CN104671770A - 一种制造电阻的方法 - Google Patents
一种制造电阻的方法 Download PDFInfo
- Publication number
- CN104671770A CN104671770A CN201310634529.4A CN201310634529A CN104671770A CN 104671770 A CN104671770 A CN 104671770A CN 201310634529 A CN201310634529 A CN 201310634529A CN 104671770 A CN104671770 A CN 104671770A
- Authority
- CN
- China
- Prior art keywords
- per hour
- hour
- hours
- room temperature
- cooled
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种电阻的制造方法,电阻材料由氧化锌、三氧化二铋、四氧化三钴、氧化亚镍、三氧化二铬、硝酸铝、银玻璃、聚乙烯醇和分散剂组成,其组分重量比为80-90%、0.5-1.5%、0.5-2%、1-2%、1-2.5%、0.5-1.5%、1-2.5%、0.5-2.5%,其余为分散剂,其特征在于将以上材料按照以上组分配比添加到硝酸盐溶液中,接着经过充分混合、溶解、干燥、压制成型,最后在惰性气体气氛下从室温开始以每小时150-200℃的速度升到900℃,再以40-80℃升温到1400-1600℃时保持3-9小时,然后进行分阶段冷却:以每小时80-100℃冷却到1100℃保持3-5小时,再以每小时80-100℃冷却到900℃保持3-5小时,再以每小时80-110℃冷却到室温为止。
Description
技术领域
本发明涉及一种制造电阻的方法。
背景技术
随着科学技术的迅速发展,电子器件以及分立元件的应用日益广泛,其中电阻元件更是使用最多的一种,虽然目前制造电阻的方法在现有技术中已有广泛报道,但是目前的制造电阻方法已不能满足目前的实际需要,尤其是在后期的烧结和冷却阶段温度控制是一个难题,亟需一种新型的能够很好地控制烧结温度而制造电阻的方法。
发明内容
本发明提供一种电阻的制造方法,电阻材料由氧化锌、三氧化二铋、四氧化三钴、氧化亚镍、三氧化二铬、硝酸铝、银玻璃、聚乙烯醇和分散剂组成,其组分重量比为80-90%、0.5-1.5%、0.5-2%、1-2%、1-2.5%、0.5-1.5%、1-2.5%、0.5-2.5%,其余为分散剂,其特征在于,将以上材料按照以上组分配比添加到硝酸盐溶液中,接着经过充分混合、溶解、干燥、压制成型,最后在惰性气体气氛下从室温开始以每小时150-200℃的速度升到900℃,再以40-80℃升温到1400-1600℃时保持3-9小时,然后进行分阶段冷却:以每小时80-100℃冷却到1100℃保持3-5小时,再以每小时80-100℃冷却到900℃保持3-5小时,再以每小时80-110℃冷却到室温为止。
具体实施方式
下面结合具体实施例,进一步阐述本发明。应理解,这些实施例仅用于说明本发明而不用于限制本发明的范围。此外应理解,在阅读了本发明讲授的内容之后,本领域技术人员可以对本发明作各种改动或修改,这些等价形式同样落于本申请所附权利要求书所限定的范围。
实施例1
该制造电阻的方法,电阻材料由氧化锌、三氧化二铋、四氧化三钴、氧化亚镍、三氧化二铬、硝酸铝、银玻璃、聚乙烯醇和分散剂组成,其组分重量比为80%、1.5%、0.5%、2%、1%、1.5%、1%、2.5%,其余为分散剂,将以上材料按照以上组分配比添加到硝酸盐溶液中,接着经过充分混合、溶解、干燥、压制成型,最后在惰性气体气氛下从室温开始以每小时150℃的速度升到900℃,再以40℃升温到1400℃时保持3小时,然后进行分阶段冷却:以每小时80℃冷却到1100℃保持3小时,再以每小时80℃冷却到900℃保持3小时,再以每小时80℃冷却到室温为止。
实施例2
该制造电阻的方法,电阻材料由氧化锌、三氧化二铋、四氧化三钴、氧化亚镍、三氧化二铬、硝酸铝、银玻璃、聚乙烯醇和分散剂组成,其组分重量比为90%、0.5%、2%、1%、2.5%、0.5%、2.5%、0.5%,其余为分散剂,将以上材料按照以上组分配比添加到硝酸盐溶液中,接着经过充分混合、溶解、干燥、压制成型,最后在惰性气体气氛下从室温开始以每小时200℃的速度升到900℃,再以80℃升温到1600℃时保持9小时,然后进行分阶段冷却:以每小时100℃冷却到1100℃保持5小时,再以每小时100℃冷却到900℃保持5小时,再以每小时110℃冷却到室温为止。
实施例3
该制造电阻的方法,电阻材料由氧化锌、三氧化二铋、四氧化三钴、氧化亚镍、三氧化二铬、硝酸铝、银玻璃、聚乙烯醇和分散剂组成,其组分重量比为85%、1%、1.2%、1.5%、1.7%、1%、1.2%、1.5%,其余为分散剂,将以上材料按照以上组分配比添加到硝酸盐溶液中,接着经过充分混合、溶解、干燥、压制成型,最后在惰性气体气氛下从室温开始以每小时175℃的速度升到900℃,再以60℃升温到1500℃时保持6小时,然后进行分阶段冷却:以每小时90℃冷却到1100℃保持4小时,再以每小时90℃冷却到900℃保持4小时,再以每小时95℃冷却到室温为止。
通过以上方法制造的电阻,其满足了用户的需求,而降低了生产成本,有利于节能减排和资源的充分利用,本发明方法,工艺合理,得到的氧化锌电阻片成品率高,非线性系数高,保护性能好,热稳定性可靠。
Claims (2)
1.一种电阻的制造方法,电阻材料由氧化锌、三氧化二铋、四氧化三钴、氧化亚镍、三氧化二铬、硝酸铝、银玻璃、聚乙烯醇和分散剂组成,其组分重量比为80-90%、0.5-1.5%、0.5-2%、1-2%、1-2.5%、0.5-1.5%、1-2.5%、0.5-2.5%,其余为分散剂,其特征在于将以上材料按照以上组分配比添加到硝酸盐溶液中,接着经过充分混合、溶解、干燥、压制成型,最后在惰性气体气氛下从室温开始以每小时150-200℃的速度升到900℃,再以40-80℃升温到1400-1600℃时保持3-9小时,然后进行分阶段冷却:以每小时80-100℃冷却到1100℃保持3-5小时,再以每小时80-100℃冷却到900℃保持3-5小时,再以每小时80-110℃冷却到室温为止。
2.如权利要求1所述的电阻的制造方法,电阻材料由氧化锌、三氧化二铋、四氧化三钴、氧化亚镍、三氧化二铬、硝酸铝、银玻璃、聚乙烯醇和分散剂组成,其组分重量比为85%、1%、1.2%、1.5%、1.7%、1%、1.2%、1.5%,其余为分散剂,将以上材料按照以上组分配比添加到硝酸盐溶液中,接着经过充分混合、溶解、干燥、压制成型,最后在惰性气体气氛下从室温开始以每小时175℃的速度升到900℃,再以60℃升温到1500℃时保持6小时,然后进行分阶段冷却:以每小时90℃冷却到1100℃保持4小时,再以每小时90℃冷却到900℃保持4小时,再以每小时95℃冷却到室温为止。