CN104845508A - Powder coating - Google Patents
Powder coating Download PDFInfo
- Publication number
- CN104845508A CN104845508A CN201510277234.5A CN201510277234A CN104845508A CN 104845508 A CN104845508 A CN 104845508A CN 201510277234 A CN201510277234 A CN 201510277234A CN 104845508 A CN104845508 A CN 104845508A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder coating
- epoxy resin
- powder
- tetramethoxymethylglycoluril
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a powder coating, which is prepared from the following components in parts by weight: 9-12 parts of epoxy resin, 9-13 parts of resin, 3-7 parts of novolac epoxy resin, 1-4 parts of magnesium carbonate, 1-3 parts of vitrified calcium, 1-3 parts of tetramethoxy methyl glycoluril, 1-3 parts of precipitated barium sulphate, 2-5 parts of decabromodiphenyl ether, 1-4 parts of lanthanum oxide and 2-4 parts of nanometer carbon powder. According to the powder coating disclosed by the invention, kinds of liquid chemical harmful assistants such as a film-forming agent, a dispersing agent, a wetting agent, a flatting agent and antiseptic and anti-mildew agents added to reach the coating property are omitted; the powder coating has the characteristics of being harmless, high in efficiency and environment-friendly; and resources are saved.
Description
Technical field
The invention belongs to technical field of coatings, be specifically related to a kind of environmental protection, the good powder coating of vision suburb fruit.
Background technology
Current China upholstery adopts emulsion paint, wallpaper or wall paper to be main, and these materials respectively exist certain shortcoming, although as fine and close in emulsion paint smooth surface, its echo is large, and soundproof effect is bad, and water-absorbent is poor, causes indoor humidity large; Although wallpaper, wall paper its paste convenient, it uses a large amount of tackiness agent when producing and paste, and produces the gases such as formaldehyde, be detrimental to health and work-ing life short, bring certain trouble to the life of people.
Summary of the invention
for the above-mentioned problems in the prior art, object of the present invention provides a kind of environmental protection, the good powder coating of vision suburb fruit.Its technical scheme is as follows:
A kind of powder coating, be made up of the component of following parts by weight: epoxy resin 9-12 part, resin 9-13 part, novolac epoxy 3-7 part, magnesiumcarbonate 1-4 part, porcelain calcium 1-3 part, tetramethoxymethylglycoluril 1-3 part, process white 1-3 part, decabromodiphenyl oxide 2-5 part, lanthanum trioxide 1-4 part, nano-carbon powder 2-4 part.
Further, epoxy resin 9 parts, 13 parts, vibrin, novolac epoxy 5 parts, 2 parts, magnesiumcarbonate, porcelain calcium 1 part, tetramethoxymethylglycoluril 3 parts, process white 1 part, decabromodiphenyl oxide 2 parts, lanthanum trioxide 4 parts, nano-carbon powder 2 parts.
Further, epoxy resin 11 parts, 12 parts, vibrin, novolac epoxy 7 parts, 1 part, magnesiumcarbonate, porcelain calcium 3 parts, tetramethoxymethylglycoluril 1 part, process white 2 parts, decabromodiphenyl oxide 4 parts, lanthanum trioxide 3 parts, nano-carbon powder 4 parts.
Further, epoxy resin 12 parts, 9 parts, vibrin, novolac epoxy 3 parts, 4 parts, magnesiumcarbonate, porcelain calcium 2 parts, tetramethoxymethylglycoluril 2 parts, process white 3 parts, decabromodiphenyl oxide 5 parts, lanthanum trioxide 1 part, nano-carbon powder 2 parts.
Powder coating of the present invention eliminates the various liquid chemicals added for reaching coating property and is harmful to the auxiliary agent such as film forming, dispersion, wetting, levelling, anticorrosive mildewproof, has harmless, high-level efficiency, saving resource and environmental protection feature.
