CN103497506A - Compound environment-friendly flame retardant for nylon - Google Patents
Compound environment-friendly flame retardant for nylon Download PDFInfo
- Publication number
- CN103497506A CN103497506A CN201310458484.XA CN201310458484A CN103497506A CN 103497506 A CN103497506 A CN 103497506A CN 201310458484 A CN201310458484 A CN 201310458484A CN 103497506 A CN103497506 A CN 103497506A
- Authority
- CN
- China
- Prior art keywords
- nylon
- flame retardant
- parts
- compound environment
- friendly flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a compound environment-friendly flame retardant for nylon. The compound environment-friendly flame retardant is characterized by being prepared from the following raw materials in parts by weight: 20-40 parts of phenolic resin, 15-30 parts of carbon black, 5-10 parts of zinc oxide, 3-8 parts of phosphate ester, 10-20 parts of adhesive, 10-15 of amino silicone oil and 5-10 parts of chlorinated polyethylene. The compound environment-friendly flame retardant for nylon, disclosed by the invention, has a good flame retardant function, good compatibility with nylon, good weather resistance and good durability, does not migrate, is not separated out and extracted in the nylon and is easy to uniformly disperse. The compound environment-friendly flame retardant for the nylon does not decompose in a high-temperature melting forming and thermal forming processing process. The thermal deformation temperature, the mechanical temperature, the electrical insulation property and the like of produced nylon 66 flame retardant plastic are not affected, and the plastic has long-term flame retardance.
Description
Technical field
The present invention relates to a kind of nylon composite environmental-friendly fire retardant.
Background technology
The selection of fire retardant in plastics, be a very complicated process, must consider above-mentioned every factor.In existing textbook, provided such as: protective membrane mechanism, not so mechanism such as gas mechanism, coolant mechanism and terminating chain lock reactor mechanism; these can select to provide a fuzzy direction to fire retardant, but but can't provide real, effectively help.
Summary of the invention
For the deficiencies in the prior art, technical problem to be solved by this invention is, provides that a kind of cost is low, environmental protection, the nylon of excellent performance composite environmental-friendly fire retardant.
For solving the problems of the technologies described above, the technical solution used in the present invention is: a kind of nylon composite environmental-friendly fire retardant, it is characterized in that: the raw material by following parts by weight is made: resol 20-40 part, carbon black 15-30 part, zinc oxide 5-10 part, phosphoric acid ester 3-8 part, sizing agent 10-20 part, amido silicon oil 10-15 part, chlorinatedpolyethylene 5-10 part.
Nylon of the present invention by the advantage of composite environmental-friendly fire retardant is: nylon of the present invention has good anti-flaming function with the composite environmental-friendly fire retardant, good with the consistency of nylon, do not move in nylon, do not separate out, be not extracted, be easy to be uniformly dispersed, good weatherability, persistence is good, in high-temperature fusion moulding and thermoforming process engineering, do not decompose, the performances such as the nylon 66 flame retardant plastics heat-drawn wires, mechanics temperature and the electrical insulation capability that make are not affected, and plastics have long-term flame retardant resistance.
Embodiment
Below in conjunction with embodiment, the invention will be further described.
A kind of nylon composite environmental-friendly fire retardant is characterized in that: the raw material by following parts by weight is made: resol 20-40 part, carbon black 15-30 part, zinc oxide 5-10 part, phosphoric acid ester 3-8 part, sizing agent 10-20 part, amido silicon oil 10-15 part, chlorinatedpolyethylene 5-10 part.
Certainly, above-mentioned explanation is not limitation of the present invention, and the present invention also is not limited to above-mentioned giving an example; those skilled in the art; in essential scope of the present invention, the variation of making, change, interpolation or replacement, all should belong to protection scope of the present invention.
Claims (1)
1. a nylon composite environmental-friendly fire retardant, it is characterized in that: the raw material by following parts by weight is made: resol 20-40 part, carbon black 15-30 part, zinc oxide 5-10 part, phosphoric acid ester 3-8 part, sizing agent 10-20 part, amido silicon oil 10-15 part, chlorinatedpolyethylene 5-10 part.