CN104676458B - A kind of LED anti-reflection anti-dazzle glas lampshade and production method thereof - Google Patents
A kind of LED anti-reflection anti-dazzle glas lampshade and production method thereof Download PDFInfo
- Publication number
- CN104676458B CN104676458B CN201510066374.8A CN201510066374A CN104676458B CN 104676458 B CN104676458 B CN 104676458B CN 201510066374 A CN201510066374 A CN 201510066374A CN 104676458 B CN104676458 B CN 104676458B
- Authority
- CN
- China
- Prior art keywords
- led
- dazzle
- ethanol
- mass ratio
- white carbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of LED anti-reflection anti-dazzle glas lampshade and production method thereof, belong to glass anti-dazzle technical field.This LED is anti-reflection anti-dazzle glas lampshade, by successively carrying out plated film, anti-dazzle coating film treatment or successively carrying out anti-dazzle plated film, saturating coating film treatment or carry out the most saturating anti-dazzle coating film treatment and obtain to LED glass lamp shade surface.The method is by LED glass lamp shade pretreatment;By saturating coating liquid plated film in LED glass lamp shade surface, drying at room temperature, obtain LED anti-reflective glass lampshade;By anti-dazzle coating liquid plated film in LED saturating glass lamp shade surface, after carrying out cured cooling in high temperature furnace, obtain LED anti-reflection anti-dazzle glas lampshade.The production method of a kind of LED of the present invention anti-reflection anti-dazzle glas lampshade, production technology is simple, low cost, is suitable for industrial-scale production, the LED anti-reflection anti-dazzle glas lampshade light transmittance produced and anti-dazzle performance significantly improve, and can significantly improve luminous flux and the antiglare effect of light fixture.
Description
Technical field
The present invention relates to glass anti-dazzle technical field, particularly to a kind of LED anti-reflection anti-dazzle glas lampshade and producer thereof
Method.
Background technology
Owing to LED luminous efficiency improves constantly, and have that life-span length, volume be little, tunable optical, the photochromic advantage such as abundant,
Popularity rate in lighting application market improves the most rapidly, and the characteristics of luminescence phase of the characteristics of luminescence of LED light source and conventional light source
Difference is very remote, in addition to optical design maneuver is completely different, owing to LED light-emitting area is less than the light-emitting area of conventional light source, causes
Glare problem is serious.Particular design through fitting structure can partly reduce the glare problem of LED, such as patent
CN2013101371818, CN201310265674X, CN201310589770X, propose special LED lamp respectively
Anti-dazzle design, more structurally sound method is then the glare reduction techniques using lampshade, as the micropartical being used for traditional monitor industry mixed
Miscellaneous diffuser plate as LED lamp cover or the PMMA lampshade that uses frosted, but diffuser plate lampshade or frosted PMMA lampshade by
Relatively low in its light transmission rate, cause the luminous efficiency of LED lamp substantially to reduce, cause the waste of the energy.
Summary of the invention
The present invention provides a kind of LED anti-reflection anti-dazzle glas lampshade, it is therefore intended that overcome existing LED glass lamp shade anti-dazzle
The defect that in technology, lampshade light transmittance is relatively low.It is a further object of the present invention to provide the production of a kind of LED anti-reflection anti-dazzle glas lampshade
Method.
The present invention be the technical scheme is that a kind of LED anti-reflection anti-dazzle glas lampshade, its feature for achieving the above object
Be: by LED glass lamp shade surface is successively carried out plated film, anti-dazzle coating film treatment or successively carry out anti-dazzle plated film,
Thoroughly coating film treatment or carry out the most saturating anti-dazzle coating film treatment and obtain.
The production method of a kind of LED is anti-reflection anti-dazzle glas lampshade, it is characterised in that: comprise the following steps:
(1) LED glass lamp shade pure water is cleaned up, be dried in an oven, cooling;
(2) by saturating coating liquid plated film in LED glass lamp shade surface, drying at room temperature, LED anti-reflective glass lampshade is obtained;
(3) by anti-dazzle coating liquid plated film in LED saturating glass lamp shade surface, high temperature furnace carries out cured, process temperature
Degree is 500~720 DEG C, obtains LED anti-reflection anti-dazzle glas lampshade after cooling.
