CN104809960A - Display device and manufacturing method thereof, as well as transparent resin filler - Google Patents

Display device and manufacturing method thereof, as well as transparent resin filler Download PDF

Info

Publication number
CN104809960A
CN104809960A CN201510219100.8A CN201510219100A CN104809960A CN 104809960 A CN104809960 A CN 104809960A CN 201510219100 A CN201510219100 A CN 201510219100A CN 104809960 A CN104809960 A CN 104809960A
Authority
CN
China
Prior art keywords
transparent resin
resin filler
resin
display device
image display
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510219100.8A
Other languages
Chinese (zh)
Other versions
CN104809960B (en
Inventor
渡边有希
新家由久
神谷贤志
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dexerials Corp
Original Assignee
Dexerials Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dexerials Corp filed Critical Dexerials Corp
Priority to CN201510219100.8A priority Critical patent/CN104809960B/en
Priority claimed from CN200980162976.6A external-priority patent/CN102667892B/en
Publication of CN104809960A publication Critical patent/CN104809960A/en
Application granted granted Critical
Publication of CN104809960B publication Critical patent/CN104809960B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention provides a display device with excellent reprocessability, a manufacturing method thereof, as well as transparent resin filler. The transparent resin filler (5) which presents that a value of multiplying hardness of Shore E by bonding strength is below 400 after resin hardening is used as a material of a transparent resin layer (4) between an image display panel (2) and a surface panel (3). Therefore, under the condition that foreign matters and the like are mixed into the transparent resin layer (4), a reprocessed member is easy to move between the image display panel (2) and the surface panel (3), and thus the image display panel (2) and the surface panel (3) can be separated.

Description

Display device and manufacture method thereof and transparent resin filler
Technical field
The present invention relates to the display device and manufacture method thereof and transparent resin filler between image display panel and surface panel with the transparent resin layer after making transparent resin filler harden.
Background technology
In the past, propose and fill transparent resin filler and the display device making it harden between image display panel and surface panel.As transparent resin filler, use the Photoelasticity resin with index matching, the visuality of display device and impact resistance are improved (for example, referring to patent documentation 1,2.）。
As the fill method of resin, used inversion mode as follows: to any one application of resin of image display panel or surface panel, resin is not oppositely hung down with deadweight, and the mode be mixed into not have bubble is fitted in the past.
In addition, propose any one that make image display panel or surface panel tilt and to the angled manner carrying out therebetween filling, guarantee the gap value ground that specifies configuration image display panel and surface panel gap-distribution (Gap-Dispense) mode of potting resin between gap betwixt abreast.
; when having the foreign matter of bubble etc. to be mixed in the resin of filling between image display panel and surface panel; upon hardening or harden and be laggardly about to repairing (repair) operation that image display panel is separated with surface panel (for example, referring to patent documentation 3,4.）。Particularly in repair operation after the resin has hardened, the peel strength required for image display panel and surface panel being peeled off becomes large, likely causes damage to image display panel, surface panel.Therefore, wish that image display panel and surface panel can easily and reliably be peeled off by raising and the stripping carrying out recycling recycles property, so-called reprocessing (rework) property.
Prior art document
Patent documentation
Patent documentation 1:WO2008/007800 publication;
Patent documentation 2:WO2008/126893 publication;
Patent documentation 3: Japanese Unexamined Patent Publication 2009-186961 publication;
Patent documentation 4: Japanese Unexamined Patent Publication 2009-186962 publication.
Summary of the invention
the problem that invention will solve
The present invention completes in view of above-mentioned actual conditions, its object is to provide a kind of there is superior re-workability display device and manufacture method and transparent resin filler.
for solving the scheme of problem
The present inventors carry out found that of various research repeatedly, if the value after being multiplied by bonding strength (cohesiveness) to the hardness showing as shore (Shore) E is less than 400, then stripping image display panel and the peel strength required for surface panel diminish, and can improve the re-workability after hardening of resin.
Namely, display device of the present invention, it is the image display device between image display panel and surface panel with the transparent resin layer after making transparent resin filler harden, it is characterized in that, the hardness showing as shore E of transparent resin layer is E4/15 ~ E8/15, and being multiplied by the value after bonding strength to hardness is less than 400.
