CN104867403B - The preparation process of Magnetic guidance development anti-counterfeiting mark and anti-counterfeiting mark obtained - Google Patents
The preparation process of Magnetic guidance development anti-counterfeiting mark and anti-counterfeiting mark obtained Download PDFInfo
- Publication number
- CN104867403B CN104867403B CN201510350942.7A CN201510350942A CN104867403B CN 104867403 B CN104867403 B CN 104867403B CN 201510350942 A CN201510350942 A CN 201510350942A CN 104867403 B CN104867403 B CN 104867403B
- Authority
- CN
- China
- Prior art keywords
- magnetic guidance
- counterfeiting mark
- preparation process
- guidance development
- development
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to field of anti-counterfeit technology, and in particular to a kind of preparation process of Magnetic guidance development anti-counterfeiting mark and anti-counterfeiting mark obtained.The preparation process of Magnetic guidance development anti-counterfeiting mark of the present invention, is to mix paramagnetism ferroferric oxide powder with polyurethane light-cured resin, ethylene glycol is added, and using ultraviolet light initiation reaction, Magnetic guidance development nano material coating fluid is made;Coating fluid is coated in substrate using anilox roll, Magnetic guidance development coating is obtained after dry solidification;Gloss oil is coated on coating, carries out ultraviolet light solidification;Using adhesive coating, dry, overlay film, Magnetic guidance development anti-counterfeiting mark is made.The present invention solves the application problem of Magnetic guidance development nano material product, breach the Magnetic guidance development industrialized bottleneck of nano material, the magnetic induction nano material of paramagnetic is used in anti-fake material or anti-counterfeiting mark, is easy to discern the false from the genuine, realizes unique antifalse effect.Anti-counterfeiting mark Magnetic guidance development coating adhesion of the present invention is strong, stability is good.
Description
Technical field
The present invention relates to field of anti-counterfeit technology, and in particular to a kind of preparation process of Magnetic guidance development anti-counterfeiting mark and is made
Anti-counterfeiting mark.
Background technique
Anti-counterfeiting technology is to identify a kind of technology of authenticity of products, but the means that criminal fakes also are continuously improved, perhaps
More counterfeit protection measures have gradually lost its uniqueness, anti-fake therefore, it is difficult to achieve the purpose that, the release of new anti-counterfeiting technology, which becomes, to disappear
Take the urgent need in market.
There is universal concern for magnetic anti-counterfeit material both at home and abroad, Magnetic guidance developing material is a kind of novel nanometer
Material, belongs to the scope of photonic crystal, and such material has already passed through scientific research exploration, realizes such material package in laboratory
With in material, the Magnetic guidance developing material of paramagnetic is solidified on the rougher substrate in surface by photocuring.In recent years
There are many scientific research institutions successfully to have developed nano magnetic Induced Photon crystalline material, but because of the office of applications to nanostructures popularization
Sex-limited, such material is difficult to realize industrialize.
Up to now, there are no such applications in anti-counterfeiting mark.The application of Magnetic guidance developing material is primarily limited to
Two aspects, are on the one hand the selections for identifying substrate, still further aspect be Magnetic guidance developing material adhesive force on base material with
And stability.Adhesive force is small to cause such material to be difficult to film-forming on the substrate, and stability is bad to lead to Magnetic guidance effect
Unstable, the two predicaments are that such material is applied to anti-fake industry head technical problems to be solved.
Summary of the invention
That the object of the present invention is to provide a kind of adhesive force is strong, stability is good, the Magnetic guidance development with Magnetic guidance effect is anti-
Puppet mark, present invention simultaneously provides its preparation processes.
The preparation process of Magnetic guidance development anti-counterfeiting mark of the present invention, comprising the following steps:
(1) paramagnetism ferroferric oxide powder is mixed with polyurethane light-cured resin, ethylene glycol is added, using ultraviolet light
Initiation reaction is irradiated, Magnetic guidance development nano material coating fluid is made;
(2) gravure coating method is utilized, Magnetic guidance development nano material coating fluid is coated in substrate using anilox roll,
Magnetic guidance development coating is obtained after dry solidification;
(3) on the Magnetic guidance development coating that step (2) obtains, gloss oil is coated, it is aobvious to Magnetic guidance by ultraviolet light solidification
Shadow coating is packaged covering;
(4) it by the Magnetic guidance development coating after encapsulation covering, is first coated using adhesive, then be dried, finally
Surface coating is carried out, Magnetic guidance development anti-counterfeiting mark is made.
