CN104695094A - Double-silk-ramie-surface different-weft twill fabric and processing method thereof - Google Patents
Double-silk-ramie-surface different-weft twill fabric and processing method thereof Download PDFInfo
- Publication number
- CN104695094A CN104695094A CN201310640001.8A CN201310640001A CN104695094A CN 104695094 A CN104695094 A CN 104695094A CN 201310640001 A CN201310640001 A CN 201310640001A CN 104695094 A CN104695094 A CN 104695094A
- Authority
- CN
- China
- Prior art keywords
- fabric
- yarns
- yarn
- weft
- silk
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a double-silk-ramie-surface different-weft twill fabric and a processing method thereof. The fabric is characterized in that warp yarns of the fabric adopt CJ9.7tex (compact spinning) yarns, weft yarns are formed by arranging LY/M/CJ (9.2*2) tencel ramie cotton blended yarns and JS/LY/CJ19.6 spun silk yarn tencel cotton blended yarns according to a certain ratio (the best ratio is 1:1); the warp density of the fabric is 746 warps/10 cm; the weft density is 162.5 wefts/10 cm; the breadth is 162.5 cm; the texture is made into 3/1 twills or other texture structures; the content of the fibers in the fabric is as follows: C accounts for 65.87%, LY accounts for 18.26%, JS accounts for 9.27% and M accounts for 6.6%. The double-silk-ramie-surface different-weft twill fabric has advantages that the yarns blended by spun silk, hemp yarns and tencel cotton are used for making the weft yarns; the two types of yarns integrate the characteristics of four fibers in property; the yarns can complement mutually; the defect of the single fiber component is overcome; the effect that the fabric is skin-friendly and smooth is not achieved by using one type of the yarns; the fabric has an excellent skin-friendly effect and also has roughness of the hemp yarns and the gorgeous property of the spun silk; the fabric is an excellent fabric for spring and autumn women dresses.
Description
Technical field
The present invention relates to tencel field of textiles, specifically the different weft twill fabric of a kind of mariages pitted skin and processing technology.
Background technology
Along with growth in the living standard, the requirement of people to Fashion and Accessories is also more and more higher, natural fabric is that any textile raw material is all irreplaceable with aspects such as its intrinsic texture, environmental protection, comfortable and skin-friendly, but natural fabric because of its cost high, although true, but it creases easily, not docile, these shortcomings of sag difference are difficult to solve equally.
Summary of the invention
The object of the invention is to overcome the deficiencies in the prior art, fabric location fine work dress fabric, the texture that natural fabric is intrinsic and skin-friendly are that any textile raw material is all irreplaceable, are the constant themes in fabric market, are also the eternal pursuits of people.Along with the continuous progress of science and technology, the blending of different fiber, the quasi-complement deficiency of single natural fabric, for natural fabric material adds new intension, meet the requirement of crowd to natural fabric material of different hierarchy of consumption, improve the class of product, improve the wearability of fabric.Carrying out the analysis of comparatively sufficient market popularity trend analysis and natural fiber mixed spinning performance for this reason, improve my Products competitiveness in industry, design and develop certain cost advantage unique style, weft yarn uses the novel fabric of multiple natural fiber mixed yarn.Rough and the spun silk of the fabric fiber crops that have good pro-skin effect to contain again magnificent is a splendid spring and autumn dress shell fabric.
In order to achieve the above object, a kind of SEILE textile elastic fabric of the present invention and processing technology, its feature: the 1. different weft twill fabric of mariages pitted skin and processing technology thereof, it is characterized in that: the warp thread of this fabric is CJ9.7tex (compact spinning) yarn, weft yarn adopts LY/M/CJ (9.2*2) sky silk, ramie and cotton blended yarn and JS/LY/CJ19.6 spun silk Tencel blended yarn wherein to rearrange in the mode of 1:1 optimum with certain proportion, fabric is through close 746/10cm, filling density is 162.5/10cm, fabric width is 162.5cm, tissue does twill or other institutional frameworks with 3/1, in fabric, fiber content is C65.87%, LY18.26%, JS9.27%, M6.6%, production procedure is divided into selects yarn-sizing-weave-rear whole technique.
2. according to claim 1: selecting its method of yarn to be warp is compact spinning, through the process of natural storage method.Time is optimum with 24 hours.Weft yarn can adopt the process of nature air-humidification method, and the time is optimum with 24 hours.
3. according to claim 1: sizing adopts two oar pot sizing, double flute, double-clip-double-nip process line, coverage coefficient is 77.64% is optimum.
