CN104744688B - 一种聚酰胺树脂和由其组成的聚酰胺模塑组合物 - Google Patents
一种聚酰胺树脂和由其组成的聚酰胺模塑组合物 Download PDFInfo
- Publication number
- CN104744688B CN104744688B CN201510135949.7A CN201510135949A CN104744688B CN 104744688 B CN104744688 B CN 104744688B CN 201510135949 A CN201510135949 A CN 201510135949A CN 104744688 B CN104744688 B CN 104744688B
- Authority
- CN
- China
- Prior art keywords
- monomer
- polyamide
- acid
- fibre
- content
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种聚酰胺树脂，该聚酰胺树脂在苯酚中pH值小于7，其包含衍生自如下单体混合物的重复单元：具有两个氨基官能团的第一单体，称为单体A；具有两个羧基官能团或其前体基团的第二单体，称为单体B；和/或具有一个氨基和一个羧基官能团的第三单体和/或内酰胺，称为单体D；其中，所述单体混合物中单体A至少含有一种具有十个碳原子的单体A10；单体B至少含有一种具有八个碳原子的非脂肪族单体B8；该聚酰胺树脂具有双熔点，其二者熔点之差为5oC‑20oC，基于单体A的摩尔量，含有0.009mol%‑5mol%的含有3个或3个以上氮原子、含仲胺基团的化合物X。该聚酰胺树脂及其模塑组合物能缩短注塑产品成型周期，注塑产品表面光泽度好，且能够显著改善热滞留稳定性。
Description
技术领域
本发明涉及高分子材料领域，特别涉及一种聚酰胺树脂和由其组成的聚酰胺模塑组合物。
背景技术
聚酰胺因具有良好的综合性能，包括力学性能、耐热性、耐磨损性、耐化学药品性和自润滑性，且摩擦系数低，有一定的阻燃性等，其被广泛适于用玻璃纤维和其它填料填充增强改性，提高性能和扩大应用范围等方面。近几年来半芳香族聚酰胺由于其耐热性能和力学性能更优而被重点开发。
然而，均聚PA6T由于熔点高于分解温度，通常向其中添加一定量的共聚组分降低其熔点，得到PA6T/66、PA6T/6等。但共聚组分的加入破坏了均聚物的晶体结构，导致上述6T共聚物性能下降，注塑时成型周期延长，不利于模塑制件生产。
另外一种降低半芳香族聚酰胺熔点的方法是增加脂肪胺碳链的长度，例如，将己二胺更换为壬二胺，得到PA9T，其熔点低于320oC，远低于分解温度，熔融加工时的热分解问题得到一定程度解决，可以正常使用。然而，对于聚酰胺9T，由于作为其构成成分的二胺的碳原子数为奇数，所以聚酰胺的化学结构不对称，同样破坏了其结晶性，进而导致性能下降。
另外，目前聚酰胺树脂的端基测试已经成为本行业一个通用的手段，用以表征聚酰胺的数均分子量、反应程度等各方面的信息。尽管聚酰胺的末端基团可能会影响溶液的pH值，这并非唯一重要因素。不同聚酰胺分子链的刚性、酰胺基浓度、第二维利系数、Huggins参数、θ溶剂行为等都会对其pH值造成重大影响。即使类似结构的聚酰胺，由于上述因素的共同作用，其pH值都可能差别巨大，从而引起聚合物性能的差异。
而且，通常半芳香族聚酰胺注塑时，大部分物料的停留时间最高可达30min以上。注塑初期的制品和注塑后期的制品由于滞留时间不同，性能会发生较明显的变化。并且由于半芳香族聚酰胺熔点较高，导致其注塑温度很高，滞留时间对注塑制件性能的影响更成为一个重要课题。
本发明人通过大量实验发现，采用具有十个碳原子的二胺作为共聚组分，并通过控制树脂的pH值满足特定的要求，进一步向反应体系加入含有3个或3个以上氮原子、含仲胺基团的化合物，能够得到不同于一般聚酰胺树脂行为的聚酰胺树脂。该聚酰胺树脂具有特殊的结晶和熔融行为，能够缩短注塑产品的成型周期，同时注塑产品的表面光泽度得到提升，聚酰胺树脂及其组合物的热滞留稳定性得到提高。
发明内容
为了克服现有技术的缺点与不足，本发明的首要目的在于提供一种能够缩短注塑产品成型周期和具有改进表面性能，且能够显著改善热滞留稳定性的聚酰胺树脂。
本发明还提供一种包含上述聚酰胺树脂的聚酰胺模塑组合物。
本发明是通过以下技术方案实现的：
一种聚酰胺树脂，该聚酰胺树脂在苯酚中pH值小于7，其包含衍生自如下单体混合物的重复单元：具有两个氨基官能团的第一单体，称为单体A；具有两个羧基官能团或其前体基团的第二单体，称为单体B；和/或具有一个氨基和一个羧基官能团的第三单体和/或内酰胺，称为单体D；
其中，所述单体混合物中单体A至少含有一种具有十个碳原子的单体A10；单体B至少含有一种具有八个碳原子的非脂肪族单体B8；
其中，基于全部单体总的摩尔份数，A10和B8的含量同时满足如下α和β的关系：7.5≤α≤8.5，4.6≤β≤7，优选7.7≤α≤8，4.7≤β≤5；α和β的定义如式i和ii所示；
……………………（式i）
……………………（式ii）
其中，基于全部单体总的摩尔份数，
表示上述具有十个碳原子的单体A10的摩尔份数；
表示上述具有八个碳原子的非脂肪族单体B8的摩尔份数；
表示上述具有一个氨基和一个羧基官能团的第三单体和/或内酰胺的单体D的摩尔份数；其占全部单体总的摩尔份数含量为0≤≤50mol%；
表示上述单体A的总摩尔份数，m表示单体Am中的碳原子个数；
表示上述单体B的总摩尔份数，n表示单体Bn中的碳原子个数；