Wherein, preferred technical solution is as follows:
In step (1), the mass ratio of paramagnetism ferroferric oxide powder and polyurethane light-cured resin is 1:20~25, second
Glycol volume and polyurethane light-cured resin mass ratio are 3~4:1, and ethylene glycol is in terms of L, and polyurethane light-cured resin is with Kg
Meter.The preferred UV3000-B of polyurethane light-cured resin reacts 45~50min under 254nm ultraviolet light.
In step (2), drying temperature is 85~90 DEG C, and speed is 41~45m/min, and anilox roll is 200 or 220 mesh, base
Bottom is paper or PET film.
Adhesive force is high after Magnetic guidance of the present invention development nano material coating fluid film forming, with taking off after No. 6 tape-strippings of 3M standard
It plays coating cloth to fall off, and hardness is suitable for, and successfully solves the problems, such as that Magnetic guidance developing material adhesive force in substrate is low.
In step (3), gloss oil is sub- beauty UV-1100 or UV-1200, and gloss oil is coated by way of silk-screen, silk screen
For 200 or 250 mesh, speed is 30~35m/min.
In step (4) adhesive be CF-206 solvent type adhesive, speed be 45~50m/min, drying temperature be 100~
110 DEG C, overlay film uses the BOPET film of 12~20 μ m thicks.Overlay film plays a protective role to anti-counterfeiting mark, both prevents in air
Impurity etc. it is polluted, prevent surface abrasion, keep Magnetic guidance material more stable, also make it more beautiful.
The present invention can also be compound by the substrate of Magnetic guidance development anti-counterfeiting mark and release paper, then is die cut, and is made single
A anti-counterfeiting mark.It is preferred that using hot-fusible pressure-sensitive adhesive that the substrate of Magnetic guidance development anti-counterfeiting mark and release paper is compound.Coating heat
The speed of molten pressure sensitive adhesive is 50~55m/min, and hot-fusible pressure-sensitive adhesive glue amount is controlled in 16~18g/m2。
Beneficial effects of the present invention are as follows:
The present invention solves the application problem of Magnetic guidance development nano material product, breaches Magnetic guidance development nano material
The magnetic induction nano material of paramagnetic is used in anti-fake material or anti-counterfeiting mark, is easy to discern the false from the genuine by industrialized bottleneck, realizes
Unique antifalse effect.Anti-counterfeiting mark Magnetic guidance development coating adhesion of the present invention is strong, stability is good.
Under normal condition, anti-counterfeiting mark of the present invention contains stealthy information, no visual information.By being placed around in mark
The methods of magnet generates externally-applied magnetic field, and the information for inducing it stealthy is as it can be seen that simple, intuitive, can not copy, anti-counterfeiting power is strong.
Specific embodiment
The present invention is described further with reference to embodiments.
Embodiment 1
The described Magnetic guidance development anti-counterfeiting mark the preparation method is as follows:
(1) paramagnetic ferroferric oxide powder 50g is weighed, 1kg polyurethane light-cured resin UV3000-B and powder are weighed
End mixing, stirs evenly, and the ethylene glycol of 3.2L is then added into blender, is configured to stable solution, the case where stirring
It is lower to solidify 50min with 254nm ultraviolet light, Magnetic guidance development nano material coating fluid is made, as standby raw material.
(2) it is coated with the special edition gravure roll of commodity logo, selects 200 mesh anilox rolls, speed is controlled in 40m/
Min, by the emulsion coating of gained Magnetic guidance developing material in 30 μm of BOPET film, temperature control is at 85 DEG C, dry solidification
Film forming obtains Magnetic guidance development coating.
(3) sub- beauty UV-1200 gloss oil is selected, surface glazing process is carried out by way of silk-screen, silk screen is 250 mesh, vehicle
Speed control is in 35m/min.
