CN104845436A - Environment-friendly type wear-resistant auxiliary agent used for printing ink - Google Patents
Environment-friendly type wear-resistant auxiliary agent used for printing ink Download PDFInfo
- Publication number
- CN104845436A CN104845436A CN201510185221.5A CN201510185221A CN104845436A CN 104845436 A CN104845436 A CN 104845436A CN 201510185221 A CN201510185221 A CN 201510185221A CN 104845436 A CN104845436 A CN 104845436A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- auxiliary agent
- friendly type
- printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an environment-friendly type wear-resistant auxiliary agent used for printing ink, which comprises the following components by weight part: 15-25 parts of extinction micro powder wax, 4-6 parts of linseed oil, 4-5 parts of nano titanium carbide, 8-12 parts of epoxy soybean oil, 2-4 parts of powdered carbon, 2-4 parts of tungsten carbide, 2-4 parts of diphenyl silanediol, 3-5 parts of calcining kaolin, 2-4 parts of amorphous silica, and 2-4 parts of potassium phosphotungstate. The components and preparation technology are simple, the raw materials are easily purchased, cost is low, auxiliary agent wear-resistance is increased, no petroleum mineral oil component is contained, soya-bean oil substitutes total petroleum solvent, the soya-bean oil has characteristics of easy degradation, low toxicity and low VOC, consumption of non-renewable resources during a printing process can be effectively reduced, and environment pollution is reduced.
Description
Technical field
The present invention relates to ink product technical field, be specifically related to a kind of printing-ink environment-friendly type antiwear assistant.
Background technology
Ink is the important materials for wrapping material printing, and it is by printing by pattern, literal table now on the substrate, and ink comprises main component and ancillary component, and they mix equably and form the gluey fluid of a kind of viscosity through repeat-rolling.Be made up of pigment, low-melting ink vehicle and auxiliary agent etc.For various printings such as books and periodicals, packing and decorating, building decorations.Along with social demand increases, ink kind and output is respective extension and growth also.
Along with the stable development in China's offset printing market, flexographic ink have also been obtained very fast development, and its quality level is substantially close or reach international most advanced level.According to incompletely statistics, the ratio occupied in China's ink market of flexographic ink rises to 50% ~ 60%, still occupies an leading position, and this ratio can not great changes have taken place within significant period of time from now on.In recent years, along with expanding economy, environmental protection cry is more and more high, and printing bound pair flexographic ink proposes new requirement in nontoxic, pollution-free, and environment-friendlyadhesive adhesive printing ink is subject to the extensive concern of user and starts to be applied to packaging, newspaper, commercial printing etc.Environment-friendlyadhesive adhesive printing ink has obtained large-scale application in the U.S., Japan and other countries, but application is at home also quite few, and this wherein has the factor of technical elements, but more chief reason is that understanding is not enough.Environment-friendlyadhesive adhesive printing ink is mainly without aromatic hydrocarbons soya-bean ink.The PAH (polycyclic aromatic hydrocarbons) contained in tradition ink composition is a kind of volatile solvent printing film, harmful; The volatile organic compounds wherein contained not only increases topsoil, also can damage human body.Offset printing soya-bean ink adopts soybean ep-type material to replace part petroleum solvent, can reduce the injury of pollution to environment and human body.
Auxiliary agent (auxiliaries; Additives) in medical science, definition is vehicle used and additives when producing medicine and prescription being dispensed, and namely the general name of all materials except key agents activeconstituents, is the important composition composition of pharmaceutical preparation.In the industrial production, for improving production process, improving product quality and yield, or for giving the product auxiliary chemicals that certain distinctive applicability the subject of knowledge and the object of knowledge adds.Ink also can use auxiliary agent in preparation process, and traditional ink addition agent wears no resistance, and manufacturing cost is high.
Summary of the invention
It is simple that technical problem to be solved by this invention is to provide a kind of composition, the printing-ink environment-friendly type antiwear assistant that result of use is good.
Technical problem to be solved by this invention realizes by the following technical solutions.
A kind of printing-ink environment-friendly type antiwear assistant, is made up of the component of following parts by weight: delustring micro mist wax 15-25 part, oleum lini 4-6 part, nano titanium carbide 4-5 part, epoxy soybean oil 8-12 part, carbon dust 2-4 part, wolfram varbide 2-4 part, Diphenylsilanediol 2-4 part, calcined kaolin 3-5 part, amorphous silicon di-oxide 2-4 part, phospho-wolframic acid potassium 2-4 part.
