CN104745014A - Ship corrosion-resistant coating with strong light reflection - Google Patents

Ship corrosion-resistant coating with strong light reflection Download PDF

Info

Publication number
CN104745014A
CN104745014A CN201510144353.3A CN201510144353A CN104745014A CN 104745014 A CN104745014 A CN 104745014A CN 201510144353 A CN201510144353 A CN 201510144353A CN 104745014 A CN104745014 A CN 104745014A
Authority
CN
China
Prior art keywords
resistant coating
revs
ship
dispersion machine
container
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510144353.3A
Other languages
Chinese (zh)
Inventor
张家俊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
MA'ANSHAN XINGLONG CASTING Co Ltd
Original Assignee
MA'ANSHAN XINGLONG CASTING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by MA'ANSHAN XINGLONG CASTING Co Ltd filed Critical MA'ANSHAN XINGLONG CASTING Co Ltd
Priority to CN201510144353.3A priority Critical patent/CN104745014A/en
Publication of CN104745014A publication Critical patent/CN104745014A/en
Pending legal-status Critical Current

Abstract

The invention discloses ship corrosion-resistant coating with strong light reflection. The ship corrosion-resistant coating with strong light reflection is formed by pulping, grinding and mixing the following components: soft water, a 30% ammonium polycarboxylate dispersing agent, an organic silicon defoaming agent, propylene glycol, a methylisothiazolinone preservative, 0.15-micron rutile titanium dioxide powder, 0.3-micron precipitate aluminum silicate, glass beads with grain sizes of 0.2 micron and 0.4 micron, a fluorescer, water-based acrylic resin, a 30% polyurethane associative thickener, and a methyl ethanol amine pH value regulator. The ship corrosion-resistant coating with strong light reflection disclosed by the invention is good in corrosion resistance, capable of strongly reflecting light to display a ship position and self-laminating to display the ship body position without light, so that the safety during ship sailing is increased, and the water resistance is strong.

Description

A kind of strong reflective corrosion resistant coating peculiar to vessel
Technical field
The present invention relates to a kind of strong reflective corrosion resistant coating, particularly a kind of coating being coated in hull lofty perch peculiar to vessel.
Background technology
Ship is constantly walked with korneforos through sea of being everlasting, how can better near other position of ship oneself generally adopt strong lamp, consumes resources, and when breaking in the supply, strong lamp cannot play a role the Position Approximate cannot informing hull well, danger very.
Summary of the invention
The object of the invention is to overcome above deficiency, providing corrosion-resistant, one strong reflective corrosion resistant coating peculiar to vessel that strong adhesion, reflecting effect are good.
Object of the present invention is achieved through the following technical solutions: a kind of strong reflective corrosion resistant coating peculiar to vessel, and the described strong composition of reflective corrosion resistant coating peculiar to vessel and the per-cent of formula are:
(1) soft water 18.09%
(2) 30% poly carboxylic acid ammonium salt dispersion agents 1.18%
(3) silicone antifoam agent 0.28%
(4) propylene glycol 1.72%
(5) methylisothiazolinone sanitas 0.05%
(6) 0.15 microns of Rutile type Titanium Dioxides 25.6%
(7) 0.3 microns of precipitated silicate aluminium 2.0%
(8) soft water 4.1%
(9) 0.2 micron grain size gravels 1.52%
(10) 0.4 micron grain size granulated glass spherees 6.0%
(11) fluorescent agent 8%
(13) water-borne acrylic resin 4.3%
(14) 30% polyurethane associative thickeners 1.31%
(15) soft water 5.0%
(16) benzene emulsion 20.7%
(17) Mono Methyl Ethanol Amine pH value conditioning agent 0.15%;
Described reflective corrosion resistant coating peculiar to vessel preparation method be:
A, making beating: the soft water adding (1) in the container that dispersion machine is housed, be under the whipped state of 300 revs/min at rotating speed, (2), (3), (4), (5) are added successively by formula order, stir 3 minutes, the rotating speed of dispersion machine is increased to 600 revs/min, added successively in container in (6), (7), just the rotating speed of dispersion machine is increased to 1200 revs/min, stirs 8 minutes to obtain slurry to be ground;
B, grinding: the slurry to be ground in container is ground by shredder, obtains ground slurry;
C, mixing: ground slurry is dropped into another and be equipped with in the container of dispersion machine, add the soft water of (8), the rotating speed of dispersion machine is adjusted to 1000 revs/min, add (9), (10), (11) successively, stir 5 minutes, the rotating speed of dispersion machine is adjusted to 1200 revs/min, add (12), (13), uniform swirling is formed in container, dispersing speed is kept to be 1200 revs/min, add (14), (15), (16), (17) successively, be fully uniformly mixed 8 minutes, obtain described strong reflective corrosion resistant coating peculiar to vessel.
The present invention compared with prior art has and has advantage below:
In the present invention, anticorrosion and reflective and self-luminescence are combined, more be applicable to shipping agency industry, when light is bad, light can be reflected by granulated glass sphere, demonstrate the position of hull, when there is no light, also can send certain light voluntarily, increasing the safety of self ship and other ships; The granulated glass sphere 6.0% that present invention utilizes the gravel of 0.2 micron grain size of 1.52% and 0.4 micron grain size of 6.0% improves the intensity of emission of light; Used fluorescent agent in the present invention, can when there is no light self-luminescence, increase the safety performance of whole hull; Methylisothiazolinone in the present invention, can the growth of anti-bacteria and algae as sanitas, plays rot-resistant effect, can not produce toxic substance simultaneously; Use soft water in the present invention, effectively decrease the quality of water mineral to described reflective corrosion resistant coating peculiar to vessel; The present invention has rotproofness well, can reflective display hull position, and increase degree of safety when navigating, water tolerance is strong.
embodiment:
in order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, and this embodiment only for explaining the present invention, does not form limiting the scope of the present invention.
Object of the present invention is achieved through the following technical solutions: a kind of strong reflective corrosion resistant coating peculiar to vessel, and the described strong composition of reflective corrosion resistant coating peculiar to vessel and the per-cent of formula are:
(1) soft water 18.09%
(2) 30% poly carboxylic acid ammonium salt dispersion agents 1.18%
(3) silicone antifoam agent 0.28%
(4) propylene glycol 1.72%
(5) methylisothiazolinone sanitas 0.05%
(6) 0.15 microns of Rutile type Titanium Dioxides 25.6%
(7) 0.3 microns of precipitated silicate aluminium 2.0%
(8) soft water 4.1%
(9) 0.2 micron grain size gravels 1.52%
(10) 0.4 micron grain size granulated glass spherees 6.0%
(11) fluorescent agent 8%
(13) water-borne acrylic resin 4.3%
(14) 30% polyurethane associative thickeners 1.31%
(15) soft water 5.0%
(16) benzene emulsion 20.7%
(17) Mono Methyl Ethanol Amine pH value conditioning agent 0.15%;
Described reflective corrosion resistant coating peculiar to vessel preparation method be:
A, making beating: the soft water adding (1) in the container that dispersion machine is housed, be under the whipped state of 300 revs/min at rotating speed, (2), (3), (4), (5) are added successively by formula order, stir 3 minutes, the rotating speed of dispersion machine is increased to 600 revs/min, added successively in container in (6), (7), just the rotating speed of dispersion machine is increased to 1200 revs/min, stirs 8 minutes to obtain slurry to be ground;
B, grinding: the slurry to be ground in container is ground by shredder, obtains ground slurry;
C, mixing: ground slurry is dropped into another and be equipped with in the container of dispersion machine, add the soft water of (8), the rotating speed of dispersion machine is adjusted to 1000 revs/min, add (9), (10), (11) successively, stir 5 minutes, the rotating speed of dispersion machine is adjusted to 1200 revs/min, add (12), (13), uniform swirling is formed in container, dispersing speed is kept to be 1200 revs/min, add (14), (15), (16), (17) successively, be fully uniformly mixed 8 minutes, obtain described strong reflective corrosion resistant coating peculiar to vessel.
The present invention has rotproofness well, can reflective display hull position, increases degree of safety when navigating, and water tolerance is strong, also can give out certain light voluntarily when not having light.

