CN104710775A - Flame retardant nylon alloy material for electrical material in electro-technology field - Google Patents
Flame retardant nylon alloy material for electrical material in electro-technology field Download PDFInfo
- Publication number
- CN104710775A CN104710775A CN201310671907.6A CN201310671907A CN104710775A CN 104710775 A CN104710775 A CN 104710775A CN 201310671907 A CN201310671907 A CN 201310671907A CN 104710775 A CN104710775 A CN 104710775A
- Authority
- CN
- China
- Prior art keywords
- nylon alloy
- flame retardant
- electro
- nylon
- flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a flame retardant nylon alloy material for electrical material in the electro-technology field. Nylon resin, a flexibilizer, a reinforcing agent, and a fire retardant are mixed according to a certain ration and then processed by a technology to prepare a nylon alloy with a special phase structure. The nylon alloy has the advantages of low water absorption rate, good size stability, good dry-state and low temperature flexibility, and improved flame retardant and heatproof performance, and is widely used in the fields of electrical material and electro-technology.
Description
Technical field
The present invention relates to electrician's electrical materials and appliances flame-retardant nylon alloy material, especially the preparation method of enhanced type automobile fan leaf PP Pipe Compound.
Background technology
Nylon (polymeric amide, english abbreviation is PA) be that in the engineering plastics of input application, output is maximum, kind maximum, purposes is the widest, the base resin of excellent property, but because its water-absorbent is large, shape and size poor stability, dry state and low-temperature flexibility poor, resistance toheat and flame retardant properties are general, limit it in automotive industry, electronics, application electrically and in construction industry.Therefore, reduce nylon material water-absorbent, improve its product size stability, dry state toughness and resistance to low temperature, improve its flame retardant properties and resistance toheat, become a large focus of polymer research field.For many years, in order to improve the above-mentioned shortcoming of nylon material, macromolecular material worker is devoted to strengthen it always, toughness reinforcing and flame-retardant modified, but nylon resin is strengthened simultaneously, toughness reinforcing and flame-retardant modified be contradiction on concrete enforcement: the toughness reinforcing intensity that must damage PA6, flame-retardant system add intensity and the toughness that can affect PA6 simultaneously, the filling of strongthener in most cases can be given again and flame-retardant modifiedly be brought difficulty.Therefore, the balance of seeking intensity, toughness and flame retardant properties in the preparation process of alloy is very necessary.
In order to expand the range of application of nylon material at engineering field, to meet the demand of current electrician's electrical materials and appliances thermoforming material, the present invention adopts advanced reactive blending technology, with nylon resin/toughner/toughener/fire retardant for main ingredient, prepare with higher-strength, toughness and better flame retardant properties and resistance toheat, the nylon alloy material of high comprehensive performance.
Summary of the invention
The object of this invention is to provide electrician's electrical materials and appliances flame-retardant nylon alloy material.By twin screw extruder under certain processing condition, nylon resin/toughner/toughener/fire retardant is prepared into the nylon alloy with specific phase structure by certain proportioning and technical process, this kind nylon alloy water-intake rate is low, product size good stability, dry state and low-temperature flexibility are good, flame retardant properties and resistance toheat are all increased, and is widely used at engineering field.
The object of the invention is to be realized by following technical scheme
Electrician's electrical materials and appliances flame-retardant nylon alloy material of the present invention, comprise first by a certain amount of POE(toughner), POE-g-MAH(expanding material) and compound flame retardant to add mixture in high mixer successively even, be placed in twin screw extruder extruding pelletization at 150-190 DEG C, obtained with toughness reinforcing and master batch that is anti-flaming function; Again by this kind of master batch and a certain amount of glass fibre (toughener) and PA6(nylon resin) to be placed in high mixer mixture even, and join reactive extrursion, granulation at 210-250 DEG C in twin screw extruder, obtain electrician's electrical materials and appliances flame-retardant nylon alloy material.
Embodiment
The raw material that the embodiment of the present invention uses and formula:
Nylon 6 70kg
POE(toughner) 2kg
POE-g-MAH(expanding material) 0.5kg
Glass fibre 0.5kg
Photostabilizer 0.5kg
The equipment that the embodiment of the present invention uses:
The extrusion shaping machine that granulation uses is parallel dual-screw extruding machine group KY75/180 Nanjing Ke Bei Long Keya Machinery Co., Ltd.;
The high mixer that batch mixing uses is SRL-Z500/1000 Yili Machinery Co., Ltd., Zhangjiagang City;
The above, it is only preferred embodiment of the present invention, not any pro forma restriction is done to the present invention, every above embodiment is done according to method essence of the present invention any simple modification, equivalent variations and modification, all still belong in the scope of the inventive method scheme.
Claims (2)
1.
electrician's electrical materials and appliances flame-retardant nylon alloy material, comprise material component, technical process, the dispersion state of component, and fabrication process condition.
2. electrician's electrical materials and appliances flame-retardant nylon alloy material according to claim 1, is characterized in that: wherein said material component is PA6(nylon resin), POE(toughner), POE-g-MAH(expanding material) and, glass fibre (toughener).