In addition, the feature of the manufacture method of display device of the present invention is to have: filling work procedure, between image display panel and surface panel, fill transparent resin filler; Hardening process, makes transparent resin filler harden, and forms transparent resin layer; And removal step, when having foreign matter to be mixed in transparent resin layer, reprocessing component is moved between surface panel and image display panel, removing transparent resin layer, the hardness showing as shore E of transparent resin layer is E4/15 ~ E8/15, and being multiplied by the value after bonding strength to hardness is less than 400.
In addition, transparent resin filler of the present invention, is the transparent resin filler be filled between image display panel and surface panel, it is characterized in that, the hardness showing as shore E after sclerosis is E4/15 ~ E8/15, and being multiplied by the value after bonding strength to hardness is less than 400.
At this, the hardness showing as shore E is the E type hardness tester meter (durometer) by being positioned over by the sample (sample) after the sclerosis of transparent resin filler according to JIS K6253, carries out measuring obtaining from giving as security the contact of pin after 15 seconds.
In addition, bonding strength obtains in the following manner: fixed by a panel, utilizes pressing fixture to press the edge part of another panel, is determined at stress required before both are separated, by stress divided by unit area.
According to the present invention, little owing to being multiplied by the value after bonding strength to the hardness showing as shore E of hardening of resin thing, so stripping image display panel and the peel strength required for surface panel also diminish, and can improve the re-workability after hardening of resin.
Accompanying drawing explanation
Fig. 1 is the sectional view of the major part representing display device.
Fig. 2 is the process flow diagram of an example of the manufacture method representing display device.
Fig. 3 is the sectional view of the major part of the display device represented in filling work procedure.
Fig. 4 is the sectional view of the major part of the display device represented in hardening process.
Fig. 5 is the sectional view of the major part of the display device represented in removal step.
Fig. 6 is the vertical view of the concrete example 1 representing shearing device.
Fig. 7 is the vertical view of the concrete example 2 representing shearing device.
Embodiment
Below, for applying concrete embodiment of the present invention, reference accompanying drawing is also described in detail according to following order.
1. display device
2. the manufacture method of display device
3. embodiment
< 1. display device >
Fig. 1 is the sectional view of the major part representing display device.This display device 1 has: image display panel 2, surface panel 3 and the transparent resin layer 4 after the chien shih transparent resin filler sclerosis of image display panel 2 and surface panel 3.At this, display device 1 is not particularly limited, and is the electronic equipment with display part of liquid crystal indicator, pocket telephone, portable game device etc.
Image display panel 2 is such as display panels or plasma panel, organic EL(Electroluminescence Display, electroluminescent display) panel that can show image of sheet material etc.As the surfacing of imaging surface panel 2, preferably use optical glass or plastics (acryl resin etc.).
Surface panel 3 is made up of the component with the tabular of the equal size of image display panel 2, sheet or film-form.As component, preferably use optical glass or plastics (acryl resins, polycarbonate etc. of polymethylmethacrylate (PMMA) etc.).In addition, form the optical layers such as antireflection film, photomask, viewing angle control film on the surface of surface panel 3 or the back side also can.
Transparent resin layer 4 is arranged between image display panel 2 and surface panel 3, the layer after transparent resin filler is hardened.Although in the sclerosis of transparent resin filler use heating or Ultraviolet radiation at least any one, from the view point of preventing from, to the cause thermal damage of image display panel 2, preferably using Ultraviolet radiation.
At this, the transparent resin filler of the ultraviolet ray hardening type hardened for utilizing Ultraviolet radiation is described.Transparent resin filler is preferably using the photoreactivity acrylate material of urethane acrylate, isobornyl acrylate etc. and Photoepolymerizationinitiater initiater as host.
Such as, the resin combination containing following material can preferably be used: more than one more than one the Photoepolymerizationinitiater initiater such as acrylic ester monomer and 1-hydroxycyclohexylphenylketone such as polymkeric substance, isobornyl acrylate, (methyl) acrylic acid dicyclopentenyl oxygen base ethyl ester, (methyl) acrylic acid 2-hydroxybutyl such as urethane acrylate, polyisoprene class acrylate or its carboxylate, terpenes hydrogenation resin, butadiene polymers.Also other adjuvant can be added in the scope of the object of the invention, such as, sensitizer, plastifier, transparent particles etc.
