CN104752641B - Preparation method of car storage battery protection sleeve - Google Patents
Preparation method of car storage battery protection sleeve Download PDFInfo
- Publication number
- CN104752641B CN104752641B CN201510077777.2A CN201510077777A CN104752641B CN 104752641 B CN104752641 B CN 104752641B CN 201510077777 A CN201510077777 A CN 201510077777A CN 104752641 B CN104752641 B CN 104752641B
- Authority
- CN
- China
- Prior art keywords
- composite fibre
- fibre net
- storage battery
- acid
- carrying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a preparation method of a car storage battery protection sleeve. The preparation method comprises the following steps: a, mixing 90 to 99 percent by weight of black acid-resisting PET fibers and 2 to 10 percent by weight of black double-component PET fibers; b, carrying out the loosening treatment; c, carding by adopting a carding machine; d, carrying out the needling treatment by utilizing a needling machine; e, carrying out the primary rolling by utilizing a rolling machine; f, carrying out the water repellency treatment; g, carrying out the drying treatment by utilizing a drying machine; h, carrying out the secondary rolling in the rolling machine; i, spreading PE, PA or resin powder by utilizing a powder spreading machine; j, carrying out the drying treatment in the drying machine; k, carrying out the tertiary rolling in the rolling machine; l, cutting an acid-resisting nonwoven fabric and sponge, and sequentially stacking the acid-resisting nonwoven fabric, the sponge and the acid-resisting nonwoven fabric; and m, carrying out the hot press molding. By adopting the technological procedures, the car storage battery protection sleeve can be effectively prepared; the prepared car storage battery protection sleeve can be used for effectively preventing the leakage of an electrolyte in a car storage battery so as not to corrode a car body, and the car safety of the car can be effectively improved.
Description
Technical field
The present invention relates to Automobile Products technical field, particularly relate to a kind of automobile storage battery protection set preparation method.
Background technology
For automobile storage battery, when running car (particularly during jolting), the acid in automobile storage battery
Property electrolyte be easy to occur leakage, when automobile storage battery internal leakage electrolyte out drips in body of a motor car, easily make
Become vehicle body corrosion；For the steelframe part of vehicle body, once by electrolytic corrosion, its intensity will be greatly affected, very
To the personal safety influencing whether driver and crew.
For solving the problems referred to above, automobile storage battery is the most all sheathed with a protection set.
Summary of the invention
It is an object of the invention to provide a kind of automobile storage battery protection set preparation method, this automobile storage battery protection set system
Preparation Method can prepare processing automobile storage battery protection set effectively, and the automobile storage battery protection set after preparation processing can have
Effect prevents the electrolyte leakage in automobile storage battery from causing vehicle body to corrode, and i.e. can be effectively improved vehicle safety.
For reaching above-mentioned purpose, the present invention is achieved through the following technical solutions.
A kind of automobile storage battery protection set preparation method, includes following processing step, particularly as follows:
A, the acidproof PET of black and the double-component PET of black are respectively put into mixer and are stirred,
The acid resistance of acidproof PET is persistently to soak under the temperature conditions of 90 DEG C 24 hours in the electrolyte containing 25% sulphuric acid
Not corroding, wherein, acidproof PET, double-component PET mix according to the proportioning of following weight portion:
Acidproof PET 90%-98%
Double-component PET 2%-10%；
B, put into opener and carry out shredding process by mix homogeneously and in a composite fibre for dress；
C, by shredding process after composite fibre feeding to carding machine, carry out fiber combing operation, carding machine exports into
The composite fibre net of net；
D, by composite fibre net feeding to needing machine, carry out acupuncture processing；
E, the composite fibre net after acupuncture processed is fed through in winder carries out for the first time rolling；
F, the composite fibre net after rolling is put into water repellent solution, carry out immersion treatment and composite fibre net is complete
Being impregnated with, penetration period is ＜ 5 seconds, wherein, water repellent solution be every double centner purified water in containing 5-15 kilogram of water repellent
Mixed solution；
G, water repellent is processed after the tiling of composite fibre net be continually fed into dehydrator and carry out drying and processing, mixing fibre
It is that 10-15 rice is per minute that the linear velocity of dehydrator is crossed by dimension Netcom, and the drying temperature of dehydrator is 120-130 DEG C；
H, the composite fibre net after drying machine drying processes is fed through in winder carry out second time rolling；
I, the composite fibre net after second time rolling is tiled continually by duster, duster by PE, PA or
Person's resin powder is spread in composite fibre net, and by PE, PA in the composite fibre net after duster or resin powder gram
It is heavily 5-15 g/m2；
J, carry out drying and processing by tiling to be continually fed into dehydrator by composite fibre net after duster, mixing
Fleece is that 15-20 rice is per minute by the linear velocity of dehydrator, and the drying temperature of dehydrator is 160-170 DEG C；
K, the composite fibre net after drying machine drying processes is fed through in winder carry out third time rolling, acidproof
Prepared by non-woven fabrics；
L, cut Acid-proof non-woven fabric and sponge, and the sponge holder cut is put in two Acid-proof non-woven fabric cut
Between；
M, sponge good for superposition and Acid-proof non-woven fabric are positioned in hot pressing die carry out hot-forming, the temperature of hot pressing die
Degree is for 200-210 DEG C.