采用DSC仪器，将聚酰胺树脂样品以10oC/min的升温速率升温直至DSC谱图上出现第一个吸热峰，将此时温度记为T；取另一个样品以10oC/min的升温速率升至某一温度T+40oC，恒温3min，再以10oC/min的降温速率降至50oC、恒温3min，最后以10oC/min的升温速率升至T+40oC；以另一个样品第二次升温记录的DSC曲线为准，该聚酰胺树脂具有双熔点，其中二者熔点之差为5oC -20oC；
基于单体A的摩尔量，含有0.009mol%-5mol%的含有3个或3个以上氮原子、含仲胺基团的化合物X。
优选地，所述聚酰胺树脂在苯酚中pH值呈现：1≤pH≤6；更优选为2≤pH≤5。
所述含有3个或3个以上氮原子、含仲胺基团的化合物X选自NH(C2H4NH2)2、H2N[C2H4NH]2C2H4NH2、H2N[C2H4NH]3C2H4NH2、NH[(CH2)4NH2)2、NH[(CH2)5NH2)2、NH[(CH2)6NH2)2、NH[(CH2)7NH2)2、NH[(CH2)8NH2)2、NH[(CH2)9NH2)2、NH[(CH2)10NH2)2、NH[(CH2)11NH2)2、NH[(CH2)12NH2)2、NH[(CH2)13NH2)2、NH[(CH2)14NH2)2、NH[(CH2)15NH2)2、NH[(CH2)16NH2)2、NH[(CH2)17NH2)2、NH[(CH2)18NH2)2、H2N(H2C)10NH(CH2)5NH2、H2N(H2C)10NH(CH2)6NH2、H2N(H2C)10NH(CH2)7NH2、H2N(H2C)10NH(CH2)8NH2、H2N(H2C)10NH(CH2)9NH2、H2N(H2C)10NH(CH2)11NH2、H2N(H2C)10NH(CH2)12NH2、H2N(H2C)9NH(CH2)6CH(CH3)CH2NH2、
H2N(H2C)9NHCH2CH(CH3)(CH2)6NH2、NH[(CH2)6CH(CH3)CH2NH2]2、NH[CH2CH(CH3)(CH2)6NH2]2中的一种或几种。
优选地，基于单体A的摩尔量，所述含有3个或3个以上氮原子、含仲胺基团的化合物X的含量为0.3mol%<[X]<1.5mol%。
优选地，基于单体A的摩尔量，所述含有3个或3个以上氮原子、含仲胺基团的化合物X的含量为1.5mol%≤[X]≤5mol%。
其中，所述聚酰胺树脂在在25oC，98%的浓硫酸中测量浓度为10mg/ml的聚酰胺树脂的相对粘度大于1.85。
所述单体A中区别于A10的具有两个氨基官能团的第一单体包括但不仅限于1，4-丁二胺、1，5-戊二胺、1,6-己二胺、1，8-辛二胺(OMDA)、1，9-壬二胺(NMDA)、2-甲基-1，8-辛二胺(MODA)、1，11-十一烷二胺、2-丁基-2-乙基-1，5-戊二胺、1，12-十二烷二胺、1，13-十三烷二胺、1，14-十四烷二胺、1，16-十六烷二胺、1，18-十八烷二胺、环己二胺、1，3-双(端胺基甲基)环己烷(BAC)、异佛尔酮二胺、降莰烷二甲胺、4，4’-二端胺基二环己基甲烷(PACM)、2，2-(4，4’-二端胺基二环己基)丙烷(PACP)、和3，3’-二甲基-4，4’-二端胺基二环己基甲烷(MACM)、及其组合。
所述单体B8包括但不仅限于对苯二甲酸、间苯二甲酸、1,4-环己烷二甲酸、顺式和/或反式环己烷-1，3-二羧酸(CHDA)、及其组合；区别于B8的具有两个羧基官能团或其前体基团的第二单体包括但不仅限于丁二酸、戊二酸、己二酸、辛二酸、壬二酸、癸二酸、十一烷二酸、十二烷二酸、十三烷二酸、十四烷二酸、十五烷二酸、十六烷二酸、十八烷二酸、二聚体酸、及其组合。
所述单体A10优选1，10-癸二胺，所述单体B8优选对苯二甲酸和/或1，4-环己烷二甲酸。
所述具有一个氨基和一个羧基官能团的第三单体和/或内酰胺包括但不仅限于己内酰胺CL、α，ω-氨基己酸、α，ω-氨基壬酸、α，ω-氨基十一酸AUA、月桂内酰胺LL、ω-氨基十二酸ADA、及其组合。
一种聚酰胺模塑组合物，包括以下组成：
a、30wt%-99.9wt%的上述聚酰胺树脂；
b、含量为x的增强材料和/或填料；其中，x=0-70wt%；
c、含量为y的添加剂和/或其它聚合物；其中，y=0-70wt%；
其中，a、b、c三种组分的重量百分比之和为100wt%。
优选地，一种聚酰胺模塑组合物，包括以下组成：
a、30wt%-97wt%的聚酰胺树脂；
b、含量为x的增强填料；其中，x=1wt%-66wt%；
c、含量为y的添加剂和/或其它聚合物；其中，y=0.1wt%-64wt%；
其中，a、b、c三种组分的重量百分数之和为100wt%。所述组分b的含量x进一步优选为10wt%-50wt%，更优选为15wt%-40wt%；
增强填料含量过低，导致聚酰胺组合物力学性能较差；增强填料含量过高，聚酰胺组合物制品表面浮纤严重，影响产品外观。
所述增强填料的形状为纤维状，其平均长度为0.01mm-20mm，优选为0.1mm-6mm；其长径比为5:1-2000:1，优选为30:1-600:1，当纤维状的增强填料含量在上述范围内时，聚酰胺组合物就会表现出高热变形温度和增高的高温刚性。
所述增强填料为无机增强填料或有机增强填料；
所述无机增强填料选自玻璃纤维、钛酸钾纤维、金属包层的玻璃纤维、陶瓷纤维、硅灰石纤维、金属碳化物纤维、金属固化纤维、石棉纤维、氧化铝纤维、碳化硅纤维、石膏纤维或硼纤维的一种或几种，优选为玻璃纤维；
使用玻璃纤维不仅可提高聚酰胺组合物的可模塑性，而且可提高力学性能例如拉伸强度、弯曲强度和弯曲模量，及提高耐热性例如热塑性树脂组合物进行模塑时的热变形温度。
所述有机增强填料选自芳族聚酰胺纤维和/或碳纤维。
所述增强填料的形状为非纤维状，例如粉末状、颗粒状、板状、针状、织物或毡状，其平均粒径为0.001μm-100μm，优选为0.01μm-50μm。
