CN104875321A - Latex pillow production technology - Google Patents
Latex pillow production technology Download PDFInfo
- Publication number
- CN104875321A CN104875321A CN201510200409.2A CN201510200409A CN104875321A CN 104875321 A CN104875321 A CN 104875321A CN 201510200409 A CN201510200409 A CN 201510200409A CN 104875321 A CN104875321 A CN 104875321A
- Authority
- CN
- China
- Prior art keywords
- latex
- ratio
- powder
- weight ratio
- zinc oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a latex pillow production technology. The latex pillow production technology is characterized by comprising the following steps: preparing a latex solution containing ion powder, then adding the prepared latex solution together with zinc oxide and a coagulator into a foaming device for foaming so as to prepare a material A; preparing a latex solution containing ochre powder, then adding the latex solution together with zinc oxide and a coagulator into a foaming device for foaming so as to prepare a material B; preparing a latex solution containing magnet powder, then adding the latex solution together with zinc oxide and a coagulator into a foaming device for foaming so as to prepare a material C; then adding the material A, the material B and the material C with the same weight into a mold, wherein the material A is on the left, the material B is in the middle and the material C is on the right; and finally, putting the mold into a steaming box for hot steaming, opening the mold after the material A, the material B and the material C are steamed completely, and thus taking out the latex pillow product. The latex pillow prepared by the production technology is not different from the pure natural latex product; negative ion powder, ochre powder and magnet powder are added reasonably, and three parts of the pillow have different health functions.
Description
[technical field]
The present invention relates to a kind of latex pillow production technology.
[background technology]
Along with the raising of people's living standard, the pillow that pure natural latex is made is as the high-grade bedding of one, more and more entered ordinary people other, natural emulsion has that anti-mite is fungi-proofing, fine air permeability and hygroscopicity, soft touch and the latex high resiliency of its uniqueness can comply with human body head, not only more meet permanent sleep habit, more allowed natural emulsion pillow bring user healthy comfortable sleep.In addition, for increasing health care, in latex pillow, past contact can add one or more of negative ion powder, ochre powder and magnet powder, here Problems existing has: 1. the distribution density of negative ion powder in latex is little, if do not have due health-care effect. and distribution density is large, need in whole latex pillow to add a large amount of negative ion powders, there is no need at all, also waste can be caused, be unfavorable for environmental protection, therefore, in prior art, negative ion powder often occurs with bulk form, but obviously destroys the soft touch of latex uniqueness, 2. ochre has the health-care effect of suppressing hyperactive liver for calming endogenous wind, if but ochre is applied directly on latex pillow, obviously the soft touch of latex uniqueness can be destroyed, therefore needing clays into power ochre adds in latex, but, ochre powder mixes completely with latex, not only need a large amount of ochre powder, and ochre powder just could embody the health-care effect of its real suppressing hyperactive liver for calming endogenous wind in the position close with human body, ochre is so just caused to waste, what is more important, if add magnet powder in latex pillow, their can magnetic attracting and lump, fully can not mix with latex, not only affect latex product quality, do not have due health-care effect simultaneously, if 3. will magnet powder be added in latex pillow, also must add in whole latex pillow, very large waste can be caused.
[summary of the invention]
For solving the deficiency that background technology exists, the present invention takes following technical scheme to realize:
Latex pillow production technology, is characterized in that comprising the following steps: 1. the latex solution of 60% solid content and negative ion powder are mixed high-speed stirred with the ratio of weight ratio 100: 2.0, mixing speed 350 revs/min, 30 minutes time; 2. above-mentioned obtained mixed solution and zinc oxide, coagulating agent are foamed to join foaming machine together with the ratio of weight ratio 100: 2.5: 1.5, need to add appropriate air according to expansion density, make A material; 3. the latex solution of 60% solid content and ochre powder are mixed high-speed stirred with the ratio of weight ratio 100: 1.5, mixing speed 350 revs/min, 30 minutes time; 4. above-mentioned obtained mixed solution and zinc oxide, coagulating agent are foamed to join foaming machine together with the ratio of weight ratio 100: 2.5: 1.5, need to add appropriate air according to expansion density, make B material; 5. the latex solution of 60% solid content and magnet powder are mixed high-speed stirred with the ratio of weight ratio 100: 1.5, mixing speed 350 revs/min, 30 minutes time; 6. above-mentioned obtained mixed solution and zinc oxide, coagulating agent are foamed to join foaming machine together with the ratio of weight ratio 100: 2.5: 1.5, need to add appropriate air according to expansion density, make C material; 7. expected by the A of identical weight, B material adds mould together with C material, A material is placed in a left side, and B material is placed in the middle, and C material is placed in the right side; 8. mould is put in steam box and carries out heat steaming, and A material, B material and C material cook rear die sinking and take out latex pillow goods.
