CN104894866A - Manufacturing method for new physical therapy tent material - Google Patents
Manufacturing method for new physical therapy tent material Download PDFInfo
- Publication number
- CN104894866A CN104894866A CN201510191007.0A CN201510191007A CN104894866A CN 104894866 A CN104894866 A CN 104894866A CN 201510191007 A CN201510191007 A CN 201510191007A CN 104894866 A CN104894866 A CN 104894866A
- Authority
- CN
- China
- Prior art keywords
- tent
- physiotherapy
- parts
- manufacture method
- new material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a manufacturing method for a new physical therapy tent material. The manufacturing method is characterized by comprising: 1) mixing the following components according to a certain weight part ratio to obtain a coating agent, wherein the components comprise, by weight, 100 parts of a PVC paste resin, 50-100 parts of plasticizer, 1-5 parts of a stabilizer, 6-15 parts of far infrared ceramic powder, and 1-8 parts of a pigment; 2) grinding and filtering the obtained coating agent; and 3) adding 1-5 kg of a cross-linking agent to per 100 kg of the coating agent, uniformly coating on a base fabric, and then carrying out a drying treatment. According to the present invention, the base fabric woven by using the high-strength and low-shrinkage industrial polyester filaments is utilized (can be the warp knitting biaxial fabric or woven fabric), the PVC, the plasticizer and the stabilizer are adopted as the main raw materials, a certain amount of the active far infrared ceramic powder is added, complete dispersion is performed to prepare the liquid slurry, the liquid slurry is uniformly coated on the front surface and the back surface of the base fabric by using the cutter scrapping coating process, and high temperature plasticizing, pattern pressing and other processes are performed to prepare the new cutter scrapping coating physical therapy tent material.
Description
Technical field
The invention belongs to textile material technical field, specifically belong to a kind of manufacture method of healthcare face fabric.
Background technology
Modern's operating pressure is large, sub-health population is wide, the time of amusement and recreation is at ordinary times few, and many people suffer from one or more diseases such as such as lumbar muscle strain, cervical spondylopathy, scapulohumeral periarthritis, rheumatism, rheumatoid arthritis, skin disease, and these diseases belong to chronic disease, generally be not easy to cure, can far-infrared physiotherapy be passed through, improve immunity of organisms, activating cell, stimulate circulation to regulate physiological function, progressively obtain rehabilitation.But current tent is on the market mainly used in becalming and takes shelter from rain, and function singleness, cannot meet the higher demand of modern, therefore physiotherapy tent new material can meet patient while tourism, can obtain health-care physiotherapeutic again, accord with the demands of the market.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of manufacture method of physiotherapy tent new material, and this tent, by far-infrared physiotherapy, improves immunity of organisms, activating cell, stimulate circulation to regulate physiological function, meet patient while tourism, can health-care physiotherapeutic be obtained again.
In order to solve above technical problem, the present invention by the following technical solutions: a kind of manufacture method of physiotherapy tent new material, is characterized in that it comprises the following steps:
1) component of following weight portion is mixed into coating agent:
PVC paste resin 100 parts
50 ~ 100 parts, plasticizer
Stabilizing agent 1 ~ 5 part
Far-infared ceramic powder 6 ~ 15 parts
Pigment 1 ~ 8 part
2) coating agent be mixed into is ground and filters;
3) add 1 ~ 5 kg crosslinking agent in every 100kg coating agent, be spread evenly across Ji Bushang, then carry out drying and processing;
4) again after baking oven plasticizing forming with carrying out surface treatment, get product.
Apply the coating agent that one deck above-mentioned steps is obtained again, and carry out drying and processing.
During coating agent coating, coating weight is at 100 ~ 350g/ m
2, temperature during oven dry is 140 DEG C ~ 200 DEG C, and temperature during plasticizing is 150 DEG C ~ 210 DEG C.
The domestic existing comparatively multi items of PVC paste resin, as P440, PSM-31, R1069 etc., can use one wherein, or to use wherein several simultaneously, but gross weight is constant.
In crosslinking agent, the content of isocyanate groups is 3%-5%.