Although the viscosity of transparent resin filler is not particularly limited, from the view point of surface tension, moistening expansion rate, preferably 500 ~ 5000mPas, more preferably 500 ~ 3000mPas.
Refractive index when making transparent resin filler harden is determined by the relation of the material of image display panel 2, surface panel 3.Such as, when the surface of transparent resin layer 4 side of image display panel 2 be optical glass, the surface of transparent resin layer 4 side of surface panel 3 be the acryl resin of polymethylmethacrylate etc., the refractive index of transparent resin layer 4 is preferably 1.51 ~ 1.52.
In addition, the curing shrinkage rate when making transparent resin filler harden is less than 2.5%.Thus, the internal stress put aside when transparent resin filler is hardened can be made to reduce, can prevent from producing distortion at the interface of image display panel 2 or surface panel 3 and transparent resin layer 4.At this, curing shrinkage rate is with reference to JIS K6901(5. 12) volumetric shrinkage.
In addition, the hardness showing as shore E of the transparent resin layer 4 after making transparent resin filler harden is E4/15 ~ E8/15.Thereby, it is possible to guarantee impact resistance.The hardness showing as shore E is positioned over E type hardness tester meter according to JIS K6253 by the sample after transparent resin filler being hardened, and carries out measuring obtaining from the contact of signature pin after 15 seconds.
In addition, the bonding strength (cohesiveness) of transparent resin layer 4 is at room temperature 20 ~ 80N/cm 2.Thereby, it is possible to prevent from following warpage and produce the situation of condensing and destroying.As the assay method in this bonding strength, a panel is fixed, utilize pressing fixture to press the edge part of another panel.Then, the maximal value of stress when being separated this two panels is determined at, divided by unit area, thus as bonding strength.
In addition, with regard to transparent resin layer 4, the value after being multiplied by bonding strength (cohesiveness) to the hardness showing as shore E is less than 400.If the value after hardness being multiplied with bonding strength is more than 400, then likely damage is caused to image display panel 2 or surface panel 3.Value after hardness being multiplied with bonding strength is less than 400, and thus, reprocessing component (line (wire)) is mobile in transparent resin layer 4 becomes easy, and re-workability can be made to improve.
The manufacture method > of < 2. display device
Then, the manufacture method for above-mentioned display device is described.Fig. 2 is the process flow diagram of an example of the manufacture method representing display device.In addition, Fig. 3 ~ 5 are the sectional view of the major part of the display device represented in filling work procedure, hardening process and removal step respectively.Further, mark identical Reference numeral to the structure identical with the display device 1 shown in Fig. 1, omit the description.
The manufacture method of this display device has: filling work procedure (step S1), fills transparent resin filler 5 between image display panel 2 and surface panel 3; And hardening process (step S2), transparent resin filler 5 is hardened and forms transparent resin layer 4.Also have: check operation (step S3), check whether the exception having foreign matter to be mixed in transparent resin layer 4 etc.; And removal step (step S4), when having abnormal in transparent resin layer 4, reprocessing component is moved between image display panel 2 and surface panel 3 and removes transparent resin layer 4.
First, in the filling work procedure of step S1, as shown in Figure 3, between surface panel 3 and image display panel 2, transparent resin filler 5 is filled.As the fill method of transparent resin filler 5, inversion mode, angled manner, gap-allocation scheme etc. can be used.In inversion mode, to any one coating transparent resin filler 5 of image display panel 2 or surface panel 3, transparent resin filler 5 is not oppositely hung down with deadweight, and the mode be mixed into not have bubble carries out fitting filling.In addition, in angled manner, any one inclination of image display panel 2 or surface panel 3 is made, to filling transparent resin filler 5 therebetween.In addition, in gap-allocation scheme, guarantee gap value ground configuration image display panel 2 and the surface panel 3 abreast specified, fill transparent resin filler 5 between gap betwixt.In such filling mode, from the view point of the maximization of reply display device 1, preferably use gap-allocation scheme.In addition, by using the viscosity of transparent resin filler 5 to be the transparent resin filler of 500 ~ 3000mPas, thus can expand under the weight of image display panel 2 or surface panel 3, and moistening expansion rate improves.
