CN104714709A - Novel GX-cell capacitive touch screen module and manufacturing method thereof - Google Patents
Novel GX-cell capacitive touch screen module and manufacturing method thereof Download PDFInfo
- Publication number
- CN104714709A CN104714709A CN201510140648.3A CN201510140648A CN104714709A CN 104714709 A CN104714709 A CN 104714709A CN 201510140648 A CN201510140648 A CN 201510140648A CN 104714709 A CN104714709 A CN 104714709A
- Authority
- CN
- China
- Prior art keywords
- telegraph circuit
- base material
- fpc
- liquid crystal
- colored filter
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a novel GX-cell capacitive touch screen module. The novel GX-cell capacitive touch screen module comprises a cover plate, a substrate and a liquid crystal displayer. A first electrode circuit of a touch sensor is manufactured on the upper surface or the lower surface of the substrate. A second electrode circuit of the touch sensor is manufactured on the upper surface or the lower surface of a color filter of the liquid crystal displayer. The cover plate is attached to the face, provided with the first electrode circuit or not provided with the first electrode circuit, of the cover plate through optical adhesive. The other face of the substrate is attached to the upper surface of an upper polaroid of the touch sensor through optical adhesive. The touch sensor further comprises an upper FPC and a lower FPC. The upper FPC is bound on the substrate and electrically connected with the first electrode circuit, and the lower FPC is bound on the color filter and electrically connected with the second electrode circuit. The novel GX-cell capacitive touch screen module has the properties of being high in sensitivity, high in point recording rate, capable of carrying out rapid responding, not prone to being disturbed by noise signals and the like; meanwhile, the novel GX-cell capacitive touch screen module can achieve the function that touch control and displaying are deeply integrated.
Description
Technical field
The invention belongs to touch-screen field, relate to a kind of novel GX-cell capacitive touch screen module and preparation method thereof.
Background technology
Touch-control and display depth are integrated and have been become a kind of large trend, this product structure mainly contains On-Cell type and In-Cell type at present, their common ground is incorporated in liquid crystal module by the touch function of external hanging type, to reducing the thickness effect of display device clearly.
But current On-Cell type and In-Cell type structure exist obvious shortcoming, touch electrode layer is away from touch form, near liquid crystal module drive electrode layer and power supply, touching signals is subject to the impact of driving circuit and power supply, shows that noise signal disturbing is obvious, high etc. to the performance requirement of IC.
Summary of the invention
For the deficiencies in the prior art, object of the present invention is intended to provide a kind of and has high sensitivity, a high report point rate, can respond fast and not by the novel GX-cell capacitive touch screen module of noise signal disturbing.
For achieving the above object, the present invention adopts following technical scheme:
A kind of novel GX-cell capacitive touch screen module, it comprises cover plate, base material and liquid crystal display, the upper surface of described base material or lower surface are manufactured with the first telegraph circuit of touch sensor, the upper surface of the colored filter of liquid crystal display or lower surface are manufactured with the second telegraph circuit of touch sensor, described cover plate and base material are manufactured with the one side of the first telegraph circuit or are not had the one side of making first telegraph circuit to be fitted by optical cement, the upper surface of the another side of base material and the upper polaroid of liquid crystal display is fitted by optical cement, described touch sensor also comprises FPC and lower FPC, described upper FPC to be bundled on base material and to be electrically connected with the first telegraph circuit, described lower FPC to be bundled on colored filter and to be electrically connected with the second telegraph circuit.
Preferably, described liquid crystal display also comprises the colored filter, liquid crystal cell, TFT glass, lower polaroid and the backlight that assemble successively from top to bottom, and upper polaroid is positioned at above colored filter.
Preferably, described cover plate is made up of the one in tempered glass, acrylic board and plastics.
The invention still further relates to a kind of method for making of novel GX-cell capacitive touch screen module, comprise the following steps:
Step 1, on base material, make the first telegraph circuit of touch sensor;
Step 2, on base material, bind the upper FPC of touch sensor, and described upper FPC and the first telegraph circuit are formed be electrically connected;
Step 3, make the second telegraph circuit of touch sensor at the upper surface of the colored filter of liquid crystal display or lower surface;
Step 4, on the colored filter of liquid crystal display, bind the lower FPC of touch sensor, and described lower FPC and the second telegraph circuit are formed be electrically connected;
Step 5, cover plate and base material are manufactured with the first telegraph circuit one side or do not have the one side of making first telegraph circuit to be fitted by optical cement, the upper surface of the upper polaroid of the another side of base material and liquid crystal display is fitted by optical cement.