(4) selection CF-206 solvent type adhesive carries out overlay film, and speed is controlled in 45m/min, oven drying temperature 105
DEG C, surface coating is carried out with the BOPET film of 12 μ m thicks.
(5) compound with the bottom surface of substrate after being coated with EVA hot-fusible pressure-sensitive adhesive in release paper, speed is controlled in 50m/min,
Glue amount is controlled in 17g/m2。
(6) automatic die cutting is carried out at volume identification to after gluing, obtains single anti-counterfeiting mark.
Embodiment 2
(1) weigh paramagnetic ferroferric oxide powder 45g, weigh 1.1kg polyurethane light-cured resin UV3000-B with
Powder mixing, stirs evenly, and the ethylene glycol of 3.5L is then added into blender, stable solution is configured to, in the feelings of stirring
Solidify 50min with 254nm ultraviolet light under condition, Magnetic guidance development nano material coating fluid is made, as standby raw material.
(2) it is coated with the special edition gravure roll of commodity logo, selects 200 mesh anilox rolls, speed is controlled in 45m/
Min, by the emulsion coating of gained Magnetic guidance developing material on two-sided art paper, at 90 DEG C, dry solidification forms a film for temperature control,
Obtain Magnetic guidance development coating.
(3) sub- beauty UV-1100 gloss oil is selected, surface glazing process is carried out by way of silk-screen, silk screen is 250 mesh, vehicle
Speed control is in 30m/min.
(4) selection CF-206 solvent type adhesive carries out overlay film, and speed is controlled in 50m/min, oven drying temperature 100
DEG C, surface coating is carried out with the BOPET film of 12 μ m thicks.
(5) compound with the bottom surface of substrate after being coated with EVA hot-fusible pressure-sensitive adhesive in release paper, speed is controlled in 55m/min,
Glue amount is controlled in 16g/m2。
(6) automatic die cutting is carried out at volume identification to after gluing, obtains single anti-counterfeiting mark.
Embodiment 3
(1) weigh paramagnetic ferroferric oxide powder 48g, weigh 1.1kg polyurethane light-cured resin UV3000-B with
Powder mixing, stirs evenly, and the ethylene glycol of 3.7L is then added into blender, stable solution is configured to, in the feelings of stirring
Solidify 48min with 254nm ultraviolet light under condition, Magnetic guidance development nano material coating fluid is made, as standby raw material.
(2) it is coated with the special edition gravure roll of commodity logo, selects 220 mesh anilox rolls, speed is controlled in 43m/
Min, by the emulsion coating of gained Magnetic guidance developing material on two-sided art paper, at 90 DEG C, dry solidification forms a film for temperature control,
Obtain Magnetic guidance development coating.
(3) sub- beauty UV-1100 gloss oil is selected, surface glazing process is carried out by way of silk-screen, silk screen is 250 mesh, vehicle
Speed control is in 33m/min.
(4) selection CF-206 solvent type adhesive carries out overlay film, and speed is controlled in 50m/min, oven drying temperature 110
DEG C, surface coating is carried out with the BOPET film of 20 μ m thicks.
(5) compound with the bottom surface of substrate after being coated with EVA hot-fusible pressure-sensitive adhesive in release paper, speed is controlled in 50m/min,
Glue amount is controlled in 18g/m2。
(6) automatic die cutting is carried out at volume identification to after gluing, obtains single anti-counterfeiting mark.
Embodiment 4
(1) weigh paramagnetic ferroferric oxide powder 50g, weigh 1.2kg polyurethane light-cured resin UV3000-B with
Powder mixing, stirs evenly, and the ethylene glycol of 4.0L is then added into blender, stable solution is configured to, in the feelings of stirring
Solidify 47min with 254nm ultraviolet light under condition, Magnetic guidance development nano material coating fluid is made, as standby raw material.
(2) it is coated with the special edition gravure roll of commodity logo, selects 200 mesh anilox rolls, speed is controlled in 41m/
Min, by the emulsion coating of gained Magnetic guidance developing material on two-sided art paper, at 88 DEG C, dry solidification forms a film for temperature control,
Obtain Magnetic guidance development coating.