In the hardening process of step S2, transparent resin filler 5 is hardened and forms transparent resin layer 4.Although in the sclerosis of transparent resin filler 5 use heating or Ultraviolet radiation at least any one, from the view point of preventing from, to the cause thermal damage of image display panel 2, preferably using Ultraviolet radiation.As the transparent resin filler 5 of ultraviolet ray hardening type, use using the photoreactivity acrylate material of above-mentioned urethane acrylate, isobornyl acrylate etc. and Photoepolymerizationinitiater initiater as the transparent resin filler of host.
As shown in Figure 4, ultraviolet (UV:Ultraviolet) is irradiated via the transparent resin filler 4 of surface panel 3 to the thickness remaining regulation.At this, hardening uniformly from the view point of realizing resin further, preferably carrying out Ultraviolet radiation from the direction of the surface normal with surface panel 3.In addition, preferably, use such as optical fiber etc. from the edge part side irradiation ultraviolet radiation of display device 1 simultaneously, prevent the leakage of transparent resin filler 5.
In the inspection operation of step S3, check between image display panel 2 and surface panel 3 formed transparent resin layer 4 in have being mixed into of the foreign matter such as bubble-free, dust.Check by utilizing light-struck visual, image procossing etc. to carry out.In step s3, when check result is good, terminate this operation.
On the other hand, in step s3, in the transparent resin layer 4 confirmed as between image display panel 2 and surface panel 3, be mixed into the foreign matter of bubble etc., when having abnormal, enter step S4, carry out the repair operation removing transparent resin layer 4.
In the removal step of step S4, as shown in Figure 5, make the reprocessing component of line 20 grade move to cut off transparent resin layer 4, thus, image display panel 2 is separated with surface panel 3.
Fig. 6 and Fig. 7 is the figure of the concrete example of the shearing device representing the cut-out being preferred for transparent resin layer.Concrete example 1 shown in Fig. 6 is example line 20 being set up in a pair pulley 10,11.This shearing device make line 20 on one side in the drawings left and right directions slide while push and shove the transparent resin layer 4 between image display panel 2 and surface panel 3, make display device 1 move in the direction orthogonal with line 20 in this condition.Thereby, it is possible to cut off transparent resin layer 4, image display panel 2 is separated with surface panel 3.
In addition, concrete example 2 shown in Fig. 7 is formed as follows: between the multiple pulleys 10 ~ 13 configured in the mode forming a pair coaster, set up line 20, and then is linked with the pulley 12,13 carrying out movement as coaster respectively by the lax extension spring 14,15 of the line 20 absorbed between pulley 10,11.In this shearing device, transparent resin layer 4 between image display panel 2 and surface panel 3 is pushed and shoved line 20, make display device 1 move in the direction orthogonal with line 20 in this condition, thus, cut off transparent resin layer 4 and image display panel 2 is separated with surface panel 3.The resilient absorbent of the lax spring 14,15 that is stretched of the line 20 between pulley 10,11, the line 20 between pulley 10,11 is always the state of stretching, extension.
As line 20, the metal wire (such as, piano wire) etc. made by carbon steel preferably can be used.In addition, as long as the thickness of line 20 is not particularly limited than the thickness detailed rules and regulations of the transparent resin layer 4 between image display panel 2 and surface panel 3, but, from the view point of cuttability, preferably use the line of 50 μm ~ 100 μm.
When using such shearing device to cut off transparent resin layer 4, as mentioned above, by using, the transparent resin filler 5 that the value after bonding strength is less than 400 is multiplied by the hardness showing as shore E after hardening of resin, thus line 20 movement in transparent resin layer 4 becomes easy, re-workability improves.In addition, also can shorten the time that cut-out spends, the productive temp time (tact time) can be made to improve.
After transparent resin layer 4 is cut-off, utilize removing solution wiping removing containing organic solvent at the hardening of resin thing of the remained on surface of image display panel 2 and surface panel 3.Such as, utilization (spray) method of dripping or spray applies removing solution on hardening of resin thing, at room temperature place about 5 minutes, hardening of resin thing is flooded expand, use (wipe) component that wipes be made up of the elastic body (elastomer) etc. being impregnated with the solvent identical with the organic solvent of the removing solution applied on hardening of resin thing to carry out wiping hardening of resin thing.