The production method of a kind of LED is anti-reflection anti-dazzle glas lampshade, it is characterised in that: comprise the following steps:
(1) LED glass lamp shade pure water is cleaned up, be dried in an oven, cooling;
(2) anti-dazzle coating liquid being sprayed at LED glass lamp shade surface, carry out cured in high temperature furnace, treatment temperature is
200~250 DEG C, after cooling, obtain LED anti-dazzle glas lampshade;
(3) by saturating coating liquid dip-coating in LED anti-dazzle glas cover surface, high temperature furnace carries out cured, process temperature
Degree is 500~720 DEG C, obtains LED saturating anti-dazzle glas lampshade after cooling.
Further, described coating liquid is prepared by following steps:
(1) tetraethoxysilane is disperseed in ethanol, add the aqueous acetic acid that concentration is 0.1~0.3N, ethanol and tetrem
The mass ratio of TMOS is 1~2, and ethanol is 1~2 with the mass ratio of acetum, is stirred at room temperature at least 24 hours,
By rotary evaporation, concentrating silica is obtained Nano silica sol 1;
(2) tetraethoxysilane is disperseed in ethanol, add the ammonia that concentration is 0.1~0.2N, ethanol and tetraethoxy-silicane
The mass ratio of alkane is 5~7, and ethanol is 10~12 with the mass ratio of ammonia spirit, is stirred at room temperature at least 24 hours, passes through
Rotary evaporation, obtains Nano silica sol 2 by concentrating silica;
(3) under magnetic stirring, Nano silica sol 1 is joined in the mixed solution of ethanol and isopropanol, ethanol and isopropyl
The mass ratio of alcohol is 1, magnetic agitation uniformly after, continue to be slowly added into by Nano silica sol 2 under magnetic stirring above-mentioned
In the solution of stirring, after addition, it is stirred at room temperature reaction at least 12 hours, prepares coating liquid.
Further, described anti-dazzle coating liquid is prepared by following steps:
(1) tetraethoxysilane is disperseed in ethanol, add the aqueous hydrochloric acid solution that concentration is 0.1~0.3N, ethanol and tetrem
The mass ratio of TMOS is 1~2, and ethanol is 1~2 with the mass ratio of hydrochloric acid solution, is stirred at room temperature at least 24 hours,
By rotary evaporation, concentrating silica is obtained Nano silica sol 4;
(2) white carbon is joined in isopropanol, adds silicone active agent, the mass ratio of isopropanol and white carbon be 20~
50, white carbon is 30~50 with the mass ratio of silicone active agent, is stirred at room temperature and obtains homodisperse white carbon dispersion liquid;
(3) under magnetic stirring, gained white carbon dispersion liquid in step (2) is slowly added in Nano silica sol 4, adds
After, it is stirred at room temperature uniformly, prepares anti-dazzle coating liquid.
The production method of a kind of LED is anti-reflection anti-dazzle glas lampshade, it is characterised in that: comprise the following steps:
(1) LED glass lamp shade pure water is cleaned up, be dried in an oven, cooling;
(2) by saturating anti-dazzle coating liquid plated film in LED glass lamp shade surface, high temperature furnace carries out cured, process temperature
Degree is 500~720 DEG C, obtains LED saturating anti-dazzle glas lampshade after cooling.
Further, described anti-dazzle coating liquid is prepared by following steps:
(1) white carbon is joined in isopropanol, adds silicone active agent, the mass ratio of isopropanol and white carbon be 10~
20, white carbon is 40~60 with the mass ratio of silicone active agent, is stirred at room temperature and obtains homodisperse white carbon dispersion liquid;
(2) under magnetic stirring, gained white carbon dispersion liquid in step (1) is slowly added in coating liquid, has added
Bi Hou, is stirred at room temperature uniformly, prepares anti-dazzle coating liquid.
The production method of a kind of LED of the present invention anti-reflection anti-dazzle glas lampshade, production technology is simple, and low cost is suitable
Closing industrial-scale production, the LED anti-reflection anti-dazzle glas lampshade light transmittance produced and anti-dazzle performance significantly improve, Ke Yiming
The aobvious luminous flux improving light fixture and antiglare effect.
Accompanying drawing explanation
Fig. 1 is light design sketch when passing through common LED glass lamp shade.
Fig. 2 is that light is by utilizing design sketch during LED of the present invention anti-reflection anti-dazzle glas lampshade.