Wherein, the grammes per square metre of described Acid-proof non-woven fabric is 85g/m2-120 g/m2。
Wherein, the thickness of described sponge is 5-20mm.
The invention have the benefit that a kind of automobile storage battery protection set preparation method of the present invention, it include with
Lower processing step: a, it is that acidproof PET 90%-98% of black, black double-component PET 2%-10% are carried out by weight
Mixing；B, shredding process；C, carding machine combing；D, needing machine acupuncture processing；The rolling for the first time of e, winder；F, water repellent process；
G, drying machine drying process；Second time rolling in h, winder；I, duster spread PE, PA or resin powder；In j, dehydrator
Drying and processing；Third time rolling in winder；L, cut Acid-proof non-woven fabric, sponge, and by Acid-proof non-woven fabric, sponge, acidproof nothing
Spin cloth to stack successively；M, hot-forming.Being designed by above-mentioned processing step, the present invention can prepare processing automobile electric power storage effectively
Pond protection set, and the automobile storage battery protection set after preparation processing can effectively prevent the electrolyte leakage in automobile storage battery and
Cause vehicle body to corrode, i.e. can be effectively improved vehicle safety.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention will be described.
A kind of automobile storage battery protection set preparation method, includes following processing step, particularly as follows:
A, the acidproof PET of black and the double-component PET of black are respectively put into mixer and are stirred,
The acid resistance of acidproof PET is persistently to soak under the temperature conditions of 90 DEG C 24 hours in the electrolyte containing 25% sulphuric acid
Not corroding, wherein, acidproof PET, double-component PET mix according to the proportioning of following weight portion:
Acidproof PET 90%-98%
Double-component PET 2%-10%；
B, put into opener and carry out shredding process by mix homogeneously and in a composite fibre for dress；
C, by shredding process after composite fibre feeding to carding machine, carry out fiber combing operation, carding machine exports into
The composite fibre net of net；
D, by composite fibre net feeding to needing machine, carry out acupuncture processing；
E, the composite fibre net after acupuncture processed is fed through in winder carries out for the first time rolling；
F, the composite fibre net after rolling is put into water repellent solution, carry out immersion treatment and composite fibre net is complete
Being impregnated with, penetration period is ＜ 5 seconds, wherein, water repellent solution be every double centner purified water in containing 5-15 kilogram of water repellent
Mixed solution；
G, water repellent is processed after the tiling of composite fibre net be continually fed into dehydrator and carry out drying and processing, mixing fibre
It is that 10-15 rice is per minute that the linear velocity of dehydrator is crossed by dimension Netcom, and the drying temperature of dehydrator is 120-130 DEG C；
H, the composite fibre net after drying machine drying processes is fed through in winder carry out second time rolling；
I, the composite fibre net after second time rolling is tiled continually by duster, duster by PE, PA or
Person's resin powder is spread in composite fibre net, and by PE, PA in the composite fibre net after duster or resin powder gram
It is heavily 5-15 g/m2；
J, carry out drying and processing by tiling to be continually fed into dehydrator by composite fibre net after duster, mixing
Fleece is that 15-20 rice is per minute by the linear velocity of dehydrator, and the drying temperature of dehydrator is 160-170 DEG C；
K, the composite fibre net after drying machine drying processes is fed through in winder carry out third time rolling, acidproof
Prepared by non-woven fabrics；
L, cut Acid-proof non-woven fabric and sponge, and the sponge holder cut is put in two Acid-proof non-woven fabric cut
Between；
M, sponge good for superposition and Acid-proof non-woven fabric are positioned in hot pressing die carry out hot-forming, the temperature of hot pressing die
Degree is for 200-210 DEG C.
