CN104846266A - Preparation method of wear-resistant bucket teeth for loader - Google Patents
Preparation method of wear-resistant bucket teeth for loader Download PDFInfo
- Publication number
- CN104846266A CN104846266A CN201510222920.2A CN201510222920A CN104846266A CN 104846266 A CN104846266 A CN 104846266A CN 201510222920 A CN201510222920 A CN 201510222920A CN 104846266 A CN104846266 A CN 104846266A
- Authority
- CN
- China
- Prior art keywords
- wear
- resistant bucket
- preparation
- bucket tooth
- loader
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of wear-resistant bucket teeth for a loader. Raw materials including, in weight percent, 2.2-2.5% of C, 8.5-11% of V, 5-6.5% of Cr, 2-3% of Ni, 0.8-1.1% of Mn, 0.5-1% of W, 0.6-0.8% of Si, less than or equal to 0.03% of impurities P, less than or equal to 0.02% of impurities S and the balance Fe are smelted and cast to obtain the wear-resistant bucket teeth. The wear-resistant bucket teeth prepared by the method have fine hardness and toughness and excellent wear resistance.
Description
Technical field
The present invention relates to a kind of preparation method of shovel loader wear-resistant bucket tooth.
Background technology
Shovel loader is one of engineering machinery main in earthwork, and bucket tooth is one of frayed more serious part on shovel loader, in use not only to be subject to the strong wear of the abrasive particles such as sandstone, but also the intense impact of large stone will be subject to, therefore, when select materials, need hardness and the toughness of considering material, to reduce wearing and tearing and the fracture of material.
Summary of the invention
The technical problem to be solved in the present invention overcomes existing defect, provides a kind of shovel loader wear-resistant bucket tooth.
In order to solve the problems of the technologies described above, the invention provides following technical scheme:
A kind of preparation method of shovel loader wear-resistant bucket tooth, the raw material of consumption obtains described wear-resistant bucket tooth through melting, casting as following weight percent: C 2.2 ~ 2.5%, V 8.5 ~ 11%, Cr 5 ~ 6.5%, Ni 2 ~ 3%, Mn 0.8 ~ 1.1%, W 0.5 ~ 1%, Si 0.6 ~ 0.8%, surplus is Fe, wherein, impurity P≤0.03%, impurity S≤0.02%.
Further, the weight percent consumption of described raw material is as follows: C 2.3 ~ 2.5%, V 8.5 ~ 11%, Cr 6 ~ 6.5%, Ni 2.5 ~ 3%, Mn 1 ~ 1.1%, W 0.8 ~ 1%, Si 0.7 ~ 0.8%, surplus is Fe, impurity P≤0.03%, impurity S≤0.02%.
Compared with the wear-resistant bucket tooth of existing loading shovel, wear-resistant bucket tooth prepared by the inventive method can significantly improve hardness and the toughness of material, alleviates the wearing and tearing of bucket tooth.
Embodiment
Below the preferred embodiments of the present invention are described, should be appreciated that preferred embodiment described herein is only for instruction and explanation of the present invention, is not intended to limit the present invention.
embodiment 1
Prepare burden as following weight percent: C 2.2%, V 9%, Cr 5%, Ni 2%, Mn 0.8%, W 0.5%, Si 0.6%, surplus are Fe, shove charge, melting, and cast molding obtains described wear-resistant bucket tooth.Phosphorus, sulphur are inevitable impurity, should control P≤0.03% in final finished, S≤0.02%.
The hardness of described wear-resistant bucket tooth is 60HRC, and impelling strength is 35J/cm
2.
embodiment 2
Prepare burden as following weight percent: C 2.3%, V 8.5%, Cr 6%, Ni 2.5%, Mn 1.1%, W 0.8%, Si 0.7%, surplus are Fe, shove charge, melting, and cast molding obtains described wear-resistant bucket tooth.Phosphorus, sulphur are inevitable impurity, should control P≤0.03% in final finished, S≤0.02%.
The hardness of described wear-resistant bucket tooth is 65HRC, and impelling strength is 42J/cm
2.
embodiment 3
Prepare burden as following weight percent: C 2.5%, V 11%, Cr 6.5%, Ni 3%, Mn 1%, W 1%, Si 0.8%, surplus are Fe, shove charge, melting, and cast molding obtains described wear-resistant bucket tooth.Phosphorus, sulphur are inevitable impurity, should control P≤0.03% in final finished, S≤0.02%.
The hardness of described wear-resistant bucket tooth is 70HRC, and impelling strength is 51J/cm
2.
Last it is noted that the foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, although with reference to previous embodiment to invention has been detailed description, for a person skilled in the art, it still can be modified to the technical scheme described in foregoing embodiments, or carries out equivalent replacement to wherein portion of techniques feature.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (2)
1. the preparation method of a shovel loader wear-resistant bucket tooth, the raw material of consumption obtains described wear-resistant bucket tooth through melting, casting as following weight percent: C 2.2 ~ 2.5%, V 8.5 ~ 11%, Cr 5 ~ 6.5%, Ni 2 ~ 3%, Mn 0.8 ~ 1.1%, W 0.5 ~ 1%, Si 0.6 ~ 0.8%, surplus is Fe, wherein, impurity P≤0.03%, impurity S≤0.02%.
2. preparation method according to claim 1, it is characterized in that: the weight percent consumption of described raw material is as follows: C 2.3 ~ 2.5%, V 8.5 ~ 11%, Cr 6 ~ 6.5%, Ni 2.5 ~ 3%, Mn 1 ~ 1.1%, W 0.8 ~ 1%, Si 0.7 ~ 0.8%, surplus is Fe, impurity P≤0.03%, impurity S≤0.02%.