Detailed description of the invention
Embodiment 1
First, coating liquid is prepared by following steps:
(1) being dispersed in 450g ethanol by 313g tetraethoxysilane, adding 233g concentration is the aqueous acetic acid of 0.2N,
It is stirred at room temperature 24 hours, by rotary evaporation, concentrating silica is obtained 460g Nano silica sol 1;
(2) being dispersed in 1080g ethanol by 178g tetraethoxysilane, adding 98g concentration is the ammonia of 0.16N, in room
The lower stirring of temperature 24 hours, by rotary evaporation, obtains 630g Nano silica sol 2 by concentrating silica;
(3) mixing that under magnetic stirring, 460g Nano silica sol 1 joins 1210g ethanol and 1210g isopropanol is molten
In liquid, magnetic agitation uniformly after, continue to be slowly added into by 630g Nano silica sol 2 under magnetic stirring and above-mentioned stirring
In solution, after addition, it is stirred at room temperature reaction 12 hours, prepares coating liquid.
Secondly, anti-dazzle coating liquid is prepared by following steps:
(1) being dispersed in 400g ethanol by 270g tetraethoxysilane, adding 233g concentration is the aqueous hydrochloric acid solution of 0.2N,
It is stirred at room temperature 24 hours, by rotary evaporation, concentrating silica is obtained 360g Nano silica sol 4;
(2) 3.9g white carbon is joined in 120g isopropanol, add 0.1g silicone active agent, be stirred at room temperature
Obtain homodisperse white carbon dispersion liquid;
(3) under magnetic stirring, gained white carbon dispersion liquid in step (2) is slowly added in 360g Nano silica sol 4,
After addition, it is stirred at room temperature uniformly, prepares anti-dazzle coating liquid.
A kind of LED anti-reflection anti-dazzle glas lampshade, by successively carrying out plated film, anti-dazzle plating to LED glass lamp shade surface
Film processes and obtains, and specifically includes following steps:
(1) LED glass lamp shade pure water is cleaned up, be dried in an oven, cooling;
(2) by saturating coating liquid plated film in LED glass lamp shade surface, drying at room temperature, LED anti-reflective glass lampshade is obtained;
(3) by anti-dazzle coating liquid plated film in LED saturating glass lamp shade surface, high temperature furnace carries out cured, process temperature
Degree is 720 DEG C, obtains LED anti-reflection anti-dazzle glas lampshade after cooling.
Embodiment 2
A kind of LED anti-reflection anti-dazzle glas lampshade, by successively carrying out anti-dazzle plated film to LED glass lamp shade surface, thoroughly plate
Film processes and obtains, and specifically includes following steps:
(1) LED glass lamp shade pure water is cleaned up, be dried in an oven, cooling;
(2) anti-dazzle coating liquid being sprayed at LED glass lamp shade surface, carry out cured in high temperature furnace, treatment temperature is
200 DEG C, after cooling, obtain LED anti-dazzle glas lampshade;
(3) by saturating coating liquid dip-coating in LED anti-dazzle glas cover surface, high temperature furnace carries out cured, process temperature
Degree is 500 DEG C, obtains LED saturating anti-dazzle glas lampshade after cooling.
Embodiment 3
First, anti-dazzle coating liquid is prepared by following steps:
(1) 5.6g white carbon is joined in 100g isopropanol, add 0.1g silicone active agent, be stirred at room temperature
Obtain homodisperse white carbon dispersion liquid;
(2) under magnetic stirring, gained white carbon dispersion liquid in step (1) is slowly added in coating liquid, has added
Bi Hou, is stirred at room temperature uniformly, prepares anti-dazzle coating liquid.
A kind of LED anti-reflection anti-dazzle glas lampshade, by carrying out the most saturating anti-dazzle coating film treatment to LED glass lamp shade surface
Obtain, specifically include following steps:
(1) LED glass lamp shade pure water is cleaned up, be dried in an oven, cooling;
(2) by saturating anti-dazzle coating liquid plated film in LED glass lamp shade surface, high temperature furnace carries out cured, process temperature
Degree is 600 DEG C, obtains LED saturating anti-dazzle glas lampshade after cooling.