It should further be noted that the grammes per square metre of Acid-proof non-woven fabric is 85g/m2-120 g/m2, the thickness of sponge is 5-20mm.
Being designed by above-mentioned processing step, the present invention can prepare processing automobile storage battery protection set, and preparation effectively
Automobile storage battery protection set after processing can effectively prevent the electrolyte leakage in automobile storage battery from causing vehicle body to corrode, i.e.
Vehicle safety can be effectively improved.
Above content is only presently preferred embodiments of the present invention, for those of ordinary skill in the art, according to the present invention's
Thought, the most all will change, and this specification content should not be construed as the present invention
Restriction.
Claims (3)
1. kind of automobile storage battery protection set preparation method, it is characterised in that include following processing step, particularly as follows:
A, the acidproof PET of black and the double-component PET of black are respectively put into mixer and are stirred, acidproof
The acid resistance of PET is persistently to soak 24 hours to be stale-proof in the electrolyte containing 25% sulphuric acid under the temperature conditions of 90 DEG C
Erosion, wherein, acidproof PET, double-component PET mix according to the proportioning of following weight portion:
Acidproof PET 90%-98%
Double-component PET 2%-10%；
B, put into opener and carry out shredding process by mix homogeneously and in a composite fibre for dress；
C, will shredding process after composite fibre feeding to carding machine carries out fiber combing operation, carding machine output is into the net
Composite fibre net；
D, by composite fibre net feeding to needing machine, carry out acupuncture processing；
E, the composite fibre net after acupuncture processed is fed through in winder carries out for the first time rolling；
F, the composite fibre net after rolling put into water repellent solution, carry out immersion treatment and composite fibre net is impregnated with completely,
Penetration period is ＜ 5 seconds, and wherein, water repellent solution is the mixing containing 5-15 kilogram of water repellent in the purified water of every double centner
Solution；
G, water repellent is processed after the tiling of composite fibre net be continually fed into dehydrator and carry out drying and processing, composite fibre net
Being that 10-15 rice is per minute by the linear velocity of dehydrator, the drying temperature of dehydrator is 120-130 DEG C；
H, the composite fibre net after drying machine drying processes is fed through in winder carry out second time rolling；
I, by after second time rolling composite fibre net tile continually by duster, duster is by PE, PA or tree
Cosmetics material is spread in composite fibre net, and by the grammes per square metre of PE, PA or resin powder in the composite fibre net after duster is
5-15 g/m2；
J, carry out drying and processing, composite fibre by tiling to be continually fed into dehydrator by composite fibre net after duster
It is that 15-20 rice is per minute that the linear velocity of dehydrator is crossed by Netcom, and the drying temperature of dehydrator is 160-170 DEG C；
K, the composite fibre net after drying machine drying processes is fed through in winder carry out third time rolling, acidproof nonwoven
Prepared by cloth；
L, cut Acid-proof non-woven fabric and sponge, and the sponge holder cut is put in two Acid-proof non-woven fabric cut it
Between；
M, sponge good for superposition and Acid-proof non-woven fabric being positioned in hot pressing die and carry out hot-forming, the temperature of hot pressing die is
200-210℃。
2. according to automobile storage battery protection set preparation method a kind of described in claim 1, it is characterised in that: described Acid-proof non-woven fabric
Grammes per square metre is 85g/m2-120 g/m2。
3. a kind of automobile storage battery protection set preparation method described in claim 2, it is characterised in that: the thickness of described sponge is 5-
20mm。