CN101050070A - Method for producing Portland cement - Google Patents

Method for producing Portland cement Download PDF

Info

Publication number
CN101050070A
CN101050070A CNA2007100141071A CN200710014107A CN101050070A CN 101050070 A CN101050070 A CN 101050070A CN A2007100141071 A CNA2007100141071 A CN A2007100141071A CN 200710014107 A CN200710014107 A CN 200710014107A CN 101050070 A CN101050070 A CN 101050070A
Authority
CN
China
Prior art keywords
slag
portland cement
cement
steel slag
sandstone
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2007100141071A
Other languages
Chinese (zh)
Inventor
孙建成
刘希海
王国庆
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JINLUCHENG CO Ltd SHANDONG
Original Assignee
JINLUCHENG CO Ltd SHANDONG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JINLUCHENG CO Ltd SHANDONG filed Critical JINLUCHENG CO Ltd SHANDONG
Priority to CNA2007100141071A priority Critical patent/CN101050070A/en
Publication of CN101050070A publication Critical patent/CN101050070A/en
Pending legal-status Critical Current

Abstract

This invention discloses a method for producing Portland cement. The raw materials of the Portland cement comprise steel slag 4-5.5%. The cement clinker is produced with a new dry-method production line, and comprises: limestone 76.6 wt.%, clay 14.1 wt.%, sandstone 4.3 wt.%, and steel slag 5 wt.%. The method can save coal resources, and can utilize waste steel slag.

Description

A kind of method for producing Portland cement
Technical field
The present invention relates to cement, be specially a kind of method for producing Portland cement.
Background technology
Producing at present generally needs in the employed prescription of ordinary Portland cement to add a certain proportion of iron powder, and following table is a common prescription:
The name of an article Wingdale Clay Sandstone Iron powder Slag
Former scheme 82.7 11.4 4.1 1.8 0
Do not see that also the waste steel slag that uses steel mill to dump replaces iron powder and other raw materials of part to produce the report of Portland clinker on new type dry kiln.
Summary of the invention
The objective of the invention is to replace iron powder in the cement clinker raw material, to reach utilization of waste material, energy-conservation, the purpose that reduces production costs by the waste steel slag that uses steel mill to dump.
The present invention implements like this: a kind of production method of silicate cement, contain the slag of 4%-5.5% in its raw mix formula; Calcination of chamotte on new type nonaqueous cement production line.
More specifically, cement slurry formulation weight per-cent is: Wingdale 76.6, clay 14.1, sandstone 4.3, slag 5.
Employed slag composition sees the following form:
Moisture content loss SiO 2 Al 2O 3 Fe 2O 3 CaO MgO ∑
4.00 1.56 16.15 9.68 16.18 45.31 7.55 96.43
Adopt above-mentioned design, the excellent effect that obtains is as follows:
1, raw ingredients is basicly stable, and slag can replace iron powder to use as ferriferous raw material.
2, use the grog composition of slag and original composition to be consistent, can satisfy the requirement of grog composition.
3, the variation of grog free ca is not obvious, adds 5% slag free ca and descends 0.08%.
4,, add 5% slag scheme and improve 1Mpa from 3 days intensity of grog.
5, add slag and reduced carbonate decomposition amount in the decomposing furnace, the corresponding reduction of tail coal consumption has tangible effect of coal saving, and slag falls coal 4kg/t grog for iron powder.
6, increased the consumption of industrial residue, calculated the original industrial residue 3% that consumes more by complete substituting.
Embodiment
Cement clinker composition of raw materials weight percent is: Wingdale 76.6, clay 14.1, sandstone 4.3, slag 5.
Adopt above-mentioned prescription to produce cement clinker and regular convention formula comparative result:
Its raw ingredients relatively sees the following form:
Scheme Loss SiO 2 Al 2O 3 Fe 2O 3 CaO MgO ∑ kh n p
Slag 0% 35.7 11.96 2.61 2 2.08 3 43.44 1.428 97.15 1.145 2.58 1.32
Slag 5% 33.9 12.24 2.70 3 1.95 8 43.43 5 1.428 95.81 1.242 2.63 1.38
Its grog composition comparative result sees the following form:
Scheme Loss SiO 2 Al 2O 3 Fe 2O 3 CaO MgO SO 3 F-CaO
Slag 0% 0.64 21.94 4.78 3.35 65.03 2.25 0.64 2.12
Slag 5% 0.64 22.54 4.80 3.46 64.19 2.37 0.57 2.10
Scheme KH KH’ N P C 3S C 2S C 3A C 4AF 3d (Mpa)
Slag 0% 0.912 0.869 2.703 1.423 50.42 24.84 7.00 10.21 29.90
Slag 5% 0.894 0.854 2.634 1.402 46.95 27.43 7.07 10.45 29.56

Claims (2)

1. the production method of a silicate cement is characterized in that containing in the raw mix formula slag of 4%-6%, calcination of chamotte on new type nonaqueous cement production line.
2. the production method of a kind of silicate cement as claimed in claim 1 is characterized in that its grog composition of raw materials weight percent is: Wingdale 76.6, clay 14.1, sandstone 4.3, slag 5.
CNA2007100141071A 2007-03-30 2007-03-30 Method for producing Portland cement Pending CN101050070A (en)