purifying water Download PDFInfo
- Publication number
- CN104909618A CN104909618A CN201510286184.7A CN201510286184A CN104909618A CN 104909618 A CN104909618 A CN 104909618A CN 201510286184 A CN201510286184 A CN 201510286184A CN 104909618 A CN104909618 A CN 104909618A
- Authority
- CN
- China
- Prior art keywords
- gained
- weight parts
- water
- stir
- mud
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a manufacturing method of a regenerated brick capable of purifying water, relating to the technical field of building materials. The manufacturing method comprises the following steps: preparing glue, dehydrating sugar mill lime sludge, evenly mixing the dehydrated lime sludge with slag and construction waste, grinding, roasting to obtain roasted granules, evenly mixing the obtained glue and roasted granules with polyacrylamide, carrying out compression molding, demolding and curing. The method solves the problem that abundant sugar mill sludge is recycled and subjected to innocent treatment and is used for effectively purifying a polluted water body, and has obvious compression resistance, water resistance, corrosion resistance and anti-seepage capacity.
Description
Technical field
The present invention relates to building material technical field, especially a kind of making method of the regeneration brick that can purify water.
Background technology
Current water pollution situation is very severe, is badly in need of carrying out effective purification of water quality to improve this situation.
Guangxi is the tap of national sugar-refining industry, annual produces a large amount of filter mud the like waste, because these sugar refinery are nearly all adopt carbonatation process production technique, to make in filter mud, except containing except large amount of organic, to be also rich in basic carbonate calcium.The current recycling mode of these filter mud of sugar refinery is mainly done fertilizer, feed, acid soil improving agent, is produced commercial lime stone etc.But because alkalescence is high, easily harden, the sales volume doing fertilizer and feed is all little.Cannot be used up so still there is a large amount of filter mud profits, cause environmental pollution.
If these filter mud of sugar refinery are applied to purification of water quality aspect, not only can solve the problem that filter mud pollutes, make pollutent obtain resource utilization, innoxious use, can also contribute for purification of water quality cause, make economic benefit, social benefit and ecological benefits to obtain effect.
Summary of the invention
The invention provides a kind of regeneration brick method that can purify water that filter mud of sugar refinery makes, it can solve the problem of a large amount of sludge from sugar house resource utilization, harmless treatment being carried out effective purification to polluted-water.
In order to solve the problem, the technical solution adopted in the present invention is: the making method of this regeneration brick that can purify water is as follows:
A, the protein powder of 5 ~ 10 weight parts to be joined in the water of 40 ~ 70 weight parts, stir and obtain protein solution;
B, steps A gained protein solution carried out the supersound process 50 ~ 70 minutes that power is 100 ~ 120W, treatment temp is 45 ~ 55 DEG C;
C, add the Sodium dodecylbenzene sulfonate of 0.1 ~ 0.5 weight part to step B gained solution, stir 0.5 ~ 2 hour;
D, add the boric acid of 2 ~ 10 weight parts to step C gained solution, stir 0.5 ~ 3 hour to obtain glue;
E, by water content be 50 ~ 70% filter mud of sugar refinery dehydration must not to dewater filter mud higher than 30% to water content;
F, get 60 ~ 80 weight parts steps A gained dehydration filter mud, the slag of 50 ~ 70 weight parts and the construction waste of 70 ~ 90 weight parts stir, grind to form 150 ~ 200 order particles and obtain composite grain, roasting 20 ~ 40 minutes at 800 ~ 1200 DEG C, obtains roasting particle after cooling;
G, the polyacrylamide of step D gained glue, step F gained roasting particle and 15 ~ 20 weight parts stirred make the ripe mud of adobe;
H, the just ripe mud of step G gained enter mold forming, the demoulding and maintenance and get final product.
In technique scheme, technical scheme can also be more specifically: described protein powder is the mixture of one or more of Zein powder, soybean protein powder, animal globulin powder.
Owing to have employed technique scheme, the present invention compared with prior art has following beneficial effect:
1, raw material filter mud of sugar refinery of the present invention, slag, broken concrete are all trade wastes, have both achieved utilization of waste as resource, and have again reduced cost; Simultaneously under the effect of filter mud and polyacrylamide, easily form microbial film in water body, can effectively purify water; The interpolation of protein powder, Sodium dodecylbenzene sulfonate and boric acid simultaneously makes bonding strength and water tolerance stronger, makes regeneration brick resistance to compression of the present invention, waterproof, protection against corrosion, seepage capability more remarkable, reaches the doulbe-sides' victory of economic benefit and ecological benefits.
2, the present invention after testing, and the ultimate compression strength of load face is about 6.5MPa, and GB is only 5.1 MPa, and water-intake rate is less than 17.1%, and GB is only 20%; Thermal resistance value is greater than 1.2, and contract with dry rate is less than 0.2%, and GB is for being less than 0.5%.As can be seen here, the performance such as Novel lightweight brick resistance to compression of the present invention, fire prevention, waterproof is better.
Embodiment
Below in conjunction with specific embodiment, the invention will be further described:
Embodiment one:
This regeneration brick that can purify water comprises the raw material of following weight part: water content not higher than 30% filter mud of sugar refinery 60, protein powder 5, Sodium dodecylbenzene sulfonate 0.1, boric acid 2, polyacrylamide 15, construction waste 70, slag 50.