The better parts by weight of each component are: delustring micro mist wax 20 parts, oleum lini 5 parts, nano titanium carbide 5 parts, epoxy soybean oil 10 parts, carbon dust 3 parts, wolfram varbide 3 parts, Diphenylsilanediol 3 parts, calcined kaolin 4 parts, amorphous silicon di-oxide 3 parts, 3 parts, phospho-wolframic acid potassium.
The preparation method of above-mentioned antiwear assistant is: above-mentioned each component mixing and stirring, three-roller is ground to fineness and is less than or equal to 25 microns, tinning.
Beneficial effect of the present invention: instant component and preparation technology simple, raw material is easily purchased, cost is low, improve the wear resistance of auxiliary agent, and not containing petroleum mineral oil component, substitute whole petroleum solvent with soya-bean oil, soya-bean oil has the characteristics such as easy degraded, hypotoxicity and low VOC, effectively can reduce the consumption of Nonrenewable resources in printing, thus reduce the pollution to environment.
Embodiment
The technique means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with specific embodiment, setting forth the present invention further.
Embodiment 1
A kind of printing-ink environment-friendly type antiwear assistant, is made up of the component of following parts by weight: delustring micro mist wax 20 parts, oleum lini 5 parts, nano titanium carbide 5 parts, epoxy soybean oil 10 parts, carbon dust 3 parts, wolfram varbide 3 parts, Diphenylsilanediol 3 parts, calcined kaolin 4 parts, amorphous silicon di-oxide 3 parts, 3 parts, phospho-wolframic acid potassium.
The preparation method of above-mentioned antiwear assistant is: above-mentioned each component mixing and stirring, three-roller is ground to fineness and is less than or equal to 25 microns, tinning.
Embodiment 2
A kind of printing-ink environment-friendly type antiwear assistant, is made up of the component of following parts by weight: delustring micro mist wax 25 parts, oleum lini 4 parts, nano titanium carbide 5 parts, epoxy soybean oil 8 parts, carbon dust 4 parts, wolfram varbide 2 parts, Diphenylsilanediol 4 parts, calcined kaolin 3 parts, amorphous silicon di-oxide 4 parts, 2 parts, phospho-wolframic acid potassium.
The preparation method of above-mentioned antiwear assistant is: above-mentioned each component mixing and stirring, three-roller is ground to fineness and is less than or equal to 25 microns, tinning.
Embodiment 3
A kind of printing-ink environment-friendly type antiwear assistant, is made up of the component of following parts by weight: delustring micro mist wax 15 parts, oleum lini 6 parts, nano titanium carbide 4 parts, epoxy soybean oil 12 parts, carbon dust 2 parts, wolfram varbide 4 parts, Diphenylsilanediol 2 parts, calcined kaolin 5 parts, amorphous silicon di-oxide 2 parts, 4 parts, phospho-wolframic acid potassium.
The preparation method of above-mentioned antiwear assistant is: above-mentioned each component mixing and stirring, three-roller is ground to fineness and is less than or equal to 25 microns, tinning.
More than show and describe ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (2)
1. a printing-ink environment-friendly type antiwear assistant, it is characterized in that, be made up of the component of following parts by weight: delustring micro mist wax 15-25 part, oleum lini 4-6 part, nano titanium carbide 4-5 part, epoxy soybean oil 8-12 part, carbon dust 2-4 part, wolfram varbide 2-4 part, Diphenylsilanediol 2-4 part, calcined kaolin 3-5 part, amorphous silicon di-oxide 2-4 part, phospho-wolframic acid potassium 2-4 part.
2. printing-ink environment-friendly type antiwear assistant according to claim 1, it is characterized in that, be made up of the component of following parts by weight: delustring micro mist wax 20 parts, oleum lini 5 parts, nano titanium carbide 5 parts, epoxy soybean oil 10 parts, carbon dust 3 parts, wolfram varbide 3 parts, Diphenylsilanediol 3 parts, calcined kaolin 4 parts, amorphous silicon di-oxide 3 parts, 3 parts, phospho-wolframic acid potassium.