Preferably, described step 1 specifically comprises following sub-step:
Step 11, on base material, gold-tinted processing procedure is adopted to make frame ink;
Step 12, on base material, plate ito film layer;
Step 13, on ito film layer, apply photoresist, and carry out successively exposing, develop, etch, to obtain described first telegraph circuit;
Step 14, on the first telegraph circuit metal-coated membrane or print exposure silver, and utilize gold-tinted processing procedure to make the edge be connected with described first telegraph circuit to go between.
Preferably, step 12 specifically comprises the following steps: before plating ito film layer, base material plates the silicon dioxide of 180-200 dust and the potpourri of niobium pentaoxide, then plates the ito film layer of 200-700 dust.
Preferably, described step 2 comprises following sub-step:
Adopt hot press to be bundled on base material by upper FPC, wherein, the hot pressing pressure acting on the both sides of base material is 4.25 ± 0.5Kg, and the hot pressing pressure acting on the centre of base material is 2.75 ± 0.5kg, and it is 150-165 DEG C/12 ± 1S that temperature/time is held in hot pressing;
The edge of the first telegraph circuit lead-in wire is connected with upper FPC.
Preferably, described step 3 specifically comprises following sub-step:
Step 31, silicon dioxide at the upper surface of colored filter or lower surface plating 120-160 dust, and plate ito film layer on silica;
Step 32, on ito film layer, apply photoresist, and carry out successively exposing, develop, etch, to obtain described second telegraph circuit;
Step 33, on the second telegraph circuit metal-coated membrane or print exposure silver, and utilize gold-tinted processing procedure to make the edge be connected with described second telegraph circuit to go between.
Preferably, described step 4 comprises following sub-step:
Hot press is adopted to be bundled on colored filter by lower FPC, wherein, the hot pressing pressure acting on the both sides of colored filter is 4.25 ± 0.5Kg, and the hot pressing pressure acting on the centre of colored filter is 2.75 ± 0.5kg, and it is 150-165 DEG C/12 ± 1S that temperature/time is held in hot pressing;
The edge of the second telegraph circuit lead-in wire is connected with lower FPC.
Preferably, the thickness of photoresist is between 1.6-2.1 μm; Exposure is 100-120mj/cm
2; Developer solution adopt concentration be 0.4% NaOH or concentration be 0.7% potassium hydroxide; The thickness of the silver slurry coating that print exposure silver adopts is at 5-8 μm; Live width/the line-spacing of edge lead-in wire is at 10/10-200/200 μm.
Beneficial effect of the present invention is as follows: this novel GX-cell capacitive touch screen module has high sensitivity, high report point rate, can respond fast and not be subject to the performances such as noise signal disturbing; It also can realize the function of touch-control and display depth integration simultaneously.Method for making of the present invention is simple; by making the first telegraph circuit of touch sensor on substrate; it is made to have the effect of better protection the first telegraph circuit; simultaneously at the upper surface of the colored filter of liquid crystal display or the second telegraph circuit of lower surface making touch sensor; and by connecting upper and lower FPC, the first telegraph circuit is connected with the second telegraph circuit, to realize an overall highly sensitive jamproof function.
Accompanying drawing explanation
Fig. 1 is the structural representation of the better embodiment of the present invention's novel GX-cell capacitive touch screen module.
Fig. 2 is the structural representation of the present invention's novel GX-cell capacitive touch screen module cover plate.
Fig. 3 is the structural representation of colored filter in the present invention's novel GX-cell capacitive touch screen module.
Fig. 4 is the STRUCTURE DECOMPOSITION figure of the present invention's novel GX-cell capacitive touch screen module.
Reference numeral: 10, cover plate; 11, base material; 20, the first telegraph circuit; 21, upper FPC; 30, optical cement; 40, the second telegraph circuit; 41, lower FPC; 50, upper polaroid; 60, colored filter; 70, liquid crystal cell; 80, TFT glass; 90, lower polaroid; 100, backlight.