Embodiment
Below in conjunction with embodiment, the invention will be further described, but protection scope of the present invention is not limited in this:
Embodiment 1
Powder coating of the present invention, is made up of the component of following parts by weight: epoxy resin 9 parts, 13 parts, vibrin, novolac epoxy 5 parts, 2 parts, magnesiumcarbonate, porcelain calcium 1 part, tetramethoxymethylglycoluril 3 parts, process white 1 part, decabromodiphenyl oxide 2 parts, lanthanum trioxide 4 parts, nano-carbon powder 2 parts.
Its preparation method is as follows: by said ratio amount, above-mentioned each component is dropped into high speed compounding jar high-speed mixing 5 minutes, then carry out classification abrasive dust at pulverizing mill, then cross 160-180 mesh sieve, making particle diameter reach D50 is 35-40mm, obtains upholstery facing powder coating of the present invention.
Embodiment 2
Powder coating of the present invention, is made up of the component of following parts by weight: epoxy resin 11 parts, 12 parts, vibrin, novolac epoxy 7 parts, 1 part, magnesiumcarbonate, porcelain calcium 3 parts, tetramethoxymethylglycoluril 1 part, process white 2 parts, decabromodiphenyl oxide 4 parts, lanthanum trioxide 3 parts, nano-carbon powder 4 parts.
Its preparation method is as embodiment 1.
Embodiment 3
Powder coating of the present invention, is made up of the component of following parts by weight: epoxy resin 12 parts, 9 parts, vibrin, novolac epoxy 3 parts, 4 parts, magnesiumcarbonate, porcelain calcium 2 parts, tetramethoxymethylglycoluril 2 parts, process white 3 parts, decabromodiphenyl oxide part 5, lanthanum trioxide 1 part, nano-carbon powder 2 parts.
Its preparation method is as embodiment 1.
The powder coating of each embodiment above-mentioned is added 30 jin of water soakings 30 minutes according to 100 jin of coating, carries out stirring 10 minutes, can criticize and scrape or spray, then surface drying is after 1 hour, various pattern can be made.It is as follows that it obtains detected result through Performance Detection: its stereoscopic sense is strong, and water-tolerant, strong adhesion, shock-resistant, good fluidity, dry surface density reaches 780kg/m
3, its ultimate compression strength is 7.0MPa, and above-mentioned each Performance Detection is all by National Standard Method.
Above specific embodiments of the invention are described.It should be noted that, the present invention is not limited to above-mentioned particular implementation, and those skilled in the art can make various distortion or amendment within the scope of the claims, and this does not affect flesh and blood of the present invention.
Claims (4)
1. a powder coating, be made up of the component of following parts by weight: epoxy resin 9-12 part, resin 9-13 part, novolac epoxy 3-7 part, magnesiumcarbonate 1-4 part, porcelain calcium 1-3 part, tetramethoxymethylglycoluril 1-3 part, process white 1-3 part, decabromodiphenyl oxide 2-5 part, lanthanum trioxide 1-4 part, nano-carbon powder 2-4 part.
2. powder coating as claimed in claim 1, it is characterized in that: each component is as follows: epoxy resin 9 parts, 13 parts, vibrin, novolac epoxy 5 parts, 2 parts, magnesiumcarbonate, porcelain calcium 1 part, tetramethoxymethylglycoluril 3 parts, process white 1 part, decabromodiphenyl oxide 2 parts, lanthanum trioxide 4 parts, nano-carbon powder 2 parts.
3. powder coating as claimed in claim 1, it is characterized in that: each component is as follows: epoxy resin 11 parts, 12 parts, vibrin, novolac epoxy 7 parts, 1 part, magnesiumcarbonate, porcelain calcium 3 parts, tetramethoxymethylglycoluril 1 part, process white 2 parts, decabromodiphenyl oxide 4 parts, lanthanum trioxide 3 parts, nano-carbon powder 4 parts.
4. powder coating as claimed in claim 1, it is characterized in that: each component is as follows: epoxy resin 12 parts, 9 parts, vibrin, novolac epoxy 3 parts, 4 parts, magnesiumcarbonate, porcelain calcium 2 parts, tetramethoxymethylglycoluril 2 parts, process white 3 parts, decabromodiphenyl oxide 5 parts, lanthanum trioxide 1 part, nano-carbon powder 2 parts.