As the organic solvent contained in removing solution, such as can Shi limonene (limonene) (C 6h 10, solubility parameter: 0.6), toluene (C 7h 8, solubility parameter: 8.8).In these, from the view point of raising security, Shi limonene is selected as organic solvent You.In addition, from raising wiping, volatile viewpoint, also ethanol, isopropyl alcohol can be added.
Eliminating transparent resin layer 4(transparent resin filler 5) after, by the wipe surfaces such as utilizing microscopical cosmetic variation to observe check image display panel 2 and surface panel 3.When there is no the residue of hardening of resin thing and go bad in surface, returning step S1, repeating above-mentioned initial operation.
Like this, by using, the transparent resin filler 5 that the value after bonding strength is less than 400 is multiplied by the hardness showing as shore E after hardening of resin, thus when the exception having foreign matter to be mixed in transparent resin layer 4 etc., reprocessing component can be made easily to move between image display panel 2 and surface panel 3.That is, being multiplied by the value after bonding strength to the hardness showing as shore E of the hardening thing of transparent resin filler 5 is less than 400, thereby, it is possible to easily and reliably peel off image display panel 2 and surface panel 3 and recycle, re-workability can be made to improve.
< 3. embodiment >
Below, enumerate embodiment, specifically describe the present invention.In this embodiment, the screening characteristics, reliability, re-workability etc. of resin are evaluated.Further, the present invention is not limited by these embodiments.
［ resin 1 ］
Utilize mixing machine that following material mixing is made resin 1: the maleic anhydride adducts of polyisoprene polymer and carboxylate (the trade name UC102 of (methyl) acrylic acid 2-hydroxy methacrylate, (Co., Ltd.) Kuraray system, molecular weight 12500) 40 mass parts, (methyl) acrylic acid dicyclopentenyl oxygen base ethyl ester (trade name FA512M, Hitachi changes into industry (Co., Ltd.) system) 35 mass parts, acrylic acid 2-hydroxy propyl ester (trade name LIGHT ESTER HOP, common prosperity company chemistry (Co., Ltd.) makes) 3 mass parts, acryloyl morpholine (trade name ACMO, (Co., Ltd.) emerging people's system) 3 mass parts, benzyl acrylate (trade name C160, Osaka organic industry (Co., Ltd.) is made) 15 mass parts, terpenes hydrogenation resin (trade name ClearonP-85, YASUHARA chemistry (Co., Ltd.) is made) 35 mass parts, butadiene polymers (trade name Polyoil110, ZEON(Co., Ltd. of Japan) system) 120 mass parts, Photoepolymerizationinitiater initiater (trade name SpeedCure TPO, SiberHegner(Co., Ltd. of Japan) system) 0.5 mass parts, and Photoepolymerizationinitiater initiater (trade name IRGACURE 184D, Ciba (Co., Ltd.) is made) 4 mass parts.The cooperation of above-mentioned resin 1 is shown in Table 1.
［ resin 2 ］
Utilize mixing machine that following material mixing is made resin 2: the maleic anhydride adducts of polyisoprene polymer and carboxylate (the trade name UC102 of (methyl) acrylic acid 2-hydroxy methacrylate, (Co., Ltd.) Kuraray system, molecular weight 12500) 50 mass parts, (methyl) acrylic acid dicyclopentenyl oxygen base ethyl ester (trade name FA512M, Hitachi changes into industry (Co., Ltd.) system) 30 mass parts, acrylic acid 2-hydroxy propyl ester (trade name LIGHT ESTER HOP, common prosperity company chemistry (Co., Ltd.) makes) 6 mass parts, benzyl acrylate (trade name C160, Osaka organic industry (Co., Ltd.) is made) 10 mass parts, terpenes hydrogenation resin (trade name ClearonP-85, YASUHARA chemistry (Co., Ltd.) is made) 30 mass parts, butadiene polymers (trade name Polyoil110, ZEON(Co., Ltd. of Japan) system) 130 mass parts, Photoepolymerizationinitiater initiater (trade name SpeedCure TPO, SiberHegner(Co., Ltd. of Japan) system) 3.5 mass parts, and Photoepolymerizationinitiater initiater (trade name IRGACURE 184D, Ciba (Co., Ltd.) is made) 0.5 mass parts.The cooperation of above-mentioned resin 2 is shown in Table 1.
