CN104672567A - Dust-proof rubber cover for automobile - Google Patents
Dust-proof rubber cover for automobile Download PDFInfo
- Publication number
- CN104672567A CN104672567A CN201510045527.0A CN201510045527A CN104672567A CN 104672567 A CN104672567 A CN 104672567A CN 201510045527 A CN201510045527 A CN 201510045527A CN 104672567 A CN104672567 A CN 104672567A
- Authority
- CN
- China
- Prior art keywords
- parts
- dust
- rubber cover
- proof rubber
- automobile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a dust-proof rubber cover for an automobile. The dust-proof rubber cover is prepared from the following raw materials in parts by weight: 25-35 parts of 1,3-butadiene, 25-35 parts of styrene, 20-26 parts of nickel naphthenate, 15-19 parts of triisobutyl aluminum, 10-16 parts of isoprene, 8-12 parts of ethylene, 8-12 parts of propylene, 10-16 parts of dicyclopentadiene, 3-5 parts of rosin, 3-5 parts of ethylidene norbornene, 20-24 parts of 1-allylpropene, 12-16 parts of zinc oxide, 5-8 parts of clay, 5-8 parts of chalk, 7-12 parts of baryte, 7-15 parts of carbon black, 3-5 parts of methylbenzene and 1-2 parts of toluene-heptane. The dust-proof rubber cover for the automobile disclosed by the invention has the beneficial effects that the aging speed of the rubber can be effectively reduced, and the wear-resisting property of the rubber is improved; and compared with the commercially available products, the dust-proof rubber cover has the advantages that the aging speed is reduced by 30 percent, and the wear-resisting property improved by 50 percent.
Description
Technical field
The present invention relates to a kind of automobile boot seal.
Background technology
Dirt-proof boot, as the term suggests be exactly dust-proof rubber coating, position is mainly distributed in turning device's shaft portion, and other distribution is also very wide, such as parking brake, service brake, throttle line, master cylinder, wheel cylinder etc.But owing to wearing and tearing greatly mostly in these positions, very easily there is aging and wear phenomenon in dirt-proof boot.
Summary of the invention
Object of the present invention is exactly for above-mentioned defect of the prior art, provides a kind of automobile boot seal.
To achieve these goals, technical scheme provided by the invention is: a kind of automobile boot seal, prepared by the following raw material according to parts by weight: 1, 3-divinyl 25-35 part, vinylbenzene 25-35 part, nickel naphthenate 20-26 part, triisobutyl aluminium 15-19 part, isoprene 10-16 part, ethene 8-12 part, propylene 8-12 part, dicyclopentadiene 10-16 part, rosin 3-5 part, ethylidene norbornene 3-5 part, 1, 4-hexadiene 20-24 part, zinc oxide 12-16 part, clay 5-8 part, chalk 5-8 part, barite 7-12 part, carbon black 7-15 part, toluene 3-5 part, toluene-heptane 1-2 part.
Beneficial effect of the present invention is: a kind of automobile boot seal provided by the invention, effectively can slow down the aging speed of rubber, improve the wear resisting property of rubber, and compared with commercially available prod, aging speed reduces by 30%, and wear resisting property improves 50%.
Embodiment
embodiment 1:
A kind of automobile boot seal, prepared by the following raw material according to parts by weight: 1,3-divinyl 25-35 part, vinylbenzene 25-35 part, nickel naphthenate 20-26 part, triisobutyl aluminium 15-19 part, isoprene 10-16 part, ethene 8-12 part, propylene 8-12 part, dicyclopentadiene 10-16 part, rosin 3-5 part, ethylidene norbornene 3-5 part, Isosorbide-5-Nitrae-hexadiene 20-24 part, zinc oxide 12-16 part, clay 5-8 part, chalk 5-8 part, barite 7-12 part, carbon black 7-15 part, toluene 3-5 part, toluene-heptane 1-2 part.
Last it is noted that the foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, although with reference to previous embodiment to invention has been detailed description, for a person skilled in the art, it still can be modified to the technical scheme described in foregoing embodiments, or carries out equivalent replacement to wherein portion of techniques feature.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (1)
1. an automobile boot seal, it is characterized in that, prepared by the following raw material according to parts by weight: 1,3-divinyl 25-35 part, vinylbenzene 25-35 part, nickel naphthenate 20-26 part, triisobutyl aluminium 15-19 part, isoprene 10-16 part, ethene 8-12 part, propylene 8-12 part, dicyclopentadiene 10-16 part, rosin 3-5 part, ethylidene norbornene 3-5 part, Isosorbide-5-Nitrae-hexadiene 20-24 part, zinc oxide 12-16 part, clay 5-8 part, chalk 5-8 part, barite 7-12 part, carbon black 7-15 part, toluene 3-5 part, toluene-heptane 1-2 part.