Plasticizer can be DOP, DINP or other kind, adding of plasticizer, the active force between PVC strand can be reduced, the fusing point of the vitrification point of PVC plastic, flowing temperature and contained crystallite is all reduced, and plasticizer can improve the plasticity of resin, makes goods softness, resistance to low temperature good.
Stabilizing agent is domestic also the multiple trade mark and kind, according to the environmental requirement of product, can select liquid barium zinc stabilizer.Polyvinyl chloride can produce thermal degradation, variable color and mechanical performance to be worsened when high temperature, for preventing hydraulic performance decline, need add stabilizing agent.Its mechanism of action specifically has: 1. absorb in and HCl, suppress its autocatalysis.2. replace allyl chloride atom unstable in PVC molecule or tertiary carbon chlorine atom, suppress de-PVC.3., with polyene structure generation addition reaction, destroy the formation of large conjugated system, reduce painted.4. catch free radical, stop oxidation reaction.
Far-infared ceramic powder is a kind of white powder, and far-infared ceramic powder is can give off than the more far infrared (infrared emittance is higher) of normal object as principal character function.Activation far-infared ceramic powder adopts stearic acid to carry out surface treatment to far-infared ceramic powder exactly.Physical and chemical character outward appearance: white powder.About 3500 orders, nonionic, anionic property, pH value: 6 ~ 8 dissolubilities: water insoluble and general chemical solvent.The far-infrared temperature thermal effect that product performance 1. is good.2. washing durability is good.After it absorbs extraneous heat energy, the far infrared that wavelength is 4-14 micron can be discharged, be easily absorbed by the body.
In this formula use that pigment is titanium dioxide, one or more during phthalocyanine blue, phthalocyanine green, purple B, medium chrome yellow, lemon yellow, carbon black, floridity are red etc.Adding of pigment can make prevention product make shades of colour, can obtain different colors, be made into colourful pattern and kind because of the difference of addition.
The preferred terylene woven fabric of base cloth of this product.
The present invention compared with prior art has following beneficial effect:
1. cutter scraping coating physiotherapy tent new material is the Ji Bu be made into high intensity low shrinkage industry polyester filament, (can be warp-knitted bi-axial fabric or woven fabric), with PVC, plasticizer, stabilizing agent for main raw material, add a certain amount of activation far-infared ceramic powder, through fully disperseing to be made into liquid slurry, evenly be coated on the tow sides of base cloth by cutter scraping coating technique, be made through operations such as high temperature plasticizing, embossings.
2. product has carried out reforming thoroughly in the formula produced.The new formula of employing, adds activation far-infrared ceramic material, is applied to tent fabric, and making the people's acquisition physiotherapy to a certain degree inhabited in tent, is a kind of novel healthcare face fabric.
3. product has the large feature of peel strength, and be different from laminating, calendered product, fastness is fairly good.
Product is mainly used in and makes physiotherapy tent, while people's leisure, carries out omnibearing maintenance to health, promotes the quality of life of the people.
Detailed description of the invention
Below in conjunction with exemplifying embodiment, the invention will be further described.
embodiment one:
A manufacture method for physiotherapy tent new material, comprises the following steps:
1) following composition by weight is mixed into coating agent:
PVC paste resin 100 parts
65 parts, plasticizer
Stabilizing agent 3 parts
Activation far-infared ceramic powder 10 parts
Carbon black 2 parts
2) coating agent be mixed into is ground and filters, filter and select 80 order nylon wires;
3) by 1000D*1000D density be 8*8 root/centimetre terylene woven fabric pass through coating machine evenly by unreeling structure, 1.8 kg crosslinking agents are added in every 100kg coating agent, in crosslinking agent, isocyanate groups (-NCO) content is 3%, and coating weight is at 105g/ m
2, be spread evenly across on terylene woven fabric, carry out drying and processing through baking oven, the temperature of oven dry is 140 DEG C;
4) again after baking oven plasticizing forming with carrying out surface treatment, temperature during plasticizing is 200 DEG C, and embossing, gets product.
embodiment two:
A manufacture method for physiotherapy tent new material, comprises the following steps:
1) following composition by weight is mixed into coating agent:
PVC paste resin 100 parts
100 parts, plasticizer
Stabilizing agent 5 parts
Activation far-infared ceramic powder 15 parts
Red 8 parts of floridity
2) coating agent be mixed into is ground and filters, filter and select 80 order nylon wires;
3) by 1000D*1000D density be 8*8 root/centimetre terylene woven fabric by unreeling structure evenly by coating machine, add 5 kg crosslinking agents in every 100kg coating agent, in crosslinking agent, isocyanate groups (-NCO) content is 5%, and coating weight is at 350g/ m
2, be spread evenly across on terylene woven fabric, carry out drying and processing through baking oven, the temperature of oven dry is 200 DEG C, then applies one deck coating agent, and carries out drying and processing.