当增强填料的平均粒径小于0.001μm将导致聚酰胺树脂差的熔融加工性；当增强填料的平均粒径大于100μm，将导致不良的注塑成型品表面外观。
上述增强填料的平均粒径通过吸附法来测定，其可选自钛酸钾晶须、氧化锌晶须、硼酸铝晶须、硅灰石、沸石、绢云母、高岭土、云母、滑石、粘土、叶腊石、膨润土、蒙脱土、锂蒙脱土、合成云母、石棉、硅铝酸盐、氧化铝、氧化硅、氧化镁、氧化锆、氧化钛、氧化铁、碳酸钙、碳酸镁、白云石、硫酸钙、硫酸钡、氢氧化镁、氢氧化钙、氢氧化铝、玻璃珠、陶瓷珠、氮化硼、碳化硅或二氧化硅的一种或几种。
这些增强填料可以是中空的；此外，对于膨润土、蒙脱土、锂蒙脱土、合成云母等溶胀性层状硅酸盐，可以使用采用有机铵盐将层间离子进行阳离子交换后的有机化蒙脱土。
为了使聚酰胺组合物获得更为优良的机械性能，可采用偶联剂对无机增强填料进行功能性处理。
其中偶联剂选自异氰酸酯系化合物、有机硅烷系化合物、有机钛酸酯系化合物、有机硼烷系化合物、环氧化合物；优选为有机硅烷系化合物；
其中，所述有机硅烷系化合物选自含有环氧基的烷氧基硅烷化合物、含有巯基的烷氧基硅烷化合物、含有脲基的烷氧基硅烷化合物、含有异氰酸酯基的烷氧基硅烷化合物、含有端胺基的烷氧基硅烷化合物、含有羟基的烷氧基硅烷化合物、含有碳-碳不饱和基的烷氧基硅烷化合物、含有酸酐基的烷氧基硅烷化合物的一种或几种。
所述含有环氧基的烷氧基硅烷化合物选自γ-环氧丙氧基丙基三甲氧基硅烷、γ-环氧丙氧基丙基三乙氧基硅烷、β-(3，4-环氧环己基)乙基三甲氧基硅烷的一种或几种；
所述含有巯基的烷氧基硅烷化合物选自γ-巯基丙基三甲氧基硅烷和/或γ-巯基丙基三乙氧基硅烷；
所述含有脲基的烷氧基硅烷化合物选自γ-脲基丙基三乙氧基硅烷、γ-脲基丙基三甲氧基硅烷、γ-(2-脲基乙基)端胺基丙基三甲氧基硅烷的一种或几种；
所述含有异氰酸酯基的烷氧基硅烷化合物选自γ-异氰酸酯基丙基三乙氧基硅烷、γ-异氰酸酯基丙基三甲氧基硅烷、γ-异氰酸酯基丙基甲基二甲氧基硅烷、γ-异氰酸酯基丙基甲基二乙氧基硅烷、γ-异氰酸酯基丙基乙基二甲氧基硅烷、γ-异氰酸酯基丙基乙基二乙氧基硅烷、γ-异氰酸酯基丙基三氯硅烷的一种或几种；
所述含有端胺基的烷氧基硅烷化合物选自γ-(2-端胺基乙基)端胺基丙基甲基二甲氧基硅烷、γ-(2-端胺基乙基)端胺基丙基三甲氧基硅烷、γ-端胺基丙基三甲氧基硅烷的一种或几种；
所述含有羟基的烷氧基硅烷化合物选自γ-羟基丙基三甲氧基硅烷和/或γ-羟基丙基三乙氧基硅烷；
所述含有碳-碳不饱和基的烷氧基硅烷化合物选自γ-甲基丙烯酰氧基丙基三甲氧基硅烷、乙烯基三甲氧基硅烷、N-β-(N-乙烯基苄基端胺基乙基)-γ-端胺基丙基三甲氧基硅烷•盐酸盐的一种或几种；
所述含有酸酐基的烷氧基硅烷化合物选自3-三甲氧基甲硅烷基丙基琥珀酸酐；
所述有机硅烷系化合物优选为γ-甲基丙烯酰氧基丙基三甲氧基硅烷、γ-(2-端胺基乙基)端胺基丙基甲基二甲氧基硅烷、γ-(2-端胺基乙基)端胺基丙基三甲氧基硅烷、γ-端胺基丙基三甲氧基硅烷或3-三甲氧基甲硅烷基丙基琥珀酸酐。
可以按照常规的方法采用上述有机硅烷系化合物对无机增强填料进行表面处理，然后再将其与聚酰胺树脂进行熔融混炼，以制备所述聚酰胺组合物。
也可以直接在无机增强填料与聚酰胺树脂熔融混炼的同时，加入有机硅烷系化合物进行原位共混。
其中，所述偶联剂的用量为相对于无机增强填料重量的0.05wt%-10wt%，优选为0.1wt%-5wt%。
当偶联剂的用量小于0.05wt%时，其达不到明显的改良机械性能的效果；当偶联剂的用量大于10wt%时，无机增强填料容易发生凝聚，并且在聚酰胺树脂中分散不良的风险，最终导致机械性能发生下降。
所述添加剂选自阻燃剂、冲击改性剂、其它聚合物、加工助剂的一种或几种；所述其它聚合物优选为脂肪族聚酰胺、聚烯烃均聚物、乙烯-α-烯烃共聚物、乙烯-丙烯酸酯共聚物的一种或几种；所述加工助剂选自抗氧化剂、耐热稳定剂、耐候剂、脱模剂、润滑剂、颜料、染料、增塑剂、抗静电剂的一种或几种。
所述阻燃剂为阻燃剂或阻燃剂与阻燃协助剂的组合物，基于聚酰胺模塑组合物总重量，其含量优选为10wt%-40wt%；阻燃剂含量过低导致阻燃效果变差，阻燃剂含量过高导致材料力学性能下降。
所述阻燃剂为卤系阻燃剂或无卤阻燃剂；
所述卤系阻燃剂选自溴化聚苯乙烯、溴化聚苯醚、溴化双酚A型环氧树脂、溴化苯乙烯-马来酸酐共聚物、溴化环氧树脂、溴化苯氧基树脂、十溴二苯醚、十溴代联苯、溴化聚碳酸酯、全溴三环十五烷或溴化芳香族交联聚合物的一种或几种，优选为优选溴化聚苯乙烯；
所述无卤阻燃剂选自含氮阻燃剂、含磷阻燃剂或含氮和磷的阻燃剂的一种或几种；优选为含磷阻燃剂。
所述含磷阻燃剂选自单磷酸芳基磷酸酯、双磷酸芳基磷酸酯、烷基膦酸二甲酯、磷酸三苯酯、磷酸三甲苯酯、磷酸三(二甲苯)酯、丙苯系磷酸酯、丁苯系磷酸酯或次膦酸盐的一种或几种；优选为次膦酸盐；
次膦酸盐化合物以例如下式I和/或II表示的化合物为代表。
在式I及式II中，R1及R2可以相同，也可以不同，分别表示直链状或分支状的C1-C6-烷基、芳基或苯基。R3表示直链状或分支状的C1-C10-亚烷基、C6-C10-亚芳基、C6-C10-烷基亚芳基、C6-C10-芳基亚烷基。M表示钙原子、镁原子、铝原子和/或锌原子。m是2或3，n是1或3，x是1或2。