4, according to claim 1: weave and should adopt little opening, weft yarn weft insertion technique coordinates openings of sizes to formulate, control ripple, crosspiece and centipede and produce.
4.1 specific design techniques: the back rest+1*5, warp stop frame 0, combines flat 290 ° of steady 4-300 °, combine high: 1:140 mm, 2 ~ 9:143-1mm, dobby shedding 9 pages, opening: 1 ~ 5:90 ~ 60 mm, 6 ~ 9:90 ~ 80mm, tension force 260kg, pad 2mm, input filling density 93.5s/inch(shrinkage 3%), if this fabric is by the 4 pages of calculating of ground tissue, heald density 16.65/cm, in technique allowed band (≤17), through the analysis to product specification, can weave with cam shedding weaving machine equipment.By initial design dobby shedding 9 pages, changing comprehensive number of pages into is 5 pages, cam shedding.
4.2 preferred knitting technologies: the back rest+2*3, warp stop frame 0, combines flat 290 °, steady amount 4 mm, stationary time 290 °, combines high: 1-4 page is 98-1 mm, and the 5th page is 96 mm, opening amount 1-4:160-110mm, 5:110mm, tension force 240kg, pad 2mm, fell plate 3mm combines high 1-4 page 98-1mm, 5 page of 96 mm.Input filling density 93.5s/inch(shrinkage 3%).
4.3 levels of production: speed 652rpm, efficiency 75-85%.
5. according to claim 1: dyeing and finishing technology flow process is soda boiling--oxygen bleaching-mercerising-pad dyeing-tentering material loading-preshrunk of singing.
6. according to claim 3: formula of size needed for sizing is: Nanpi-3:50KG, Nanpi-8:50KG, SQ-1:8KG, CLH-98:25KG, PVA:25KG, wax disk(-sc): 5 KG.Amount of solid: 11%, viscosity 11-12 〞.Slurry pot pressure: 8 ~ 20KN (5 ~ 70m/min), slurry pot temperature: 95 DEG C, the speed of a motor vehicle: 50m/min; Cylinder temperature: 120 DEG C, main baking temperature: 100 DEG C.Index test: destarch 16.2%, moisture regain 7.3%, yarn breaking force 297CN, percentage elongation 3.7%.
concrete enforcement
1. the different weft twill fabric of mariages pitted skin and processing technology thereof, it is characterized in that: the warp thread of this fabric is CJ9.7tex (compact spinning) yarn, weft yarn adopts LY/M/CJ (9.2*2) sky silk, ramie and cotton blended yarn and JS/LY/CJ19.6 spun silk Tencel blended yarn wherein to rearrange in the mode of 1:1 optimum with certain proportion, fabric is through close 746/10cm, filling density is 162.5/10cm, fabric width is 162.5cm, tissue does twill or other institutional frameworks with 3/1, in fabric, fiber content is C65.87%, LY18.26%, JS9.27%, M6.6%, production procedure is divided into selects yarn-sizing-weave-rear whole technique.
2. according to claim 1: selecting its method of yarn to be warp is compact spinning, through the process of natural storage method.Time is optimum with 24 hours.Weft yarn can adopt the process of nature air-humidification method, and the time is optimum with 24 hours.
3. according to claim 1: sizing adopts two oar pot sizing, double flute, double-clip-double-nip process line, coverage coefficient is 77.64% is optimum.
4, according to claim 1: weave and should adopt little opening, weft yarn weft insertion technique coordinates openings of sizes to formulate, control ripple, crosspiece and centipede and produce.
4.1 specific design techniques: the back rest+1*5, warp stop frame 0, combines flat 290 ° of steady 4-300 °, combine high: 1:140 mm, 2 ~ 9:143-1mm, dobby shedding 9 pages, opening: 1 ~ 5:90 ~ 60 mm, 6 ~ 9:90 ~ 80mm, tension force 260kg, pad 2mm, input filling density 93.5s/inch(shrinkage 3%), if this fabric is by the 4 pages of calculating of ground tissue, heald density 16.65/cm, in technique allowed band (≤17), through the analysis to product specification, can weave with cam shedding weaving machine equipment.By initial design dobby shedding 9 pages, changing comprehensive number of pages into is 5 pages, cam shedding.
