CN104710777A - Socket connecting piece prepared from high-stability nylon 12 composite material - Google Patents
Socket connecting piece prepared from high-stability nylon 12 composite material Download PDFInfo
- Publication number
- CN104710777A CN104710777A CN201510071191.5A CN201510071191A CN104710777A CN 104710777 A CN104710777 A CN 104710777A CN 201510071191 A CN201510071191 A CN 201510071191A CN 104710777 A CN104710777 A CN 104710777A
- Authority
- CN
- China
- Prior art keywords
- parts
- nylon
- nano
- connecting piece
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a socket connecting piece prepared from a high-stability nylon 12 composite material. The socket connecting piece is prepared from the following raw materials in parts by weight: 65 to 98 parts of nylon 12, 3 to 5 parts of low molecular weight polypropylene, 4 to 8 parts of nano-attapulgite, 35 to 58 parts of a sintering packing, 10 to 15 parts of polytetrafluoroethylene, 5 to 10 parts of polypropylene fibers, 2 to 4 parts of nano-carbon powder, 1 to 2 parts of dimethyl silicone oil, 1 to 2 parts of chlorinated paraffin, 1 to 2 parts of an antioxidant 168 and 1 to 2 parts of zinc stearate. The socket connecting piece has reinforced rigidity, hardness, heat resistance and dimensional stability, the shortcomings of poor dimensional stability and heat resistance of the conventional connecting piece are effectively overcome, and the requirement for higher performance during production and use can be met.
Description
Technical field
The present invention relates to field of plastic products, is exactly the preparation of a kind of high stability nylon 12 matrix material and the receptacle connectors that obtains.
Background technology
Utilize the favorable elasticity of plastics, the characteristics such as flexibility, excellent antifatigue can design the reliable web member of various practicality.Because plastics tubing has numerous advantages, as resistance to pressure with resistance to air loss is good, resistance to corrosion is strong. in construction, interface is few, quantities is little, easy construction etc. and thus comparatively steel pipe is low for construction costs.
Summary of the invention
A kind of high stability nylon 12 matrix material is the object of the present invention is to provide to prepare and the receptacle connectors that obtains.
Above-mentioned purpose is realized by following scheme:
The receptacle connectors that high stability nylon 12 matrix material is prepared and obtained, is characterized in that: it is obtained by the raw material of following weight parts:
Nylon 12 65-98, low-molecular-weight polypropylene 3-5, nano-attapulgite 4-8, sintering filler 35-58, tetrafluoroethylene 10-15, polypropylene fibre 5-10, nano-carbon powder 2-4, dimethyl silicone oil 1-2, clorafin 1-2, irgasfos 168 1-2, Zinic stearas 1-2;
Sintering filler is obtained by the raw material of following weight parts:
Sepiolite powder 8-10, boehmite powder 1.3-2.5, polyacrylamide 0.5-1.2, calcium metasilicate 2-4, gypsum 0.1-0.3, stearic acid 1-1.2, lithium chloride 0.6-0.8, magnesium nitrate 0.1-0.3, butyl acrylate 1.2-2.6, concentration are that hydrochloric acid 1-3, the oleic acid 0.3-0.4 of 3-5%, carob bean gum 0.5-0.8, deionized water are appropriate;
The preparation method of sintering filler is:
Magnesium nitrate, butyl acrylate, concentration be the hydrochloric acid of 3-5%, oleic acid, carob bean gum, deionized water and stirring evenly after, add boehmite powder again, 60-80 rev/min is stirred 20-30 minute, water-bath 30-40min at 60-80 DEG C again, adds all the other raw materials again after taking out cooling, stirs 10-20min under 100-200 rev/min, after gained raw material drying, 4-7 minute is sintered again, grinding, after crossing 100-200 mesh sieve and get final product at 180-220 DEG C.
The receptacle connectors that described a kind of high stability nylon 12 matrix material is prepared and obtained, is characterized in that:
Preparation method comprises the following steps:
(1), after nylon 12, low-molecular-weight polypropylene, nano-attapulgite, irgasfos 168, Zinic stearas being mixed, at 150-160 DEG C, 8-13min mediated by kneader, obtains mixing materials for subsequent use;
(2) surplus stock is stirred 10-20min at 60-80 rev/min of lower 50-60 DEG C, obtain compound;
(3), after being mixed with mixing materials by gained compound, after melt extruding granulation at 160-175 DEG C on the twin screw extruder, namely material is obtained,
(4) by after gained material forming, to obtain final product.