次膦酸盐化合物的更具体例子包括二甲基次膦酸钙、二甲基次膦酸镁、二甲基次膦酸铝、二甲基次膦酸锌、乙基甲基次膦酸钙、乙基甲基次膦酸镁、乙基甲基次膦酸铝、乙基甲基次膦酸锌、二乙基次膦酸钙、二乙基次膦酸镁、二乙基次膦酸铝、二乙基次膦酸锌、甲基正丙基次膦酸钙、甲基正丙基次膦酸镁、甲基正丙基次膦酸铝、甲基正丙基次膦酸锌、甲烧二 (甲基次膦酸）钙、甲烷二（甲基次膦酸）镁、甲烷二（甲基次膦酸）铝、甲烷二（甲基次膦酸）锌、苯-1，4-( 二甲基次膦酸）钙、苯-1，4-( 二甲基次膦酸）镁、苯-1，4-( 二甲基次膦酸）铝、苯-1，4-( 二甲基次膦酸）锌、甲基苯基次膦酸钙、甲基苯基次膦酸镁、甲基苯基次膦酸铝、甲基苯基次膦酸锌、二苯基次膦酸钙、二苯基次膦酸镁、二苯基次膦酸铝、二苯基次膦酸锌等，优选二甲基次膦酸钙、二甲基次膦酸铝、二甲基次膦酸锌、乙基甲基次膦酸 I丐、乙基甲基次膦酸铝、乙基甲基次膦酸锌、二乙基次膦酸钙、二乙基次膦酸铝、二乙基次膦酸锌，更优选二乙基次膦酸铝。
作为阻燃剂的次膦酸盐化合物可容易地从市场获得。可从市场获得的次膦酸盐化合物的例子包括科莱恩公司（Clariant）制造的EXOLIT OP1230、OP1311、OP1312、OP930、OP935等。
本发明的包含上述聚酰胺树脂的聚酰胺组合物，基于聚酰胺模塑组合物的总重量，所述添加剂组分还可以包含至多45wt%的一种或更多种冲击改性剂，优选为5wt%-30wt%。
其中，所述冲击改性剂可以是天然橡胶、聚丁二烯、聚异戊二烯、聚异丁烯、丁二烯和/或异戊二烯与苯乙烯或与苯乙烯衍生物和与其它共聚单体的共聚物、氢化共聚物、和/或通过接枝或与酐、（甲基）丙烯酸或其酯共聚而制得的共聚物；所述冲击改性剂还可以是具有交联弹性体芯的接枝橡胶，所述交联弹性体芯由丁二烯、异戊二烯或烷基丙烯酸酯构成，并且具有由聚苯乙烯构成的接枝壳或者可以是非极性或极性烯烃均聚物或共聚物，例如乙丙橡胶，乙烯-丙烯-二烯烃橡胶，或乙烯-辛烯橡胶，或乙烯-乙酸乙烯酯橡胶，或通过接枝或与酐、（甲基）丙烯酸或其酯共聚而得到的非极性或极性烯烃均聚物或共聚物；所述冲击改性剂还可以是羧酸官能化的共聚物，例如聚（乙烯-共-（甲基）丙烯酸）或聚（乙烯-1-烯烃-共-（甲基）丙烯酸），其中1-烯烃是链烯烃或者具有多于4个原子的不饱和（甲基）丙烯酸酯，包括酸基团被金属离子中和到一定程度的那些共聚物。
基于苯乙烯单体（苯乙烯和苯乙烯衍生物）和其它乙烯基芳族单体的冲击改性剂，是由链烯基芳族化合物和共轭二烯烃构成的嵌段共聚物，和由链烯基芳族化合物和共轭二烯烃构成的氢化嵌段共聚物，和这些类型冲击改性剂的组合。所述嵌段共聚物包含至少一种衍生自链烯基芳族化合物的嵌段a和至少一种衍生自共轭二烯烃的嵌段b。在氢化嵌段共聚物的情况下，脂肪族不饱和碳-碳双键的比例通过氢化而降低。合适的嵌段共聚物是具有直链结构的二、三、四和多嵌段共聚物。但是，根据本发明也可以使用支化和星形结构。以已知方式获得支化嵌段共聚物，例如通过聚合物“侧支链”到聚合物主链的接枝反应。
可以与苯乙烯一起使用或以与苯乙烯的混合物形式使用的其它链烯基芳族化合物是在芳环和/或在C＝C双键上被C1～20烃基或被卤原子取代的乙烯基芳族单体。
链烯基芳族单体的实例是苯乙烯、对甲基苯乙烯、α-甲基苯乙烯、乙基苯乙烯、叔丁基苯乙烯、乙烯基甲苯、1，2-二苯基乙烯、1，1-二苯基乙烯、乙烯基二甲苯、乙烯基甲苯、乙烯基萘、二乙烯基苯、溴代苯乙烯、和氯代苯乙烯、及其组合。优选苯乙烯、对甲基苯乙烯、α-甲基苯乙烯、和乙烯基萘。
优选使用苯乙烯、α-甲基苯乙烯、对甲基苯乙烯、乙基苯乙烯、叔丁基苯乙烯、乙烯基甲苯、1，2-二苯基乙烯、1，1-二苯基乙烯、或这些物质的混合物。特别优选的是使用苯乙烯。但是，也可以使用链烯基萘。
可以使用的二烯烃单体的实例是1，3-丁二烯、2-甲基-1，3-丁二烯、2，3-二甲基-1，3-丁二烯、1，3-戊二烯、1，3-己二烯、异戊二烯、氯丁二烯和间戊二烯。优选1，3-丁二烯和异戊二烯，尤其是1，3-丁二烯(下文中以缩写形式丁二烯表示)。
所使用的链烯基芳族单体优选包括苯乙烯，所使用的二烯烃单体优选包括丁二烯，这意味着优选苯乙烯-丁二烯嵌段共聚物。所述嵌段共聚物通常通过阴离子聚合以其本身已知的方式制备。
除了苯乙烯单体和二烯烃单体以外，还可以同时使用其它另外的单体。基于所使用单体的总量，共聚单体的比例优选为0-50wt%，特别优选为0-30wt%，特别优选为0-15wt%。合适的共聚单体的实例分别是丙烯酸酯，尤其是丙烯酸C1～C12烷基酯，例如丙烯酸正丁酯或丙烯酸2-乙基己酯，和甲基丙烯酸酯，尤其是甲基丙烯酸C1～C12烷基酯，例如甲基丙烯酸甲酯（MMA）。其它可能的共聚单体是（甲基）丙烯腈、（甲基）丙烯酸缩水甘油酯、乙烯基甲基醚、二元醇的二烯丙基和二乙烯基醚、二乙烯基苯和乙酸乙烯酯。
除了共轭二烯烃之外，如果合适的话，氢化嵌段共聚物还包含低级烃部分，例如乙烯、丙烯、1-丁烯、二环戊二烯或非共轭二烯烃。源于嵌段b的未还原的脂肪族不饱和键在氢化嵌段共聚物中的比例小于50%，优选小于25%，尤其是小于10%。衍生自嵌段a的芳族部分还原到至多25%的程度。通过苯乙烯-丁二烯共聚物的氢化和苯乙烯-丁二烯-苯乙烯共聚物的氢化，得到氢化嵌段共聚物，即苯乙烯-（乙烯-丁烯）双嵌段共聚物和苯乙烯-（乙烯-丁烯）-苯乙烯三嵌段共聚物。
嵌段共聚物优选包含20wt%-90wt%的嵌段a、尤其是50wt%-85wt%的嵌段a。二烯烃可以以1，2-取向或1，4-取向引入到嵌段b中。
嵌段共聚物的摩尔质量为5000g/mol-500000g/mol，优选20000g/mol-300000g/mol，特别是40000g/mol-200000g/mol。
合适的氢化嵌段共聚物是可以从市场上购得的产品，例如(Kraton聚合物)G1650、G1651和G1652，以及(Asahi Chemicals)H1041、H1043、H1052、H1062、H1141和H1272。
非氢化嵌段共聚物的实例是聚苯乙烯-聚丁二烯、聚苯乙烯-聚（乙烯-丙烯）、聚苯乙烯-聚异戊二烯、聚（α-甲基苯乙烯）-聚丁二烯、聚苯乙烯-聚丁二烯-聚苯乙烯（SBS）、聚苯乙烯-聚（乙烯-丙烯）-聚苯乙烯、聚苯乙烯-聚异戊二烯-聚苯乙烯、和聚（α-甲基苯乙烯）聚丁二烯-聚（α-甲基苯乙烯）、及其组合。