(3) sub- beauty UV-1100 gloss oil is selected, surface glazing process is carried out by way of silk-screen, silk screen is 200 mesh, vehicle
Speed control is in 35m/min.
(4) selection CF-206 solvent type adhesive carries out overlay film, and speed is controlled in 50m/min, oven drying temperature 106
DEG C, surface coating is carried out with the BOPET film of 15 μ m thicks.
(5) compound with the bottom surface of substrate after being coated with EVA hot-fusible pressure-sensitive adhesive in release paper, speed is controlled in 50m/min,
Glue amount is controlled in 17g/m2。
(6) automatic die cutting is carried out at volume identification to after gluing, obtains single anti-counterfeiting mark.
Claims (10)
1. a kind of preparation process of Magnetic guidance development anti-counterfeiting mark, it is characterised in that the following steps are included:
(1) paramagnetism ferroferric oxide powder is mixed with polyurethane light-cured resin, ethylene glycol is added, using ultraviolet light
Magnetic guidance development nano material coating fluid is made in initiation reaction;
(2) Magnetic guidance development nano material coating fluid is coated in substrate using anilox roll, Magnetic guidance is obtained after dry solidification
Develop coating;
(3) on the Magnetic guidance development coating that step (2) obtains, gloss oil is coated, is developed by ultraviolet light solidification to Magnetic guidance and is applied
Layer is packaged covering;
(4) it by the Magnetic guidance development coating after encapsulation covering, is first coated using adhesive, then be dried, is finally carried out
Magnetic guidance development anti-counterfeiting mark is made in surface coating;
Substrate described in step (2) is paper or PET film.
2. the preparation process of Magnetic guidance development anti-counterfeiting mark according to claim 1, it is characterised in that: suitable in step (1)
The mass ratio of magnetic ferroferric oxide powder and polyurethane light-cured resin is 1:20~25, and ethylene glycol volume and polyurethane light are solid
Changing the ratio between resin quality is 3~4:1, and ethylene glycol is in terms of L, and polyurethane light-cured resin is in terms of Kg.
3. the preparation process of Magnetic guidance development anti-counterfeiting mark according to claim 1, it is characterised in that: in step (1), gather
Urethane light-cured resin is UV3000-B, under 254nm ultraviolet light, reacts 45~50min.
4. the preparation process of Magnetic guidance development anti-counterfeiting mark according to claim 1, it is characterised in that: in step (2), do
Dry temperature is 85~90 DEG C, and speed is 41~45m/min, and anilox roll is 200 or 220 mesh.
5. the preparation process of Magnetic guidance development anti-counterfeiting mark according to claim 1, it is characterised in that: in step (3), light
Oil is UV-1100 or UV-1200, and gloss oil coated by way of silk-screen, and silk screen is 200 or 250 mesh, speed is 30~
35m/min。
6. the preparation process of Magnetic guidance development anti-counterfeiting mark according to claim 1, it is characterised in that: glue in step (4)
Glutinous agent is CF-206 solvent type adhesive, and speed is 45~50m/min, and drying temperature is 100~110 DEG C, overlay film using 12~
The BOPET film of 20 μ m thicks.
7. the preparation process of Magnetic guidance development anti-counterfeiting mark according to claim 1, it is characterised in that: Magnetic guidance develops
The substrate of anti-counterfeiting mark and release paper are compound, then carry out cross cutting and single anti-counterfeiting mark is made.
8. the preparation process of Magnetic guidance development anti-counterfeiting mark according to claim 7, it is characterised in that: use melt pressure sensitive
Glue is compound by the substrate of Magnetic guidance development anti-counterfeiting mark and release paper.
9. the preparation process of Magnetic guidance development anti-counterfeiting mark according to claim 8, it is characterised in that: coating melt pressure sensitive
The speed of glue is 50~55m/min, and hot-fusible pressure-sensitive adhesive glue amount is controlled in 16~18g/m2。
The anti-counterfeiting mark 10. a kind of Magnetic guidance develops, it is characterised in that: using any preparation process preparation of claim 1~9
It obtains.