CN104711464A - 一种可控制强度可阳极氧化可压铸的铝镍稀土合金 - Google Patents

一种可控制强度可阳极氧化可压铸的铝镍稀土合金 Download PDF

Info

Publication number
CN104711464A
CN104711464A CN201510073339.9A CN201510073339A CN104711464A CN 104711464 A CN104711464 A CN 104711464A CN 201510073339 A CN201510073339 A CN 201510073339A CN 104711464 A CN104711464 A CN 104711464A
Authority
CN
China
Prior art keywords
rare earth
alloy
die casting
quality
strength
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510073339.9A
Other languages
English (en)
Inventor
朱岳群
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510073339.9A priority Critical patent/CN104711464A/zh
Publication of CN104711464A publication Critical patent/CN104711464A/zh
Pending legal-status Critical Current

Abstract

本发明涉及铝合金技术领域，具体是提供一种可控强度可阳极氧化可压铸的铝镍稀土合金。本合金特征在于：包含1.0～3.0％质量的Ni，0.1～1.0％质量的稀土，稀土是Ce或者La或者两者混合物。还包含添加剂Fe，其含量不超过1.0％；或添加剂Mn，其含量不超过2.0％；或两者同时添加时，其总量不超过2.0％。此外还可添加一种调节铝镍稀土合金强度的元素Zn，Zn质量含量为0～30％。余量为Al及不可避免杂质。本发明铝镍稀土合金是一种强度可控、可阳极氧化、可压铸、导热性好、综合性能优良的铝合金新材料。

