CN104878464A - Anti-blot textile material and preparation method thereof - Google Patents
Anti-blot textile material and preparation method thereof Download PDFInfo
- Publication number
- CN104878464A CN104878464A CN201510312761.5A CN201510312761A CN104878464A CN 104878464 A CN104878464 A CN 104878464A CN 201510312761 A CN201510312761 A CN 201510312761A CN 104878464 A CN104878464 A CN 104878464A
- Authority
- CN
- China
- Prior art keywords
- weight portion
- textile material
- parts
- stain
- add
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an anti-blot textile material and a preparation method thereof. The anti-blot textile material is prepared from the following components in parts by weight: 68 to 81 parts of fibers, 15 to 20 parts of epoxypropane butyl ether, 8 to 10 parts of polyethylene glycol, 4 to 7 parts of ethyl cellulose, 3 to 5 parts of laurinol, 1 to 3 parts of montan wax acid diethyl ester, 1.5 to 2 parts of silk protein, 0.2 to 1.8 parts of tung oil anhydride and 0.2 to 0.8 parts of carbaldrate. The invention also provides a preparation method of the anti-blot textile material.
Description
Technical field
The invention belongs to textile material field, particularly a kind of anti-stain textile material and preparation method thereof.
Background technology
Natural fabric is that nature exists, and directly can obtain fiber, is divided into string, animal fiber and mineral fibres three class according to its source.Because natural fabric has good comfort level, pliability and gas permeability, thus get more and more people's extensive concerning.
Natural fabric can speckle with spot unavoidably in usual use procedure, but the spot of these attachments is often difficult to removing.Wherein, the antifouling processing of cotton textiles is generally arranged by fluoroplast, make textiles have oil preventing performance, thus prevent greasy dirt from staiing fabric face or stop greasy dirt to penetrate into fabric, to ensure to prevent dirt from staiing fabric face in wearing process.But also have WATER REPELLENCY because common fluoroplast has oil repellent, then have higher requirements to hydrophily as when wearing next to the skin containing cotton textiles, thus fluoroplast is processed and is not suitable for this type of purposes simultaneously.
In Chinese patent CN101258284A through fluoroplast finishing agent process fabric to give grease proofness, when grease soils etc. is expressed between fiber by this kind of antifouling textile product under external force, fluoroplast layer near dirt can hinder cleaning solution to arrive greasy dirt their location, thus is more difficult to remove.
Summary of the invention
For above-mentioned demand, invention especially provides a kind of anti-stain textile material and preparation method thereof.
Object of the present invention can be achieved through the following technical solutions:
A kind of anti-stain textile material, be made up of the component comprising following weight portion:
Described fiber is selected from one or more in cotton fiber, flax fibre, wool fibre and silk fiber.
Described fiber is through methyl triacetoxysilane process.
Described component also comprises polyacrylonitrile fibre 10-15 weight portion.
A preparation method for anti-stain textile material, the method comprises the following steps:
(1) take fiber 68-81 weight portion, epoxy propane butyl ether 15-20 weight portion, ethyl cellulose 4-7 weight portion, brown coal cerinic acid second diester 1-3 weight portion, silk-fibroin 1.5-2 weight portion, Dawsonite Kompensan 0.2-0.8 weight portion and polyacrylonitrile fibre 10-15 weight portion, add in cutter and mix;
(2) add polyethylene glycol 8-10 weight portion, laruyl alcohol 3-5 weight portion, at 80-100 DEG C, stir 20-40 minute, add tung oil acid anhydride 0.2-1.8 weight portion, mix, melting at airtight condition, 205-215 DEG C, spinning, by tractive process, obtained anti-stain textile material.
Described spinning speed is 1600-1800m/min.
Compared with prior art, its beneficial effect is in the present invention:
(1) the anti-stain textile material that obtains of the present invention is by adding brown coal cerinic acid second diester, silk-fibroin, tung oil acid anhydride and Dawsonite Kompensan, the textile material obtained is made to have good mechanical strength and pliability, textile material of the present invention has good antifouling effect simultaneously, can effectively prevent spot from adhering to.
(2) the anti-stain textile material long service life that obtains of the present invention, has good gas permeability.
(3) anti-stain textile material of the present invention, its preparation method is simple, and raw material environmental protection in process of production.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is further illustrated.
Embodiment 1
(1) take cotton fiber 68kg, epoxy propane butyl ether 15kg, ethyl cellulose 4kg, brown coal cerinic acid second diester 1kg, silk-fibroin 1.5kg, Dawsonite Kompensan 0.2kg and polyacrylonitrile fibre 30kg, add in cutter and mix;
(2) add polyethylene glycol 8kg, laruyl alcohol 3kg, stir 20 minutes at 80 DEG C, add tung oil acid anhydride 0.2kg, mix, in airtight condition, melting at 205 DEG C, with the speed spinning of 1600m/min, by tractive process, obtained anti-stain textile material.
The performance test results of obtained anti-stain textile material is as shown in table 1.
Embodiment 2
(1) take the cotton fiber 68kg of methyl triacetoxysilane process, epoxy propane butyl ether 15kg, ethyl cellulose 4kg, brown coal cerinic acid second diester 1kg, silk-fibroin 1.5kg, Dawsonite Kompensan 0.2kg and polyacrylonitrile fibre 10kg, add in cutter and mix;
(2) add polyethylene glycol 8kg, laruyl alcohol 3kg, stir 20 minutes at 80 DEG C, add tung oil acid anhydride 0.2kg, mix, in airtight condition, melting at 205 DEG C, with the speed spinning of 1600m/min, by tractive process, obtained anti-stain textile material.
