CN104891848A - 一种缓凝水泥助磨剂 - Google Patents
一种缓凝水泥助磨剂 Download PDFInfo
- Publication number
- CN104891848A CN104891848A CN201510270020.5A CN201510270020A CN104891848A CN 104891848 A CN104891848 A CN 104891848A CN 201510270020 A CN201510270020 A CN 201510270020A CN 104891848 A CN104891848 A CN 104891848A
- Authority
- CN
- China
- Prior art keywords
- parts
- cement
- grinding aid
- sodium
- trolamine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种缓凝水泥助磨剂。其特征在于由以下重量份的组分组成：元明粉20-30，亚硝酸钠10-15，乙二醇3-6，尼泊金乙酯6-10，醋酸钠3-6，木质素3-7，三乙醇胺5-10，硫酸铝1-3，木钙3-6，三乙醇胺10-16，吐温1-2，废糖渣5-10，粉煤灰2-6。本发明能够显著地提高水泥的磨机粉磨效率8％-15％，适当提高水泥早期强度2-3MPa和增加水泥后期强度2-4MPa的作用；各组分相互协同，提高助磨剂的适应性，以适用于不同等级的水泥，增大使用范围，助磨效果大大提高，也提高了台时产量，降低能耗，且掺量低，为0.02-0.06％/吨水泥。
Description
技术领域
本发明涉及一种缓凝水泥助磨剂。
背景技术
水泥行业是资源消耗大户，不仅大量消耗石灰石等矿物资源，而且对煤炭等能源资源需求量巨大，水泥工业面临着严峻的资源问题。在国家可持续发展的大政策环境下，水泥生产中各个环节的节能减排工作逐渐为人们所重视，而水泥助磨剂是水泥产业链中的重要一环，对提产降耗有显著作用，为水泥企业带来了巨大的经济效益，因而水泥助磨剂逐渐成为研究热点。
发明内容
针对现有技术中存在的问题，本发明的目的在于提供一种缓凝水泥助磨剂的技术方案。
所述的一种缓凝水泥助磨剂，其特征在于由以下重量份的组分组成：元明粉20-30，亚硝酸钠10-15，乙二醇3-6，尼泊金乙酯6-10，醋酸钠3-6，木质素3-7，三乙醇胺5-10，硫酸铝1-3，木钙3-6，三乙醇胺10-16，吐温1-2，废糖渣5-10，粉煤灰2-6。
所述的一种缓凝水泥助磨剂，其特征在于由以下重量份的组分组成：元明粉24-26，亚硝酸钠12-14，乙二醇4-5，尼泊金乙酯7-9，醋酸钠4-5，木质素4-6，三乙醇胺6-8，硫酸铝1.5-2.5，木钙4-5，三乙醇胺12-14，吐温1.4-1.6，废糖渣6-8，粉煤灰3-5。
所述的一种缓凝水泥助磨剂，其特征在于由以下重量份的组分组成：元明粉25，亚硝酸钠13，乙二醇4.5，尼泊金乙酯8，醋酸钠4.5，木质素5，三乙醇胺7，硫酸铝2，木钙4.5，三乙醇胺13，吐温1.5，废糖渣7，粉煤灰4。
本发明的组合配方使用本发明具有进一步提高水泥的后期强度的作用，能够显著地提高水泥的磨机粉磨效率8％-15％，适当提高水泥早期强度2-3MPa和增加水泥后期强度2-4MPa的作用，并且该组合配方不含任何有害成分，符合环保要求；各组分相互协同，提高助磨剂的适应性，以适用于不同等级的水泥，增大使用范围，助磨效果大大提高，也提高了台时产量，降低能耗，且掺量低，为0.02-0.06％/吨水泥。
具体实施方式
实施例1
一种缓凝水泥助磨剂，由以下重量份的组分组成：元明粉20，亚硝酸钠15，乙二醇6，尼泊金乙酯10，醋酸钠6，木质素7，三乙醇胺10，硫酸铝3，木钙6，三乙醇胺16，吐温2，废糖渣10，粉煤灰6，将上述原料混合搅拌30分钟即得本发明的产品。
实施例2
一种缓凝水泥助磨剂，由以下重量份的组分组成：元明粉30，亚硝酸钠10，乙二醇3，尼泊金乙酯6，醋酸钠3，木质素3，三乙醇胺5，硫酸铝1，木钙3，三乙醇胺10，吐温1，废糖渣5，粉煤灰2，将上述原料混合搅拌30分钟即得本发明的产品。
实施例3
一种缓凝水泥助磨剂，由以下重量份的组分组成：元明粉24，亚硝酸钠14，乙二醇5，尼泊金乙酯9，醋酸钠5，木质素6，三乙醇胺8，硫酸铝2.5，木钙5，三乙醇胺14，吐温1.6，废糖渣8，粉煤灰5，将上述原料混合搅拌30分钟即得本发明的产品。
实施例4
一种缓凝水泥助磨剂，由以下重量份的组分组成：元明粉26，亚硝酸钠12，乙二醇4，尼泊金乙酯7，醋酸钠4，木质素4，三乙醇胺6，硫酸铝1.5，木钙4，三乙醇胺12，吐温1.4，废糖渣6，粉煤灰3，将上述原料混合搅拌30分钟即得本发明的产品。
实施例5
一种缓凝水泥助磨剂，由以下重量份的组分组成：元明粉25，亚硝酸钠13，乙二醇4.5，尼泊金乙酯8，醋酸钠4.5，木质素5，三乙醇胺7，硫酸铝2，木钙4.5，三乙醇胺13，吐温1.5，废糖渣7，粉煤灰4，将上述原料混合搅拌30分钟即得本发明的产品。
助磨效果对比试验：
采用本发明实施例1-5制备得的助磨剂及市售助磨剂 (型号 ：GA-100) 掺入水泥原料粉磨过程中，对各助磨剂进行测试，测试结果见表 1：
表 1 水泥助磨测试结果
注：上述水泥粉磨用的全部是管磨机。
Claims (3)
1.一种缓凝水泥助磨剂，其特征在于由以下重量份的组分组成：元明粉20-30，亚硝酸钠10-15，乙二醇3-6，尼泊金乙酯6-10，醋酸钠3-6，木质素3-7，三乙醇胺5-10，硫酸铝1-3，木钙3-6，三乙醇胺10-16，吐温1-2，废糖渣5-10，粉煤灰2-6。
2.根据权利要求1所述的一种缓凝水泥助磨剂，其特征在于由以下重量份的组分组成：元明粉24-26，亚硝酸钠12-14，乙二醇4-5，尼泊金乙酯7-9，醋酸钠4-5，木质素4-6，三乙醇胺6-8，硫酸铝1.5-2.5，木钙4-5，三乙醇胺12-14，吐温1.4-1.6，废糖渣6-8，粉煤灰3-5。
3.根据权利要求1所述的一种缓凝水泥助磨剂，其特征在于由以下重量份的组分组成：元明粉25，亚硝酸钠13，乙二醇4.5，尼泊金乙酯8，醋酸钠4.5，木质素5，三乙醇胺7，硫酸铝2，木钙4.5，三乙醇胺13，吐温1.5，废糖渣7，粉煤灰4。