CN104861423A - Self-repair macromolecular material - Google Patents
Self-repair macromolecular material Download PDFInfo
- Publication number
- CN104861423A CN104861423A CN201510288592.6A CN201510288592A CN104861423A CN 104861423 A CN104861423 A CN 104861423A CN 201510288592 A CN201510288592 A CN 201510288592A CN 104861423 A CN104861423 A CN 104861423A
- Authority
- CN
- China
- Prior art keywords
- capsule
- macromolecular material
- repair
- parts
- epoxy resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a self-repair macromolecular material. The self-repair macromolecular material comprises a modified epoxy resin, a repair capsule and a catalysis capsule, wherein the repair capsule and the catalysis capsule are mixed in the epoxy resin, the repair capsule and the catalysis capsule comprise capsule walls which consist of the following ingredients of 100-120 parts of epoxy resin-tetrahydrophthalic acid diglycidyl ester and 60-100 parts of an epoxy acrylic resin. The self-repair macromolecular material disclosed by the invention has the advantages that damage in the macromolecular material can be discovered as soon as possible, and the damage can be repaired as soon as possible; the solidifying degree and the destruction degree of the capsule walls are moderate, and the repair rate is as high as 90%.
Description
Technical field
The present invention relates to a kind of biomimetic material technology field, particularly relate to a kind of selfreparing macromolecular material.
Background technology
Macromolecular material inevitably produces local damage and tiny crack in its forming process and use procedure, and then cause macroscopic fracture and destroy, affect normal use and the reduction of service life of related products, and often these micro-damages are being difficult to find at first, even if or be found also because the restrictions such as shape of product cannot be repaired in time.Therefore, if macromolecular material self-repair function can be given, can solve the problem, significantly improve the security of product, extend its work-ing life.
Summary of the invention
Goal of the invention: the present invention is in order to repair the micro-damage problem of macromolecular material inside.
Technical scheme: the invention provides a kind of selfreparing macromolecular material, the repairing capsule comprising modified epoxy and be mixed in described epoxy resin and catalysis capsule, described repairing capsule and described catalysis capsule comprise capsule wall, described capsule wall consists of the following composition, 100-120 part epoxy resin-tetrahydrophthalic acid glycidyl ester, 60-100 part Epocryl.
Preferably, described repairing capsule inside comprises renovation agent, and described repair machine agent comprises: 60-80 part epoxy resin, 30-40 part polythiol-tetramethylolmethane four mercaptopropionic acid ester, 20-35 part sulfonated polyether-ether-ketone, 12-19 part PAH, 5-8 part water, 30-45 part perfluoro capryl Trimethoxy silane.
Preferably, be provided with catalyzer in described catalysis capsule, described catalyzer is benzyldimethylamine.
Preferably, described catalyzer can also be imidazoles renovation agent and dibrominated cylinder mixture the former have particulate state, profile is irregular and can produce focal point of stress, ensures to repair temperature at 120-140, has played renovation agent high temperature fixed line advantage.
Beneficial effect: compared with prior art, its advantage is to find the infringement in macromolecular material early, repairs infringement early in the present invention, capsule wall state of cure of the present invention and damaged degree moderate, repair rate is up to 90%.
Embodiment
Below in conjunction with embodiment, illustrate the present invention further.
Embodiment 1
Technical scheme: the invention provides a kind of selfreparing macromolecular material, comprise modified epoxy as the base-material of this macromolecular material be mixed in repairing capsule in described epoxy resin and catalysis capsule, described repairing capsule and described catalysis capsule comprise capsule wall, described capsule wall consists of the following composition, 100 parts of epoxy resin-tetrahydrophthalic acid glycidyl esters, 60 parts with Epocryl, 50 parts of emulsifying agents, use this capsule wall, along with the increase of emulsifying agent, emulsive rate also increases, capsule grain diameter is caused to reduce, be conducive to reducing the particle diameter of capsule, find in test, use equal other materials, use 50 parts of emulsifying agents, capsule grain diameter 80 μm, use 55 parts of emulsifying agents, capsule grain diameter 70 μm, use 60 parts of emulsifying agents, capsule grain diameter 55 μm, capsule is little, distribution then in macromolecular material, density is large, repairing effect is good.
