CN104877395A - Ship steel plate coating with superhigh anticorrosive and self-cleaning functions - Google Patents
Ship steel plate coating with superhigh anticorrosive and self-cleaning functions Download PDFInfo
- Publication number
- CN104877395A CN104877395A CN201510210066.8A CN201510210066A CN104877395A CN 104877395 A CN104877395 A CN 104877395A CN 201510210066 A CN201510210066 A CN 201510210066A CN 104877395 A CN104877395 A CN 104877395A
- Authority
- CN
- China
- Prior art keywords
- coating
- inorganic
- inorganic coating
- steel plate
- self
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a ship steel plate coating with superhigh anticorrosive and self-cleaning functions, which comprises a finishing inorganic coating, a surface inorganic coating, a middle inorganic coating and a primer inorganic coating. The ship steel plate coating with superhigh anticorrosive and self-cleaning functions is also provided with an inorganic coating, wherein the inorganic coating sequentially comprises a finishing inorganic coating, a surface inorganic coating, a middle inorganic coating and a primer inorganic coating from top to bottom; and the surface inorganic coating is honeycombed. The inorganic nano resin mixed layer coated on the ship steel plate can perform effective corrosion resistance. The added inorganic nano carbon zinc coating can selectively inhibit microbes and prokaryotes from being attached to the ship without damaging the marine microbes and planktons, so that the microbes can not be attached, thereby ensuring the cleanness of the ship steel plate. The added inorganic nano silicon carbide-silicon dioxide mixed coating can slowly release CO2 when meeting water, thereby blowing down the ash and stains. By adding the activated carbon coating, the stains entering the inorganic coating can be adsorbed and decolorated by carbon granules.
Description
Technical field
The invention belongs to domain of inorganic chemistry, particularly relate to a kind of Ship Steel plate coating with superpower anticorrosion, self-cleaning function.
Background technology
Ship Steel plate coating is also known as Coated Steel.There is the mild steel plate surface-coated Sn of good deep drawability, Zn, Al, Cr, Pb-Sn alloy, the general designation of the goods of organic coating, inorganic paint and plastics etc.Conventional painting (plating) layer steel plate comprises dry plate, tin free steel sheet, steel plate galvanized, Aludip, lead-tin alloy plating alloy steel plate and steel plate with organic coating etc.After Ship Steel plate coating is coated with these inorganic coatings, there is the functions such as the anticorrosion and self-cleaning in superpower property ground, thus halobiontic object can be protected, the ecological requirements of health environment-friendly harsh now can be met again.
Ship Steel plate coating is a large study hotspot of domain of inorganic chemistry at present.The coating process of current employing mainly based on anti-corrosion function, or carries out assistant coating with self-cleaning function, to improve its coating result.
But this method coating is single, and whole process does not reach desirable state, poor effect, inefficiency.
Summary of the invention
The object of the present invention is to provide a kind of Ship Steel plate coating with superpower anticorrosion, self-cleaning function, adopt the means of multi-functional combination to complete coating procedure, to solve existing coating single method, inefficient defect.
The present invention solves the problems of the technologies described above adopted scheme:
A kind of Ship Steel plate coating with superpower anticorrosion, self-cleaning function, described naval vessel steel plate is also provided with inorganic coating, described inorganic coating comprises Lacquer finish inorganic coating, surface inorganic coating, middle painting inorganic coating and primary coat inorganic coating from top to bottom successively, and described surface inorganic coating is cellular.
Preferably, the material of described Lacquer finish inorganic coating is aqueous inorganic nanometer titanium dioxide silicone resin, can superpower property ground anticorrosion.
Preferably, the material of described surface inorganic coating is aqueous inorganic nano silicon carbide zinc.
Preferably, the material of described middle painting inorganic coating is inorganic nano silicon carbide, and meeting water can slowly-releasing CO
2, thus grey stain is blown off.
Preferably, the material of described primary coat inorganic coating is gac, can make to enter the unfortunate spot entering inorganic coating and be faded by carbon granules absorption.
Beneficial effect of the present invention:
(1) be coated with inorganic nano mixed with resin layer at naval vessel steel plate, can carry out effectively anticorrosion;
(2) add silica dioxide coating, limited obstruction microorganism and prokaryotic organism can depend on naval vessel, also be unlikely to injury marine microorganism and planktonic organism, make microorganism non-cohesive thus ensure the cleaning of naval vessel steel plate;
(3) add coat of silicon carbide, meeting water can slowly-releasing CO2, thus grey stain is blown off;
(4) also add inorganic nano silicon carbide and carbon dioxide mix coating, can make to enter the unfortunate spot entering inorganic coating and be faded by carbon granules absorption.