Embodiment
Below in conjunction with accompanying drawing and embodiment, the present invention is described further:
Refer to Fig. 1 to Fig. 4, the present invention relates to a kind of novel GX-cell capacitive touch screen module, its better embodiment comprises cover plate 10, base material 11 and liquid crystal display, the upper surface of base material 11 or lower surface are manufactured with the first telegraph circuit 20 of touch sensor, (present embodiment is made as example with colored filter upper surface to the upper surface of the colored filter 60 of liquid crystal display, also second circuit can be made at its lower surface) be manufactured with the second telegraph circuit 40 of touch sensor, cover plate 10 and base material 11 are manufactured with the one side of the first telegraph circuit 20 or are not had the one side of making first telegraph circuit 20 to be fitted by optical cement 30, the upper surface of the another side of base material 11 and the upper polaroid 50 of liquid crystal display is fitted by optical cement 30, touch sensor also comprises FPC 21 and lower FPC 41, upper FPC 21 to be bundled on base material 11 and to be electrically connected with the first telegraph circuit 20, lower FPC 41 to be bundled on colored filter 60 and to be electrically connected with the second telegraph circuit 40.
Wherein, liquid crystal display can also comprise the liquid crystal cell 70, TFT glass 80, lower polaroid 90 and the backlight 100 that assemble successively from top to bottom, and upper polaroid 50 is positioned at above colored filter 60.
Preferably, cover plate 10 can be made up of the one in tempered glass, acrylic board and plastics.Certainly, cover plate 10 can also select other material to make as required.
In addition, the electrode material of the first telegraph circuit and the second telegraph circuit can be the combination between the material such as ITO, nano-silver thread, Graphene, carbon nano-tube, carbon nanometer bud, metal mesh, PEDOT or these materials.Preferably, the electrode material selected in the present embodiment is ITO.Base material can be made up of the one in tempered glass, PET, PSA, acrylic board and plastics.Preferably, the base material selected in the present embodiment is PET.
The invention still further relates to a kind of method for making of novel GX-cell capacitive touch screen module, it comprises the following steps:
Step S1, on base material, make the first telegraph circuit of touch sensor.
Step S2, on base material, bind the upper FPC of touch sensor, and FPC and the first telegraph circuit are formed be electrically connected.
Step S3, make the second telegraph circuit of touch sensor at the upper surface of the colored filter of liquid crystal display or lower surface.
Step S4, on the colored filter of liquid crystal display, bind the lower FPC of touch sensor, and lower FPC and the second telegraph circuit are formed be electrically connected.
Step S5, cover plate and base material are manufactured with the first telegraph circuit one side or do not have the one side of making first telegraph circuit to be fitted by optical cement, the upper surface of the upper polaroid of the another side of base material and liquid crystal display is fitted by optical cement.This optical cement can be OCA, also can be OCR.Preferably, OCA can be adopted entirely to fit, OCA thickness can between 50-200um, and required roller pressure of wherein fitting can be 0.2 ± 0.5MPA, and wheel speeds can be 250 ± 50mm/s.Meanwhile, also need to connect upper and lower FPC, to make the first telegraph circuit and the second telegraph circuit be electrical connected, thus obtain novel touch screen module of the present invention.
Concrete, making the method that the first telegraph circuit uses can be open greatly the method for making of PET plating ito film, also can be the method for making of plating ito film on granule PET.Preferably, the present embodiment selects the method for making of plating ito film on a large PET, and namely above-mentioned steps S1 correspondingly can comprise following sub-step:
Step S11, on base material, gold-tinted processing procedure is adopted to make frame ink.Preferably, the thickness of ink is between 1-4um.
Step S12, on base material, plate ito film layer.Preferably, before plating ito film layer, the silicon dioxide of 180-200 dust and the potpourri of niobium pentaoxide can be plated on base material, then plate the ito film layer of 200-700 dust.The potpourri of applying silicon oxide and niobium pentaoxide on base material, can improve the quality of ito film layer.
Step S13, on ito film layer, apply photoresist, and carry out successively exposing, develop, etch, to obtain the first telegraph circuit.Wherein, preferably, the thickness of photoresist is between 1.6-2.1 μm; Exposure is 100-120mj/cm
2; Developer solution adopt concentration be 0.4% NaOH or concentration be 0.7% potassium hydroxide.
Step S14, on the first telegraph circuit metal-coated membrane or print exposure silver, and utilize gold-tinted processing procedure to make the edge be connected with the first telegraph circuit to go between (if telegraph circuit adopts is ITO material entirely, then can without this step).Concrete, the plating metal film such as CU, MOALMO, AG can be adopted and utilize gold-tinted processing procedure to make the edge is connected with the first telegraph circuit and go between, also can adopt print silver-colored starch or print exposure silver-colored and utilize gold-tinted processing procedure to make the edge be connected with the first telegraph circuit to go between.Preferably, can select to adopt print exposure silver and utilize gold-tinted processing procedure to make edge lead-in wire.More preferably, the thickness of the silver slurry coating that print exposure silver adopts is at 5-8 μm, and the live width/line-spacing of edge lead-in wire is at 10/10-200/200 μm.