Described repairing capsule inside comprises renovation agent, and described repair machine agent comprises: 80 parts of epoxy resin, 30 parts of polythiol-tetramethylolmethane four mercaptopropionic acid esters, 35 parts of sulfonated polyether-ether-ketones, 19 parts of PAH, 8 parts of water, 45 parts of perfluoro capryl Trimethoxy silanes.
Embodiment 2
The invention provides a kind of selfreparing macromolecular material, the repairing capsule comprising modified epoxy and be mixed in described epoxy resin and catalysis capsule, described repairing capsule and described catalysis capsule comprise capsule wall, described capsule wall consists of the following composition, 120 parts of epoxy resin-tetrahydrophthalic acid glycidyl esters, 100 parts with Epocryl, 60 parts of emulsifying agents, shell-broken effect is good.
Simultaneously the thickness of capsule wall and hardness also determine the effect of reparation, if capsule is too fragile, causes macromolecular material not damaged, and break, too hard, cause repairing in time,
Preferably, described repairing capsule inside comprises renovation agent, described repair machine agent comprises: 60 parts of epoxy resin, 30 parts of polythiol-tetramethylolmethane four mercaptopropionic acid esters, 20 parts of sulfonated polyether-ether-ketones, 12 parts of PAH, 5 parts of water, 30 parts of perfluoro capryl Trimethoxy silanes, 12 parts of PAH, 5 parts of water, 30 parts of perfluoro capryl Trimethoxy silanes, when 30 parts of perfluoro capryl Trimethoxy silanes, after 12 parts of PAH, 5 parts of water, 30 parts of perfluoro capryl Trimethoxy silane mixing, produce one deck super-hydrophobic layer, improve repair rate.
Preferably, be provided with catalyzer in described catalysis capsule, described catalyzer is benzyldimethylamine, and when two capsule walls are all damaged, catalyzer promotes to repair.
Preferably, described catalyzer can also be imidazoles renovation agent and dibrominated copper mixture the former have particulate state, profile is irregular and can produce focal point of stress, ensures to repair temperature at 120-140, has played the advantage of renovation agent hot setting.
Embodiment 3
Described repairing capsule inside comprises renovation agent, and described repair machine agent comprises: 70 parts of epoxy resin, 35 parts of polythiol-tetramethylolmethane four mercaptopropionic acid esters, 25 parts of sulfonated polyether-ether-ketones, 17 parts of PAH, 6 parts of water, 33 parts of perfluoro capryl Trimethoxy silanes.
The reparation situation of different renovation agent component in embodiment 1/2/3:
Embodiment 1 | Embodiment 2 | Embodiment 3 | |
Repair rate | 75% | 83% | 90% |
Claims (4)
1. a selfreparing macromolecular material, it is characterized in that, the repairing capsule comprising modified epoxy and be mixed in described epoxy resin and catalysis capsule, described repairing capsule and described catalysis capsule comprise capsule wall, described capsule wall consists of the following composition, and 100-120 part epoxy resin-tetrahydrophthalic acid glycidyl ester, 60-100 part are with Epocryl, 50-60 part emulsifying agent.
2. selfreparing macromolecular material according to claim 1, it is characterized in that, described repairing capsule inside comprises renovation agent, and described repair machine agent comprises: 60-80 part epoxy resin, 30-40 part polythiol-tetramethylolmethane four mercaptopropionic acid ester, 20-35 part sulfonated polyether-ether-ketone, 12-19 part PAH, 5-8 part water, 30-45 part perfluoro capryl Trimethoxy silane.
3. selfreparing macromolecular material according to claim 1, is characterized in that, is provided with catalyzer in described catalysis capsule, and described catalyzer is benzyldimethylamine.
4. selfreparing macromolecular material according to claim 3, is characterized in that, described catalyzer can also be imidazoles renovation agent and dibrominated copper mixture.