CN104876476A - Energy-saving environment-friendly building material - Google Patents
Energy-saving environment-friendly building material Download PDFInfo
- Publication number
- CN104876476A CN104876476A CN201510235494.6A CN201510235494A CN104876476A CN 104876476 A CN104876476 A CN 104876476A CN 201510235494 A CN201510235494 A CN 201510235494A CN 104876476 A CN104876476 A CN 104876476A
- Authority
- CN
- China
- Prior art keywords
- parts
- energy
- building material
- friendly building
- saving environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an energy-saving environment-friendly building material which is prepared from the following raw materials in parts by weight: 3-7 parts of mixed solvent, 3-4 parts of water-based wetting agent, 2-6 parts of high-temperature-resistant adhesive, 13-26 parts of water-based elastic acrylic emulsion, 7-11 parts of polypropylene, 4-10 parts of antioxidant, 4-6 parts of hydroxymethyl cellulose, 1-5 parts of paraffin, 3-5 parts of epoxy resin, 2-4 parts of kaolin, 16-28 parts of magnesium chloride water solution, 3-7 parts of anatase titanium white, 5-8 parts of hollow glass microsphere, 1.8-2.4 parts of graphite powder and 4-8 parts of azobisformamide. The energy-saving environment-friendly building material has the advantages of low energy consumption, low emission, low pollution and favorable oxidation resistance, and can effectively protect the environment.
Description
Technical field
The present invention relates to a kind of energy saving and environment friendly material of construction.
Background technology
At present, the clay class that building field uses and take cement as the wall body building material of jelling agent, also exist high cost source and fuel, complex process, very easily to environment.Building material industry is the rich and influential family of energy consumption and exhaust gas emission, it is reported, building materials industry year, total energy consumption was more than 200,000,000 tons of mark coals, account for that national industrial circle always consumes energy more than 10%, 87% of building materials power consumption total amount shared by the consumption of raw coal and electric power, along with the growth of national economy and the development of construction industry, increase the weight of carrying capacity of environment further.And traditional building material consumes mass energy and Nonrenewable resources, cause serious environment and ecological problem, the quantity discharged of CO accounts for the 15%-20% of national CO total emission volumn, so building material industry will strengthen technological innovation, improve energy consumption and low row's energy-saving building material is met the need of market.
Summary of the invention
For the deficiencies in the prior art, the problem to be solved in the present invention is, provides a kind of energy saving and environment friendly material of construction, less energy-consumption, low emission, low stain, can available protecting environment, and has good oxidation-resistance.
For solving prior art problem, technical scheme provided by the invention is, a kind of energy saving and environment friendly material of construction, and it is made up of the raw material of following parts by weight:
Mixed solvent 3-7 part, aqueous wetting agent 3-4 part, high temperature resistant adhesive 2-6 part, aqueous elastic ACRYLIC EMULSION 13-26 part, polypropylene 7-11 part, oxidation inhibitor 4-10 part, Walocel MT 20.000PV 4-6 part, paraffin 1-5 part, epoxy resin 3-5 part, kaolin 2-4 part, magnesium chloride brine 16-28 part, Detitanium-ore-type titanium dioxide 3-7 part, hollow glass micropearl 5-8 part, Graphite Powder 99 1.8-2.4 part, Cellmic C 121 4-8 part.
The invention has the beneficial effects as follows: energy saving and environment friendly material of construction of the present invention, less energy-consumption, low emission, low stain, can available protecting environment, and there is good oxidation-resistance.
Embodiment
embodiment 1
A kind of energy saving and environment friendly material of construction, it is made up of the raw material of following parts by weight:
Mixed solvent 3 parts, aqueous wetting agent 3 parts, high temperature resistant adhesive 2 parts, aqueous elastic ACRYLIC EMULSION 13 parts, polypropylene 7 parts, 4 parts, oxidation inhibitor, Walocel MT 20.000PV 4 parts, 1 part, paraffin, epoxy resin 3 parts, kaolin 2 parts, magnesium chloride brine 16 parts, Detitanium-ore-type titanium dioxide 3 parts, hollow glass micropearl 5 parts, Graphite Powder 99 1.8 parts, Cellmic C 121 4 parts.
embodiment 2
A kind of energy saving and environment friendly material of construction, it is made up of the raw material of following parts by weight:
Mixed solvent 7 parts, aqueous wetting agent 4 parts, high temperature resistant adhesive 6 parts, aqueous elastic ACRYLIC EMULSION 26 parts, polypropylene 11 parts, 10 parts, oxidation inhibitor, Walocel MT 20.000PV 6 parts, 5 parts, paraffin, epoxy resin 5 parts, kaolin 4 parts, magnesium chloride brine 28 parts, Detitanium-ore-type titanium dioxide 7 parts, hollow glass micropearl 8 parts, Graphite Powder 99 2.4 parts, Cellmic C 121 8 parts.
Claims (1)
1. an energy saving and environment friendly material of construction, is characterized in that: it is made up of the raw material of following parts by weight:
Mixed solvent 3-7 part, aqueous wetting agent 3-4 part, high temperature resistant adhesive 2-6 part, aqueous elastic ACRYLIC EMULSION 13-26 part, polypropylene 7-11 part, oxidation inhibitor 4-10 part, Walocel MT 20.000PV 4-6 part, paraffin 1-5 part, epoxy resin 3-5 part, kaolin 2-4 part, magnesium chloride brine 16-28 part, Detitanium-ore-type titanium dioxide 3-7 part, hollow glass micropearl 5-8 part, Graphite Powder 99 1.8-2.4 part, Cellmic C 121 4-8 part.