Further, the large Zhang Jicai making the first telegraph circuit can be cut as required, namely cut into the substrate shapes that we need, make to facilitate follow-up technique.
Preferably, step S2 can also comprise following sub-step:
Adopt hot press to be bundled on base material by upper FPC, wherein, the hot pressing pressure acting on the both sides of base material is 4.25 ± 0.5Kg, and the hot pressing pressure acting on the centre of base material is 2.75 ± 0.5kg, and it is 150-165 DEG C/12 ± 1S that temperature/time is held in hot pressing; The edge of the first telegraph circuit lead-in wire is connected with upper FPC.
Meanwhile, the making of the second telegraph circuit can be opened on colored filter large, also can on granule colored filter.Preferably, the present embodiment can be selected to make on a large colored filter.Therefore step S3 specifically can comprise following sub-step:
Step S31, back of the body glass surface at the colour matrix point of colored filter, the i.e. silicon dioxide of the upper surface plating 120-160 dust of colored filter, or also at the silicon dioxide of the lower surface plating 120-160 dust of colored filter, and ito film layer can be plated on silica.Most preferred, the thickness of silicon dioxide is 150 dusts, and applying silicon oxide layer can improve the quality of ito film layer.
Step S32, on ito film layer, apply photoresist, and carry out successively exposing, develop, etch, to obtain described second telegraph circuit.Wherein, preferably, the thickness of photoresist is between 1.6-2.1 μm; Exposure is 100-120mj/cm
2; Developer solution adopt concentration be 0.4% NaOH or concentration be 0.7% potassium hydroxide.
Step S33, on the second telegraph circuit metal-coated membrane or print exposure silver, and utilize gold-tinted processing procedure to make the edge be connected with described second telegraph circuit to go between (if telegraph circuit adopts is ITO material entirely, then can without this step).Concrete, the plating metal film such as CU, MOALMO, AG can be adopted and utilize gold-tinted processing procedure to make the edge is connected with the first telegraph circuit and go between, also can adopt print silver-colored starch or print exposure silver-colored and utilize gold-tinted processing procedure to make the edge be connected with the first telegraph circuit to go between.Preferably, can select to adopt print exposure silver and utilize gold-tinted processing procedure to make edge lead-in wire.More preferably, the thickness of the silver slurry coating that print exposure silver adopts is at 5-8 μm, and the live width/line-spacing of edge lead-in wire is at 10/10-200/200 μm.
Further, large the upper polaroid making the second telegraph circuit can be cut as required, namely cut into the shape of the upper polaroid that we need, bind with lower FPC after carrying out functional test.
Preferably, step S4 can also comprise following sub-step:
Hot press is adopted to be bundled on colored filter by lower FPC, wherein, the hot pressing pressure acting on the both sides of colored filter is 4.25 ± 0.5Kg, and the hot pressing pressure acting on the centre of colored filter is 2.75 ± 0.5kg, and it is 150-165 DEG C/12 ± 1S that temperature/time is held in hot pressing; The edge of the second telegraph circuit lead-in wire is connected with lower FPC.
Further, upper polaroid, upper surface are formed touch-control display module with the colored filter of the second telegraph circuit, liquid crystal cell, TFT glass, lower polaroid, backlight assembling.
Further, by order from top to bottom, cover plate, optical cement, base material, the first telegraph circuit, upper FPC, optical cement, upper polaroid, lower FPC, the second telegraph circuit, colored filter, liquid crystal cell, TFT glass, lower polaroid and backlight are assembled into novel GX-cell capacitive touch screen module of the present invention successively, wherein, binding had the cover plate of upper FPC and binding to have the touch-control of lower FPC to show module to be fitted by optical cement, this optical cement can be OCA or OCR.According to actual needs, the position of cover plate, optical cement, base material, the first telegraph circuit, upper FPC, optical cement, upper polaroid, lower FPC, the second telegraph circuit, colored filter, liquid crystal cell, TFT glass, lower polaroid and backlight can certainly be adjusted.
For a person skilled in the art, according to technical scheme described above and design, other various corresponding change and distortion can be made, and all these change and distortion all should belong within the protection domain of the claims in the present invention.