Beneficial effect of the present invention is: the present invention has the rigidity of strengthening and hardness, thermotolerance, dimensional stability, effectively overcomes the shortcoming of existing web member poor dimensional stability, poor heat resistance, makes the receptacle connectors obtained meet more high performance requirement in production and application.
Embodiment
The receptacle connectors that high stability nylon 12 matrix material is prepared and obtained, it is obtained by the raw material of following weight (kg):
Nylon 12 68, low-molecular-weight polypropylene 5, nano-attapulgite 8, sintering filler 38, tetrafluoroethylene 10, polypropylene fibre 10, nano-carbon powder 4, dimethyl silicone oil 2, clorafin 2, irgasfos 168 2, Zinic stearas 2;
Sintering filler is obtained by the raw material of following weight (kg):
Sepiolite powder 10, boehmite powder 1.5, polyacrylamide 1.2, calcium metasilicate 2, gypsum 0.3, stearic acid 1.2, lithium chloride 0.8, magnesium nitrate 0.3, butyl acrylate 1.6, concentration be 3% hydrochloric acid 1, oleic acid 0.3, carob bean gum 0.5, deionized water appropriate;
The preparation method of sintering filler is:
Magnesium nitrate, butyl acrylate, concentration be the hydrochloric acid of 3-5%, oleic acid, carob bean gum, deionized water and stirring evenly after, add boehmite powder again, 60 revs/min are stirred 30 minutes, water-bath 40min at 80 DEG C again, adds all the other raw materials again after taking out cooling, stirs 20min under 200 revs/min, after gained raw material drying, at 220 DEG C, sinter 6 minutes again, grinding, cross after 200 mesh sieves and get final product.
The receptacle connectors that described a kind of high stability nylon 12 matrix material is prepared and obtained, preparation method comprises the following steps:
(1), after nylon 12, low-molecular-weight polypropylene, nano-attapulgite, irgasfos 168, Zinic stearas being mixed, at 150 DEG C, 8min mediated by kneader, obtains mixing materials for subsequent use;
(2) surplus stock is stirred 20min at 60 revs/min lower 60 DEG C, obtain compound;
(3), after being mixed with mixing materials by gained compound, after melt extruding granulation at 165 DEG C on the twin screw extruder, namely material is obtained,
(4) by after gained material forming, to obtain final product.
The performance detection data for plastic fastening that the present embodiment obtains sees the following form:
Claims (2)
1. the preparation of high stability nylon 12 matrix material and the receptacle connectors that obtains, is characterized in that: it is obtained by the raw material of following weight parts:
Nylon 12 65-98, low-molecular-weight polypropylene 3-5, nano-attapulgite 4-8, sintering filler 35-58, tetrafluoroethylene 10-15, polypropylene fibre 5-10, nano-carbon powder 2-4, dimethyl silicone oil 1-2, clorafin 1-2, irgasfos 168 1-2, Zinic stearas 1-2;
Sintering filler is obtained by the raw material of following weight parts:
Sepiolite powder 8-10, boehmite powder 1.3-2.5, polyacrylamide 0.5-1.2, calcium metasilicate 2-4, gypsum 0.1-0.3, stearic acid 1-1.2, lithium chloride 0.6-0.8, magnesium nitrate 0.1-0.3, butyl acrylate 1.2-2.6, concentration are that hydrochloric acid 1-3, the oleic acid 0.3-0.4 of 3-5%, carob bean gum 0.5-0.8, deionized water are appropriate;
The preparation method of sintering filler is:
Magnesium nitrate, butyl acrylate, concentration be the hydrochloric acid of 3-5%, oleic acid, carob bean gum, deionized water and stirring evenly after, add boehmite powder again, 60-80 rev/min is stirred 20-30 minute, water-bath 30-40min at 60-80 DEG C again, adds all the other raw materials again after taking out cooling, stirs 10-20min under 100-200 rev/min, after gained raw material drying, 4-7 minute is sintered again, grinding, after crossing 100-200 mesh sieve and get final product at 180-220 DEG C.
2. a kind of high stability nylon 12 matrix material preparation according to claim 1 and the receptacle connectors that obtains, is characterized in that:
Preparation method comprises the following steps:
(1), after nylon 12, low-molecular-weight polypropylene, nano-attapulgite, irgasfos 168, Zinic stearas being mixed, at 150-160 DEG C, 8-13min mediated by kneader, obtains mixing materials for subsequent use;
(2) surplus stock is stirred 10-20min at 60-80 rev/min of lower 50-60 DEG C, obtain compound;
(3), after being mixed with mixing materials by gained compound, after melt extruding granulation at 160-175 DEG C on the twin screw extruder, namely material is obtained,
(4) by after gained material forming, to obtain final product.