CN104805395A - 一种秸秆收割机刀片的制备方法 - Google Patents
一种秸秆收割机刀片的制备方法 Download PDFInfo
- Publication number
- CN104805395A CN104805395A CN201510215587.2A CN201510215587A CN104805395A CN 104805395 A CN104805395 A CN 104805395A CN 201510215587 A CN201510215587 A CN 201510215587A CN 104805395 A CN104805395 A CN 104805395A
- Authority
- CN
- China
- Prior art keywords
- blade
- preparation
- hours
- heating
- full
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种秸秆收割机刀片的制备方法，包括以下步骤，将工业级氯化钡加热至850℃～900℃进行熔化；将工业级氯化钠在350℃～400℃干燥3小时，加入到氯化钡中混合均匀，混合比例为氯化钡比氯化钠为7：3，升温至800℃～850℃，使其充满待处理的刀刃四周，保持5个小时；将氨气经过净化，通过螺旋管道加热至550℃～650℃，氨气经加热析出氮高子，在混合器中加入硫代硫酸钠，并使温度保持在650℃～850℃之内，并施加0.2～0.4Pa大气压力，硫氮离子经旋流管道形成涡流慢速地充满刀刃四周，经过3小时后，降温，在温度降至350℃～400℃时，停止氮气通入，继续降温至刀刃冷却。具有不易磨损，节约成本的特点。
Description
技术领域
本发明属于农用机械领域，具体涉及一种秸秆收割机刀片的制备方法。
背景技术 秸秆收割机是将收获后的秸秆就地切碎翻埋入土中，以提高土地肥力的农业生产设备，也是综合利用秸秆的重要措施之一。粉碎刀片结构决定了作业效果和作业效益。目前应用的刀片结构采用锯齿形刀片，该结构加工难度大，耐磨性差，切碎阻力大。
发明内容
为了解决现有技术存在的问题，本发明提供一种秸秆收割机刀片的制备方法。具有不易磨损，节约成本的特点。
本发明的目的通过以下技术方案来具体实现：
一种秸秆收割机刀片的制备方法，包括以下步骤，将工业级氯化钡加热至850℃～ 900℃进行熔化；将工业级氯化钠在350℃～ 400℃干燥3 小时，加入到氯化钡中混合均匀，混合比例为氯化钡比氯化钠为7：3，升温至800℃～ 850℃，使其充满待处理的刀刃四周，保持5 个小时；将氨气经过净化，通过螺旋管道加热至550℃～ 650℃，氨气经加热析出氮高子，在混合器中加入硫代硫酸钠，并使温度保持在650℃～ 850℃之内，并施加0.2 ～ 0.4Pa 大气压力，硫氮离子经旋流管道形成涡流慢速地充满刀刃四周，经过3 小时后，降温，在温度降至350℃～ 400℃时，停止氮气通入，继续降温至刀刃冷却。
进一步地，刀片材料为65M钢或55Si2Mn弹簧钢。
进一步地，刀片刃部厚度≤0.5mm，硬度为38~60HRC。
与现有技术相比较，本发明具有如下的有益效果：
本发明不易磨损，延长了秸秆收割机刀片的使用寿命，节约了成本，整个热处理过程绿色环保。由于采用了上述技术方案，本发明不仅便于生产，而且成本非常低廉适于广泛推广。
具体实施方式
以下对本发明的优选实施例进行说明，应当理解，此处所描述的优选实施例仅用于说明和解释本发明，并不用于限定本发明。
实施例 一种秸秆收割机刀片的制备方法，包括以下步骤，将工业级氯化钡加热至850℃～ 900℃进行熔化；将工业级氯化钠在350℃～ 400℃干燥3 小时，加入到氯化钡中混合均匀，混合比例为氯化钡比氯化钠为7：3，升温至800℃～ 850℃，使其充满待处理的刀刃四周，保持5 个小时；将氨气经过净化，通过螺旋管道加热至550℃～ 650℃，氨气经加热析出氮高子，在混合器中加入硫代硫酸钠，并使温度保持在650℃～ 850℃之内，并施加0.2 ～ 0.4Pa 大气压力，硫氮离子经旋流管道形成涡流慢速地充满刀刃四周，经过3 小时后，降温，在温度降至350℃～ 400℃时，停止氮气通入，继续降温至刀刃冷却。
进一步地，刀片材料为65M钢或55Si2Mn弹簧钢。
进一步地，刀片刃部厚度≤0.5mm，硬度为38~60HRC。
最后应说明的是：以上所述仅为说明本发明的实施方式，并不用于限制本发明，对于本领域的技术人员来说，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (3)
1.一种秸秆收割机刀片的制备方法，包括以下步骤，其特征在于，将工业级氯化钡加热至850℃～ 900℃进行熔化；将工业级氯化钠在350℃～ 400℃干燥3 小时，加入到氯化钡中混合均匀，混合比例为氯化钡比氯化钠为7：3，升温至800℃～ 850℃，使其充满待处理的刀刃四周，保持5 个小时；将氨气经过净化，通过螺旋管道加热至550℃～ 650℃，氨气经加热析出氮高子，在混合器中加入硫代硫酸钠，并使温度保持在650℃～ 850℃之内，并施加0.2 ～ 0.4Pa 大气压力，硫氮离子经旋流管道形成涡流慢速地充满刀刃四周，经过3 小时后，降温，在温度降至350℃～ 400℃时，停止氮气通入，继续降温至刀刃冷却。
2.如权利要求1所述一种秸秆收割机刀片的制备方法，其特征在于，刀片材料为65M钢或55Si2Mn弹簧钢。
3.如权利要求1所述一种秸秆收割机刀片的制备方法，其特征在于，刀片刃部厚度≤0.5mm，硬度为38~60HRC。