CN104671675A - Glass marble with polished edges and manufacture method thereof - Google Patents
Glass marble with polished edges and manufacture method thereof Download PDFInfo
- Publication number
- CN104671675A CN104671675A CN201310607377.9A CN201310607377A CN104671675A CN 104671675 A CN104671675 A CN 104671675A CN 201310607377 A CN201310607377 A CN 201310607377A CN 104671675 A CN104671675 A CN 104671675A
- Authority
- CN
- China
- Prior art keywords
- glass
- reason
- stone
- edging
- edges
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Glass marble with polished edges is provided. The glass marble with the polished edges is toughened glass and comprises an upper surface, a lower surface and four sides; the four sides comprise at least one straight edge and a plurality of abnormal-shaped edges, and the number of the plurality of the abnormal-shaped edges is 1-3; the upper surface is provided with a UV colored painting or marbling, and the UV colored painting or marbling is sprayed and painted on the upper surface of the toughened glass by a UV ink. The glass marble with the polished edges is not easy to fade, has the advantages of high-temperature resistance, environmental protection, easy cleaning, relatively strong flintiness and aging resistance, can be used for a long time, is a best substitute for various stone materials, and is largely used for cooking benches, windowsills, stairs, stepped background walls, crystal steel door sheets, sliding doors, wall bricks, round tables, square tables, and glass products of indoor and outdoor plaques, exterior walls and other decoration industries. According to the requirements, the glass with corresponding thickness size is taken and used in different places.
Description
Technical field
The present invention relates to decoration field, particularly relate to a kind of glass with glass edging reason stone and manufacture method thereof.
Background technology
At present, the manufacture method with the glass reason stone of edging is mainly divided into following a few class: 1, be coated with synthetic glass paint at glass surface, allow paint flows form similar marmorean pattern.2, coat binding agent in the one side of glass, re-lay drawing paper, form the effect of one side Picture sticked with chunk glass.3, be transferred on glass surface with the paint picture of transfer printing.The reason of the glass with the edging stone colour image that this several method is produced is dull, and easily fades, and easy aging fracture.
Summary of the invention
The present invention is for solving the problem, and provide a kind of glass with edging to manage stone, it is fugitive color not, high temperature resistant, environmental protection, and flintiness is comparatively strong, can use for a long time.
Another object of the present invention is to provide a kind of method manufacturing this glass with edging reason stone.
Concrete, the invention provides a kind of glass with edging reason stone, the described reason of the glass with edging stone is toughened glass, it comprises upper surface, lower surface and four edges or rounded outer edge, described four edges comprises at least one straight flange and many special-edges, the quantity of described many heterotype edges is 1-3 bar, described upper surface is provided with UV colored drawing or reason shell stone patterns, and described UV colored drawing or reason shell stone patterns pass through the air brushing of UV ink on the upper surface of described toughened glass.
Manufacture a method for the above-mentioned glass with edging reason stone, it comprises the following steps:
S1: choose common glass and cut;
S2: carry out edging process to the four edges of the glass of well cutting, grinds at least one straight flange and many special-edges;
S3: the glass on milled limit is carried out tempering;
S4: spray transparent varnish on the upper surface of toughened glass, puts into combined padding and drying system by toughened glass after having sprayed transparent varnish and toasts;
S5: spray UV colored drawing pattern or reason shell stone patterns on varnish;
S6: spray white glass paint on UV colored drawing or reason shell stone patterns;
S7: after having sprayed white glass paint, puts into combined padding and drying system and carries out baking vanish by toughened glass.
Further, on varnish after air brushing UV colored drawing, monoblock toughened glass UV lamp is filtered.
Further, to be also included in white paint top sticky or scrape one deck and truly paint for described step 5.
Further, described true paint also can use texture paint, and sandstone or film replace.
Further, described heterotype edge is duckbilled limit, phoenix trailing edge, hypotenuse or round edge.
Further, the thickness of described toughened glass is 12mm---36mm.
Further, the thickness of described toughened glass is 3.6mm---22mm.
Further, finally at the attached layer of transparent film of glass surface heating tool.
Further, described transparent film can be crystal film or rubber type transparent film.
