CN104851475B - 一种电线用绝缘材料 - Google Patents

一种电线用绝缘材料 Download PDF

Info

Publication number
CN104851475B
CN104851475B CN201510222093.7A CN201510222093A CN104851475B CN 104851475 B CN104851475 B CN 104851475B CN 201510222093 A CN201510222093 A CN 201510222093A CN 104851475 B CN104851475 B CN 104851475B
Authority
CN
China
Prior art keywords
parts
adhesive
insulating materials
electric wire
polyacrylate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201510222093.7A
Other languages
English (en)
Other versions
CN104851475A (zh
Inventor
董桂香
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong far view Electrical Equipment Co., Ltd.
Original Assignee
HAIAN COUNTY TIANXING ELECTRICAL MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HAIAN COUNTY TIANXING ELECTRICAL MATERIALS Co Ltd filed Critical HAIAN COUNTY TIANXING ELECTRICAL MATERIALS Co Ltd
Priority to CN201510222093.7A priority Critical patent/CN104851475B/zh
Publication of CN104851475A publication Critical patent/CN104851475A/zh
Application granted granted Critical
Publication of CN104851475B publication Critical patent/CN104851475B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种电线用绝缘材料。绝缘材料由以下重量份数的成分制成：纳米陶瓷30‑40份、二氧化钼2‑8份、聚氨酯12‑18份、碳化硅15‑22份、硅酸钠1.5‑3.2份、橡胶1‑3份、二甲苯酚10‑14份、硫磺1.2‑1.8份、乙二酸聚酯10‑15份、环己烷二甲酸二缩水甘油酯10‑15份、沥青2‑6份和粘合剂2‑6份。本发明的电线用绝缘材料以纳米陶瓷为主要原料，其余各原料共同作用，使得本发明的绝缘材料具有良好的绝缘性能，且强度高，防潮性能好，适合作为电线使用；粘合剂为环氧树脂、丙烯酸、聚丙烯酸酯和硅烷偶联剂的混合物，通过高温混合，具有良好的粘合性。