［ resin 3 ］
Utilize mixing machine that following material mixing is made resin 3: the maleic anhydride adducts of polyisoprene polymer and carboxylate (the trade name UC203 of (methyl) acrylic acid 2-hydroxy methacrylate, (Co., Ltd.) Kuraray system, molecular weight 25000) 100 mass parts, (methyl) acrylic acid dicyclopentenyl oxygen base ethyl ester (trade name FA512M, Hitachi changes into industry (Co., Ltd.) system) 30 mass parts, acrylic acid 2-hydroxy propyl ester (trade name LIGHT ESTER HOP, common prosperity company chemistry (Co., Ltd.) makes) 10 mass parts, terpenes hydrogenation resin (trade name ClearonP-85, YASUHARA chemistry (Co., Ltd.) is made) 30 mass parts, butadiene polymers (trade name Polyoil110, ZEON(Co., Ltd. of Japan) system) 210 mass parts, Photoepolymerizationinitiater initiater (trade name SpeedCure TPO, SiberHegner(Co., Ltd. of Japan) system) 1.5 mass parts, and Photoepolymerizationinitiater initiater (trade name IRGACURE 184D, Ciba (Co., Ltd.) is made) 7 mass parts.The cooperation of above-mentioned resin 3 is shown in Table 1.
［ resin 4 ］
Utilize mixing machine that following material mixing is made resin 4: the maleic anhydride adducts of polyisoprene polymer and carboxylate (the trade name UC102 of (methyl) acrylic acid 2-hydroxy methacrylate, (Co., Ltd.) Kuraray system, molecular weight 12500) 55 mass parts, (methyl) acrylic acid dicyclopentenyl oxygen base ethyl ester (trade name FA512M, Hitachi changes into industry (Co., Ltd.) system) 33 mass parts, acrylic acid 2-hydroxy propyl ester (trade name LIGHT ESTER HOP, common prosperity company chemistry (Co., Ltd.) makes) 7 mass parts, benzyl acrylate (trade name C160, Osaka organic industry (Co., Ltd.) is made) 5 mass parts, terpenes hydrogenation resin (trade name ClearonP-85, YASUHARA chemistry (Co., Ltd.) is made) 30 mass parts, butadiene polymers (trade name Polyoil110, ZEON(Co., Ltd. of Japan) system) 130 mass parts, Photoepolymerizationinitiater initiater (trade name SpeedCure TPO, SiberHegner(Co., Ltd. of Japan) system) 0.5 mass parts, and Photoepolymerizationinitiater initiater (trade name IRGACURE 184D, Ciba (Co., Ltd.) is made) 4 mass parts.The cooperation of above-mentioned resin 4 is shown in Table 1.
［ resin 5 ］
Utilize mixing machine that following material mixing is made resin 5: the maleic anhydride adducts of polyisoprene polymer and carboxylate (the trade name UC102 of (methyl) acrylic acid 2-hydroxy methacrylate, (Co., Ltd.) Kuraray system, molecular weight 12500) 50 mass parts, (methyl) acrylic acid dicyclopentenyl oxygen base ethyl ester (trade name FA512M, Hitachi changes into industry (Co., Ltd.) system) 28 mass parts, acrylic acid 2-hydroxy propyl ester (trade name LIGHT ESTER HOP, common prosperity company chemistry (Co., Ltd.) makes) 7 mass parts, benzyl acrylate (trade name C160, Osaka organic industry (Co., Ltd.) is made) 15 mass parts, terpenes hydrogenation resin (trade name ClearonP-85, YASUHARA chemistry (Co., Ltd.) is made) 56 mass parts, butadiene polymers (trade name Polyoil110, ZEON(Co., Ltd. of Japan) system) 100 mass parts, Photoepolymerizationinitiater initiater (trade name SpeedCure TPO, SiberHegner(Co., Ltd. of Japan) system) 0.5 mass parts, and Photoepolymerizationinitiater initiater (trade name IRGACURE 184D, Ciba (Co., Ltd.) is made) 4 mass parts.The cooperation of above-mentioned resin 5 is shown in Table 1.