Accompanying drawing explanation
Fig. 1 is the structural representation of Ship Steel plate coating of the present invention.In figure, the Lacquer finish inorganic coating of 1 superpower protection against corrosion, self-cleaning function; The surface inorganic coating of 2 superpower anticorrosion, self-cleaning functions; The middle painting inorganic coating of 3 superpower anticorrosion, self-cleaning functions; The primary coat inorganic coating of 4 superpower anticorrosion, self-cleaning functions; 5 naval vessel steel plates.
Embodiment
Below in conjunction with most preferred embodiment of the present invention, technical scheme of the present invention is further described.
Please refer to Fig. 1, a kind of Ship Steel plate coating
,comprise: the Lacquer finish inorganic coating 1 of superpower protection against corrosion, self-cleaning function; The surface inorganic coating 2 of superpower anticorrosion, self-cleaning function; The middle painting inorganic coating 3 of superpower anticorrosion, self-cleaning function; The primary coat inorganic coating 4 of superpower anticorrosion, self-cleaning function; Naval vessel steel plate 5.
Wherein, the naval vessel steel plate 5 of described superpower anticorrosion, self-cleaning function is also provided with inorganic coating.
Wherein, described inorganic coating comprises Lacquer finish inorganic coating 1, surface inorganic coating 2, middle painting inorganic coating 3 and primary coat inorganic coating 4 from top to bottom successively.
Wherein, described surface inorganic coating 2 is cellular.
Wherein, the material of described Lacquer finish inorganic coating 1 is aqueous inorganic nanometer titanium dioxide silicone resin, can superpower property ground anticorrosion.
Wherein, the material of described surface inorganic coating 2 is inorganic nano carbon zinc.
Wherein, the material of described middle painting inorganic coating 3 is inorganic nano silicon carbide, and meeting water can slowly-releasing CO
2, thus grey stain is blown off.
Wherein, the material of described primary coat inorganic coating 4 is inorganic nano silicon carbide and carbon dioxide mix, can make to enter the unfortunate spot entering inorganic coating and be faded by carbon granules absorption.
Beneficial effect of the present invention:
Be coated with inorganic nano silicon carbide and carbon dioxide mix layer at naval vessel steel plate, can carry out effectively anticorrosion; Add carbon zinc coating, limited obstruction microorganism and prokaryotic organism can depend on naval vessel, also be unlikely to injury marine microorganism and planktonic organism, make microorganism non-cohesive thus ensure the cleaning of naval vessel steel plate; Add coat of silicon carbide, meeting water can slowly-releasing CO
2, thus grey stain is blown off; Also add silicon carbide and carbonic acid gas coating, can make to enter the unfortunate spot entering inorganic coating and be faded by carbon granules absorption.
Claims (5)
1. one kind has the naval vessel steel plate of superpower anticorrosion, self-cleaning function, comprise naval vessel steel plate, it is characterized in that, described naval vessel steel plate is also provided with inorganic coating, described inorganic coating comprises Lacquer finish inorganic coating, surface inorganic coating, middle painting inorganic coating and primary coat inorganic coating from top to bottom successively, and described surface inorganic coating is cellular.
2. a kind of Ship Steel plate coating with superpower anticorrosion, self-cleaning function as claimed in claim 1, it is characterized in that, the material of described Lacquer finish inorganic coating is aqueous inorganic nanometer titanium dioxide silicone resin.
3. a kind of Ship Steel plate coating with superpower anticorrosion, self-cleaning function as claimed in claim 2, it is characterized in that, the material of described surface inorganic coating is inorganic nano carbon zinc.
4. a kind of Ship Steel plate coating with superpower anticorrosion, self-cleaning function as claimed in claim 3, it is characterized in that, the material of described middle painting inorganic coating is inorganic nano silicon carbide.
5. a kind of Ship Steel plate coating with superpower anticorrosion, self-cleaning function as claimed in claim 4, it is characterized in that, the material of described primary coat inorganic coating is that inorganic nano silicon carbide mixes with silicon-dioxide.