4.2 preferred knitting technologies: the back rest+2*3, warp stop frame 0, combines flat 290 °, steady amount 4 mm, stationary time 290 °, combines high: 1-4 page is 98-1 mm, and the 5th page is 96 mm, opening amount 1-4:160-110mm, 5:110mm, tension force 240kg, pad 2mm, fell plate 3mm combines high 1-4 page 98-1mm, 5 page of 96 mm.Input filling density 93.5s/inch(shrinkage 3%).
4.3 levels of production: speed 652rpm, efficiency 75-85%.
5. according to claim 1: dyeing and finishing technology flow process is soda boiling--oxygen bleaching-mercerising-pad dyeing-tentering material loading-preshrunk of singing.
6. according to claim 3: formula of size needed for sizing is: Nanpi-3:50KG, Nanpi-8:50KG, SQ-1:8KG, CLH-98:25KG, PVA:25KG, wax disk(-sc): 5 KG.Amount of solid: 11%, viscosity 11-12 〞.Slurry pot pressure: 8 ~ 20KN (5 ~ 70m/min), slurry pot temperature: 95 DEG C, the speed of a motor vehicle: 50m/min; Cylinder temperature: 120 DEG C, main baking temperature: 100 DEG C.Index test: destarch 16.2%, moisture regain 7.3%, yarn breaking force 297CN, percentage elongation 3.7%.
Claims (6)
1. the different weft twill fabric of mariages pitted skin and processing technology thereof, it is characterized in that: the warp thread of this fabric is CJ9.7tex (compact spinning) yarn, weft yarn adopts LY/M/CJ (9.2*2) sky silk, ramie and cotton blended yarn and JS/LY/CJ19.6 spun silk Tencel blended yarn wherein to rearrange in the mode of 1:1 optimum with certain proportion, fabric is through close 746/10cm, filling density is 162.5/10cm, fabric width is 162.5cm, tissue does twill or other institutional frameworks with 3/1, in fabric, fiber content is C65.87%, LY18.26%, JS9.27%, M6.6%, production procedure is divided into selects yarn-sizing-weave-rear whole technique.
2., according to claim 1: selecting its method of yarn to be warp is compact spinning, through the process of natural storage method, the time is optimum with 24 hours; Yarn can adopt the process of nature air-humidification method, and the time is optimum with 24 hours.
3. according to claim 1: sizing adopts two oar pot sizing, double flute, double-clip-double-nip process line, coverage coefficient is 77.64% is optimum.
4. according to claim 1: weave and should adopt little opening, weft yarn weft insertion technique coordinates openings of sizes to formulate, control ripple, crosspiece and centipede and produce;
4.1 specific design techniques: the back rest+1*5, warp stop frame 0, combine flat 290 ° of steady 4-300 °, combine high: 1:140 mm, 2 ~ 9:143-1mm, dobby shedding 9 pages, opening: 1 ~ 5:90 ~ 60 mm, 6 ~ 9:90 ~ 80mm, tension force 260kg, pad 2mm, input filling density 93.5s/inch(shrinkage 3%), if this fabric is by the 4 pages of calculating of ground tissue, heald density 16.65/cm, in technique allowed band (≤17), through the analysis to product specification, can weave with cam shedding weaving machine equipment, by initial design dobby shedding 9 pages, changing comprehensive number of pages into is 5 pages, cam shedding,
4.2 preferred knitting technologies: the back rest+2*3, warp stop frame 0, combines flat 290 °, steady amount 4 mm, stationary time 290 °, combines high: 1-4 page is 98-1 mm, 5th page is 96 mm, opening amount 1-4:160-110mm, 5:110mm, tension force 240kg, pad 2mm, fell plate 3mm combines high 1-4 page 98-1mm, 5 page of 96 mm, input filling density 93.5s/inch(shrinkage 3%);
4.3 levels of production: speed 652rpm, efficiency 75-85%.
5. according to claim 1: dyeing and finishing technology flow process is soda boiling--oxygen bleaching-mercerising-pad dyeing-tentering material loading-preshrunk of singing.
6. according to claim 3: formula of size needed for sizing is: Nanpi-3:50KG, Nanpi-8:50KG, SQ-1:8KG, CLH-98:25KG, PVA:25KG, wax disk(-sc): 5 KG;
Amount of solid: 11%, viscosity 11-12 〞;
Slurry pot pressure: 8 ~ 20KN (5 ~ 70m/min), slurry pot temperature: 95 DEG C, the speed of a motor vehicle: 50m/min; Cylinder temperature: 120 DEG C, main baking temperature: 100 DEG C;
Index test: destarch 16.2%, moisture regain 7.3%, yarn breaking force 297CN, percentage elongation 3.7%.