CN104845469A - Fireproof paint - Google Patents
Fireproof paint Download PDFInfo
- Publication number
- CN104845469A CN104845469A CN201510270036.6A CN201510270036A CN104845469A CN 104845469 A CN104845469 A CN 104845469A CN 201510270036 A CN201510270036 A CN 201510270036A CN 104845469 A CN104845469 A CN 104845469A
- Authority
- CN
- China
- Prior art keywords
- parts
- resistance
- dioxide
- boride
- urea
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to fireproof paint. The fireproof paint is characterized by consisting of the following components in parts by weight: 20 to 30 parts of acrylic emulsion, 15 to 25 parts of melamine, 20 to 30 parts of urea, 15 to 25 parts of pentaerythritol, 6 to 12 parts of boride, 6 to 12 parts of titanium dioxide, 8 to 12 parts of chlorinated paraffin, 6 to 10 parts of ammonium polyphosphate, 2 to 6 parts of zinc borate, 2 to 6 parts of silicon dioxide, 2 to 6 parts of expanded vermiculite, 2 to 6 parts of flatting agent, 2 to 6 parts of defoaming agent and 1 to 4 parts of thickening agent. The fireproof paint disclosed by the invention has the advantages of water resistance as high as 89h, good alkali resistance, high outrush resistance, high heat and humidity resistance, long burning-resistant time, low toxicity, burning resistance, good strength, loose foam layer, low heat conductivity, good fireproof and heat insulating effects and suitability for popularization and application.
Description
Technical field
The present invention relates to a kind of refractory paint.
Background technology
Particularly all need paint coating in indoor decorating field at material of construction, according to different user demands, the coating of various performance arises at the historic moment.Building Fire Protection is a key areas of science and technology of fire protection, and frie retardant coating is the important component part in fire-proof construction material.Frie retardant coating refers to that painting is contained in body surface, can prevent fire from occurring, and stops fire spreading to be propagated or isolation burning things which may cause a fire disaster, extends base material ignition time or increases heat-insulating property to postpone a class coating of structure deteriorate time.But existing fire-proof insulation coating cost of manufacture is high, and function singleness, does not possess environment protecting.
Summary of the invention
For problems of the prior art, the object of the present invention is to provide a kind of technical scheme of refractory paint.
Described a kind of refractory paint, is characterized in that being made up of the component of following weight part: ACRYLIC EMULSION 20-30, trimeric cyanamide 15-25, urea 20-30, tetramethylolmethane 15-25, boride 6-12, titanium dioxide 6-12, clorafin 8-12, ammonium polyphosphate 6-10, zinc borate 2-6, silicon-dioxide 2-6, expanded vermiculite 2-6, flow agent 2-6, defoamer 2-6, thickening material 1-4.
Described a kind of refractory paint, is characterized in that being made up of the component of following weight part: ACRYLIC EMULSION 24-26, trimeric cyanamide 18-22, urea 24-26, tetramethylolmethane 18-22, boride 8-10, titanium dioxide 8-10, clorafin 9-11, ammonium polyphosphate 7-9, zinc borate 3-5, silicon-dioxide 3-5, expanded vermiculite 3-5, flow agent 3-5, defoamer 3-5, thickening material 2-3.
Described a kind of refractory paint, is characterized in that being made up of the component of following weight part: ACRYLIC EMULSION 25, trimeric cyanamide 20, urea 25, tetramethylolmethane 20, boride 9, titanium dioxide 9, clorafin 10, ammonium polyphosphate 8, zinc borate 4, silicon-dioxide 4, expanded vermiculite 4, flow agent 4, defoamer 4, thickening material 2.5.
The present invention can be attached on organic synthesis material and steel plate effectively, sun-proof, waterproof, flameproof effect are good, is not easy decolouring, is particularly suitable for being coated in material of construction outside surface.