可以从市场上购得的合适的非氢化嵌段共聚物有商标为（Phillips）、（Shell）、（Dexco）和（Kuraray）的多种产品。
本发明的包含上述聚酰胺树脂的聚酰胺组合物，所述添加剂组分还可以包含其它聚合物，所述其它聚合物选自脂肪族聚酰胺、聚烯烃均聚物或乙烯-α-烯烃共聚物、乙烯-丙烯酸酯共聚物。
所述脂肪族聚酰胺包括但不仅限于源自4-20个碳原子的脂肪族二酸和脂肪族二胺，或者4-20个碳原子的内酰胺，或者4-20个碳原子的脂肪族二酸、脂肪族二胺和内酰胺的聚合物中的一种或多种。包括但不仅限于，聚己二酰己二胺（PA66）、聚己内酰胺（PA6）、聚癸二酰己二胺（PA610）、聚癸二酰癸二胺（PA1010）、己二酸－己二胺－己内酰胺共聚物（PA66/6）、聚十一内酰胺（PA11）、聚十二内酰胺（PA12），及其两种或多种的混合物。
所述乙烯-α-烯烃共聚物优选EP弹性体和/或EPDM弹性体（分别是乙烯-丙烯橡胶和乙烯-丙烯-二烯烃橡胶）。例如，弹性体可以包括基于含有20wt%-96wt%、优选25wt%-85wt%乙烯的乙烯-C3-C12-α-烯烃共聚物的弹性体，其中此处特别优选的是C3-C12-α-烯烃包括选自丙烯、1-丁烯、1-戊烯、1-己烯、1-辛烯、1-癸烯和/或1-十二烯的烯烃，特别优选其它聚合物包括乙烯-丙烯橡胶、LLDPE、VLDPE的一种或几种。
作为替代地或附加地（例如在混合物中），所述其它聚合物还可以包含基于乙烯-C3-C12-α-烯烃和非共轭二烯烃的三元共聚物，此处优选的是其含有25wt%-85wt%乙烯和至多最大量为10wt%的非共轭二烯烃，此处特别优选C3-C12-α-烯烃包括选自丙烯、1-丁烯、1-戊烯、1-己烯、1-辛烯、1-癸烯和/或1-十二烯的烯烃，和/或其中非共轭二烯烃优选地选自二环[2.2.1]庚二烯、1，4-己二烯、双环戊二烯和/或尤其是5-亚乙基降冰片烯。
乙烯-丙烯酸酯共聚物也可以用作所述其它聚合物的成分。
所述其它聚合物的其它可能形式分别是乙烯-丁烯共聚物和包含这些体系的混合物（共混物）。
优选地，所述其它聚合物包含具有酐基团的成分，这些通过主链聚合物与不饱和二酸酐、与不饱和二羧酸、或与不饱和二羧酸的单烷基酯的热反应或自由基反应，以足以与聚酰胺良好结合的浓度引入，并且此处优选的是使用选自以下的试剂：
马来酸、马来酸酐、马来酸单丁酯、富马酸、乌头酸和/或衣康酸酐。优选0.1wt%-4.0wt%的不饱和酸酐接枝到作为C的成分的抗冲击组分上，或者不饱和二酸酐或其前体通过与其它不饱和单体一起接枝来施加。通常优选接枝度为0.1%-1.0%，特别优选为0.3%-0.7%。其它聚合物的另一可能成分是由乙烯-丙烯共聚物和乙烯-丁烯共聚物构成的混合物，此处马来酸酐接枝度（MA接枝度）为0.3%-0.7%。
用于该其它聚合物的上述可能体系还可以以混合物的形式使用。
此外，所述添加剂组分可以包含具有官能团的组分，所述官能团例如为羧酸基团、酯基团、环氧基团、噁唑啉基团、碳二亚胺基团、异氰酸酯基团、硅烷醇基团、和羧酸酯基团，或者所述添加剂组分可以包含上述官能团中的两种或更多种的组合。具有所述官能团的单体可以通过共聚或接枝到弹性体聚烯烃上来结合。
此外，基于烯烃聚合物的冲击改性剂还可以通过用不饱和硅烷化合物接枝来改性，所述不饱和硅烷化合物例如为乙烯基三甲氧基硅烷、乙烯基三乙氧基硅烷、乙烯基三乙酰基硅烷、甲基丙烯酰氧基丙基三甲氧基硅烷、或丙烯基三甲氧基硅烷。
弹性体聚烯烃是具有直链、支链或核壳结构的无规、交替或嵌段共聚物，并含有可以与聚酰胺的端基反应的官能团，由此在聚酰胺和冲击改性剂之间提供足够的可相容性。
因此，本发明的冲击改性剂包括烯烃（例如乙烯、丙烯、1-丁烯）的均聚物或共聚物，或者烯烃和可共聚单体（例如乙酸乙烯酯、（甲基）丙烯酸酯、和甲基己二烯）的共聚物。
结晶性烯烃聚合物的实例是低密度、中密度和高密度聚乙烯、聚丙烯、聚丁二烯、聚-4-甲基戊烯、乙烯-丙烯嵌段共聚物、或乙烯-丙烯无规共聚物、乙烯-甲基己二烯共聚物、丙烯-甲基己二烯共聚物、乙烯-丙烯-丁烯共聚物、乙烯-丙烯-己烯共聚物、乙烯-丙烯-甲基己二烯共聚物、聚（乙烯-乙酸乙烯酯）（EVA）、聚（乙烯-丙烯酸乙酯）（EEA）、乙烯-辛烯共聚物、乙烯-丁烯共聚物、乙烯-己烯共聚物、乙烯-丙烯-二烯烃三元共聚物、以及上述聚合物的组合。
可以用于所述添加剂组分的可市购的冲击改性剂实例有：
TAFMER MC201：g-MA(-0.6%)67%EP共聚物(20mol%丙烯)+33%EB共聚物(15mol%1-丁烯))的共混物：Mitsui Chemicals，日本。
TAFMER MH5010：g-MA(-0.6%)乙烯-丁烯共聚物；Mitsui。
TAFMER MH7010：g-MA(-0.7%)乙烯-丁烯共聚物；Mitsui。
TAFMER MH7020：g-MA(-0.7%)EP共聚物；Mitsui。
EXXELOR VA1801：g-MA(-0.7%)EP共聚物；Exxon Mobile Chemicals，US。
EXXELOR VA1803：g-MA(0.5-0.9%)EP共聚物，无定形，Exxon。
EXXELOR VA1810：g-MA(-0.5%)EP共聚物，Exxon。
EXXELOR MDEX 941l：g-MA(0.7%)EPDM，Exxon。
FUSABOND MN493D：g-MA(-0.5%)乙烯-辛烯共聚物，DuPont，US。
FUSABOND A EB560D：(g-MA)乙烯-丙烯酸正丁酯共聚物，DuPont ELVALOY，DuPont。