［ resin 6 ］
Utilize mixing machine that following material mixing is made resin 6: the maleic anhydride adducts of polyisoprene polymer and carboxylate (the trade name UC203 of (methyl) acrylic acid 2-hydroxy methacrylate, (Co., Ltd.) Kuraray system, molecular weight 25000) 70 mass parts, (methyl) acrylic acid dicyclopentenyl oxygen base ethyl ester (trade name FA512M, Hitachi changes into industry (Co., Ltd.) system) 30 mass parts, acrylic acid 2-hydroxy propyl ester (trade name LIGHT ESTER HOP, common prosperity company chemistry (Co., Ltd.) makes) 10 mass parts, terpenes hydrogenation resin (trade name ClearonP-85, YASUHARA chemistry (Co., Ltd.) is made) 30 mass parts, butadiene polymers (trade name Polyoil110, ZEON(Co., Ltd. of Japan) system) 140 mass parts, Photoepolymerizationinitiater initiater (trade name SpeedCure TPO, SiberHegner(Co., Ltd. of Japan) system) 0.5 mass parts, and Photoepolymerizationinitiater initiater (trade name IRGACURE 184D, Ciba (Co., Ltd.) is made) 4 mass parts.The cooperation of above-mentioned resin 6 is shown in Table 1.
[table 1]
Various mensuration is carried out for the transparent resin filler (resin 1 ~ 6) after adjusting like this.Each measurement result is shown in table 2.
[table 2]
［ viscosimetric analysis ］
E type viscosity meter (HAAK Inc. rheometer (rheometer) PK100) is used at room temperature to measure the viscosity of presclerotic transparent resin filler (resin 1 ~ 6).Consequently, the viscosity of resin 1 is 800mPas, and the viscosity of resin 2 is 1100mPas, and the viscosity of resin 3 is 3800mPas, and the viscosity of resin 4 is 1200mPas, and the viscosity of resin 5 is the viscosity of 1300mPas and resin 6 is 3500mPas.At this, the viscosity of resin 1,2,4,5 is the scope of fully expansion under the weight of image display panel or surface panel, and in addition, the viscosity of resin 3,6 is the scope fully expanded by pushing image display panel or surface panel.That is, known resin 1 ~ 6 has superior screening characteristics.
［ hardening thing detecting refractive index ］
Abbe refractomecer (sodium D-line (585nm), 25 DEG C) is used to measure the refractive index of the transparent resin layer (resin 1 ~ 6) after sclerosis.Consequently, the refractive index of resin 1 ~ 6 is all 1.52.
［ curing shrinkage rate mensuration ］
Use electronic hydrometer (MIRAGE Inc. SD-120L) to measure the proportion of presclerotic resin and the resin after hardening, based on both difference in specific gravity, go out curing shrinkage rate by following formulae discovery.Consequently, the curing shrinkage rate of resin 1,2,4 ~ 6 is 1.8, and the curing shrinkage rate of resin 3 is 1.0.
Resin proportion × 100 after curing shrinkage rate (%)=(after sclerosis the front resin proportion of resin proportion-sclerosis)/sclerosis
According to the measurement result of hardening thing refractive index and the measurement result of curing shrinkage rate, about visuality, resin 1 ~ 6 has superior reliability.
［ determining bonding strength ］
To drip at the central portion of glass substrate the transparent resin filler (resin 1 ~ 6) of diameter 5mm, to load via the mode of the orthogonal from it acryl resin substrate of 0.1mm pad (spacer), utilize ultraviolet to make it harden to make test film.Fix the acryl resin substrate of this test film, on the other hand, utilize the both ends do not contacted with acryl resin substrate in pressing fixture (crosshead (cross head)) pressing glass substrate, be at room temperature determined at stress required before acryl resin substrate is separated with glass substrate.Pressing speed is 5mm/min, using the stress that obtains divided by unit area as bonding strength (cohesiveness).Consequently, the bonding strength of resin 1 is 28N/cm 2, the bonding strength of resin 2 is 20N/cm 2, the bonding strength of resin 3 is 35N/cm 2, the bonding strength of resin 4 is 39N/cm 2, the bonding strength of resin 5 is 60N/cm 2and the bonding strength of resin 6 is 50N/cm 2.