Description

一种电线用绝缘材料
技术领域：
本发明涉及一种电线用绝缘材料，属于电气工程技术领域。
背景技术：
按国家标准GB2900.5规定绝缘材料的定义是：“用来使器件在电气上绝缘的材料”。也就是能够阻止电流通过的材料。它的电阻率很高，通常在10^9～10^22Ω·m的范围内。如在电机中，导体周围的绝缘材料将匝间隔离并与接地的定子铁芯隔离开来，以保证电机的安全运行。
目前电力产业处于高速发展时期，电器产品已经普及到各个行业。电器产品的绝缘要求是非常高的，虽然市场上现有表面绝缘材料品种很多，性能比较单一，其用途针对性很强，还不能做到防潮、防腐、耐高温、绝缘的要求，绝缘材料的绝缘等级不够，限制着电器、电机行业的发展。
发明内容：
本发明目的是，用来弥补现有技术的不足，而提供一种电线用绝缘材料。
为了实现上述目的，本发明的技术方案如下：
一种电线用绝缘材料，由以下重量份数的成分制成：纳米陶瓷30-40份、二氧化钼2-8份、聚氨酯12-18份、碳化硅15-22份、硅酸钠1.5-3.2份、橡胶1-3份、二甲苯酚10-14份、硫磺1.2-1.8份、乙二酸聚酯10-15份、环己烷二甲酸二缩水甘油酯10-15份、沥青2-6份和粘合剂2-6份。
所述的一种电线用绝缘材料，所述粘合剂为环氧树脂、丙烯酸、聚丙烯酸酯和硅烷偶联剂的混合物。
所述的一种电线用绝缘材料，所述粘合剂各组分的重量份数分别为环氧树脂10-15份、丙烯酸2-6份、聚丙烯酸酯4-8份和硅烷偶联剂1-4份。
所述的一种电线用绝缘材料，所述粘合剂是通过以下步骤获得的：将环氧树脂与聚丙烯酸酯在搅拌条件下加入丙烯酸中，缓慢升温至30-40℃，加入硅烷偶联剂后升温至50-60℃，保持3-4min，即可得粘合剂。
所述的一种电线用绝缘材料，乙二酸聚酯与环己烷二甲酸二缩水甘油酯的重量比为1:1。
本发明的有益效果如下：
本发明的电线用绝缘材料以纳米陶瓷为主要原料，其余各原料共同作用，使得本发明的绝缘材料具有良好的绝缘性能，且强度高，防潮性能好，适合作为电线使用；粘合剂为环氧树脂、丙烯酸、聚丙烯酸酯和硅烷偶联剂的混合物，通过高温混合，具有良好的粘合性。
经检测，本发明的绝缘材料浸水后绝缘电阻为4.3-4.8×107Ω，弯曲强度为120-125MPa，压缩强度为138-142MPa，平行层向击穿电压为45-50KV。
具体实施方式：
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施例，进一步阐述本发明。
实施例1
本实施例中，一种电线用绝缘材料，由以下重量份数的成分制成：纳米陶瓷40份、二氧化钼2份、聚氨酯18份、碳化硅15份、硅酸钠3.2份、橡胶1份、二甲苯酚14份、硫磺1.2份、乙二酸聚酯15份、环己烷二甲酸二缩水甘油酯15份、沥青2份和粘合剂2份。
其中，所述粘合剂各组分的重量份数分别为环氧树脂15份、丙烯酸2份、聚丙烯酸酯8份和硅烷偶联剂4份；所述粘合剂是通过以下步骤获得的：将环氧树脂与聚丙烯酸酯在搅拌条件下加入丙烯酸中，缓慢升温至30-40℃，加入硅烷偶联剂后升温至50-60℃，保持3-4min，即可得粘合剂。
实施例2
本实施例中，一种电线用绝缘材料，由以下重量份数的成分制成：纳米陶瓷30份、二氧化钼8份、聚氨酯12份、碳化硅22份、硅酸钠1.5份、橡胶3份、二甲苯酚10份、硫磺1.8份、乙二酸聚酯10份、环己烷二甲酸二缩水甘油酯10份、沥青6份和粘合剂6份。
其中，所述粘合剂各组分的重量份数分别为环氧树脂10份、丙烯酸6份、聚丙烯酸酯4份和硅烷偶联剂1份；所述粘合剂是通过以下步骤获得的：将环氧树脂与聚丙烯酸酯在搅拌条件下加入丙烯酸中，缓慢升温至30-40℃，加入硅烷偶联剂后升温至50-60℃，保持3-4min，即可得粘合剂。
实施例3
本实施例中，一种电线用绝缘材料，由以下重量份数的成分制成：纳米陶瓷32份、二氧化钼6份、聚氨酯15份、碳化硅20份、硅酸钠2.5份、橡胶2份、二甲苯酚12份、硫磺1.5份、乙二酸聚酯12份、环己烷二甲酸二缩水甘油酯12份、沥青3份和粘合剂3份。
其中，所述粘合剂各组分的重量份数分别为环氧树脂11份、丙烯酸3份、聚丙烯酸酯7份和硅烷偶联剂3份；所述粘合剂是通过以下步骤获得的：将环氧树脂与聚丙烯酸酯在搅拌条件下加入丙烯酸中，缓慢升温至30-40℃，加入硅烷偶联剂后升温至50-60℃，保持3-4min，即可得粘合剂。
实施例4
本实施例中，一种电线用绝缘材料，由以下重量份数的成分制成：纳米陶瓷38份、二氧化钼4份、聚氨酯14份、碳化硅17份、硅酸钠1.8份、橡胶1份、二甲苯酚13份、硫磺1.6份、乙二酸聚酯14份、环己烷二甲酸二缩水甘油酯11份、沥青4份和粘合剂4份。
其中，所述粘合剂各组分的重量份数分别为环氧树脂14份、丙烯酸5份、聚丙烯酸酯6份和硅烷偶联剂2份；所述粘合剂是通过以下步骤获得的：将环氧树脂与聚丙烯酸酯在搅拌条件下加入丙烯酸中，缓慢升温至30-40℃，加入硅烷偶联剂后升温至50-60℃，保持3-4min，即可得粘合剂。
实施例5
本实施例中，一种电线用绝缘材料，由以下重量份数的成分制成：纳米陶瓷35份、二氧化钼5份、聚氨酯16份、碳化硅18份、硅酸钠2.8份、橡胶3份、二甲苯酚11份、硫磺1.4份、乙二酸聚酯13份、环己烷二甲酸二缩水甘油酯13份、沥青5份和粘合剂5份。
其中，所述粘合剂各组分的重量份数分别为环氧树脂12份、丙烯酸4份、聚丙烯酸酯5份和硅烷偶联剂2份；所述粘合剂是通过以下步骤获得的：将环氧树脂与聚丙烯酸酯在搅拌条件下加入丙烯酸中，缓慢升温至30-40℃，加入硅烷偶联剂后升温至50-60℃，保持3-4min，即可得粘合剂。

Claims (5)

1.一种电线用绝缘材料，其特征在于，由以下重量份数的成分制成：纳米陶瓷30-40份、二氧化钼2-8份、聚氨酯12-18份、碳化硅15-22份、硅酸钠1.5-3.2份、橡胶1-3份、二甲苯酚10-14份、硫磺1.2-1.8份、乙二酸聚酯10-15份、环己烷二甲酸二缩水甘油酯10-15份、沥青2-6份和粘合剂2-6份。
2.根据权利要求1所述的一种电线用绝缘材料，其特征在于，所述粘合剂为环氧树脂、丙烯酸、聚丙烯酸酯和硅烷偶联剂的混合物。
3.根据权利要求2所述的一种电线用绝缘材料，其特征在于，所述粘合剂各组分的重量份数分别为环氧树脂10-15份、丙烯酸2-6份、聚丙烯酸酯4-8份和硅烷偶联剂1-4份。
4.根据权利要求2或3所述的一种电线用绝缘材料，其特征在于，所述粘合剂是通过以下步骤获得的：将环氧树脂与聚丙烯酸酯在搅拌条件下加入丙烯酸中，缓慢升温至30-40℃，加入硅烷偶联剂后升温至50-60℃，保持3-4min，即可得粘合剂。
5.根据权利要求1所述的一种电线用绝缘材料，其特征在于，乙二酸聚酯与环己烷二甲酸二缩水甘油酯的重量比为1:1。
CN201510222093.7A 2015-05-05 2015-05-05 一种电线用绝缘材料 Active CN104851475B (zh)