Claims (4)
1. a LED anti-reflection anti-dazzle glas lampshade, it is characterised in that: by LED glass lamp shade surface first
After carry out plated film, anti-dazzle coating film treatment or successively carry out anti-dazzle plated film, saturating coating film treatment or carry out one
Secondary anti-dazzle coating film treatment obtains;
Solution used by described coating film treatment is prepared by following steps:
(1) tetraethoxysilane is disperseed in ethanol, add the aqueous acetic acid that concentration is 0.1~0.3N, second
Alcohol is 1~2 with the mass ratio of tetraethoxysilane, and ethanol is 1~2 with the mass ratio of acetum, in room temperature
Lower stirring at least 24 hours, by rotary evaporation, obtains Nano silica sol 1 by concentrating silica;
(2) tetraethoxysilane is disperseed in ethanol, add the ammonia that concentration is 0.1~0.2N, ethanol and four
The mass ratio of Ethoxysilane is 5~7, and ethanol is 10~12 with the mass ratio of ammonia spirit, at room temperature stirs
Mix at least 24 hours, by rotary evaporation, concentrating silica is obtained Nano silica sol 2;
(3) under magnetic stirring, Nano silica sol 1 is joined in the mixed solution of ethanol and isopropanol, ethanol
It is 1 with the mass ratio of isopropanol, after magnetic agitation is uniform, continues to be delayed by Nano silica sol 2 under magnetic stirring
Slowly join in the above-mentioned solution stirred, after addition, be stirred at room temperature reaction at least 12 hours,
Prepare coating liquid;
Solution used by described anti-dazzle coating film treatment is prepared by following steps:
(1) tetraethoxysilane is disperseed in ethanol, add the aqueous hydrochloric acid solution that concentration is 0.1~0.3N, second
Alcohol is 1~2 with the mass ratio of tetraethoxysilane, and ethanol is 1~2 with the mass ratio of hydrochloric acid solution, in room temperature
Lower stirring at least 24 hours, by rotary evaporation, obtains Nano silica sol 4 by concentrating silica;
(2) white carbon is joined in isopropanol, add the quality of silicone active agent, isopropanol and white carbon
Ratio is 20~50, and white carbon is 30~50 with the mass ratio of silicone active agent, is stirred at room temperature and obtains all
Even scattered white carbon dispersion liquid;
(3) under magnetic stirring, gained white carbon dispersion liquid in step (2) is slowly added into Nano silica sol 4
In, after addition, it is stirred at room temperature uniformly, prepares anti-dazzle coating liquid;
Solution used by the most saturating described anti-dazzle coating film treatment is prepared by following steps:
(1) white carbon is joined in isopropanol, add the quality of silicone active agent, isopropanol and white carbon
Ratio is 10~20, and white carbon is 40~60 with the mass ratio of silicone active agent, is stirred at room temperature and obtains all
Even scattered white carbon dispersion liquid;
(2) under magnetic stirring, gained white carbon dispersion liquid in step (1) is slowly added in coating liquid,
After addition, it is stirred at room temperature uniformly, prepares anti-dazzle coating liquid.
The production method of a kind of LED the most according to claim 1 anti-reflection anti-dazzle glas lampshade, its feature exists
In: comprise the following steps:
(1) tetraethoxysilane is disperseed in ethanol, add the aqueous acetic acid that concentration is 0.1~0.3N, second
Alcohol is 1~2 with the mass ratio of tetraethoxysilane, and ethanol is 1~2 with the mass ratio of acetum, in room temperature
Lower stirring at least 24 hours, by rotary evaporation, obtains Nano silica sol 1 by concentrating silica;
(2) tetraethoxysilane is disperseed in ethanol, add the ammonia that concentration is 0.1~0.2N, ethanol and four
The mass ratio of Ethoxysilane is 5~7, and ethanol is 10~12 with the mass ratio of ammonia spirit, at room temperature stirs
Mix at least 24 hours, by rotary evaporation, concentrating silica is obtained Nano silica sol 2;
(3) under magnetic stirring, Nano silica sol 1 is joined in the mixed solution of ethanol and isopropanol, ethanol
It is 1 with the mass ratio of isopropanol, after magnetic agitation is uniform, continues to be delayed by Nano silica sol 2 under magnetic stirring
Slowly join in the above-mentioned solution stirred, after addition, be stirred at room temperature reaction at least 12 hours,
Prepare coating liquid;
(4) tetraethoxysilane is disperseed in ethanol, add the aqueous hydrochloric acid solution that concentration is 0.1~0.3N, second
Alcohol is 1~2 with the mass ratio of tetraethoxysilane, and ethanol is 1~2 with the mass ratio of hydrochloric acid solution, in room temperature
Lower stirring at least 24 hours, by rotary evaporation, obtains Nano silica sol 4 by concentrating silica;
(5) white carbon is joined in isopropanol, add the quality of silicone active agent, isopropanol and white carbon
Ratio is 20~50, and white carbon is 30~50 with the mass ratio of silicone active agent, is stirred at room temperature and obtains all
Even scattered white carbon dispersion liquid;
(6) under magnetic stirring, gained white carbon dispersion liquid in step (2) is slowly added into Nano silica sol 4
In, after addition, it is stirred at room temperature uniformly, prepares anti-dazzle coating liquid;
(7) LED glass lamp shade pure water is cleaned up, be dried in an oven, cooling;
(8) by saturating coating liquid plated film in LED glass lamp shade surface, drying at room temperature, LED anti-reflective glass is obtained
Lampshade;
(9) by anti-dazzle coating liquid plated film in LED saturating glass lamp shade surface, high temperature furnace carries out cured,
Treatment temperature is 500~720 DEG C, obtains LED anti-reflection anti-dazzle glas lampshade after cooling.