Making method is:
A, the soy-protein powder of 5 weight parts to be joined in the water of 40 weight parts, stir and obtain protein solution;
B, steps A gained protein solution carried out the supersound process 50 minutes that power is 100 ~ 120W, treatment temp is 45 ~ 55 DEG C;
C, add the Sodium dodecylbenzene sulfonate of 0.1 weight part to step B gained solution, stir 0.5 hour;
D, add the boric acid of 2 weight parts to step C gained solution, stir 0.5 hour to obtain glue;
E, by water content be 50 ~ 70% filter mud of sugar refinery dehydration must not to dewater filter mud higher than 30% to water content;
F, the dehydration of steps A gained filter mud, the slag of 50 weight parts and the construction waste of 70 weight parts of getting 60 weight parts stir, and grind to form 150 ~ 200 order particles and obtain composite grain, roasting 20 minutes at 800 DEG C, must roasting particle after cooling;
G, the polyacrylamide of step D gained glue, step F gained roasting particle and 15 weight parts stirred make the ripe mud of adobe;
H, the just ripe mud of step G gained enter mold forming, the demoulding and maintenance and get final product.
Embodiment two:
This regeneration brick that can purify water comprises the raw material of following weight part: water content not higher than 30% filter mud of sugar refinery 80, protein powder 10, Sodium dodecylbenzene sulfonate 0.5, boric acid 10, polyacrylamide 20, construction waste 90, slag 70.
Making method is:
A, the soy-protein powder of 10 weight parts to be joined in the water of 70 weight parts, stir and obtain protein solution;
B, steps A gained protein solution carried out the supersound process 50 minutes that power is 100 ~ 120W, treatment temp is 45 ~ 55 DEG C;
C, add the Sodium dodecylbenzene sulfonate of 0.5 weight part to step B gained solution, stir 0.5 hour;
D, add the boric acid of 10 weight parts to step C gained solution, stir 1 hour to obtain glue;
E, by water content be 50 ~ 70% filter mud of sugar refinery dehydration must not to dewater filter mud higher than 30% to water content;
F, the dehydration of steps A gained filter mud, the slag of 70 weight parts and the construction waste of 90 weight parts of getting 80 weight parts stir, and grind to form 150 ~ 200 order particles and obtain composite grain, roasting 30 minutes at 800 DEG C, must roasting particle after cooling;
G, the polyacrylamide of step D gained glue, step F gained roasting particle and 20 weight parts stirred make the ripe mud of adobe;
H, the just ripe mud of step G gained enter mold forming, the demoulding and maintenance and get final product.
Be below experimental data part:
Experimental subjects is a rectangle pool, and area is 54m
2, average depth is 0.7m, and pool water is domestic sewage of villages and small towns, flooding quantity average out to 98 m
3/ d, water quality average out to COD76mg/L, TN19mg/L, TP1.4mg/L, pool water is black smelly, is mainly used in irrigating vegetable plot, the side of a pond.
The regeneration brick that the present invention can purify water is against pool inwall build a wall, reserve water-in, and the regeneration brick that the stacking the present invention with a gap of Stochastic choice 5 place can purify water in the pool.Again survey water quality after 1 month, find that average COD is 65mg/L, TN16 mg/L, TP1.2mg/L, pool water lighter, stink alleviates; After 3 months, average COD is 41mg/L, TN13 mg/L, TP0.8mg/L, pool water lighter, and stink alleviates; After 5 months, average COD is 39mg/L, TN9 mg/L, TP0.7mg/L, and pool water color is close to normal, and stink is less; After this all maintain below COD 40mg/L, TN9 below mg/L, below TP0.75mg/L, pool water color is close to normal, and stink is less.
Visible, the regeneration brick that the present invention can purify water can effectively purify water.
Claims (2)
1. a making method for the regeneration brick that can purify water, is characterized in that comprising following steps:
A, the protein powder of 5 ~ 10 weight parts to be joined in the water of 40 ~ 70 weight parts, stir and obtain protein solution;
B, steps A gained protein solution carried out the supersound process 50 ~ 70 minutes that power is 100 ~ 120W, treatment temp is 45 ~ 55 DEG C;
C, add the Sodium dodecylbenzene sulfonate of 0.1 ~ 0.5 weight part to step B gained solution, stir 0.5 ~ 2 hour;
D, add the boric acid of 2 ~ 10 weight parts to step C gained solution, stir 0.5 ~ 3 hour to obtain glue;
E, by water content be 50 ~ 70% filter mud of sugar refinery dehydration must not to dewater filter mud higher than 30% to water content;
F, get 60 ~ 80 weight parts steps A gained dehydration filter mud, the slag of 50 ~ 70 weight parts and the construction waste of 70 ~ 90 weight parts stir, grind to form 150 ~ 200 order particles and obtain composite grain, roasting 20 ~ 40 minutes at 800 ~ 1200 DEG C, obtains roasting particle after cooling;
G, the polyacrylamide of step D gained glue, step F gained roasting particle and 15 ~ 20 weight parts stirred make the ripe mud of adobe;
H, the just ripe mud of step G gained enter mold forming, the demoulding and maintenance and get final product.
2. the regeneration brick that can purify water according to claim 1, is characterized in that: described protein powder is the mixture of one or more of Zein powder, soybean protein powder, animal globulin powder.