Claims (10)
1. a novel GX-cell capacitive touch screen module, it comprises cover plate, base material and liquid crystal display, it is characterized in that, the upper surface of described base material or lower surface are manufactured with the first telegraph circuit of touch sensor, the upper surface of the colored filter of liquid crystal display or lower surface are manufactured with the second telegraph circuit of touch sensor, described cover plate and base material are manufactured with the one side of the first telegraph circuit or are not had the one side of making first telegraph circuit to be fitted by optical cement, the upper surface of the another side of base material and the upper polaroid of described liquid crystal display is fitted by optical cement, described touch sensor also comprises FPC and lower FPC, described upper FPC to be bundled on base material and to be electrically connected with the first telegraph circuit, described lower FPC to be bundled on colored filter and to be electrically connected with the second telegraph circuit.
2. novel GX-cell capacitive touch screen module as claimed in claim 1, is characterized in that, described liquid crystal display also comprises the liquid crystal cell, TFT glass, lower polaroid and the backlight that assemble successively from top to bottom, and upper polaroid is positioned at above colored filter.
3. novel GX-cell capacitive touch screen module as claimed in claim 1, it is characterized in that, described cover plate is made up of the one in tempered glass, acrylic board and plastics.
4. a method for making for novel GX-cell capacitive touch screen module, is characterized in that, comprise the following steps:
Step 1, on base material, make the first telegraph circuit of touch sensor;
Step 2, on base material, bind the upper FPC of touch sensor, and described upper FPC and the first telegraph circuit are formed be electrically connected;
Step 3, make the second telegraph circuit of touch sensor at the upper surface of the colored filter of liquid crystal display or lower surface;
Step 4, on the colored filter of liquid crystal display, bind the lower FPC of touch sensor, and described lower FPC and the second telegraph circuit are formed be electrically connected;
Step 5, cover plate and base material are manufactured with the first telegraph circuit one side or do not have the one side of making first telegraph circuit to be fitted by optical cement, the upper surface of the upper polaroid of the another side of base material and liquid crystal display is fitted by optical cement.
5. method for making as claimed in claim 4, it is characterized in that, described step 1 specifically comprises following sub-step:
Step 11, on base material, gold-tinted processing procedure is adopted to make frame ink;
Step 12, on base material, plate ito film layer;
Step 13, on ito film layer, apply photoresist, and carry out successively exposing, develop, etch, to obtain described first telegraph circuit;
Step 14, on the first telegraph circuit metal-coated membrane or print exposure silver, and utilize gold-tinted processing procedure to make the edge be connected with described first telegraph circuit to go between.
6. method for making as claimed in claim 5, it is characterized in that, step 12 specifically comprises the following steps: before plating ito film layer, base material plates the silicon dioxide of 180-200 dust and the potpourri of niobium pentaoxide, then plates the ito film layer of 200-700 dust.
7. method for making as claimed in claim 5, it is characterized in that, described step 2 comprises following sub-step:
Adopt hot press to be bundled on base material by upper FPC, wherein, the hot pressing pressure acting on the both sides of base material is 4.25 ± 0.5Kg, and the hot pressing pressure acting on the centre of base material is 2.75 ± 0.5kg, and it is 150-165 DEG C/12 ± 1S that temperature/time is held in hot pressing;
The edge of the first telegraph circuit lead-in wire is connected with upper FPC.
8. method for making as claimed in claim 4, it is characterized in that, described step 3 specifically comprises following sub-step:
Step 31, silicon dioxide at the upper surface of colored filter or lower surface plating 120-160 dust, and plate ito film layer on silica;
Step 32, on ito film layer, apply photoresist, and carry out successively exposing, develop, etch, to obtain described second telegraph circuit;
Step 33, on the second telegraph circuit metal-coated membrane or print exposure silver, and utilize gold-tinted processing procedure to make the edge be connected with described second telegraph circuit to go between.
9. method for making as claimed in claim 8, it is characterized in that, described step 4 comprises following sub-step:
Hot press is adopted to be bundled on colored filter by lower FPC, wherein, the hot pressing pressure acting on the both sides of colored filter is 4.25 ± 0.5Kg, and the hot pressing pressure acting on the centre of colored filter is 2.75 ± 0.5kg, and it is 150-165 DEG C/12 ± 1S that temperature/time is held in hot pressing;
The edge of the second telegraph circuit lead-in wire is connected with lower FPC.
10. the method for making as described in claim 5 or 8, is characterized in that, the thickness of photoresist is between 1.6-2.1 μm; Exposure is 100-120mj/cm
2; Developer solution adopt concentration be 0.4% NaOH or concentration be 0.7% potassium hydroxide; The thickness of the silver slurry coating that print exposure silver adopts is at 5-8 μm; Live width/the line-spacing of edge lead-in wire is at 10/10-200/200 μm.