［ Determination of Hardness ］
In special container, pour appropriate transparent resin filler (resin 1 ~ 6) into, utilize ultraviolet to make it harden.Resin (sample) after sclerosis is positioned over the E type hardness tester meter (ASKER Inc. ASKER durometer E type) according to JIS K6253, from the contact of signature pin, at room temperature measures hardness after 15 seconds.In addition, measure the circumferential part more than 5 of sample, calculate mean value.Consequently, the hardness showing as shore E of resin 1 is E4/15, and the hardness of resin 2 is E8/15, and the hardness of resin 3 is E7/15, and the hardness of resin 4 is E8/15, and the hardness of resin 5 is the hardness of E7/15 and resin 6 is E10/15.
［ bonding strength × hardness ］
Above-mentioned bonding strength (cohesiveness) is multiplied with the hardness showing as shore E, as the parameter of re-workability.Consequently, resin 1 is 112, and resin 2 is 160, and resin 3 is 245, and resin 4 is 312, resin 5 be 420 and resin 6 be 500.
［ peel strength mensuration ］
Between the glass substrate and acryl resin substrate of 15cm × 26cm size, fill transparent resin filler (resin 1 ~ 6) thick to 0.1mm, utilize ultraviolet to make it harden to make test film.Be determined at the maximal value being applied to the intensity of line when using line to peel off the transparent resin layer of the 15cm width of (cut-out) this test film.Consequently, resin 1 maximum demand 35N/15cm peels off, resin 2 maximum demand 35N/15cm peels off, resin 3 maximum demand 40N/15cm peels off, resin 4 maximum demand 44N/15cm peels off, and resin 5 maximum demand 55N/15cm carries out peeling off and resin 6 maximum demand 55N/15cm peels off.
Known when the value after bonding strength (cohesiveness) being multiplied with the hardness showing as shore E diminishes, peel strength also diminishes, and both have correlativity.That is, known basis is multiplied by the hardness showing as shore E the resin 1 ~ 4 that the value after bonding strength is less than 400, and peel strength also diminishes, and can improve the re-workability after hardening of resin.

Claims (12)

1. a display device, has the transparent resin layer after transparent resin filler is hardened between image display panel and surface panel, wherein,
The hardness showing as shore E of described transparent resin layer is E4/15 ~ E8/15, and being multiplied by the value after bonding strength to this hardness is less than 400.
2. display device according to claim 1, wherein, described bonding strength is 20 ~ 80N/cm 2.
3. display device according to claim 2, wherein, the viscosity of described transparent resin filler is 500 ~ 3000mPas.
4. display device according to claim 3, wherein, the curing shrinkage rate when making described transparent resin filler harden is less than 2.5%.
5. a manufacture method for display device, wherein, has:
Filling work procedure, fills transparent resin filler between image display panel and surface panel;
Hardening process, makes described transparent resin filler harden, and forms transparent resin layer; And
Removal step, when having foreign matter to be mixed in described transparent resin layer, makes reprocessing component move between described surface panel and described image display panel, removes described transparent resin layer,
The hardness showing as shore E of described transparent resin layer is E4/15 ~ E8/15, and being multiplied by the value after bonding strength to this hardness is less than 400.
6. the manufacture method of display device according to claim 5, wherein, described bonding strength is 20 ~ 80N/cm 2.
7. the manufacture method of display device according to claim 6, wherein, the viscosity of described transparent resin filler is 500 ~ 3000mPas.
8. the manufacture method of display device according to claim 7, wherein, the curing shrinkage rate when making described transparent resin filler harden is less than 2.5%.
9. be filled in the transparent resin filler between image display panel and surface panel, wherein,
The hardness showing as shore E after sclerosis is E4/15 ~ E8/15, and being multiplied by the value after bonding strength to this hardness is less than 400.
10. transparent resin filler according to claim 9, wherein, described bonding strength is 20 ~ 80N/cm 2.
11. transparent resin filler according to claim 10, wherein, the viscosity of described transparent resin filler is 500 ~ 3000mPas.
12. transparent resin filler according to claim 11, wherein, the curing shrinkage rate when making described transparent resin filler harden is less than 2.5%.
CN201510219100.8A 2009-10-16 2009-10-16 Display device and its manufacture method and transparent resin filler Active CN104809960B (en)