CN104771035A - Novel double-layer glass cup manufacturing process - Google Patents
Novel double-layer glass cup manufacturing process Download PDFInfo
- Publication number
- CN104771035A CN104771035A CN201510000805.0A CN201510000805A CN104771035A CN 104771035 A CN104771035 A CN 104771035A CN 201510000805 A CN201510000805 A CN 201510000805A CN 104771035 A CN104771035 A CN 104771035A
- Authority
- CN
- China
- Prior art keywords
- glass
- glass cup
- novel double
- layer glass
- carried out
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a novel double-layer glass cup manufacturing process. The novel double-layer glass cup manufacturing process includes the following steps: (1) according to the requirements for the size and the shape of a manufactured glass cup, an appropriate glass pipe is selected to be cut to serve as an inner container of the glass cup; (2) according to the requirements for the size and the shape of the manufactured glass cup, an appropriate glass pipe is selected to be cut to serve as an outer shell of the glass cup; (3) an opening is sealed, wherein an opening part of the inner container and an opening part of the outer shell are welded together through coal gas and oxygen, the welding temperature is controlled to range from 450 DEG C to 600 DEG C; (4) the bottom is sealed, wherein the bottom of the inner container and the bottom of the outer shell are welded together through coal gas and oxygen, and the welding temperature is controlled to range from 450 DEG C to 600 DEG C; (5) after welding molding is carried out, annealing treatment is carried out on the glass cup, when the temperature drops to range from 35 DEG C to 45 DEG C, heat preservation is carried out for 12 hours to 24 hours, and then cooling is carried out; and (6) the cooled glass cup is slowly heated from 0 DEG C to 600 DEG C, and then annealing treatment is carried out. The novel double-layer glass cup manufacturing process is simple in working procedure and low in manufacturing cost, and materials are saved.
Description
Technical field
The present invention relates to double-layer glass manufacture craft, specifically a kind of manufacture craft of novel double-layer glass.
Background technology
The traditional manufacturing technique of current double-layer glass is: the first step: glass inner bag pipe cutting; Second step, glass inner bag back cover; 3rd step, glass shell pipe cutting; 4th step: inner bag and shell sealing; 5th step: by shell back cover, wherein needs in traditional handicraft to carry out 2 back covers to glass, namely carries out back cover respectively to inner bag back cover and shell, there is complex procedures, waste material, production cost high problem.
Therefore, for above-mentioned technical problem, need the manufacture craft proposing a kind of new double-layer glass badly.
Summary of the invention
Instant invention overcomes prior art Problems existing, propose a kind of operation simple, cost of manufacture is low, saves the double-layer glass manufacture craft of material.
The present invention is for solving the problems of the technologies described above by the following technical solutions: a kind of manufacture craft of novel double-layer glass, comprises the following steps:
(1) according to the size and dimension requirement of prepared glass, as the inner bag of glass after selecting suitable glass tube to cut;
(2) according to the size and dimension requirement of prepared glass, as the shell of glass after selecting suitable glass tube to cut;
(3) seal: inner bag oral area and housing mouth welding are integrated by coal gas and oxygen, fusion temp controls at 450-600 DEG C;
(4) back cover: be integrated bottom inner bag with outer casing bottom welding by coal gas and oxygen, fusion temp controls at 450-600 DEG C;
(5) after fusion molding, carry out annealing in process to glass, when temperature is down to 35-45 DEG C, insulation 12-24 hour, then cools;
(6) cooled glass is slowly warming up to 600 DEG C from 0 DEG C, then carries out annealing in process.
As present invention further optimization scheme, in described step (2), fusion temp is 450 DEG C.
As present invention further optimization scheme, in described step (3), fusion temp is 450 DEG C.
As present invention further optimization scheme, described glass tube is high-temperature glass tube.
The present invention adopts above technical scheme compared with prior art, has following technique effect:
Only need carry out a back cover in the present invention, inner bag and shell are welded together, break traditional technique needing to carry out 2 back covers, make the manufacture craft of double-layer glass simpler, accelerate production efficiency, reduce cost of manufacture, should vigorously promote the use.