Claims (1)

1. a strong reflective corrosion resistant coating peculiar to vessel, is characterized in that: the described strong composition of reflective corrosion resistant coating peculiar to vessel and the per-cent of formula are:
(1) soft water 18.09%
(2) 30% poly carboxylic acid ammonium salt dispersion agents 1.18%
(3) silicone antifoam agent 0.28%
(4) propylene glycol 1.72%
(5) methylisothiazolinone sanitas 0.05%
(6) 0.15 microns of Rutile type Titanium Dioxides 25.6%
(7) 0.3 microns of precipitated silicate aluminium 2.0%
(8) soft water 4.1%
(9) 0.2 micron grain size gravels 1.52%
(10) 0.4 micron grain size granulated glass spherees 6.0%
(11) fluorescent agent 8%
(13) water-borne acrylic resin 4.3%
(14) 30% polyurethane associative thickeners 1.31%
(15) soft water 5.0%
(16) benzene emulsion 20.7%
(17) Mono Methyl Ethanol Amine pH value conditioning agent 0.15%;
Described reflective corrosion resistant coating peculiar to vessel preparation method be:
A, making beating: the soft water adding (1) in the container that dispersion machine is housed, be under the whipped state of 300 revs/min at rotating speed, (2), (3), (4), (5) are added successively by formula order, stir 3 minutes, the rotating speed of dispersion machine is increased to 600 revs/min, added successively in container in (6), (7), just the rotating speed of dispersion machine is increased to 1200 revs/min, stirs 8 minutes to obtain slurry to be ground;
B, grinding: the slurry to be ground in container is ground by shredder, obtains ground slurry;
C, mixing: ground slurry is dropped into another and be equipped with in the container of dispersion machine, add the soft water of (8), the rotating speed of dispersion machine is adjusted to 1000 revs/min, add (9), (10), (11) successively, stir 5 minutes, the rotating speed of dispersion machine is adjusted to 1200 revs/min, add (12), (13), uniform swirling is formed in container, dispersing speed is kept to be 1200 revs/min, add (14), (15), (16), (17) successively, be fully uniformly mixed 8 minutes, obtain described strong reflective corrosion resistant coating peculiar to vessel.
CN201510144353.3A 2015-03-31 2015-03-31 Ship corrosion-resistant coating with strong light reflection Pending CN104745014A (en)