After adopting technique scheme, first A material is made, B material and C material are as subsequent use, only negative ion powder is rich in A material, ochre powder is only rich in B material, only magnet powder is rich in C material, negative ion powder, the addition of ochre powder and magnet powder is reasonable, negative ion powder has high distribution density, ochre powder and magnet powder are independent of each other, except negative ion powder, outside ochre powder is different with magnet powder, A expects, B expects, other component in C material is identical, then A is expected, to add in mould together with B material and C material that (A expects to be placed in a left side, B material is placed in the middle, C material is placed in the right side) steam with mould heat, cook rear A to expect, B expects, the latex part of C material is integrated completely, so the latex pillow made and common pure natural latex are as good as, but negative ion powder, ochre powder and magnet powder are present in the position, left, center, right of latex pillow respectively, pillow three positions have three kinds of different health cares, play anion respectively, the health-care effect of suppressing hyperactive liver for calming endogenous wind and magnetic therapy.In the production process of above-mentioned latex pillow, zinc oxide plays the effect of Latex cure, and coagulating agent plays the effect that latex solidifies
[detailed description of the invention]
Latex pillow production technology of the present invention, it is characterized in that comprising the following steps: 1. the latex solution of 60% solid content and negative ion powder are mixed with the ratio of weight ratio 100: 2.0 and be put into high-speed stirred in mixer, mixing speed 350 revs/min, 30 minutes time; 2. above-mentioned obtained mixed solution and zinc oxide, coagulating agent (selecting prodan) are foamed to join foaming machine together with the ratio of weight ratio 100: 2.5: 1.5, need to add appropriate air according to expansion density, stir 10 second time, temperature controls at 30 DEG C, makes A material; 3. the latex solution of 60% solid content and ochre powder are mixed with the ratio of weight ratio 100: 1.5 and be put into high-speed stirred in mixer, mixing speed 350 revs/min, 30 minutes time; 4. above-mentioned obtained mixed solution and zinc oxide, coagulating agent (selecting prodan) are foamed to join foaming machine together with the ratio of weight ratio 100: 2.5: 1.5, need to add appropriate air according to expansion density, stir 10 second time, temperature controls at 30 DEG C, makes B material; 5. the latex solution of 60% solid content and magnet powder are mixed with the ratio of weight ratio 100: 1.5 and be put into high-speed stirred in mixer, mixing speed 350 revs/min, 30 minutes time; 6. above-mentioned obtained mixed solution and zinc oxide, coagulating agent (selecting prodan) are foamed to join foaming machine together with the ratio of weight ratio 100: 2.5: 1.5, need to add appropriate air according to expansion density, stir 10 second time, temperature controls at 30 DEG C, makes C material; 7. expected by the A of identical weight, B material adds mould together with C material, A material is placed in a left side, and B material is placed in the middle, and C material is placed in the right side; 8. mould is put in steam box and carries out heat steaming, and A material, B material and C material cook rear die sinking and take out latex pillow goods.
Claims (1)
1. latex pillow production technology, is characterized in that comprising the following steps: 1. the latex solution of 60% solid content and negative ion powder are mixed high-speed stirred with the ratio of weight ratio 100: 2.0, mixing speed 350 revs/min, 30 minutes time; 2. above-mentioned obtained mixed solution and zinc oxide, coagulating agent are foamed to join foaming machine together with the ratio of weight ratio 100: 2.5: 1.5, need to add appropriate air according to expansion density, make A material; 3. the latex solution of 60% solid content and ochre powder are mixed high-speed stirred with the ratio of weight ratio 100: 1.5, mixing speed 350 revs/min, 30 minutes time; 4. above-mentioned obtained mixed solution and zinc oxide, coagulating agent are foamed to join foaming machine together with the ratio of weight ratio 100: 2.5: 1.5, need to add appropriate air according to expansion density, make B material; 5. the latex solution of 60% solid content and magnet powder are mixed high-speed stirred with the ratio of weight ratio 100: 1.5, mixing speed 350 revs/min, 30 minutes time; 6. above-mentioned obtained mixed solution and zinc oxide, coagulating agent are foamed to join foaming machine together with the ratio of weight ratio 100: 2.5: 1.5, need to add appropriate air according to expansion density, make C material; 7. expected by the A of identical weight, B material adds mould together with C material, A material is placed in a left side, and B material is placed in the middle, and C material is placed in the right side; 8. mould is put in steam box and carries out heat steaming, and A material, B material and C material cook rear die sinking and take out latex pillow goods.