The performance test results of obtained anti-stain textile material is as shown in table 1.
Embodiment 3
(1) take the cotton fiber 81kg of methyl triacetoxysilane process, epoxy propane butyl ether 20kg, ethyl cellulose 7kg, brown coal cerinic acid second diester 1kg, silk-fibroin 2kg, Dawsonite Kompensan 0.8kg, add in cutter and mix;
(2) add polyethylene glycol 10kg, laruyl alcohol 5kg, stir 40 minutes at 100 DEG C, add tung oil acid anhydride 1.8kg, mix, in airtight condition, melting at 215 DEG C, with the speed spinning of 1800m/min, by tractive process, obtained anti-stain textile material.
The performance test results of obtained anti-stain textile material is as shown in table 1.
Embodiment 4
(1) take the cotton fiber 81kg of methyl triacetoxysilane process, epoxy propane butyl ether 20kg, ethyl cellulose 7kg, brown coal cerinic acid second diester 3kg, silk-fibroin 2kg, Dawsonite Kompensan 0.8kg, add in cutter and mix;
(2) add polyethylene glycol 10kg, laruyl alcohol 5kg, stir 40 minutes at 100 DEG C, add tung oil acid anhydride 1.8kg, mix, in airtight condition, melting at 215 DEG C, with the speed spinning of 1800m/min, by tractive process, obtained anti-stain textile material.
The performance test results of obtained anti-stain textile material is as shown in table 1.
Embodiment 5
(1) take the cotton fiber 81kg of methyl triacetoxysilane process, epoxy propane butyl ether 20kg, ethyl cellulose 7kg, brown coal cerinic acid second diester 3kg, silk-fibroin 2kg, Dawsonite Kompensan 0.2kg, add in cutter and mix;
(2) add polyethylene glycol 10kg, laruyl alcohol 5kg, stir 40 minutes at 100 DEG C, add tung oil acid anhydride 1.8kg, mix, in airtight condition, melting at 215 DEG C, with the speed spinning of 1800m/min, by tractive process, obtained anti-stain textile material.
The performance test results of obtained anti-stain textile material is as shown in table 1.
Comparative example 1
(1) take the cotton fiber 81kg of methyl triacetoxysilane process, epoxy propane butyl ether 20kg, ethyl cellulose 7kg, silk-fibroin 2kg, Dawsonite Kompensan 0.2kg, add in cutter and mix;
(2) add polyethylene glycol 10kg, laruyl alcohol 5kg, stir 40 minutes at 100 DEG C, add tung oil acid anhydride 1.8kg, mix, in airtight condition, melting at 215 DEG C, with the speed spinning of 1800m/min, by tractive process, obtained anti-stain textile material.
The performance test results of obtained anti-stain textile material is as shown in table 1.
Comparative example 2
(1) take the cotton fiber 81kg of methyl triacetoxysilane process, epoxy propane butyl ether 20kg, ethyl cellulose 7kg, brown coal cerinic acid second diester 3kg, silk-fibroin 2kg, add in cutter and mix;
(2) add polyethylene glycol 10kg, laruyl alcohol 5kg, stir 40 minutes at 100 DEG C, add tung oil acid anhydride 1.8kg, mix, in airtight condition, melting at 215 DEG C, with the speed spinning of 1800m/min, by tractive process, obtained anti-stain textile material.
The performance test results of obtained anti-stain textile material is as shown in table 1.
Scribbling lipstick by the textile material of embodiment 1-5 and comparative example 1-2, add in the aqueous solution of soap class washing agent, surveying its greasiness removal time by stirring.
Table 1
The invention is not restricted to embodiment here, those skilled in the art, according to announcement of the present invention, do not depart from improvement that scope makes and amendment all should within protection scope of the present invention.
Claims (6)
1. an anti-stain textile material, is characterized in that, is made up of the component comprising following weight portion:
2. anti-stain textile material according to claim 1, it is characterized in that, described fiber is selected from one or more in cotton fiber, flax fibre, wool fibre and silk fiber.
3. anti-stain textile material according to claim 2, is characterized in that, described fiber is through methyl triacetoxysilane process.
4. anti-stain textile material according to claim 1, it is characterized in that, described component also comprises polyacrylonitrile fibre 10-15 weight portion.
5. a preparation method for anti-stain textile material, is characterized in that, the method comprises the following steps:
(1) take fiber 68-81 weight portion, epoxy propane butyl ether 15-20 weight portion, ethyl cellulose 4-7 weight portion, brown coal cerinic acid second diester 1-3 weight portion, silk-fibroin 1.5-2 weight portion, Dawsonite Kompensan 0.2-0.8 weight portion and polyacrylonitrile fibre 10-15 weight portion, add in cutter and mix;
(2) add polyethylene glycol 8-10 weight portion, laruyl alcohol 3-5 weight portion, at 80-100 DEG C, stir 20-40 minute, add tung oil acid anhydride 0.2-1.8 weight portion, mix, melting at airtight condition, 205-215 DEG C, spinning, by tractive process, obtained anti-stain textile material.
6. the preparation method of anti-stain textile material according to claim 5, is characterized in that, described spinning speed is 1600-1800m/min.