CN104893500B - One kind is used for the anti-skidding grit coating composition of flight-deck long-life improved corrosion - Google Patents
One kind is used for the anti-skidding grit coating composition of flight-deck long-life improved corrosion Download PDFInfo
- Publication number
- CN104893500B CN104893500B CN201510304013.2A CN201510304013A CN104893500B CN 104893500 B CN104893500 B CN 104893500B CN 201510304013 A CN201510304013 A CN 201510304013A CN 104893500 B CN104893500 B CN 104893500B
- Authority
- CN
- China
- Prior art keywords
- mesh
- skidding
- powders
- flight
- coating composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
It is used for the anti-skidding grit coating composition of flight-deck long-life improved corrosion the invention discloses one kind, is made up of E 44/E 35, epoxy resin, toluene, 170 mesh alumina powders, 170 mesh zirconia powders, 150 mesh carborundum powders, 150 mesh ferrite stainless comminuted steel shots, butanol, dimethicone, rilanit special, polyamide wax.The composition of the present invention has good elasticity and toughness, still there is superior salt fog resistance, anti-seawater corrosion, anti-skidding, static conductive, anti-lightning strike characteristic under conditions of moist and ponding, with good adhesive force and sealing, it is easy to cleaning, good comfortableness is trampled while having.
Description
Technical field
It is more particularly to a kind of anti-skidding for flight-deck long-life improved corrosion the invention belongs to specific function paint field
Grit coating composition.
Background technology
Large ship flight-deck coating, the wear-resisting static conductive of its improved corrosion is a realistic problem that can not avoid, mesh
The anti-skidding solids coating of preceding long-life improved corrosion, uses the epoxy polyamide for adding alumina pellet lifting viscosity and wearability
Cold coating.In order to reach the purpose increased the service life, research is mainly around exhibition in terms of optimization epoxy resin and inserts
Open.
When construction, spraying, deck surface is carried out to the removing surface of antirust, dirt and paint first.Sandblasting, steel ball can be used
Or giant is rinsed；Then directly implement to spray on steel substrate surface.Without using priming paint.It is small that spray coating operations complete 5~6
Shi Hou, coating can be fully cured, and reach the level normally used.Anti-skidding grain material be typically inorganic matter (containing quartz, aluminum oxide,
Zirconium oxide, carborundum and stainless steel etc.), in coating, it is necessary to use region to select different pellet ratios according to the different of deck
Coating.
This kind of coating is generally made up of film-forming resin, anti-skidding pellet, solvent and pigment, and resin is that the main of coating is constituted into
Point, anti-skidding pellet is the additive for improving paint slip-resistance.In addition with other adjuvants etc..Resin fixes pellet, together
When protect base material not to be destroyed.Compared with common ship deck coating, the coating has some exclusive features：With good bullet
Property and toughness；With certain coefficient of friction (typically requiring more than 0.7), coefficient of friction is the bigger the better；In moist and ponding
Under environment, non-skid property will not degradation；With good tack and sealing, it is easy to clean and comfortable with trampling
Property.
The content of the invention
There is good elasticity and toughness the technical problem to be solved in the present invention is to provide a kind of, in the bar of moist and ponding
Still there is superior salt fog resistance, anti-seawater corrosion, anti-skidding, static conductive, anti-lightning strike characteristic under part, with good adhesive force and
Sealing, is easy to cleaning, at the same have it is good trample comfortableness be used for anti-skidding hard of flight-deck long-life improved corrosion
Grain coating composition.
The present invention adopts the following technical scheme that solution above-mentioned technical problem：
One kind is used for the anti-skidding grit coating composition of flight-deck long-life improved corrosion, each component and its quality percentage
Number is：
The remarkable advantage of the composition of the present invention has：With good elasticity and toughness；With certain coefficient of friction, one
As require more than 0.7, coefficient of friction is the bigger the better；Under moist and ponding environment, non-skid property will not degradation；Have
Good tack and sealing, is easy to clean and with trampling comfortableness.
Embodiment
Embodiment 1：
The each component of following masses percentage is reconciled and formed：
| Component | Mass percent content |
| The E-44 or E-35 and 20% epoxy resin of mass ratio 80% are combined | Surplus |
| Toluene | 11.0% |
| 170 mesh alumina powders of mass ratio 50% and 50% 170 mesh zirconia powders are compound | 6.0% |
| 150 mesh carborundum powders of mass ratio 50% and 50% 150 mesh ferrite stainless comminuted steel shots are compound | 6.0% |
| Butanol | 3.0% |
| Dimethicone | 300ppm |
| Rilanit special | 8.0% |
| Polyamide wax | 3.0% |
The summation of above each component mass percent is 100%.
Embodiment 2：
The each component of following masses percentage is reconciled and formed：
| Component | Mass percent content |
| The E-44 or E-35 and 20% epoxy resin of mass ratio 80% are combined | Surplus |
| Toluene | 12.0% |
| 170 mesh alumina powders of mass ratio 50% and 50% 170 mesh zirconia powders are compound | 7.0% |
| 150 mesh carborundum powders of mass ratio 50% and 50% 150 mesh ferrite stainless comminuted steel shots are compound | 6.5% |
| Butanol | 3.0% |
| Dimethicone | 300ppm |
| Rilanit special | 9.0% |
| Polyamide wax | 2.0% |
The summation of above each component mass percent is 100%.
Embodiment 3：
The each component of following masses percentage is reconciled and formed：
| Component | Mass percent content |
| 80% E-44 or E-35 and 20% epoxy resin are compound | Surplus |
| Toluene | 11.0% |
| 50% 170 mesh alumina powders and 50% 170 mesh zirconia powders are compound | 7.0% |
| 50% 150 mesh carborundum powders and 50% 150 mesh ferrite stainless comminuted steel shots are compound | 6.5% |
| Butanol | 3.0% |
| Dimethicone | 300ppm |
| Rilanit special | 9.0% |
| Polyamide wax | 3.0% |
The summation of above each component mass percent is 100%.
The main physical and chemical index of film of the product of embodiment 3：
Claims (1)
1. one kind be used for the anti-skidding grit coating composition of flight-deck long-life improved corrosion, it is characterised in that each component and
Its mass percent is：
The E-44 or E-35 and 20% epoxy resin of mass ratio 80% are combined surplus,
Toluene 10.0%~13.0%,
170 mesh alumina powders of mass ratio 50% and 50% 170 mesh zirconia powders compound 5.0%~8.0%,
150 mesh carborundum powders of mass ratio 50% and 50% 150 mesh ferrite stainless comminuted steel shots compound 6.0%~7.0%,
Butanol 2.0%~4.0%,
100~500ppm of dimethicone,
Rilanit special 8.0%~10.0%,
Polyamide wax 2.0%~4.0%.