还优选为离子聚合物，其中聚合物键合的羧基通过金属离子全部相互键合或键合到一定程度。
特别优选马来酸酐接枝官能化的丁二烯与苯乙烯的共聚物、通过与马来酸酐接枝制得的非极性或极性烯烃均聚物和共聚物、以及羧酸官能化的共聚物，例如聚(乙烯-共(甲基)丙烯酸)或聚（乙烯-共-1-烯烃-共-（甲基）丙烯酸），其中所述酸基团已在一定程度上被金属离子中和。
此外，在不破坏本发明效果的范围内，可以在任意时刻在本发明的聚酰胺树脂中添加各种加工助剂，例如抗氧化剂和/或耐热稳定剂（受阻酚系、氢醌系、亚磷酸酯系以及它们的取代体、卤化铜、碘化合物等）、耐候剂（间苯二酚系、水杨酸酯系、苯并三唑系、二苯甲酮系、受阻胺系等）、脱模剂和润滑剂（脂肪族醇、脂肪族酰胺、脂肪族双酰胺、二脲和聚乙烯蜡等）、颜料（硫化镉、酞菁、炭黑等）、染料（尼格洛辛、苯胺黑等）、增塑剂（对羟基苯甲酸辛酯、N-丁基苯磺酰胺等）、抗静电剂（烷基硫酸盐型阴离子系抗静电剂、季铵盐型阳离子系抗静电剂、聚氧乙烯失水山梨糖醇单硬脂酸酯等非离子系抗静电剂、甜菜碱系两性抗静电剂等）。
为了获得本发明的成型品，可以将本发明的聚酰胺树脂或聚酰胺树脂组合物通过注射成型、挤出成型、吹塑成型、真空成型、熔融纺丝、膜成型等任意成型方法来成型。可以将这些成型品成型成所需形状，并可以在汽车部件、机械部件等的树脂成型品等中使用。作为具体的用途，在下列用途中是有用的：汽车发动机冷却水系部件、特别是散热器水箱的顶部和底部等散热器水箱部件、冷却液储备箱、水管、水泵壳、水泵叶轮、阀等水泵部件等在汽车发动机房内与冷却水接触下使用的部件，以开关类、超小型滑动开关、DIP开关、开关的外壳、灯座、捆扎带、连接器、连接器的外壳、连接器的壳、IC插座类、绕线轴、线轴罩、继电器、继电器箱、电容器壳体、马达的内部部件、小型马达壳体、齿轮凸轮、均衡轮、垫片、绝缘体、紧固件、扣、线夹、自行车车轮、小脚轮、安全帽、端子台、电动工具的外壳、起动器的绝缘部分、阻流板、罐、散热器水箱、腔罐（Chamber tank）、贮液罐、保险丝盒、空气净化器壳体、空调风扇、端子的外壳、轮罩、吸排气管、轴承承托、气缸头盖、进气歧管、水管叶轮（waterpipeimpeller）、离合器分离杆、扬声器振动板、耐热容器、微波炉部件、电饭煲部件、打印机色带导向器等为代表的电气/电子相关部件，汽车/车辆相关部件、家电/办公电器部件、计算机相关部件、传真机/复印机相关部件、机械相关部件、其它各种用途。
实施方式
聚酰胺树脂相对粘度的测试方法：参照GB12006.1-89，聚酰胺粘数测定方法；具体测试方法为：在25±0.01oC的98%的浓硫酸中测量浓度为10mg/ml的聚酰胺的相对粘度ηr；
聚酰胺的熔点的测试方法：参照ASTM D3418-2003，Standard Test Method forTransition Temperatures of Polymers By Differential Scanning Calorimetry；具体测试方法是：采用Perkin Elmer Dimond DSC分析仪测试样品的熔点；氮气气氛，流速为40mL/min；测试时先将聚酰胺树脂样品以10oC/min的升温速率升温直至DSC谱图上出现第一个吸热峰，将此时温度记为T；取另一个样品以10oC/min的升温速率升至某一温度T+40oC，恒温3min，再以10oC/min的降温速率降至50oC、恒温3min，最后10oC/min的升温速率升至T+40oC；以第二次升温记录的DSC曲线为准，该聚酰胺树脂具有双熔点，较高熔点记为Tm1，较低熔点记为Tm2。
聚酰胺树脂的pH测定：取0.5000g聚酰胺树脂，加苯酚50mL，加热回流后冷至室温，使用非水电极测试其pH值。
表面光泽度的测试方法：
表面光泽度按照GB8807-1988《塑料镜面光泽试验方法》进行测试，测试角度为60o。测试制件尺寸为100mm×100mm×3.2mm。
成型周期的测试方法：
成型周期，是指注塑机完成一个塑件所需的全部时间。注塑温度高于熔点30oC，取注塑5个测试表面光泽度的制件，注塑成型时间的平均值。
拉伸强度：根据ISO 527-2测定，测试条件为23oC和10mm/min。其中，注塑用样条是在注塑机腔体中高于熔点20oC滞留10min以内得到的。
拉伸强度（热滞留）：根据ISO 527-2测定，测试条件为23oC和10mm/min。其中，注塑用样条是在注塑机腔体中高于熔点20oC保持20min的物料注塑得到样条的测试结果。
拉伸强度保持率：拉伸强度保持率=拉伸强度（热滞留）/拉伸强度×100%。
断裂伸长率：根据ISO 527-2测定，测试条件为23oC和10mm/min；
缺口冲击强度：根据ISO 180/1A测定，测试条件为23oC，缺口类型为A型。
实施例1-12和对比例1-10
熔点低于280oC的聚酰胺树脂的合成：
在配有磁力偶合搅拌、冷凝管、气相口、加料口、压力防爆口的压力釜中按表格中的比例加入反应原料；再加入次磷酸钠、苯甲酸和去离子水；次磷酸钠重量为除去离子水外其他投料重量的1‰-5‰，苯甲酸物质的量为二酸总物质的量的2%-4%，去离子水重量为总投料重量的25%-30%。抽真空充入高纯氮气作为保护气，开始反应。将反应混合物升温至290oC-310oC搅拌3小时-5小时，然后打开阀门慢慢泄压，同时保持温度不变；压力泄至常压后，开始抽真空；抽真空至30Pa-100Pa，保持反应温度；根据搅拌桨功率的变化判断反应终点；反应结束后，停止抽真空，冲入氮气至0.2MPa；将熔融物料通过模头压出，经水槽冷却、风冷、切粒后，得到聚酰胺树脂。聚酰胺树脂的熔点等性能指标列于表1-2中。
熔点高于280oC的聚酰胺树脂的合成：