Glass with edging reason stone, not fugitive color of the present invention, high temperature resistant, environmental protection, flintiness is comparatively strong, can use for a long time, anti-aging, be the best substitute of various stone material, the present invention is in a large number for the kitchen range top, windowsill, stair, mark time, wall, brilliant steel casement door plate, sliding door, wall brick, round table, square table, indoor and outdoor board, the glasswork of the decoration industries such as exterior wall.
Embodiment
Below in conjunction with embodiment, the present invention is further explained,
In the present invention, after upper surface refers to glass reason stone finished product, the surface of user's naked eyes viewing, lower surface refers to the reverse side of upper surface.
A kind of reason of the glass with edging stone, should be toughened glass with the glass reason stone of edging, it comprises upper surface, lower surface and four edges or rounded outer edge, described four edges comprises at least one straight flange and many special-edges, the quantity of described many heterotype edges is 1-3 bar, described upper surface arranges reasonable shell stone patterns, and described reason shell stone patterns passes through the air brushing of UV ink on the upper surface of described toughened glass.
Embodiment 1
The step made with the glass reason stone of edging is as follows:
S1: choose common glass and cut;
S2: carry out edging process to the four edges of the glass of well cutting, grinds at least one straight flange and three special-edges;
S3: the glass on milled limit is carried out tempering;
S4: spray transparent varnish on the upper surface of toughened glass, puts into combined padding and drying system by toughened glass after having sprayed varnish and toasts;
S5: spray UV colored drawing pattern or reason shell stone patterns on varnish;
S6: spray white glass paint on UV colored drawing or reason shell stone patterns;
S7: after having sprayed white glass paint, puts into combined padding and drying system and carries out baking vanish by toughened glass.
Further, on varnish after air brushing UV colored drawing, monoblock toughened glass UV lamp is filtered.
Further, to be also included in white paint top sticky or scrape one deck and truly paint for step 5.
Further, heterotype edge is duckbilled limit.One straight flange contacts metope in use.Heterotype edge does not contact metope.
Further, the thickness of toughened glass is 3.6mm.
Embodiment 2
The step made with the glass reason stone of edging is as follows:
S1: choose common glass and cut;
S2: carry out edging process to the four edges of the glass of well cutting, grinds a straight flange and three special-edges;
S3: the glass on milled limit is carried out tempering;
S4: spray transparent varnish on the upper surface of toughened glass, puts into combined padding and drying system by toughened glass after having sprayed varnish and toasts;
S5: spray UV colored drawing pattern or reason shell stone patterns on varnish;
S6: spray white glass paint on UV colored drawing or reason shell stone patterns;
S7: after having sprayed white glass paint, puts into combined padding and drying system and carries out baking vanish by toughened glass.
Further, on varnish after air brushing UV colored drawing, monoblock toughened glass UV lamp is filtered.
Further, to be also included in white paint top sticky or scrape one deck texture paint for step 5.
Further, heterotype edge is phoenix trailing edge.In use, a straight flange contact metope.
Further, the thickness of toughened glass is 22mm.
Last at the attached layer of transparent film of glass surface heating tool.
Described transparent film can be crystal film or rubber type transparent film.
Embodiment 3
The step made with the glass reason stone of edging is as follows:
S1: choose common glass and cut;
S2: carry out edging process to the four edges of the glass of well cutting, grinds a rounded outer edge;
S3: the glass on milled limit is carried out tempering;
S4: spray transparent varnish on the upper surface of toughened glass, puts into combined padding and drying system by toughened glass after having sprayed varnish and toasts;
S5: spray UV colored drawing pattern or reason shell stone patterns on varnish;
S6: spray white glass paint on UV colored drawing or reason shell stone patterns;
S7: after having sprayed white glass paint, puts into combined padding and drying system and carries out baking vanish by toughened glass.
Further, on varnish after air brushing UV colored drawing, monoblock toughened glass UV lamp is filtered.
Further, to be also included in white paint top sticky or scrape one deck sandstone for step 5.
Further, the thickness of toughened glass is 16mm.
Last at the attached layer of transparent film of glass surface heating tool.
Transparent film can be crystal film or rubber type transparent film.
Embodiment 4
S1: choose common glass and cut;
S2: carry out edging process to the four edges of the glass of well cutting, grinds four straight flanges.