Embodiment
Embodiment 1
A kind of refractory paint, is made up of the component of following weight part: ACRYLIC EMULSION 20, trimeric cyanamide 25, urea 30, tetramethylolmethane 25, boride 12, titanium dioxide 12, clorafin 12, ammonium polyphosphate 10, zinc borate 6, silicon-dioxide 6, expanded vermiculite 6, flow agent 6, defoamer 6, thickening material 4, each component mix with water routinely ratio mix.
Embodiment 2
A kind of refractory paint, is made up of the component of following weight part: ACRYLIC EMULSION 30, trimeric cyanamide 15, urea 20, tetramethylolmethane 15, boride 6, titanium dioxide 6, clorafin 8, ammonium polyphosphate 6, zinc borate 2, silicon-dioxide 2, expanded vermiculite 2, flow agent 2, defoamer 2, thickening material 1, each component mix with water routinely ratio mix.
Embodiment 3
A kind of refractory paint, is made up of the component of following weight part: ACRYLIC EMULSION 24, trimeric cyanamide 22, urea 26, tetramethylolmethane 22, boride 10, titanium dioxide 10, clorafin 11, ammonium polyphosphate 9, zinc borate 5, silicon-dioxide 5, expanded vermiculite 5, flow agent 5, defoamer 5, thickening material 3, each component mix with water routinely ratio mix.
Embodiment 4
A kind of refractory paint, is made up of the component of following weight part: ACRYLIC EMULSION 26, trimeric cyanamide 18, urea 24, tetramethylolmethane 18, boride 8, titanium dioxide 8, clorafin 9, ammonium polyphosphate 7, zinc borate 3, silicon-dioxide 3, expanded vermiculite 3, flow agent 3, defoamer 3, thickening material 2, each component mix with water routinely ratio mix.
Embodiment 5
A kind of refractory paint, is made up of the component of following weight part: ACRYLIC EMULSION 25, trimeric cyanamide 20, urea 25, tetramethylolmethane 20, boride 9, titanium dioxide 9, clorafin 10, ammonium polyphosphate 8, zinc borate 4, silicon-dioxide 4, expanded vermiculite 4, flow agent 4, defoamer 4, thickening material 2.5, each component mix with water routinely ratio mix.
The performance test results of the refractory paint that above-described embodiment 1-5 obtains by the present invention is as following table:
Can obtain from upper table, frie retardant coating of the present invention, water tolerance is up to 89h, alkali resistance is good, and the resistance to property gone out, humidity resistance are strong, and resistance to combustion is of long duration, there is low, the resistance to burning of toxicity, intensity is good, foam layer quality loose, thermal conductivity is little and fire-proof and thermal-insulation is effective, be suitable for applying.
Claims (3)
1. a refractory paint, is characterized in that being made up of the component of following weight part: ACRYLIC EMULSION 20-30, trimeric cyanamide 15-25, urea 20-30, tetramethylolmethane 15-25, boride 6-12, titanium dioxide 6-12, clorafin 8-12, ammonium polyphosphate 6-10, zinc borate 2-6, silicon-dioxide 2-6, expanded vermiculite 2-6, flow agent 2-6, defoamer 2-6, thickening material 1-4.
2. a kind of refractory paint according to claim 1, is characterized in that being made up of the component of following weight part: ACRYLIC EMULSION 24-26, trimeric cyanamide 18-22, urea 24-26, tetramethylolmethane 18-22, boride 8-10, titanium dioxide 8-10, clorafin 9-11, ammonium polyphosphate 7-9, zinc borate 3-5, silicon-dioxide 3-5, expanded vermiculite 3-5, flow agent 3-5, defoamer 3-5, thickening material 2-3.
3. a kind of refractory paint according to claim 1, is characterized in that being made up of the component of following weight part: ACRYLIC EMULSION 25, trimeric cyanamide 20, urea 25, tetramethylolmethane 20, boride 9, titanium dioxide 9, clorafin 10, ammonium polyphosphate 8, zinc borate 4, silicon-dioxide 4, expanded vermiculite 4, flow agent 4, defoamer 4, thickening material 2.5.