在配有磁力偶合搅拌、冷凝管、气相口、加料口、压力防爆口的压力釜中按表格中的比例加入反应原料；再加入次磷酸钠、苯甲酸和去离子水。次磷酸钠重量为除去离子水外其他投料重量的1‰-5‰，苯甲酸物质的量为二酸总物质的量的2%-4%，去离子水重量为总投料重量的25%-30%。抽真空充入高纯氮气作为保护气，开始反应。将反应混合物升温至200oC-220oC搅拌1小时-3小时，然后在搅拌下使反应物的温度升高到230oC-240oC；反应在230oC-240oC的恒温和2.2MPa-2.8MPa的恒压下继续进行2小时-4小时，通过移去所形成的水而保持压力恒定，反应完成后打开阀门出料，得到预聚物。预聚物于80℃下真空干燥24小时后，在230oC-260oC、50Pa-1000Pa真空条件下固相增粘10小时-20小时，得到聚酰胺树脂。聚酰胺树脂的熔点等性能指标列于表1-2中。
表1
表2
由实施例和对比例可以看出，由于实施例聚酰胺树脂具有特定含量的含有3个或3个以上氮原子、含仲胺基团的化合物X、特定pH值和具有双熔点，相对于对比例，实施例聚酰胺树脂的成型品普遍具有较高的表面光泽度和较短的成型周期。
实施例13-26及对比例11-15：聚酰胺模塑组合物的制备
按表3的配方将聚酰胺树脂、阻燃剂、其他助剂在高混机中混合均匀后，通过主喂料口加入双螺杆挤出机中，增强填料通过侧喂料秤侧喂，挤出，过水冷却，造粒并干燥后得到所述聚酰胺模塑组合物。
表3下表中配方均为重量份
从表3可以看出，由于采用了具有双熔点、特定pH值和特定含量的含有3个或3个以上氮原子、含仲胺基团的化合物X的聚酰胺树脂，实施例聚酰胺模塑组合物的表面光泽度和成型周期相对于对比例都具有明显优势。并且，热滞留拉伸强度变化较小，拉伸强度保持率较高。
Claims (24)
1.一种聚酰胺树脂，该聚酰胺树脂在苯酚中pH值小于7，其包含衍生自如下单体混合物的重复单元：具有两个氨基官能团的第一单体，称为单体A；具有两个羧基官能团或其前体基团的第二单体，称为单体B；和/或具有一个氨基和一个羧基官能团的第三单体和/或内酰胺，称为单体D；
其中，所述单体混合物中单体A至少含有一种具有十个碳原子的单体A10；单体B至少含有一种具有八个碳原子的非脂肪族单体B8；
其中，基于全部单体总的摩尔份数，A10和B8的含量同时满足如下α和β的关系：7.5≤α≤8.5，4.6≤β≤7；α和β的定义如式i和ii所示；
……………………（式i）
……………………（式ii）
其中，基于全部单体总的摩尔份数，
表示上述具有十个碳原子的单体A10的摩尔份数；
表示上述具有八个碳原子的非脂肪族单体B8的摩尔份数；
表示上述具有一个氨基和一个羧基官能团的第三单体和/或内酰胺的单体D的摩尔份数；其占全部单体总的摩尔份数含量为0≤≤50mol%；
表示上述单体A的总摩尔份数，m表示单体Am中的碳原子个数；
表示上述单体B的总摩尔份数，n表示单体Bn中的碳原子个数；
采用DSC仪器，将聚酰胺树脂样品以10oC/min的升温速率升温直至DSC谱图上出现第一个吸热峰，将此时温度记为T；取另一个样品以10oC/min的升温速率升至某一温度T+40oC，恒温3min，再以10oC/min的降温速率降至50oC、恒温3min，最后以10oC/min的升温速率升至T+40oC；以另一个样品第二次升温记录的DSC曲线为准，该聚酰胺树脂具有双熔点，其中二者熔点之差为5oC -20oC；
基于单体A的摩尔量，含有0.009mol%-5mol%的含有3个或3个以上氮原子、含仲胺基团的化合物X；
所述聚酰胺树脂在苯酚中pH值呈现2≤pH≤5；
基于单体A的摩尔量，所述含有3个或3个以上氮原子、含仲胺基团的化合物X的含量为1.5mol%≤[X]≤5mol%。
2.根据权利要求1所述的聚酰胺树脂，其特征在于，基于全部单体总的摩尔份数，A10和B8的含量同时满足如下α和β的关系：7.7≤α≤8，4.7≤β≤5。
3.根据权利要求1所述的聚酰胺树脂，其特征在于：所述含有3个或3个以上氮原子、含仲胺基团的化合物X选自NH(C2H4NH2)2、H2N[C2H4NH]2C2H4NH2、H2N[C2H4NH]3C2H4NH2、NH[(CH2)4NH2)2、NH[(CH2)5NH2)2、NH[(CH2)6NH2)2、NH[(CH2)7NH2)2、NH[(CH2)8NH2)2、NH[(CH2)9NH2)2、NH[(CH2)10NH2)2、NH[(CH2)11NH2)2、NH[(CH2)12NH2)2、NH[(CH2)13NH2)2、NH[(CH2)14NH2)2、NH[(CH2)15NH2)2、NH[(CH2)16NH2)2、NH[(CH2)17NH2)2、NH[(CH2)18NH2)2、H2N(H2C)10NH(CH2)5NH2、H2N(H2C)10NH(CH2)6NH2、H2N(H2C)10NH(CH2)7NH2、H2N(H2C)10NH(CH2)8NH2、H2N(H2C)10NH(CH2)9NH2、H2N(H2C)10NH(CH2)11NH2、H2N(H2C)10NH(CH2)12NH2、H2N(H2C)9NH(CH2)6CH(CH3)CH2NH2、
H2N(H2C)9NHCH2CH(CH3)(CH2)6NH2、NH[(CH2)6CH(CH3)CH2NH2]2、NH[CH2CH(CH3)(CH2)6NH2]2中的一种或几种。
4.根据权利要求1至3中任一项权利要求所述的聚酰胺树脂，其特征在于：基于单体A的摩尔量，所述含有3个或3个以上氮原子、含仲胺基团的化合物X的含量为0.3mol%<[X]<1.5mol%。
5.根据权利要求1或2所述的聚酰胺树脂，其特征在于：所述聚酰胺树脂在在25oC，98%的浓硫酸中测量浓度为10mg/ml的聚酰胺树脂的相对粘度大于1.85。