S3: the glass on milled limit is carried out tempering;
S4: spray transparent varnish on the upper surface of toughened glass, puts into combined padding and drying system by toughened glass after having sprayed varnish and toasts;
S5: spray UV colored drawing pattern or reason shell stone patterns on varnish;
S6: spray white glass paint on UV colored drawing or reason shell stone patterns;
S7: after having sprayed white glass paint, puts into combined padding and drying system and carries out baking vanish by toughened glass.
Further, on varnish after air brushing UV colored drawing, monoblock toughened glass UV lamp is filtered.
Further, to be also included in white paint top sticky or scrape a skim for described step 5.
Further, the thickness of described toughened glass is 36mm.
Last at the attached layer of transparent film of glass surface heating tool.
Transparent film can be crystal film.
In another embodiment, first choose common glass to cut;
Edging process is carried out to the four edges of the glass of well cutting, grinds four straight flanges.
The glass on milled limit is carried out tempering;
The upper surface of toughened glass sprays transparent varnish, after having sprayed varnish, colored drawing pattern or reason shell stone patterns is sprayed on varnish, filters with UV lamp, enter combined padding and drying system baking, and then spray one deck varnish, enter combined padding and drying system baking, produce bright glass reason stone.Produce bright glass reason stone.
Glass with edging reason stone, not fugitive color of the present invention, high temperature resistant, environmental protection, flintiness is comparatively strong, can use for a long time, anti-aging, be the best substitute of various stone material, the present invention is in a large number for the kitchen range top, windowsill, stair, mark time, wall, brilliant steel casement door plate, sliding door, wall brick, round table, square table, indoor and outdoor board, the glasswork of the decoration industries such as exterior wall.As requested, get the glass of respective thickness size, be used in different places.
Person of ordinary skill in the field is to be understood that: when not departing from ultimate principle of the present invention; can carry out various amendment, retouching, combination, supplement or the replacement of technical characteristic the present invention, these equivalent substitute modes or obviously mode of texturing all fall among protection scope of the present invention.
Claims (10)
1. the reason of the glass with an edging stone, it is characterized in that: the described reason of the glass with edging stone is toughened glass, it comprises upper surface, lower surface and four edges or rounded outer edge, described four edges comprises at least one straight flange and many special-edges, the quantity of described many heterotype edges is 1-3 bar, described upper surface is provided with UV colored drawing or reason shell stone patterns, described UV colored drawing or reason shell stone patterns pass through the air brushing of UV ink on the upper surface of described toughened glass.
2. the reason of the glass with edging stone according to claim 1, is characterized in that: described heterotype edge is duckbilled limit, phoenix trailing edge, hypotenuse or round edge.
3. the reason of the glass with edging stone according to claim 1, is characterized in that: the thickness of described toughened glass is 12mm---36mm.
4. the reason of the glass with edging stone according to claim 3, is characterized in that: the thickness of described toughened glass is 3.6mm---22mm.
5. a method for the reason of the glass with the edging stone described in manufacturing claims 1, is characterized in that: it comprises the following steps:
S1: choose common glass and cut;
S2: carry out edging process to the four edges of the glass of well cutting, grinds at least one straight flange and many special-edges;
S3: the glass on milled limit is carried out tempering;
S4: spray transparent varnish on the upper surface of toughened glass, puts into combined padding and drying system by toughened glass after having sprayed transparent varnish and toasts;
S5: spray UV colored drawing pattern or reason shell stone patterns on varnish;
S6: spray white glass paint on UV colored drawing or reason shell stone patterns;
S7: spraying after glass lacquer, puts into combined padding and drying system and carries out baking vanish by toughened glass.
6. manufacture according to claim 5 with edging glass reason stone method, it is characterized in that: on varnish air brushing UV colored drawing or reason shell stone patterns after, monoblock toughened glass UV lamp is filtered.
7. manufacture according to claim 5 is with the method for the glass reason stone of edging, it is characterized in that: it is sticky or scrape one deck and truly paint that described step 5 is also included in white paint top.
8. manufacture according to claim 7 is with the method for the glass reason stone of edging, and it is characterized in that: described true paint also can use texture paint, sandstone or film replace.
9. manufacture according to claim 5 is with the method for the glass reason stone of edging, it is characterized in that: last at the attached layer of transparent film of glass surface heating tool.
10. manufacture according to claim 9 is with the method for the glass reason stone of edging, it is characterized in that: described transparent film can be crystal film or rubber type transparent film.