Detailed description of the invention
Below technical scheme of the present invention is described in further detail:
Embodiment 1:
A manufacture craft for novel double-layer glass, is characterized in that; Comprise the following steps:
(1) according to the size and dimension requirement of prepared glass, as the inner bag of glass after selecting suitable glass tube to cut;
(2) according to the size and dimension requirement of prepared glass, as the shell of glass after selecting suitable glass tube to cut;
(3) seal: inner bag oral area and housing mouth welding are integrated by coal gas and oxygen, fusion temp controls at 450 DEG C;
(4) back cover: be integrated bottom inner bag with outer casing bottom welding by coal gas and oxygen, fusion temp controls at 450 DEG C;
(5) after fusion molding, annealing in process is carried out to glass, when temperature is down to 35 DEG C, is incubated 12 hours, then cools;
(6) cooled glass is slowly warming up to 600 DEG C from 0 DEG C, then carries out annealing in process.
Glass tube is high-temperature glass tube.
Embodiment 2:
A manufacture craft for novel double-layer glass, is characterized in that; Comprise the following steps:
(1) according to the size and dimension requirement of prepared glass, as the inner bag of glass after selecting suitable glass tube to cut;
(2) according to the size and dimension requirement of prepared glass, as the shell of glass after selecting suitable glass tube to cut;
(3) seal: inner bag oral area and housing mouth welding are integrated by coal gas and oxygen, fusion temp controls at 600 DEG C;
(4) back cover: be integrated bottom inner bag with outer casing bottom welding by coal gas and oxygen, fusion temp controls at 600 DEG C;
(5) after fusion molding, annealing in process is carried out to glass, when temperature is down to 45 DEG C, is incubated 24 hours, then cools;
(6) cooled glass is slowly warming up to 600 DEG C from 0 DEG C, then carries out annealing in process.
Glass tube is high-temperature glass tube.
The present invention is not limited to above-mentioned embodiment, in the ken that those of ordinary skill in the art possess, can also make a variety of changes under the prerequisite not departing from present inventive concept.The above, it is only preferred embodiment of the present invention, not any pro forma restriction is done to the present invention, although the present invention discloses as above with preferred embodiment, but and be not used to limit the present invention, any those skilled in the art, do not departing within the scope of technical solution of the present invention, make a little change when the technology contents of above-mentioned announcement can be utilized or be modified to the Equivalent embodiments of equivalent variations, in every case be do not depart from technical solution of the present invention content, according to technical spirit of the present invention, within the spirit and principles in the present invention, to any simple amendment that above embodiment is done, equivalent replacement and improvement etc., within the protection domain all still belonging to technical solution of the present invention.
Claims (4)
1. a manufacture craft for novel double-layer glass, is characterized in that; Comprise the following steps:
(1) according to the size and dimension requirement of prepared glass, as the inner bag of glass after selecting suitable glass tube to cut;
(2) according to the size and dimension requirement of prepared glass, as the shell of glass after selecting suitable glass tube to cut;
(3) seal: inner bag oral area and housing mouth welding are integrated by coal gas and oxygen, fusion temp controls at 450-600 DEG C;
(4) back cover: be integrated bottom inner bag with outer casing bottom welding by coal gas and oxygen, fusion temp controls at 450-600 DEG C;
(5) after fusion molding, carry out annealing in process to glass, when temperature is down to 35-45 DEG C, insulation 12-24 hour, then cools;
(6) cooled glass is slowly warming up to 600 DEG C from 0 DEG C, then carries out annealing in process.
2. the manufacture craft of a kind of novel double-layer glass according to claim 1, is characterized in that: in described step (2), fusion temp is 450 DEG C.
3. the manufacture craft of a kind of novel double-layer glass according to claim 1, is characterized in that: in described step (3), fusion temp is 450 DEG C.
4. the manufacture craft of a kind of novel double-layer glass according to claim 1, is characterized in that: described glass tube is high-temperature glass tube.