CN104893441A - Anti-formaldehyde fiber coating - Google Patents
Anti-formaldehyde fiber coating Download PDFInfo
- Publication number
- CN104893441A CN104893441A CN201510271025.XA CN201510271025A CN104893441A CN 104893441 A CN104893441 A CN 104893441A CN 201510271025 A CN201510271025 A CN 201510271025A CN 104893441 A CN104893441 A CN 104893441A
- Authority
- CN
- China
- Prior art keywords
- formaldehyde
- parts
- water
- calcium carbonate
- styrene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an anti-formaldehyde fiber coating. The anti-formaldehyde fiber coating comprises 30-70 parts of styrene-acrylate resin liquid, 20-30 parts of odor elimination emulsion, 10-30 parts of calcium carbonate, 10-20 parts of nanometer activated carbon, 20-30 parts of nanometer titanium, 5-15 parts of hydroxyethyl cellulose, 10-20 parts of sodium gluconate, 10-20 parts of formaldehyde absorbent and 20-30 parts of water in parts by weight. The anti-formaldehyde fiber coating has a relatively strong formaldehyde decomposition technique, scrubbing resistance, a super strong odor elimination function and other functions, provides optimal wall surface effects and is particularly suitable for wall surface renovation and interior decoration.
Description
Technical field
The present invention relates to a kind of house ornamentation paint field, specifically, the present invention relates to a kind of anti-formaldehyde fibers coating.
Background technology
Formaldehyde mainly comes from the product of tackiness agent that uses in a large number of furniture of clamping plate, density board, various artificial board and manufacture thereof, is a kind of colourless, has the obnoxious flavour of intense stimulus smell, soluble in water, alcohol and ether.The World Health Organization assert that formaldehyde is carcinogenic and causes deformed material, can be summarized as hormesis, toxic action and carcinogenesis to the harm of HUMAN HEALTH.
Nano material can produce negative ion, has the function of decomposing formaldehyde, and wherein nano-titanium effect is better, is widely used in paint field, for decomposing formaldehyde, improves Air quality.
Summary of the invention
For above shortcomings in prior art, technical problem to be solved by this invention is to provide a kind of effective anti-formaldehyde fibers coating.
The technical solution adopted for the present invention to solve the technical problems is: provide a kind of anti-formaldehyde fibers coating, comprise styrene-acrylic resin liquid, clean taste emulsion, calcium carbonate, active carbon nanoparticles, nano-titanium, Natvosol, Sunmorl N 60S, formaldehyde absorbent, water, the mass fraction of each component is: styrene-acrylic resin liquid 30-70, clean taste emulsion 20-30, calcium carbonate 10-30, active carbon nanoparticles 10-20, nano-titanium 20-30, Natvosol 5-15, Sunmorl N 60S 10-20, formaldehyde absorbent 10-20, water 20-30.
As preferably, the mass fraction of each component of described anti-formaldehyde fibers coating is: styrene-acrylic resin liquid 45, clean taste emulsion 25, calcium carbonate 10, active carbon nanoparticles 10, nano-titanium 30, Natvosol 8, Sunmorl N 60S 15, formaldehyde absorbent 20, water 30.
As preferably, described styrene-acrylic resin fluid solid content is 36-43wt%.
As preferably, the granularity of described calcium carbonate is 1000-1200 order, further preferred 1120 orders.
As preferably, the particle diameter≤100nm of described nano-titanium.
As preferably, described water is deionized water.
The anti-formaldehyde fibers coating of the one that the present invention obtains, has stronger decomposing formaldehyde technology, in addition, also has the function such as scrubbing resistance, superpower clean taste, provides best metope effect, is particularly suitable for metope renovation and interior decoration.
Embodiment
The anti-formaldehyde fibers coating of one provided by the invention, comprise styrene-acrylic resin liquid, clean taste emulsion, calcium carbonate, active carbon nanoparticles, nano-titanium, Natvosol, Sunmorl N 60S, formaldehyde absorbent, water, the mass fraction of each component is: styrene-acrylic resin liquid 30-70, clean taste emulsion 20-30, calcium carbonate 10-30, active carbon nanoparticles 10-20, nano-titanium 20-30, Natvosol 5-15, Sunmorl N 60S 10-20, formaldehyde absorbent 10-20, water 20-30.
As preferably, the mass fraction of each component of described anti-formaldehyde fibers coating is: styrene-acrylic resin liquid 45, clean taste emulsion 25, calcium carbonate 10, active carbon nanoparticles 10, nano-titanium 30, Natvosol 8, Sunmorl N 60S 15, formaldehyde absorbent 20, water 30.
As preferably, described styrene-acrylic resin fluid solid content is 36-43wt%.
As preferably, the granularity of described calcium carbonate is 1000-1200 order, further preferred 1120 orders.
As preferably, the particle diameter≤100nm of described nano-titanium.
As preferably, described water is deionized water.
Claims (6)
1. an anti-formaldehyde fibers coating, it is characterized in that: comprise styrene-acrylic resin liquid, clean taste emulsion, calcium carbonate, active carbon nanoparticles, nano-titanium, Natvosol, Sunmorl N 60S, formaldehyde absorbent, water, the mass fraction of each component is: styrene-acrylic resin liquid 30-70, clean taste emulsion 20-30, calcium carbonate 10-30, active carbon nanoparticles 10-20, nano-titanium 20-30, Natvosol 5-15, Sunmorl N 60S 10-20, formaldehyde absorbent 10-20, water 20-30.
2. anti-formaldehyde fibers coating according to claim 1, is characterized in that: the mass fraction of each component of described anti-formaldehyde fibers coating is: styrene-acrylic resin liquid 45, clean taste emulsion 25, calcium carbonate 10, active carbon nanoparticles 10, nano-titanium 30, Natvosol 8, Sunmorl N 60S 15, formaldehyde absorbent 20, water 30.
3. anti-formaldehyde fibers coating according to claim 2, is characterized in that: described styrene-acrylic resin fluid solid content is 36-43wt%.
4. anti-formaldehyde fibers coating according to claim 2, is characterized in that: the granularity of described calcium carbonate is 1000-1200 order, further preferred 1120 orders.
5. anti-formaldehyde fibers coating according to claim 2, is characterized in that: the particle diameter≤100nm of described nano-titanium.
6. anti-formaldehyde fibers coating according to claim 2, is characterized in that: described water is deionized water.