CN104804337A - Environment-friendly thermosetting plastic - Google Patents
Environment-friendly thermosetting plastic Download PDFInfo
- Publication number
- CN104804337A CN104804337A CN201510186922.0A CN201510186922A CN104804337A CN 104804337 A CN104804337 A CN 104804337A CN 201510186922 A CN201510186922 A CN 201510186922A CN 104804337 A CN104804337 A CN 104804337A
- Authority
- CN
- China
- Prior art keywords
- parts
- polycarbonate
- environment
- thermosetting plastic
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
An environment-friendly thermosetting plastic is prepared from the following raw materials in parts by weight: 23-48 parts of vinyl acetate resin, 6-11 parts of ammonium isocyanate, 2-4 parts of potassium titanate whisker, 3-5 parts of polycarbonate, 21-35 parts of unsaturated polyester resin, 2-4 parts of cobalt iso-octoate, 4-8 parts of polycarbonate, 12-18 parts of dimethylbenzene, 5-11 parts of trichlormethane, 2-5 parts of triphenyl phosphate, 6-11 parts of a polylactic acid, 4-6 parts of an additive, 35-56 parts of PVDF, 6-9 parts of glass fiber, and 3-7 parts of dicumyl peroxide. The environment-friendly thermosetting plastic has the benefits of having the characteristics of heat resistance, high voltage resistance, ageing resistance and flame retardance.
Description
Technical field
The present invention relates to a kind of thermosetting resin of environmental protection.
Background technology
Plastics are that a class has plastic synthesized polymer material, it is the indispensable synthetic materials of current daily life, specifically, plastics are for main component with natural or synthetic resins, add various additive, can mould under the condition such as certain temperature and pressure and make definite shape, keep the material of shape invariance at normal temperatures, plastics are widely used in all trades and professions.But the plastics of routine exist some defects, some can only keep shape invariance at normal temperatures, but some material require at high temperature works, so market needs thermosetting resin, is applicable to the material at high temperature worked.Although plastics bring a lot of facility to people's life, also there is harm, so more environmental protection will be noted.
Summary of the invention
For the deficiencies in the prior art, the problem to be solved in the present invention is, provides a kind of thermosetting resin of environmental protection, has the characteristic of heat insulation and high pressure resistant electricity, and ageing-resistant, fire-retardant.
For solving prior art problem, technical scheme provided by the invention is, a kind of thermosetting resin of environmental protection, and it is made up of the raw material of following parts by weight:
Vinyl acetate resin 23-48 part, isocyanic acid ammonium 6-11 part, potassium titanate crystal whisker 2-4 part, polycarbonate 3-5 part, unsaturated polyester resin 21-35 part, cobalt iso-octoate 2-4 part, polycarbonate 4-8 part, dimethylbenzene 12-18 part, trichloromethane 5-11 part, triphenyl phosphite 2-5 part, poly(lactic acid) 6-11 part, auxiliary agent 4-6 part, PVDF35-56 part, glass fibre 6-9 part, dicumyl peroxide alcohol 3-7 part.
The invention has the beneficial effects as follows: the thermosetting resin of environmental protection of the present invention that there is the characteristic of heat insulation and high pressure resistant electricity, and ageing-resistant, fire-retardant.
Embodiment
embodiment 1
A thermosetting resin for environmental protection, it is made up of the raw material of following parts by weight:
Vinyl acetate resin 23 parts, isocyanic acid ammonium 6 parts, potassium titanate crystal whisker 2 parts, polycarbonate 3 parts, unsaturated polyester resin 21 parts, cobalt iso-octoate 2 parts, polycarbonate 4 parts, dimethylbenzene 12 parts, trichloromethane 5 parts, triphenyl phosphite 2 parts, poly(lactic acid) 6 parts, auxiliary agent 4 parts, PVDF35 part, 6 parts, glass fibre, dicumyl peroxide alcohol 3 parts.
embodiment 2
A thermosetting resin for environmental protection, it is made up of the raw material of following parts by weight:
Vinyl acetate resin 48 parts, isocyanic acid ammonium 11 parts, potassium titanate crystal whisker 4 parts, polycarbonate 5 parts, unsaturated polyester resin 35 parts, cobalt iso-octoate 4 parts, polycarbonate 8 parts, dimethylbenzene 18 parts, trichloromethane 11 parts, triphenyl phosphite 5 parts, poly(lactic acid) 11 parts, auxiliary agent 6 parts, PVDF56 part, 9 parts, glass fibre, dicumyl peroxide alcohol 7 parts.
Claims (1)
1. a thermosetting resin for environmental protection, is characterized in that: it is made up of the raw material of following parts by weight:
Vinyl acetate resin 23-48 part, isocyanic acid ammonium 6-11 part, potassium titanate crystal whisker 2-4 part, polycarbonate 3-5 part, unsaturated polyester resin 21-35 part, cobalt iso-octoate 2-4 part, polycarbonate 4-8 part, dimethylbenzene 12-18 part, trichloromethane 5-11 part, triphenyl phosphite 2-5 part, poly(lactic acid) 6-11 part, auxiliary agent 4-6 part, PVDF35-56 part, glass fibre 6-9 part, dicumyl peroxide alcohol 3-7 part.