CN104673046B - Anode steel claw graphite-based masking liquid - Google Patents
Anode steel claw graphite-based masking liquid Download PDFInfo
- Publication number
- CN104673046B CN104673046B CN201510108777.4A CN201510108777A CN104673046B CN 104673046 B CN104673046 B CN 104673046B CN 201510108777 A CN201510108777 A CN 201510108777A CN 104673046 B CN104673046 B CN 104673046B
- Authority
- CN
- China
- Prior art keywords
- graphite
- anode steel
- steel claw
- masking liquid
- based masking
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention provides a kind of anode steel claw graphite-based masking liquid, by weight percentage, it is made up of following components：1000 mesh graphite powders 18.2~23.3%；Water soluble phenol resin 0.8~1.5%；Glass dust 0.12~0.33%；CMC 0.1~0.38%；Alkylbenzene 0.1~0.25%；Defoamer 0.1~0.25%；Bactericide 0.04~0.13%；Deionized water surplus.Compared with correlation technique, beneficial effect of the present invention is effectively to prevent anode steel claw from gluing iron, improving working environment, improve casting quality and reduce production cost.
Description
【Technical field】
The present invention relates to masking liquid technical field, more particularly to a kind of anode steel claw graphite-based masking liquid.
【Background technology】
For the ease of Ferropho hours ring pressure-disengaging, it will usually gone in anode steel claw cast and dry on anode steel claw dip in graphite powder or dip in attached
The graphite powder or smearing graphite-based masking liquid reconciled through kerosene.And the dry graphite powder that dips in of anode steel claw is disadvantageous in that：Anode steel
Attached graphite powder amount is dipped on pawl less, dip in attached uneven, viscous iron is more on anode steel claw after Ferropho hours ring pressure-disengaging, easy scratch anode steel
Pawl；The attached graphite powder reconciled through kerosene is dipped in be disadvantageous in that：Flue gas is larger when anode steel claw is poured into a mould, and working environment is poor,
And molten iron bubbling during casting, cast second-rate；Graphite-based masking liquid in correlation technique is disadvantageous in that：It is expensive,
More than 30,000/ton.So as to how to provide a kind of preventing anode steel claw from glue iron, improving working environment, improves quality of casting
The anode steel claw of production cost can also be reduced simultaneously turns into the problem of those skilled in the art institute facing with graphite-based masking liquid.
Therefore, it is necessary that provide a kind of new anode steel claw overcomes above-mentioned technical problem with graphite-based masking liquid in fact.
【The content of the invention】
The technical problem to be solved in the invention is to provide one kind can effectively prevent anode steel claw from gluing iron, improving building ring
Border, the anode steel claw graphite-based masking liquid for improving casting quality and reduction production cost.
A kind of anode steel claw graphite-based masking liquid of the present invention, by weight percentage, is made up of following components：1000 mesh stones
Ink powder 18.2~23.3%；Water soluble phenol resin 0.8~1.5%；Glass dust 0.12~0.33%；CMC
0.1~0.38%；Alkylbenzene 0.1~0.25%；Defoamer 0.1~0.25%；Bactericide 0.04~0.13%；More than deionized water
Amount.
Compared with correlation technique, the beneficial effects of the present invention are graphite powder is evenly distributed in deionized water, is difficult point
Layer, anode steel claw graphite-based masking liquid dips in attached uniform on anode steel claw, and Ferropho hours ring pressure-disengaging effect preferably, effectively prevent anode
Steel pawl glues iron；Working environment is improved, casting quality is improve；Anode steel claw is stronger with graphite-based coating liquid electrical conductivity, can be effective
Iron carbon pressure drop is reduced, and then effectively reduces power consumption, reduce production cost, and, anode steel claw graphite-based masking liquid cost
It is relatively low, it is 10,000/ton, compared to the masking liquid in correlation technique, greatly reduce the production cost for anode steel claw casting.
【Specific embodiment】
With reference to implementation method, the invention will be further described.
A kind of anode steel claw graphite-based masking liquid of the present invention, by weight percentage, is made up of following components：1000 mesh stones
Ink powder 18.2~23.3%；Water soluble phenol resin 0.8~1.5%；Glass dust 0.12~0.33%；CMC
0.1~0.38%；Alkylbenzene 0.1~0.25%；Defoamer 0.1~0.25%；Bactericide 0.04~0.13%；More than deionized water
Amount.
It is dissolved in the deionized water for weighing in proportion after above-mentioned other components in addition to deionized water are weighed in proportion,
Then all pour into mechanical agitation cylinder, mechanical agitation is all put into ultrasonic cleaner and disperses 40 minutes i.e. after 10 minutes
Obtain the anode steel claw graphite-based masking liquid that Graphite Distribution is uniform, electric conductivity is strong.
Graphite powder is evenly distributed in deionized water, is difficult layering, and anode steel claw graphite-based masking liquid is on anode steel claw
Dip in attached uniform, Ferropho hours ring pressure-disengaging effect preferably, effectively prevent the viscous iron of anode steel claw；Working environment is improved, casting is improve
Quality；Anode steel claw is stronger with graphite-based coating liquid electrical conductivity, can effectively reduce iron carbon pressure drop, and then effectively reduces power consumption, drops
Low production cost, and, anode steel claw is relatively low with graphite-based masking liquid cost, is 10,000/ton, compared to the painting in correlation technique
Liquid, greatly reduces the production cost for anode steel claw casting.