The production method of a kind of LED the most according to claim 1 anti-reflection anti-dazzle glas lampshade, its feature exists
In: comprise the following steps:
(1) tetraethoxysilane is disperseed in ethanol, add the aqueous acetic acid that concentration is 0.1~0.3N, second
Alcohol is 1~2 with the mass ratio of tetraethoxysilane, and ethanol is 1~2 with the mass ratio of acetum, in room temperature
Lower stirring at least 24 hours, by rotary evaporation, obtains Nano silica sol 1 by concentrating silica;
(2) tetraethoxysilane is disperseed in ethanol, add the ammonia that concentration is 0.1~0.2N, ethanol and four
The mass ratio of Ethoxysilane is 5~7, and ethanol is 10~12 with the mass ratio of ammonia spirit, at room temperature stirs
Mix at least 24 hours, by rotary evaporation, concentrating silica is obtained Nano silica sol 2;
(3) under magnetic stirring, Nano silica sol 1 is joined in the mixed solution of ethanol and isopropanol, ethanol
It is 1 with the mass ratio of isopropanol, after magnetic agitation is uniform, continues to be delayed by Nano silica sol 2 under magnetic stirring
Slowly join in the above-mentioned solution stirred, after addition, be stirred at room temperature reaction at least 12 hours,
Prepare coating liquid;
(4) tetraethoxysilane is disperseed in ethanol, add the aqueous hydrochloric acid solution that concentration is 0.1~0.3N, second
Alcohol is 1~2 with the mass ratio of tetraethoxysilane, and ethanol is 1~2 with the mass ratio of hydrochloric acid solution, in room temperature
Lower stirring at least 24 hours, by rotary evaporation, obtains Nano silica sol 4 by concentrating silica;
(5) white carbon is joined in isopropanol, add the quality of silicone active agent, isopropanol and white carbon
Ratio is 20~50, and white carbon is 30~50 with the mass ratio of silicone active agent, is stirred at room temperature and obtains all
Even scattered white carbon dispersion liquid;
(6) under magnetic stirring, gained white carbon dispersion liquid in step (2) is slowly added into Nano silica sol 4
In, after addition, it is stirred at room temperature uniformly, prepares anti-dazzle coating liquid;
(7) LED glass lamp shade pure water is cleaned up, be dried in an oven, cooling;
(8) anti-dazzle coating liquid is sprayed at LED glass lamp shade surface, high temperature furnace carries out cured, place
Reason temperature is 200~250 DEG C, obtains LED anti-dazzle glas lampshade after cooling;
(9) by saturating coating liquid dip-coating in LED anti-dazzle glas cover surface, high temperature furnace carries out cured,
Treatment temperature is 500~720 DEG C, obtains LED saturating anti-dazzle glas lampshade after cooling.
The production method of a kind of LED the most according to claim 1 anti-reflection anti-dazzle glas lampshade, its feature exists
In: comprise the following steps:
(1) white carbon is joined in isopropanol, add the quality of silicone active agent, isopropanol and white carbon
Ratio is 10~20, and white carbon is 40~60 with the mass ratio of silicone active agent, is stirred at room temperature and obtains all
Even scattered white carbon dispersion liquid;
(2) under magnetic stirring, gained white carbon dispersion liquid in step (1) is slowly added in coating liquid,
After addition, it is stirred at room temperature uniformly, prepares anti-dazzle coating liquid;
(3) LED glass lamp shade pure water is cleaned up, be dried in an oven, cooling;
(4) by saturating anti-dazzle coating liquid plated film in LED glass lamp shade surface, high temperature furnace carries out cured,
Treatment temperature is 500~720 DEG C, obtains LED saturating anti-dazzle glas lampshade after cooling.