6.根据权利要求1所述的聚酰胺树脂，其特征在于，所述单体A中区别于A10的具有两个氨基官能团的第一单体包括但不仅限于1，4-丁二胺、1，5-戊二胺、1,6-己二胺、1，8-辛二胺(OMDA)、1，9-壬二胺(NMDA)、2-甲基-1，8-辛二胺(MODA)、1，11-十一烷二胺、2-丁基-2-乙基-1，5-戊二胺、1，12-十二烷二胺、1，13-十三烷二胺、1，14-十四烷二胺、1，16-十六烷二胺、1，18-十八烷二胺、环己二胺、1，3-双(端胺基甲基)环己烷(BAC)、异佛尔酮二胺、降莰烷二甲胺、4，4’-二端胺基二环己基甲烷(PACM)、2，2-(4，4’-二端胺基二环己基)丙烷(PACP)、和3，3’-二甲基-4，4’-二端胺基二环己基甲烷(MACM)、及其组合。
7.根据权利要求1所述的聚酰胺树脂，其特征在于，所述单体B8包括但不仅限于对苯二甲酸、间苯二甲酸、1,4-环己烷二甲酸、顺式和/或反式环己烷-1，3-二羧酸(CHDA)、及其组合；区别于B8的具有两个羧基官能团或其前体基团的第二单体包括但不仅限于丁二酸、戊二酸、己二酸、辛二酸、壬二酸、癸二酸、十一烷二酸、十二烷二酸、十三烷二酸、十四烷二酸、十五烷二酸、十六烷二酸、十八烷二酸、二聚体酸、及其组合。
8.根据权利要求1所述的聚酰胺树脂，其特征在于，所述单体A10为1，10-癸二胺，所述单体B8为对苯二甲酸和/或1，4-环己烷二甲酸。
9.根据权利要求1所述的聚酰胺树脂，其特征在于，所述具有一个氨基和一个羧基官能团的第三单体和/或内酰胺包括但不仅限于己内酰胺CL、α，ω-氨基己酸、α，ω-氨基壬酸、α，ω-氨基十一酸AUA、月桂内酰胺LL、ω-氨基十二酸ADA、及其组合。
10.一种包含权利要求1-9任一项所述的聚酰胺模塑组合物，其特征在于：包括以下组成：
a、30wt%-99.9wt%的聚酰胺树脂；
b、含量为x的增强填料；其中，x=0-70wt%；
c、含量为y的添加剂和/或其它聚合物；其中，y=0-70wt%；
其中，a、b、c三种组分的重量百分数之和为100wt%。
11.一种如权利要求10所述的聚酰胺模塑组合物，其特征在于：包括以下组成：
a、30wt%-97wt%的聚酰胺树脂；
b、含量为x的增强填料；其中，x=1wt%-66wt%；
c、含量为y的添加剂和/或其它聚合物；其中，y=0.1wt%-64wt%；
其中，a、b、c三种组分的重量百分数之和为100wt%。
12.根据权利要求10或11所述的聚酰胺模塑组合物，其特征在于，所述增强填料的形状为纤维状，其平均长度为0.01mm-20mm；其长径比为5:1~2000:1；所述增强填料的含量为10wt%-50wt%；所述增强填料为无机增强填料或有机增强填料，所述无机增强填料包括但不仅限于玻璃纤维、钛酸钾纤维、金属包层的玻璃纤维、陶瓷纤维、硅灰石纤维、金属碳化物纤维、金属固化纤维、石棉纤维、氧化铝纤维、碳化硅纤维、石膏纤维或硼纤维的一种或几种；所述有机增强填料包括但不仅限于芳族聚酰胺纤维和/或碳纤维。
13.根据权利要求12所述的聚酰胺模塑组合物，其特征在于，所述增强填料的平均长度为0.1mm-6mm。
14.根据权利要求12所述的聚酰胺模塑组合物，其特征在于，所述增强填料的长径比为30:1-600:1。
15.根据权利要求12所述的聚酰胺模塑组合物，其特征在于，所述增强填料的含量为15wt%-40wt%。
16.根据权利要求12所述的聚酰胺模塑组合物，其特征在于，所述无机增强填料为玻璃纤维。
17.根据权利要求10或11所述的聚酰胺模塑组合物，其特征在于，所述增强填料的形状为非纤维状，其平均粒径为0.001μm-100μm，选自钛酸钾晶须、氧化锌晶须、硼酸铝晶须、硅灰石、沸石、绢云母、高岭土、云母、滑石、粘土、叶腊石、膨润土、蒙脱土、锂蒙脱土、合成云母、石棉、硅铝酸盐、氧化铝、氧化硅、氧化镁、氧化锆、氧化钛、氧化铁、碳酸钙、碳酸镁、白云石、硫酸钙、硫酸钡、氢氧化镁、氢氧化钙、氢氧化铝、玻璃珠、陶瓷珠、氮化硼、碳化硅或二氧化硅的一种或几种。
18.根据权利要求17所述的聚酰胺模塑组合物，其特征在于，所述增强填料的平均粒径为0.01μm-50μm。
19.根据权利要求10或11所述的聚酰胺模塑组合物，其特征在于，所述添加剂含有阻燃剂；阻燃剂为卤系阻燃剂或无卤阻燃剂；所述卤系阻燃剂包括但不仅限于溴化聚苯乙烯、溴化聚苯醚、溴化双酚A型环氧树脂、溴化苯乙烯-马来酸酐共聚物、溴化环氧树脂、溴化苯氧基树脂、十溴二苯醚、十溴代联苯、溴化聚碳酸酯、全溴三环十五烷或溴化芳香族交联聚合物的一种或几种；所述无卤阻燃剂包括但不仅限于含氮阻燃剂、含磷阻燃剂或含氮和磷的阻燃剂中的一种或几种；基于聚酰胺组合物的总重量，所述阻燃剂的含量为10wt%-40wt%。
20.根据权利要求19所述的聚酰胺模塑组合物，其特征在于，所述阻燃剂为无卤阻燃剂。
21.根据权利要求19所述的聚酰胺模塑组合物，其特征在于，所述卤系阻燃剂为溴化聚苯乙烯。
22.根据权利要求19所述的聚酰胺模塑组合物，其特征在于，所述无卤阻燃剂为含磷阻燃剂。
23.根据权利要求22所述的聚酰胺模塑组合物，其特征在于，所述含磷阻燃剂包括但不仅限于单磷酸芳基磷酸酯、双磷酸芳基磷酸酯、烷基膦酸二甲酯、磷酸三苯酯、磷酸三甲苯酯、磷酸三(二甲苯)酯、丙苯系磷酸酯、丁苯系磷酸酯、次膦酸盐的一种或几种
24.根据权利要求23所述的聚酰胺模塑组合物，其特征在于，所述含磷阻燃剂为具有如下结构式I和/或II的次膦酸盐：
在式I及式II中，R1及R2可以相同，也可以不同，分别表示直链状或分支状的C1-C6-烷基、芳基或苯基；R3表示直链状或分支状的C1-C10-亚烷基、C6-C10-亚芳基、C6-C10-烷基亚芳基、C6-C10-芳基亚烷基；M表示钙原子、镁原子、铝原子和/或锌原子；m是2或3，n是1或3，x是1或2。