With regard to specific embodiment, the present invention is further described below.
Embodiment one：
A kind of anode steel claw graphite-based masking liquid, is made up of following components：1000 mesh graphite powder 18.2kg；Water soluble phenolic
Resin 0.8kg；Glass dust 0.12kg；CMC 0.1kg；Alkylbenzene 0.1kg；Defoamer 0.1kg；Bactericide
0.04kg；Deionized water 80.54kg.
Other components of corresponding weight in addition to deionized water are dissolved in the deionized water of correspondence weight, then all
Pour into mechanical agitation cylinder, mechanical agitation is all put into dispersion in ultrasonic cleaner and obtains graphite in 40 minutes after 10 minutes
Be evenly distributed, the anode steel claw graphite-based masking liquid that electric conductivity is strong.
Embodiment two：
A kind of anode steel claw graphite-based masking liquid, is made up of following components：1000 mesh graphite powder 19kg；Water soluble phenolic resin
Fat 0.9kg；Glass dust 0.15kg；CMC 0.15kg；Alkylbenzene 0.15kg；Defoamer 0.15kg；Bactericide
0.06kg；Deionized water 79.44kg.
Other components of corresponding weight in addition to deionized water are dissolved in the deionized water of correspondence weight, then all
Pour into mechanical agitation cylinder, mechanical agitation is all put into dispersion in ultrasonic cleaner and obtains graphite in 40 minutes after 10 minutes
Be evenly distributed, the anode steel claw graphite-based masking liquid that electric conductivity is strong.
Embodiment three：
A kind of anode steel claw graphite-based masking liquid, is made up of following components：1000 mesh graphite powder 20kg；Water soluble phenolic resin
Fat 1.0kg；Glass dust 0.18kg；CMC 0.18kg；Alkylbenzene 0.20kg；Defoamer 0.18kg；Bactericide
0.08kg；Deionized water 78.18kg.
Other components of corresponding weight in addition to deionized water are dissolved in the deionized water of correspondence weight, then all
Pour into mechanical agitation cylinder, mechanical agitation is all put into dispersion in ultrasonic cleaner and obtains graphite in 40 minutes after 10 minutes
Be evenly distributed, the anode steel claw graphite-based masking liquid that electric conductivity is strong.
Example IV：
A kind of anode steel claw graphite-based masking liquid, is made up of following components：1000 mesh graphite powder 21kg；Water soluble phenolic resin
Fat 1.2kg；Glass dust 0.25kg；CMC 0.25kg；Alkylbenzene 0.22kg；Defoamer 0.20kg；Bactericide
0.1kg；Deionized water 76.78kg.
Other components of corresponding weight in addition to deionized water are dissolved in the deionized water of correspondence weight, then all
Pour into mechanical agitation cylinder, mechanical agitation is all put into dispersion in ultrasonic cleaner and obtains graphite in 40 minutes after 10 minutes
Be evenly distributed, the anode steel claw graphite-based masking liquid that electric conductivity is strong.
Embodiment five：
A kind of anode steel claw graphite-based masking liquid, is made up of following components：1000 mesh graphite powder 22kg；Water soluble phenolic resin
Fat 1.3kg；Glass dust 0.3kg；CMC 0.35kg；Alkylbenzene 0.23kg；Defoamer 0.22kg；Bactericide
0.11kg；Deionized water 75.49kg.
Other components of corresponding weight in addition to deionized water are dissolved in the deionized water of correspondence weight, then all
Pour into mechanical agitation cylinder, mechanical agitation is all put into dispersion in ultrasonic cleaner and obtains graphite in 40 minutes after 10 minutes
Be evenly distributed, the anode steel claw graphite-based masking liquid that electric conductivity is strong.
Embodiment six：
A kind of anode steel claw graphite-based masking liquid, is made up of following components：1000 mesh graphite powder 23.3kg；Water soluble phenolic
Resin 1.5kg；Glass dust 0.33kg；CMC 0.38kg；Alkylbenzene 0.25kg；Defoamer 0.25kg；Bactericide
0.13kg；Deionized water 73.86kg.
Other components of corresponding weight in addition to deionized water are dissolved in the deionized water of correspondence weight, then all
Pour into mechanical agitation cylinder, mechanical agitation is all put into dispersion in ultrasonic cleaner and obtains graphite in 40 minutes after 10 minutes
Be evenly distributed, the anode steel claw graphite-based masking liquid that electric conductivity is strong.
Compared with correlation technique, the beneficial effects of the present invention are, effectively prevent anode steel claw glue iron, improve building ring
Border, raising casting quality and reduction production cost.
Above-described is only embodiments of the present invention, it should be noted here that for one of ordinary skill in the art
For, without departing from the concept of the premise of the invention, improvement can also be made, but these belong to protection model of the invention
Enclose.
Claims (1)
1. a kind of anode steel claw graphite-based masking liquid, it is characterised in that：Anode steel claw graphite-based masking liquid percentage by weight
Than meter, it is made up of following components：
The % of 1000 mesh graphite powder 18.2~23.3；
The % of water soluble phenol resin 0.8~1.5；
The % of glass dust 0.12~0.33；
The % of sodium carboxymethylcellulose 0.1~0.38；
The % of alkylbenzene 0.1~0.25；
The % of defoamer 0.1~0.25；
The % of bactericide 0.04~0.13；
Deionized water surplus.