Description

一种可控制强度可阳极氧化可压铸的铝镍稀土合金
技术领域
本发明涉及铝合金技术领域，具体提供一种可控制强度可阳极氧化可压铸的导热性佳的铝镍稀土合金。
背景技术
铝合金广泛应用于各行各业，目前普遍存在以下问题：
1、能够做阳极氧化着色的铝合金，不能采用压铸工艺进行批量生产，只能用挤压工艺，产品结构简单，后续加工工作量大，效率低，其中使用最广泛的合金是6063铝合金。
2、能够采用压铸工艺进行批量生产的铝合金，譬如使用最广泛的ADC12铝合金，其压铸件不能做阳极氧化着色，很多装饰件因此不能用该合金；另外常用压铸铝合金ADC12的热传导系数低，只有80w/m.k左右，不太适合做散热器件,这大大降低压铸铝的普及率。
3、目前已经有人研发出既能压铸又可以做阳极氧化的铝合金，但是流动性差，压铸性差，流纹明显；而且因合金中铝含量太高，压铸件太软，对强度有要求的结构件无法使用，譬如汽车轮毂。
发明内容
本发明经实验获得一种压铸铝镍稀土合金，其流动性好、压铸工艺性能好，导热性能好，压铸件可以做阳极氧化着色，而且可以按照不同产品对强度的要求，调节合金强度。因此，该铝合金可同时满足“强度可控性、可阳极氧化、压铸性和导热性能佳”的理想铝合金。
本发明一种可控强度可阳极氧化可压铸的铝镍稀土合金，其特征在于：包含1.0～3.0％质量的Ni，0.1～1.0％质量的稀土，稀土是Ce或者La或者 两者混合物。还包含添加剂Fe，其含量不超过1.0％；或添加剂Mn，其含量不超过2.0％；或两者同时添加时，其总量不超过2.0％。此外还可添加一种调节铝镍稀土合金强度的元素Zn，Zn质量含量为0～30％。余量为Al及不可避免杂质。
本发明一种压铸铝镍稀土合金的成份中，Al、Ni、稀土为必含成份，其中稀土为Ce或者La或者Ce、La混合物，还包含Fe、Mn中的一种或两种；除此以外，还可添加适量的Zn。
本发明一种压铸铝镍稀土合金的成份中，添加Zn是作为调节合金强度的元素，Zn质量含量为0～30％；Zn含量不同，合金强度不同，随着Zn的百分含量增加，合金强度逐渐变强。
本发明一种压铸铝镍稀土合金，导热性好，流动性好，压铸工艺性能好；压铸件的表面可以采用阳极氧化工艺着成各种永不退颜色，色泽饱满、鲜艳，金属感强，且压铸件强度可控。不管表面装饰件还是强度要求很高的结构件，还是既要求有高导热性能又能够阳极氧化的散热器件，本发明的铝镍稀土合金都可以满足需求。且压铸件后续精加工容易。总之，本发明铝镍稀土合金是一种强度可控、可阳极氧化、可压铸、导热佳的综合性能优良的铝合金新材料。
具体实施方式
下面对本发明优选实施例进行进一步说明。发明内容中表述的成份组合及质量比范围均属于本发明的保护范围，实施例不视为对本发明保护范围的限制。
实施例1：
本实施例可控强度可阳极氧化可压铸铝镍稀土合金，包含1.2％质量的Ni，0.5％质量的La，0.5％质量的Fe，Zn的质量百分比：0～30％，余量为Al及不可避免杂质。在不同Zn含量下的机械强度如表一所示。
实施例:2：
本实施例可控强度可阳极氧化可压铸铝镍稀土合金，包含2.2％质量的Ni，0.5％质量的Ce，0.5％质量的Fe，Zn的质量百分比：0～30％，余量为 Al及不可避免杂质。其机械强度如表一所示。
实施例3：
本实施例可控强度可阳极氧化可压铸铝镍稀土合金，包含2.2％质量的Ni，0.5％质量的La，0.5％质量的Mn，Zn的质量百分比：0～30％，余量为Al及不可避免杂质。其机械强度如表一所示。
实施例4：
本实施例可控强度可阳极氧化可压铸铝镍稀土合金，包含2.2％质量的Ni，0.5％质量的Ce，1.8％质量的Mn，Zn的质量百分比：0～30％，余量为Al及不可避免杂质。其机械强度如表一所示。
实施例5：
本实施例可控强度可阳极氧化可压铸铝镍稀土合金，包含2.0％质量的Ni，0.2％质量的La，0.2％质量的Ce，0.5％质量的Fe，0.7％质量的Mn，Zn的质量百分比：0～30％，余量为Al及不可避免杂质。其机械强度如表一所示。
实施例6：
本实施例可控强度可阳极氧化可压铸铝镍稀土合金，包含1.5％质量的Ni，0.4％质量的La，0.1％质量的Ce，0.5％质量的Fe，1.5％质量的Mn，Zn的质量百分比：0～30％，余量为Al及不可避免杂质。其机械强度如表一所示。
实施例7：
本实施例可控强度可阳极氧化可压铸铝镍稀土合金，包含2.2％质量的Ni，0.1％质量的La，0.3％质量的Ce，0.5％质量的Fe，Zn的质量百分比：0～30％，余量为Al及不可避免杂质。其机械强度如表一所示。
实施例8：
本实施例可控强度可阳极氧化可压铸铝镍稀土合金，包含2.5％质量的Ni，0.6％质量的La，0.2％质量的Ce，1.5％质量的Mn，Zn的质量百分比：0～30％，余量为Al及不可避免杂质。其机械强度如表一所示。
实施例9：
本实施例可控强度可阳极氧化可压铸铝镍稀土合金，包含2.9％质量的Ni，0.1％质量的La，0.2％质量的Ce，0.2％质量的Fe，1.0％质量的Mn，Zn的质量百分比：0～30％，余量为Al及不可避免杂质。其机械强度如表一所示。
实施例10：
本实施例可控强度可阳极氧化可压铸铝镍稀土合金，包含2.0％质量的Ni，0.1％质量的La，0.6％质量的Ce，0.5％质量的Fe，1.5％质量的Mn，Zn的质量百分比：0～30％，余量为Al及不可避免杂质。其机械强度如表一所示。
表一、本实施例合金成分及机械性能

Claims (1)

1.一种可控强度可阳极氧化可压铸的铝镍稀土合金，本合金特征在于：包含1.0～3.0%质量的Ni，0.1～1.0%质量的稀土，稀土是Ce或者La或者两者混合物；还包含添加剂Fe，其含量不超过1.0%；或添加剂Mn，其含量不超过2.0%；或两者同时添加时，其总量亦不超过2.0%；此外还可添加一种调节铝镍稀土合金强度的元素Zn，Zn质量含量为0～30%；余量为Al及不可避免杂质。
CN201510073339.9A 2015-02-10 2015-02-10 一种可控制强度可阳极氧化可压铸的铝镍稀土合金 Pending CN104711464A (zh)