4) again after baking oven plasticizing forming with carrying out surface treatment, temperature during plasticizing is 210 DEG C, and embossing, gets product.
embodiment three:
A manufacture method for physiotherapy tent new material, comprises the following steps:
1) following composition by weight is mixed into coating agent:
PVC paste resin 100 parts
50 parts, plasticizer
Stabilizing agent 1 part
Activation far-infared ceramic powder 6 parts
Medium chrome yellow 1 part
2) coating agent be mixed into is ground and filters, filter and select 80 order nylon wires;
3) by 1000D*1000D density be 8*8 root/centimetre terylene woven fabric by unreeling structure evenly by coating machine, add 1kg crosslinking agent in every 100kg coating agent, in crosslinking agent, isocyanate groups (-NCO) content is 4%, and coating weight is at 100g/ m
2, be spread evenly across on terylene woven fabric, carry out drying and processing through baking oven, the temperature of oven dry is 160 DEG C, then applies one deck coating agent, and carries out drying and processing.
4) again after baking oven plasticizing forming with carrying out surface treatment, temperature during plasticizing is 180 DEG C, and embossing, gets product.
Product the key technical indexes is as follows:
1, grammes per square metre: 250-630g/m
2
2, TENSILE STRENGTH, (warp/latitude): >=1200N/5cm;
3, tearing strength, (warp/latitude): >=80N;
4, peel strength, (warp/latitude): >=80N/5cm;
5, fabric effect, can make microcirculatory blood flow improve 102% for 20 minutes.
Claims (8)
1. a manufacture method for physiotherapy tent new material, is characterized in that it comprises the following steps:
1) component of following weight portion is mixed into coating agent:
PVC paste resin 100 parts
50 ~ 100 parts, plasticizer
Stabilizing agent 1 ~ 5 part
Far-infared ceramic powder 6 ~ 15 parts
Pigment 1 ~ 8 part
2) coating agent be mixed into is ground and filters;
3) add 1 ~ 5 kg crosslinking agent in every 100kg coating agent, be spread evenly across Ji Bushang, then carry out drying and processing;
4) again after baking oven plasticizing forming with carrying out surface treatment, get product.
2. the manufacture method of a kind of physiotherapy tent new material as claimed in claim 1, is characterized in that: in step 3) after drying and processing, then apply one deck step 2) obtained coating agent, and carry out drying and processing.
3. the manufacture method of a kind of physiotherapy tent new material as claimed in claim 1 or 2, is characterized in that: during coating agent coating, coating weight is at 100 ~ 350g/m
2, temperature during oven dry is 140 DEG C ~ 200 DEG C, and temperature during plasticizing is 150 DEG C ~ 210 DEG C.
4. the manufacture method of a kind of physiotherapy tent new material as claimed in claim 1 or 2, is characterized in that: described base cloth is terylene woven fabric.
5. the manufacture method of a kind of physiotherapy tent new material as claimed in claim 1 or 2, is characterized in that: described far-infared ceramic powder is activation far-infared ceramic powder.
6. the manufacture method of a kind of physiotherapy tent new material as claimed in claim 1 or 2, is characterized in that: in described crosslinking agent, the content of isocyanate groups is 3%-5%.
7. the manufacture method of a kind of physiotherapy tent new material as claimed in claim 1 or 2, is characterized in that: described pigment be titanium dioxide, phthalocyanine blue, phthalocyanine green, purple B, medium chrome yellow, lemon yellow, carbon black, floridity red in one or more.
8. the manufacture method of a kind of physiotherapy tent new material as described in claim 1 or 2, is characterized in that: described stabilizing agent is liquid barium zinc stabilizer.